CN101358023A - Transparent anti static flame-retardant glass fibre reinforced plastic material - Google Patents
Transparent anti static flame-retardant glass fibre reinforced plastic material Download PDFInfo
- Publication number
- CN101358023A CN101358023A CNA2007100444695A CN200710044469A CN101358023A CN 101358023 A CN101358023 A CN 101358023A CN A2007100444695 A CNA2007100444695 A CN A2007100444695A CN 200710044469 A CN200710044469 A CN 200710044469A CN 101358023 A CN101358023 A CN 101358023A
- Authority
- CN
- China
- Prior art keywords
- grams
- reinforced plastic
- gram
- retardant
- static
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a glass fiber reinforced plastic material, in particular to a transparent anti-static flame-retardant glass fiber reinforced plastic material. The transparent anti-static flame-retardant glass fiber reinforced plastic material contains glass fiber and anti-static flame-retardant colloid, wherein, the anti-static flame-retardant colloid contains the components with the following portions: 70 to 90 grams of styrenated alkyd, 10 to 30 grams of methyl methacrylate, 0.25 grams of benzoyl peroxide, 4.2 to 5.4 grams of cobalt bis(2-ethylhexanoate), 4.2 to 5.4 grams of calcium carbonate, 4.2 to 5.4 grams of titanium pigment and 8 to 10 grams ofanti-static agent. The technical proposal adopted by the invention completely overcomes the shortcomings of the prior glass fiber reinforced plastic products, the glass fiber reinforced plastic is not only flame-retardant, but also anti-static and transparent, and can meet the needs in special fields.
Description
Technical field
The present invention relates to glass-reinforced plastic material, particularly a kind of glass-reinforced plastic material of transparent anti static flame-retardant.
Background technology
Glass-reinforced plastic material not only is applied to all respects as building materials owing to have physical propertys such as lightweight, high-strength, anticorrosion, insulation, sound insulation, and is applied to leading-edge field such as Aeronautics and Astronautics.But existing glass reinforced plastic can not satisfy the needs of Aeronautics and Astronautics fully, can't buy from the market such as anti-electrostatic, fire-retardant and transparent glass fiber reinforced plastics.
Summary of the invention
The objective of the invention is to overcome the deficiency of present fibre glass product manufacture, a kind of anti-electrostatic, fire-retardant and transparent glass fiber reinforced plastics are provided.
The technical scheme that realizes the object of the invention is: a kind of glass-reinforced plastic material of transparent anti static flame-retardant, comprise glass fibre and anti-static inflaming-retarding colloid, wherein, each composition of anti-static inflaming-retarding colloid and consisting of:
Styrene alkyd resin 70-90 gram
Methyl methacrylate 10-30 gram
Benzoyl peroxide 0.25 gram
Cobalt iso-octoate 4.2-5.4 gram
Lime carbonate 4.2-5.4 gram
Titanium dioxide 4.2-5.4 gram
Antistatic agent ASA-150 8-10 gram
Fire retardant 8-10 gram
Preferably, described fire retardant is a kind of in aluminium hydroxide and the magnesium hydroxide.
Owing to adopted above-mentioned technical solution, solved the deficiency of present fibre glass product manufacture fully, make glass reinforced plastic not only fire-retardant, and anti-electrostatic, transparent, make it can satisfy the needs in the field of special procuring.
Embodiment
Below the present invention is described in further detail.
A kind of glass-reinforced plastic material of transparent anti static flame-retardant comprises glass fibre and anti-static inflaming-retarding colloid, described each composition of anti-static inflaming-retarding colloid and consisting of:
Styrene alkyd resin 70-90 gram
Methyl methacrylate 10-30 gram
Benzoyl peroxide 0.25 gram
Cobalt iso-octoate 4.2-5.4 gram
Lime carbonate 4.2-5.4 gram
Titanium dioxide 4.2-5.4 gram
Antistatic agent ASA-150 8-10 gram
Fire retardant 8-10 gram
Preferably, described fire retardant is a kind of in aluminium hydroxide and the magnesium hydroxide.
Embodiment 1
Styrene alkyd resin 70 grams
Methyl methacrylate 30 grams
Benzoyl peroxide 0.25 gram
Cobalt iso-octoate 4.2 grams
Lime carbonate 4.2 grams
Titanium dioxide 4.2 grams
Antistatic agent ASA-150 8 grams
Aluminium hydroxide or magnesium hydroxide 8 grams
Compound method is: similar normal temperature mixes by the weight of above-mentioned styrene alkyd resin, methyl methacrylate and benzoyl peroxide down, adds antistatic agent and fire retardant aluminium hydroxide under continuously stirring.At normal temperatures the anti-static inflaming-retarding colloid is applied on the glass fibre, normal temperature curing down gets final product.
Embodiment 2
Styrene alkyd resin 90 grams
Methyl methacrylate 10 grams
Benzoyl peroxide 0.25 gram
Cobalt iso-octoate 5.4 grams
Lime carbonate 5.4 grams
Titanium dioxide 5.4 grams
Antistatic agent ASA-150 10 grams
Aluminium hydroxide or magnesium hydroxide 10 grams
Compound method is: similar normal temperature mixes by the weight of above-mentioned styrene alkyd resin, methyl methacrylate and benzoyl peroxide down, adds antistatic agent and fire retardant aluminium hydroxide or magnesium hydroxide under continuously stirring.At normal temperatures the anti-static inflaming-retarding colloid is applied on the glass fibre, normal temperature curing down gets final product.
Embodiment 3
Styrene alkyd resin 80 grams
Methyl methacrylate 20 grams
Benzoyl peroxide 0.25 gram
Cobalt iso-octoate 4.8 grams
Lime carbonate 4.8 grams
Titanium dioxide 4.8 grams
Antistatic agent ASA-150 9 grams
Aluminium hydroxide or magnesium hydroxide 9 grams
Compound method is: similar normal temperature mixes by the weight of above-mentioned styrene alkyd resin, methyl methacrylate and benzoyl peroxide down, adds antistatic agent and fire retardant aluminium hydroxide or magnesium hydroxide under continuously stirring.At normal temperatures the anti-static inflaming-retarding colloid is applied on the glass fibre, normal temperature curing down gets final product.
Above embodiment is only for the usefulness that the present invention is described, but not limitation of the present invention, person skilled in the relevant technique, under the situation that does not break away from the spirit and scope of the present invention, can also make various conversion or modification, therefore all technical schemes that are equal to also should belong to category of the present invention, should be limited by each claim.
Claims (2)
1, a kind of glass-reinforced plastic material of transparent anti static flame-retardant comprises glass fibre and anti-static inflaming-retarding colloid, it is characterized in that each composition of anti-static inflaming-retarding colloid and consisting of:
Styrene alkyd resin 70-90 gram
Methyl methacrylate 10-30 gram
Benzoyl peroxide 0.25 gram
Cobalt iso-octoate 4.2-5.4 gram
Lime carbonate 4.2-5.4 gram
Titanium dioxide 4.2-5.4 gram
Antistatic agent ASA-150 8-10 gram
Fire retardant 8-10 gram.
2, the glass-reinforced plastic material of transparent anti static flame-retardant according to claim 1 is characterized in that, described fire retardant is a kind of in aluminium hydroxide and the magnesium hydroxide.