CN101337373A - 荻草中密度纤维板的制造方法 - Google Patents

荻草中密度纤维板的制造方法 Download PDF

Info

Publication number
CN101337373A
CN101337373A CNA200810019073XA CN200810019073A CN101337373A CN 101337373 A CN101337373 A CN 101337373A CN A200810019073X A CNA200810019073X A CN A200810019073XA CN 200810019073 A CN200810019073 A CN 200810019073A CN 101337373 A CN101337373 A CN 101337373A
Authority
CN
China
Prior art keywords
medium density
mdf
grass
hot pressing
fibre board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA200810019073XA
Other languages
English (en)
Other versions
CN101337373B (zh
Inventor
邓玉和
王伟
朱典想
黄豪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Forestry University
Original Assignee
Nanjing Forestry University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Forestry University filed Critical Nanjing Forestry University
Priority to CN200810019073XA priority Critical patent/CN101337373B/zh
Publication of CN101337373A publication Critical patent/CN101337373A/zh
Application granted granted Critical
Publication of CN101337373B publication Critical patent/CN101337373B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是涉及木材加工工艺领域的一项技术发明，它是以禾本植物——荻草生产中密度纤维板的制造方法。以荻草为植物纤维原料，经切断粉碎、纤维分离、纤维施加脲醛树脂等胶粘剂、防水剂和其它添加剂后在干燥机中干燥到含水率7％－11％，经铺装机铺装成厚度、密度均匀的板坯，在单层和多层平板热压机中热压等工序制成中密度纤维板。本发明制备的荻草纤维形态完整、均匀，制造的中密度板成本低、强度高，制品的物理力学性能达到国家相关标准的要求，游离甲醛释放量达到E1级标准要求。本发明把废弃的荻草资源加以利用生产高附加值的产品。

Description

荻草中密度纤维板的制造方法
一、技术领域
本发明公开了一种利用禾本植物-荻草经专用的粉碎机粉碎，制成一定尺寸的秆状荻草，采用平板加压的方式生产加工中密度纤维板的方法。其主要技术特征为：利用脲醛树脂等胶粘剂生产荻草中密度纤维板。
二、技术背景
由于各国对环境及森林资源的保护，木材资源的短缺，使人造板生产所用的木材原料愈来愈缺乏，但社会对人造板的需求却在日益增大，因此利用各种原料生产人造板是世界各国研究的前沿。利用禾本植物生产人造板是国内外关注的重点。荻草植物属于禾本科荻属(Triarrhena)，按其生长的地理位置不同可分为荻和南荻，分布广泛。荻草属多年生植物，砍伐后来年生长更好，因此产量高，可以满足工厂大批量的需求。秆状荻草经分离后纤维得率高、形态好，可根据不同的使用要求生产出不同密度的中密度纤维板。其产品性能稳定，强度高变异性小。用脲醛树脂等胶粘剂生产的荻草中密度纤维板的性能能与木材生产的中密度纤维板媲美。其产品可应用于家具、建筑装修、地板等领域，因此使用荻草生产中密度纤维板具有丰富资源优势和广阔的应用前景。
三、发明内容
1.发明的目的
本发明的目的在于把废弃的荻草资源加以利用变废为宝，提高荻草的利用价值。保护湖区的生态环境和生态平衡，同时有利于天然林资源的保护。打开了用脲醛树脂胶粘剂生产秸秆类人造板的新篇章。利用低成本的荻草生产高附加值的产品。
2.技术方案
本发明涉及的是用禾本植物-荻草生产中密度纤维板的方法，它的工艺步骤：
(1)备料：专用的粉碎机将荻草打碎，经筛选去除原料中的泥沙等杂质，制成一定尺寸的秆状荻草；
(2)在150-180℃的高压蒸煮罐中蒸煮软化5-10分钟，然后在热磨机中分离成纤维。石蜡的添加量为1.0-1.8％；胶粘剂的添加量为12-16％；固化剂施加量为固体胶量的0.6-1.0％；生产功能性中密度纤维板时施加其它添加剂；
(3)干燥：荻草纤维在管道干燥机中干燥，干燥温度为130℃-180℃，干燥后荻草纤维的终含水率为7％-11％；
(4)铺装和预压：采用真空机械或真空气流铺装机进行铺装，铺装后板坯密度、厚度均匀并进行预压；
(5)热压：采用单层或多层平板热压机，热压温度为160-220℃，热压时间为15-40S/mm，热压压力：中密度纤维板为2.5-7MPa，板密度为0.45-0.88g/cm3；
(6)后期处理：热压后的板材在常温下冷却、裁边，存放48-72小时后进行砂光，制成荻草中密度纤维板。
本发明的优点：制造方法简单易行，可以变废为宝，提高荻草利用价值，制成的荻草中密度纤维板成本低，强度大。产品可以应用在家具、建筑装修、地板等行业。
四、具体实施方式
实施例1：
下面结合实例对本发明进行详细描述。但发明不限所给出的例子。
(1)粉碎机将荻草打碎，筛选出泥沙、细小原料等，制得的秆状荻草尺寸为长30-100mm，宽1.4-3.3mm；
(2)在160℃的预热蒸煮罐中蒸煮8分钟，经热磨机分离成纤维。石蜡的添加量为1.5％；胶粘剂的添加量为14％；固化剂施加量为固体胶量的0.8％；
(3)荻草纤维在管道干燥机中干燥，干燥温度为160℃，干燥后荻草纤维的终含水率为9％；
(4)采用真空机械铺装机进行铺装，铺装成密度、厚度均匀的板坯，预压压力200N/mm；
(5)采用多层平板热压机，热压温度为180℃，热压时间为20S/mm，热压压力3.0MPa；
(6)热压后的板材在常温下冷却、裁边，存放48小时后，测定荻草中密度纤维板的性能。
性能指标如下：
密度：        0.75g/cm3
内结合强度：  1.1MPa
静曲强度：    32.0MPa
弹性模量：    4669MPa

Claims (2)

1、荻草中密度纤维板的制造方法，其特征是它的工艺步骤分：
(1)备料：专用的粉碎机将荻草打碎，经筛选去除细小原料、泥沙等杂质，制成长30-100mm，宽1.4-3.3mm的秆状荻草；
(2)在150-180℃的蒸煮罐中蒸煮软化5-10分钟，然后在热磨机中分离成纤维。石蜡的添加量为1.0-1.8％；胶粘剂的添加量为12-16％；固化剂施加量为固体胶量的0.6-1.0％；生产功能性中密度纤维板时施加其它添加剂；
(3)干燥：荻草纤维在管道干燥机中干燥，干燥温度为130℃-180℃，干燥后荻草纤维的终含水率为7％-11％；
(4)铺装和预压：采用真空机械或真空气流铺装机进行铺装，铺装后板坯密度、厚度均匀并进行预压；
(5)热压：采用单层或多层平板热压机，热压温度为160-220℃，热压时间为15-40S/mm，热压压力：为2.5-7MPa，板的密度为0.45-0.88g/cm3；
(6)后期处理：热压后的板材在常温下冷却、裁边，存放48-72小时后进行砂光，制成荻草中密度纤维板。
2、权利要求1所述的方法，其特征是这种荻草中密度纤维板的胶粘剂可根据使用场合不同，选择无醛胶用于室内或防水胶用于室内外；适用于所有荻属的茎秆、叶和根茎所制成的中密度纤维板。
CN200810019073XA 2008-01-11 2008-01-11 荻草中密度纤维板的制造方法 Expired - Fee Related CN101337373B (zh)