CN101328082B - Manufacturing process of high pure negative ion far infrared multifunctional ceramic glaze additive - Google Patents
Manufacturing process of high pure negative ion far infrared multifunctional ceramic glaze additive Download PDFInfo
- Publication number
- CN101328082B CN101328082B CN200810016474A CN200810016474A CN101328082B CN 101328082 B CN101328082 B CN 101328082B CN 200810016474 A CN200810016474 A CN 200810016474A CN 200810016474 A CN200810016474 A CN 200810016474A CN 101328082 B CN101328082 B CN 101328082B
- Authority
- CN
- China
- Prior art keywords
- additive
- ceramic
- negative ion
- far infrared
- high pure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a preparation technology of a high pure negative ion far infrared multifunctional ceramic glaze additive belonging to the ceramic material preparation field, which comprises the following steps: putting chongguang stone-containing high pure negative ion far infrared multifunctional additive in a shuttle kiln, calcining and modifying the additive at a high temperature of 1100-1300 DEG C for 3-5 hours, taking the additive out when the temperature is cooled to room temperature, finally transforming into high pure negative ion far infrared multifunctional ecological antibacterial healthy ceramic glaze additive. The additive of the invention can make the ceramic glaze finish better and the self-cleaning performance stronger. The ceramic surface can permanently release negative ions to remove the harmful gases such as benzene, formaldehyde, ammonia, TDI or organic volatile and peculiar smell such as smoke smell and odor. The preparation technology can make each ceramic to have more multifunction, the glaze surface whiter than jade, which makes the price of the ceramic doubling.
Description
Technical field
The invention belongs to the preparation field of Ceramic Material, be specifically related to a kind of admixture of anti-chemistry, physics or the biological attack of in ceramic glaze, adding.
Background technology
In the modern society, indoor pollution serious threat human beings'health.Indoor pollution mainly is meant from the formaldehyde of architectural decoration material production, benzene, ammonia, radon; Indoor household electrical equipment hertzian wave and radiation; The burning of coal, liquefied gas, Sweet natural gas etc.; Fry in shallow oil and fry the smog that produces in high-temperature cooking such as baking course of processing; Family dotes on pollutents such as on one's body virus, bacterium and destroys the family daily life environment, influences health of people.The raising of Along with people's standard of living and life taste, people are to the environment optimization and the purification growing interest of public place, living space, daily life and medical facilities.Ceramic is used more and more widely in people's life, advantage such as though traditional health-care ceramic glaze has anti-water, smooth, be prone to clean, attractive in appearance, do not have antibiotic, antibacterial, purify air and multinomial functional character such as health-care effect.On the market, panoramic crockery various shapes, moist, color is bright and beautiful and be convenient to clean, and is the first-selection that most families buy tableware.The application of ceramic is very general in family and the public place, and floor, wall, tableware etc. generally adopt ceramic.But the colored glaze on the ceramic surface but might become healthy killer.Lead in the colored glaze, mercury, radium, cadmium etc. all are insalubrious elements.Radioactive element radium can kill and wound white corpuscle.When using underproof ceramic product, these objectionable impuritiess can strippings, and along with food gets into human body, the time one is long, can cause chronic poisoning.Moreover some ceramic, for example floor has very big radioactivity, and serious harm common people are healthy.How to utilize these ceramics to come environment purification to become the relevant industries problem demanding prompt solution.
Summary of the invention
In order to overcome the deficiency of prior art, the present invention provides the manufacture craft of high pure negative ion far infrared multifunctional ceramic glaze additive, and the additive that goes out through this explained hereafter can discharge negative ion, has very strong health-care effect.
The technical scheme that the present invention solves its technical problem employing is: the manufacture craft of design high pure negative ion far infrared multifunctional ceramic glaze additive; It is characterized in that being undertaken by following process step: the high pure negative ion far infrared multifunctional additive that will contain Chong Guangshi is put into shuttle kiln; Be to carry out high-temperature roasting modification in 3-5 hour under 1100 ℃-1300 ℃ the environment in temperature; Take out after being cooled to normal temperature, convert high pure negative ion far infrared multifunctional ecological antibiotic health care ceramic glaze additive at last to.
The beneficial effect that the present invention had is:
1. the present invention can make various potteries have more multifunctionality; Glaze light more is tender as beautiful, has a sudden rise in social status, according to ceramic different in kind; Receive temperature different; Proportioning is different, and addition is different, can be widely used in various potteries such as ground, architectural pottery room wall brick, decorative art brick, high-grade bone china, magnesium-intensified ceramic, aluminium strengthening ceramic, high ceramic whiteware, sanitary ware, bathtub.Coming into operation of it will bring a new revolution to world's ceramics, for human health is made immeasurable contribution.
2. it is better that the present invention can make Ceramic glaze smooth finish; Self-cleaning property is stronger, because of containing the high pure negative ion far infrared multifunctional additive, can make ceramic surface forever discharge negative ion; Dispel indoor benzene, formaldehyde, ammonia, TDI or organic volatile, and obnoxious flavour and peculiar smell such as smoke, stink; Can be emitting far-infrared, emittance is 0.91, stimulates circulation; Sterilizing rate to intestinal bacteria, streptococcus aureus, Pseudomonas aeruginosa and Candida albicans reaches more than 90%.The ceramic glaze additive of our company's invention can play the effect that purifies air; Particularly contain trace elements such as " germanium " and " strontium "; Can suppress to kill the human cancer cell; Enhancing human immune is encouraged skeleton, dental growth, and can be prevented and treated many-sided medical health care functions such as coronary heart disease, hypertension, delaying decrepitude of skin.
3. the present invention can be used for producing series such as sanitary china, wall floor tile and finishing communal facility, family room, kitchen, bathroom, sweat-steaming house, Saunas, medical health facility.
Embodiment
Embodiment one
The high pure negative ion far infrared multifunctional additive that will contain Chong Guangshi is put into shuttle kiln; Be to carry out high-temperature roasting modification in 4 hours under 1100 ℃ the environment in temperature; Take out after being cooled to normal temperature; Its loss on ignition reaches 30%, converts high pure negative ion far infrared multifunctional ecological antibiotic health care ceramic glaze additive at last to.With the pottery of this additive according to different properties, specification, kind, add mix grinding in the different ceramic glazes to according to different ratios, just can be used for going in the various potteries.Through test and the detection authentication of wall brick over the ground of national authority feeler mechanism, pottery ground wall brick glaze adds the ground wall brick that this additive is fired by 8% mass ratio, and every square centimeter of per second discharges 506 in negative ion.In the present embodiment, comprise Chong Guangshi and Tourmaline in the high pure negative ion far infrared multifunctional additive, the ratio content of Chong Guangshi and Tourmaline is looked different situations and is decided.Chong Guang stone of the present invention is a kind of paleontological fossil.Its surface is the micropore shape, and Mohs' hardness is 3.4-4, and density is about 3.7g/cm
3, the Qinghai-Tibet Platean of originating from China is regional.Be commonly called as paradise stone again in areas such as Tibet.
Embodiment two
Compare with embodiment one, in the present embodiment, the temperature of shuttle kiln is 1300 ℃, and the time of high-temperature roasting is 3 hours.All the other are identical with embodiment one, no longer statement.
Embodiment three
Compare with embodiment one, in the present embodiment, the temperature of shuttle kiln is 1200 ℃, and the time of high-temperature roasting is 5 hours.All the other are identical with embodiment one, no longer statement.
Claims (1)
1. the manufacture craft of high pure negative ion far infrared multifunctional ceramic glaze additive; It is characterized in that being undertaken by following process step: the high pure negative ion far infrared multifunctional additive that will contain Chong Guangshi is put into shuttle kiln; Be to carry out high-temperature roasting modification in 3-5 hour under 1100 ℃-1300 ℃ the environment in temperature; Take out after being cooled to normal temperature, convert high pure negative ion far infrared multifunctional ecological antibiotic health care ceramic glaze additive at last to.