CN101274816A - 硼硅酸盐玻璃组成物 - Google Patents

硼硅酸盐玻璃组成物 Download PDF

Info

Publication number
CN101274816A
CN101274816A CNA2007100909692A CN200710090969A CN101274816A CN 101274816 A CN101274816 A CN 101274816A CN A2007100909692 A CNA2007100909692 A CN A2007100909692A CN 200710090969 A CN200710090969 A CN 200710090969A CN 101274816 A CN101274816 A CN 101274816A
Authority
CN
China
Prior art keywords
glass
borosilicate glass
percent
pyrex
constituent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007100909692A
Other languages
English (en)
Other versions
CN101274816B (zh
Inventor
林忠义
林资智
彭正道
尹昭贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
United Oriental Glass Industries Co Ltd
Original Assignee
United Oriental Glass Industries Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by United Oriental Glass Industries Co Ltd filed Critical United Oriental Glass Industries Co Ltd
Priority to CN2007100909692A priority Critical patent/CN101274816B/zh
Publication of CN101274816A publication Critical patent/CN101274816A/zh
Application granted granted Critical
Publication of CN101274816B publication Critical patent/CN101274816B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种硼硅酸盐玻璃组成物,其热膨胀系数α(20-300℃)是2.7×10-6/℃,玻璃转化温度Tg是526℃,主要成分依重量比例为SiO2 81.8%、Al2O3 2.25%、Na2O 3.3%、B2O3 12.5%及0.15%的其它玻璃添加成分。

Description

硼硅酸盐玻璃组成物
技术领域
本发明属于玻璃技术领域,更详而言之是指一种抗热性、耐化学腐蚀性及电绝缘性较好的硼硅酸盐玻璃组成物。
背景技术
现有硼硅酸盐玻璃是具有低热膨胀系数的玻璃,其抗热性、耐化学腐蚀性及电绝缘性均甚佳,因此广泛应用于实验室器具、望远镜镜片、投影机反射镜等用品。一般广为业界熟知的硼硅酸盐玻璃的种类中,最负盛名的是派瑞克斯玻璃(Pyrex glass),派瑞克斯玻璃是1915年美国康宁公司(Corning)研制成功的,其商业编号有Pyrex 7740、7760、7250、7070等类型,Pyrex7740具有与硅(Si)非常接近的热膨胀系数而广被采用,其成分大约为:SiO2 81%,Al2O3 2%,Na2O4%,B2O3 13%,热膨胀系数α(20-300℃)是3.25×10-6/℃左右,玻璃转化温度Tg是500℃左右。
虽然派瑞克斯玻璃目前仍应用得十分广泛,但是,随着所应用的产品功能的提升,其抗热性渐渐无法满足需求(如投影机亮度提升将使得反射镜受热产生的温度更高)。而欲提升玻璃的抗热性,必须同时使得玻璃材料的热膨胀系数足够低、玻璃转化温度足够高。
发明内容
本发明的主要目的在于提供一种硼硅酸盐玻璃组成物,其热膨胀系数较派瑞克斯玻璃更低,而玻璃转化温度数值更高,因此,该硼硅酸盐玻璃组成物抗热性更好,可取代派瑞克斯玻璃而应用于需要更好的抗热性的产品。
为了达到上述目的,本发明采用下述技术方案:
一种硼硅酸盐玻璃组成物,其热膨胀系数α(20-300℃)是2.7×10-6/℃,玻璃转化温度Tg是526℃,主要成分依重量比例如下:SiO2 81.8%、Al2O3 2.25%、Na2O 3.3%、B2O3 12.5%及其它玻璃添加成分0.15%。
由于采用了上述技术方案,本发明所提供的硼硅酸盐玻璃组成物,其热膨胀系数α(20-300℃)为2.7×10-6/℃,玻璃转化温度Tg为526℃,其热膨胀系数较常见的派瑞克斯玻璃(Pyrex 7740、7070)低,而玻璃转化温度数值更高,因此,该硼硅酸盐玻璃组成物抗热性更好,可取代派瑞克斯玻璃应用于需要更好的抗热性的产品。
具体实施方式
下面举一较佳实施例对本发明做进一步的详细说明:
实施例1
本发明所述的硼硅酸盐玻璃组成物,其热膨胀系数α(20-300℃)是2.7×10-6/℃,玻璃转化温度Tg是526℃,由二氧化硅(SiO2)、氧化铝(Al2O3)、氧化硼(B2O3)、氧化钠(Na2O)及其它玻璃添加成分所组成,各主要成分的重量比例如下:
SiO2   81.8%
Al2O3  2.25%
Na2O   3.3%
B2O3   12.5%及
其它玻璃添加成分0.15%。
前述其它玻璃添加成分指氧化镁(MgO)、氧化钙(CaO)、氧化钾(K2O)、氧化铁(Fe2O3)、氧化锑(TiO2)、氧化锆(ZrO2)及氯(Cl)等成分。
本发明所述的硼硅酸盐玻璃组成物中的Na2O较派瑞克斯玻璃少,相对地SiO2与Al2O3就会多一些。本发明所述的硼硅酸盐玻璃组成物并未因Na2O减量而造成熔炼与玻璃产品成型上的困难,与派瑞克斯玻璃相比,具有更低的热膨胀系数与更高的玻璃转化温度。
综上所述,本发明所提供的硼硅酸盐玻璃组成物,其热膨胀系数α可低至2.7×10-6/℃,而玻璃转化温度Tg可达526℃,其抗热性显然较派瑞克斯玻璃更好,甚具实用价值。
以上所述,仅为本发明的较佳实施例而已,并非用于限定本发明的保护范围。

Claims (2)

1. 一种硼硅酸盐玻璃组成物,其热膨胀系数α(20-300℃)是2.7×10-6/℃,玻璃转化温度Tg是526℃,主要成分依重量比例如下:
SiO2    81.8%
Al2O3   2.25%
Na2O    3.3%
B2O3    12.5%及
其它玻璃添加成分0.15%。
2. 如权利要求1所述的硼硅酸盐玻璃组成物,其特征在于,所述的玻璃添加成分包含MgO、CaO、K2O、Fe2O3、TiO2、ZrO2及Cl。
CN2007100909692A 2007-03-29 2007-03-29 硼硅酸盐玻璃组成物 Expired - Fee Related CN101274816B (zh)