CN101255377A - 超薄铝箔板水基冲压拉伸油及生产方法 - Google Patents
超薄铝箔板水基冲压拉伸油及生产方法 Download PDFInfo
- Publication number
- CN101255377A CN101255377A CNA2008100111386A CN200810011138A CN101255377A CN 101255377 A CN101255377 A CN 101255377A CN A2008100111386 A CNA2008100111386 A CN A2008100111386A CN 200810011138 A CN200810011138 A CN 200810011138A CN 101255377 A CN101255377 A CN 101255377A
- Authority
- CN
- China
- Prior art keywords
- ultra
- aluminum foil
- foil plate
- thin aluminum
- drawing oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种润滑及冷却性能好,可防止冲压工件表面出现划伤、锈蚀,可保证表面光洁度、清洁度以满足直接装配要求且脱模容易的超薄铝箔板水基冲压拉伸油及生产方法。所用原料及重量百分比是植酸0.4~0.6%、苯甲酸钠1.4~1.8%、三乙醇胺2.0~2.4%、硬脂酸0.6~1.0%、磺化蓖麻油3.5~4.5%、聚乙二醇2.4~2.8%、聚氧乙烯烷基醚2.4~2.8%、丙三醇1.8~2.2%、去离子水82~85%、杀菌剂0.1~0.2%。采用常温→中温→常温的合成条件进行生产。
Description
技术领域:
本发明涉及一种冲压工艺用润滑冷却液及生产方法,尤其是一种润滑及冷却性能好,可防止冲压工件表面出现划伤、锈蚀,可保证表面光洁度、清洁度以满足直接装配要求且脱模容易的超薄铝箔板水基冲压拉伸油及生产方法。
背景技术:
冲压加工又称为板材冲压,是通过模具对板材施加压力,使之分离或产生塑性变形,从而获得一定尺寸、形状和性能的零件加工方法。在冲压加工过程中,金属材料产生塑性剪切变形,产生的剪切面与模具工作表面间如发生强烈摩擦,则使局部产生高温而导致“焊合”和粘着磨损,因此需要使用具有减少摩擦、冷却降温作用的润滑剂(冲压拉伸油),以期在金属表面形成耐压耐热且坚韧的润滑薄膜,将新生的剪切面和模具工作面隔开,从而达到提高模具使用寿命,稳定剪切面表面质量的目的。由于对超薄(厚度为0.05~0.1mm)铝箔板进行冲压拉伸时有特殊要求,而现有的冲压加工大多使用的是油基拉伸油,因此超薄(厚度为0.05~0.1mm)铝箔板进行冲压拉伸时存在着如下问题:
1.超薄铝箔板工件与模具之间会产生严重粘连而使脱膜困难,不能实现节拍型连续作业,影响生产效率;
2.因超薄铝箔板工件冲压拉伸成型后,由于结构不能进行后道常规的清洗处理,而现有工件表面并不能达到直接装配使用的要求;
3.超薄铝板工件冲压拉伸后不能进行任何表面封闭倒钝化处理,但现有工件表面防锈变色期短且有划伤及微观纤维撕裂现象。
发明内容:
本发明是为了解决现有技术所存在的上述技术问题,提供一种润滑及冷却性能好,可防止冲压工件表面出现划伤、锈蚀,可保证表面光洁度、清洁度以满足直接装配要求且脱模容易的超薄铝箔板水基冲压拉伸油及生产方法。
本发明的技术解决方案是:一种超薄铝箔板水基冲压拉伸油,所用原料及重量百分比如下:
植酸 0.4~0.6%
苯甲酸钠 1.4~1.8%
三乙醇胺 2.0~2.4%
硬脂酸 0.6~1.0%
磺化蓖麻油 3.5~4.5%
聚乙二醇 2.4~2.8%
聚氧乙烯烷基醚 2.4~2.8%
丙三醇 1.8~2.2%
去离子水 82~85%
杀菌剂 0.1~0.2%。
原料及重量百分比的最佳方案如下:
植酸 0.5%
苯甲酸钠 1.6%
三乙醇胺 2.2%
硬脂酸 0.8%
磺化蓖麻油 4%
聚乙二醇 2.6%
聚氧乙烯烷基醚 2.6%
丙三醇 2.0%
去离子水 83.55%
杀菌剂 0.15%。
一种超薄铝箔板水基冲压拉伸油的生产方法,其特征在于有如下步骤:
a.先将计算量的去离子水、植酸、硬脂酸、苯甲酸钠、三乙醇胺依次加入反应釜中,开动搅拌器按360转/分在常温下搅拌2小时;
b.边加温边搅拌依次加入计算量的磺化蓖麻油、聚乙二醇、聚氧乙烯烷基醚、丙三醇以及杀菌剂,将温度控制在50~60℃,继续搅拌2小时;
c.降至常温。
本发明同现有技术相比,具有如下优点:
1.本发明是水基冲压拉伸油,其冷却性能优良且相对粘度低,不会造成超薄铝箔板工件粘附在模具上的现象;本发明所含的脂肪酸和醇类有机化合物的活性基与铝箔表面发生反应,同时活性基中的烃链部分具有垂直排列于金属铝表面的特殊性,以形成规则排列的膜,即化学吸附膜和物理吸附膜(也称边界膜)。能有效地降低摩擦,阻止铝箔板表面擦伤磨损,不产生表面微观纤维撕裂并保持原来的光洁度。
2.本发明具备对铝箔板工件表面进行强力清洗的作用,使超薄铝箔板工件不经后道常规的清洗处理,就能够达到直接装配使用的要求。
3.本发明具有对铝箔板工件表面进行钝化封闭的作用,其防锈防变色期可达6个月以上。
4.本发明在长期贮存或使用过程中不易变质慢,尤其在夏季,保质期长,对操作者无毒无害,对环境无污染,符合SGS检测认可的国际通用的环保与安全法规要求。
具体实施方式:
实施例1:
a.取原料组分,每种原料占总重量的百分比如下:
植酸0.4~0.6%、苯甲酸钠1.4~1.8%、三乙醇胺2.0~2.4%、硬脂酸0.6~1.0%、磺化蓖麻油3.5~4.5%、聚乙二醇2.4~2.8%、聚氧乙烯烷基醚2.4~2.8%、丙三醇1.8~2.2%、去离子水82~85%、杀菌剂(异塞唑啉酮衔生物)0.1~0.2%。
每种原料可在所列取值范围内任意选取,总值应是100%;
b.先将计算量的去离子水、植酸、硬脂酸、苯甲酸钠、三乙醇胺依次加入反应釜中,开动搅拌器按360转/分在常温下搅拌2小时;
c.边加温边搅拌依次加入计算量的磺化蓖麻油、聚乙二醇、聚氧乙烯烷基醚、丙三醇以及杀菌剂,将温度控制在50~60℃,继续搅拌2小时;
d.降至常温即可检查包装。
产品外观微紫色透明液体,PH值:6.4~7.6。使用时将原液直接装槽,用于泵抽循环喷啉冲压拉伸或人工浇涂于超薄铝箔板表面上。符合国家标准GB7631.5-89各项技术要求。
实施例2:
原料及生产方法同实施例1,只是各原料总重量的百分比如下:
植酸0.5%、苯甲酸钠1.6%、三乙醇胺2.2%、硬脂酸0.8%、磺化蓖麻油4%、聚乙二醇2.6%、聚氧乙烯烷基醚2.6%、丙三醇2.0%、去离子水83.55%、杀菌剂(异塞唑啉酮衔生物)0.15%。
产品外观微紫色透明液体,PH值:6.4~7.6。使用时将原液直接装槽,用于泵抽循环喷啉冲压拉伸或人工浇涂于超薄铝箔板表面上。符合国家标准GB7631.5-89各项技术要求。
Claims (3)
1.一种超薄铝箔板水基冲压拉伸油,其特征在于所用原料及重量百分比如下:
植酸 0.4~0.6%
苯甲酸钠 1.4~1.8%
三乙醇胺 2.0~2.4%
硬脂酸 0.6~1.0%
磺化蓖麻油 3.5~4.5%
聚乙二醇 2.4~2.8%
聚氧乙烯烷基醚 2.4~2.8%
丙三醇 1.8~2.2%
去离子水 82~85%
杀菌剂 0.1~0.2%。
2.根据权利要求1所述的超薄铝箔板水基冲压拉伸油,所用原料及重量百分比如下:
植酸 0.5%
苯甲酸钠 1.6%
三乙醇胺 2.2%
硬脂酸 0.8%
磺化蓖麻油 4%
聚乙二醇 2.6%
聚氧乙烯烷基醚 2.6%
丙三醇 2.0%
去离子水 83.55%
杀菌剂 0.15%。
3.一种如权利要求1所述超薄铝箔板水基冲压拉伸油的生产方法,其特征在于有如下步骤:
a.先将计算量的去离子水、植酸、硬脂酸、苯甲酸钠、三乙醇胺依次加入反应釜中,开动搅拌器按360转/分在常温下搅拌2小时;
b.边加温边搅拌依次加入计算量的磺化蓖麻油、聚乙二醇、聚氧乙烯烷基醚、丙三醇以及杀菌剂,将温度控制在50~60℃,继续搅拌2小时;
c.降至常温。