CN101250344B - 一种抗菌涂料 - Google Patents
一种抗菌涂料 Download PDFInfo
- Publication number
- CN101250344B CN101250344B CN2008100178070A CN200810017807A CN101250344B CN 101250344 B CN101250344 B CN 101250344B CN 2008100178070 A CN2008100178070 A CN 2008100178070A CN 200810017807 A CN200810017807 A CN 200810017807A CN 101250344 B CN101250344 B CN 101250344B
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- bacterial
- water
- silane coupling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种抗菌涂料,包括以下重量份的原料:1~10份抗菌剂,2~30份有机硅酸盐,10~40份硅烷偶联剂;40~90份水;抗菌剂为三氯生和吡啶硫酮。先向配液容器中加入所需量的水,再向水中加入所需用量的有机硅酸盐,待搅拌均匀后,加入硅烷偶联剂,继续搅拌使溶液混合均匀;加入三氯生和吡啶硫酮抗菌剂,继续搅拌20分钟。本发明解决了现有抗菌涂料采用的杀菌剂和添加剂影响环境和人员健康的技术问题,有明显的防霉、抗菌、抑菌性;所使用的抗菌材料属于低毒材料,无毒无污染,对环境和人体健康没有不利影响;可达到长期高效抗菌效果。
Description
技术领域
本发明涉及一种抗菌涂料,尤其涉及一种水性抗菌涂料。
背景技术
有价证券纸张在流通过程中,易受到环境温湿度、洁净程度以及储存条件的干扰,影响其耐久性、耐物化性等耐流通性能以及抑菌效果。
专利CN1236141C公开了一种卷烟用广谱抗菌水松纸的制备方法,主要是将水松纸经过印刷辊涂布印刷,在其表面形成均匀的无机抗菌剂、有机抗菌剂和中药制剂的光谱抗菌涂层。所用连结料由改性松香、聚乙烯醇、邻苯二甲酸二丁酯、缩丁醛等组成。专利WO 91/12372公开了一种填料涂层,主要用于为纸张表面提供微孔或一定程度的粗糙度,以便获得更好的油墨结合。专利US5868902则介绍了一种水性聚氨酯涂层,经涂布的钞票纸具有如下主要显著特性:聚氨酯涂料不添加填料,无色透明;涂层通过降低表面孔隙率和粗糙度,提高了纸张的耐脏污性,增加钞票流通寿命;涂层显著改善油墨与纸张表面的结合牢度。但是两篇专利都没有提到涂层溶液对纸张抗霉、抑菌效果的贡献和影响。专利CN1236141C虽然提到纸张涂布后具有抗菌性能,但是没有提到涂层对纸张耐久性、抗霉性能的影响;专利WO 91/12372虽然提到聚氨酯涂布钞票纸的两种途径(一是纸张经施胶槽浸涂、压榨辊之后、后烘之前在其一面或两面涂布水性无填料聚氨酯涂料,二是纸张正常工艺完成后,涂布水性聚氨酯),但是没有提到涂层对纸张是否具有抗霉、抑菌性能。
发明内容
本发明目的是提出一种无毒无污染的水性抗菌涂料,其解决了现有抗菌涂料采用的杀菌剂和添加剂影响环境和人员健康的技术问题。
本发明的技术解决方案是:
一种抗菌涂料,包括以下重量份的原料:
抗菌剂 1~10份; 有机硅酸盐2~30份;
硅烷偶联剂10~40份;水 40~90份;
所述抗菌剂包括短期高效抗菌剂和长效抗菌剂,所述长效抗菌剂为吡啶硫酮锌、吡啶硫酮钠或吡啶硫酮铜,所述短期高效抗菌剂为三氯生;所述有机硅酸盐为甲基硅酸钾、甲基硅酸钠、乙基硅酸钾、乙基硅酸钠中的一种或任意两种的混合物;所述硅烷偶联剂包括氨丙基三乙氧基硅烷或异氨丙基三甲氧基硅烷。
上述抗菌涂料的较佳重量份组成包括:
抗菌剂 1~5份; 有机硅酸盐2~10份;
硅烷偶联剂10~20份;水 70~85份。
上述抗菌涂料的制备方法,包括以下步骤:
1]加水:向配液容器中加入所需量的水;
2]加有机硅酸盐:向水中加入所需用量的有机硅酸盐,搅拌5~10分钟;
3]加硅烷偶联剂:待搅拌均匀后,开始加入硅烷偶联剂,并不停搅拌;加入完成后,继续搅拌5~10分钟,使溶液混合均匀;
4]加抗菌剂:加入三氯生和/或吡啶硫酮抗菌剂,加完后继续搅拌20分钟。
本发明与现有技术相比具有如下优点:
1、本发明的抗菌涂料有明显的防霉、抗菌、抑菌性,对大肠杆菌和金黄色葡萄球菌的抗菌实验表明,抗菌率达到99%以上。
2、本发明的抗菌涂料是一种有机硅酸盐、硅烷偶联剂、水、抗菌剂组成的水性涂料,所使用的抗菌材料属于低毒材料,无毒无污染,对环境和人体健康没有不利影响。
3、本发明的涂层对钞票的其它性能无任何影响,涂布的同时不改变钞票产品的外观、防伪特征和流通耐性。
4、本发明涂料的涂布方法简单易行,可以使用辊涂设备进行涂布。
5、本发明涂料使用简单。有机硅酸盐、硅烷偶联剂是涂料的成膜物质,现场配制好后即可当天使用。
6、三氯生属于短期高效抗菌剂,吡啶硫酮抗菌剂属于长效抗菌剂,三氯生和吡啶硫酮抗菌剂混合使用,可达到长期高效抗菌效果。
具体实施方式
本发明的钞票抗菌涂料的不同重量份数组成如表1所示:
表1
配方 | 配方一 | 配方二 | 配方三 |
吡啶硫酮抗菌剂 | 0 | 1~5 | 1~3 |
三氯生 | 1~5 | 0 | 1~3 |
有机硅酸盐 | 2~10 | 2~10 | 2~10 |
硅烷偶联剂 | 10~20 | 10~20 | 10~20 |
水 | 70~85 | 70~85 | 70~85 |
配方一的具体材料名称及重量份数见表2:
表2
材料名称 | 重量份数 |
吡啶硫酮锌 | 0 |
三氯生 | 4 |
甲基硅酸钾 | 6 |
γ-氨丙基三乙氧基硅烷 | 15 |
水 | 75 |
配方二的具体材料名称及重量份数见表3:表3
材料名称 | 重量份数 |
吡啶硫酮钠 | 4 |
三氯生 | 0 |
甲基硅酸钠 | 8 |
异氨丙基三甲氧基硅烷 | 18 |
水 | 70 |
配方三的具体材料名称及重量份数见表4:
表4
材料名称 | 重量份数 |
吡啶硫酮铜 | 2 |
三氯生 | 2 |
乙基硅酸钠 | 8 |
异氨丙基三甲氧基硅烷 | 18 |
水 | 70 |
本发明抗菌涂料生产工艺为:加水-加有机硅酸盐-加硅烷偶联剂-加三氯生-加吡啶硫酮抗菌剂。具体如下:
1]加水:向配液容器中加入所需量的水;
2]加有机硅酸盐:向水中加入所需用量的有机硅酸盐,搅拌5~10分钟;
3]加硅烷偶联剂:待搅拌均匀后,开始加入硅烷偶联剂,并不停搅拌;加入完成后,继续搅拌5~~10分钟,使溶液混合均匀;
4]加三氯生:加入三氯生,加完后继续搅拌20分钟;
5]加吡啶硫酮抗菌剂:加入吡啶硫酮抗菌剂,加完后继续搅拌20分钟。
本发明抗菌涂料的涂布方式是采用辊式涂布机进行涂布的方式,涂布产品为白纸、印钞半成品或印钞成品。
本发明抗菌涂料的抗菌性能检测如下:
机型:辊式涂布机
本发明原理:本发明提供一种钞票表面的抗菌涂料及其制备方法,用于改善流通钞票的卫生状况。本发明在经过实验室材料筛选,涂料体系设计及配方试验的基础上,确定了用于钞票抗菌的涂料配方。通过初步的产品试验,显示出研究的涂层具有明显的抗菌抑菌性能。本发明将抗菌剂、有机硅酸盐、硅烷偶联剂、水按照一定的比例配制成均匀的涂料,在钞票印前或半成品或印刷完成品表面涂布,提高钞票在发行、流通使用过程的防霉、抗菌、抑菌性。
Claims (2)
1.一种抗菌涂料,其特征在于:包括以下重量份的原料:
抗菌剂 1~10份; 有机硅酸盐2~30份;
硅烷偶联剂10~40份;水 40~90份;
所述抗菌剂包括短期高效抗菌剂和长效抗菌剂,所述长效抗菌剂为吡啶硫酮锌、吡啶硫酮钠或吡啶硫酮铜,所述短期高效抗菌剂为三氯生;所述有机硅酸盐为甲基硅酸钾、甲基硅酸钠、乙基硅酸钾、乙基硅酸钠中的一种或任意两种的混合物;所述硅烷偶联剂包括氨丙基三乙氧基硅烷或异氨丙基三甲氧基硅烷。
2.根据权利要求1所述的抗菌涂料,其特征在于:所述抗菌涂料的较佳重量份组成包括:
抗菌剂 1~5份; 有机硅酸盐2~10份;
硅烷偶联剂10~20份;水 70~85份。