CN101240133A - 一种水性导电色浆 - Google Patents
一种水性导电色浆 Download PDFInfo
- Publication number
- CN101240133A CN101240133A CNA2007101267895A CN200710126789A CN101240133A CN 101240133 A CN101240133 A CN 101240133A CN A2007101267895 A CNA2007101267895 A CN A2007101267895A CN 200710126789 A CN200710126789 A CN 200710126789A CN 101240133 A CN101240133 A CN 101240133A
- Authority
- CN
- China
- Prior art keywords
- water
- color paste
- conductive color
- based conductive
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种水性导电色浆,其成分质量百分比为:乙二醇、丙二醇或丙三醇中的一种或几种8-12、润湿剂0-10、分散剂5-15、碳黑粉20-30、防腐杀菌剂0.1-0.3、消泡剂0.05-0.2、余量为水。本发明为纳米级导电色浆,具有更高的固体含量,更强的着色力,更好的导电性能,能代替油性色浆,与水性涂料的混溶性优,且电阻低,附着力强,硬度佳,印刷性能好。另外,还具有良好的贮存稳定性,贮存半年以上不会出现分水沉淀等现象,不返粗。可用于薄膜开关、触摸屏、软性线路板等原有油性色浆的传统领域,还可用于电子元件着色、乳胶制品、水性乳胶漆、水性墨水、彩泥、汽球、粉笔及相关水溶性树脂体系。
Description
技术领域
本发明涉及到一种导电色浆,特别涉及到一种水性导电色浆。
背景技术
目前导电色浆大部分仍属于油性色浆,即多数采用溶剂、油类作颜料的分散剂,因而在使用时会因溶剂的挥发而对周边环境造成污染,也会对相关使用人员的身体健康产生影响。
因此,导电色浆正朝着更好的导电能力,以及固化后各种性能更好方向;另一方面,也正在试图采用以水代油的方法制造水性色浆,消除化工溶剂对环境的污染。
发明内容
本发明的目的在于提供一种水性导电色浆,既能保持色浆原料的着色性能和电性能,又采用水,从而消除和减少了溶剂对环境的污染,有利于保护环境、保护操作人员身体健康。
为达到上述目的,本发明的技术方案是,
一种水性导电色浆,其成分质量百分比为:
乙二醇、丙二醇或丙三醇中的一种或几种 8-12
润湿剂 0-10
分散剂 5-15
碳黑粉 20-30
防腐杀菌剂 0.1-0.3
消泡剂 0.05-0.2
余量为水。
其中,所述的润湿剂为非离子表面活性剂;
所述的非离子表面活性剂为烷基酚类表面活性剂。
又,所述的分散剂为聚羚酸胺盐溶液。
所述的防腐杀菌剂为异噻唑啉酮。
所述的消泡剂是以疏水化合物为载体的矿物油溶液。
另,所述的碳黑粉为纳米级材料。
在本发明中,
本发明采用乙二醇、丙二醇或丙三醇作为溶剂;
所述的润湿剂为非离子表面活性剂,能有效的降低颜料与水之间的表面张力,有利于交颜、填料量体系的分散与稳定,有利于对基材的润湿和渗透。
所述的分散剂为聚羚酸胺盐溶液,其对无机颜料、填料及有机颜料具有极佳的润湿、分散、稳定效果,具有用量少,起泡性低,粘度稳定性好,展色性佳,不影响光泽的特点。
所述的防腐杀菌剂为异噻唑啉酮,活性成分2.5%,有较高的活性范围,能有效抑制细菌,霉菌和酵母菌等,不含甲醛和甲醛释放,使用简捷,用量少,价格低廉。
所述的消泡剂是以疏水化合物为载体的矿物油溶液,具有优异的消泡,快速破泡能力,易于分散,适用PH范围宽,与涂膜水溶,不产生鱼眼、缩孔。
本发明的有益效果
本发明为纳米级导电水性色浆,可用于薄膜开关、触摸屏、软性线路板等原有油性色浆的传统领域外,还可用于电子元件着色、乳胶制品、水性乳胶漆、水性墨水、彩泥、汽球、粉笔及相关水溶性树脂体系。
本发明的色浆有更高的固体含量,更强的着色力,更好的导电性能,能代替油性色浆,与水性涂料的混溶性优,且电阻低,附着力强,硬度佳,印刷性能好。
本发明的色浆具有良好的贮存稳定性,贮存半年以上不回出现分水沉淀等现象,且不返粗。
具体实施方式
本发明实施例参见表1:
表1
单位:质量百分比
实施例 | 溶剂(乙二醇、丙二醇、丙三醇) | 润湿剂 | 分散剂 | 碳黑粉 | 防腐杀菌剂 | 消泡剂 | 水 |
1 | 5 | 5 | 15 | 30 | 0.24 | 0.18 | 余量 |
2 | 10 | 8 | 10 | 20 | 0.20 | 0.12 | 余量 |
3 | 7.5 | 10 | 18 | 25 | 0.26 | 0.08 | 余量 |
4 | 2.5 | 7.5 | 12.5 | 22 | 0.28 | 0.15 | 余量 |
5 | 8 | 3 | 5 | 27 | 0.30 | 0.20 | 余量 |
6 | 9 | 2 | 7 | 26 | 0.10 | 0.05 | 余量 |
7 | 12 | 0 | 14 | 28 | 0.15 | 0.11 | 余量 |
本发明的生产工艺流程如下:
按配方混合,以1200转/分的速度高速分散,中间抽样检验,再次以1200转/分的速度高速分散,产品检验,包装入库。
综上所述,本发明的纳米级导电炭黑水性色浆,是一种着眼于他除可用于薄膜开关、触摸屏、软性线路板等原有油性色浆的传统领域外,还可用于电子元件着色、乳胶制品、水性乳胶漆、水性墨水、彩泥、汽球、粉笔及相关水溶性树脂体系。
Claims (7)
1. 一种水性导电色浆,其成分质量百分比为:
乙二醇、丙二醇或丙三醇中的一种或几种 8-12
润湿剂 0-10
分散剂 5-15
碳黑粉 20-30
防腐杀菌剂 0.1-0.3
消泡剂 0.05-0.2
余量为水。
2. 如权利要求1所述的水性导电色浆,其特征是,所述的润湿剂为非离子表面活性剂。
3. 如权利要求2所述的水性导电色浆,其特征是,所述的非离子表面活性剂为烷基酚类表面活性剂。
4. 如权利要求1所述的水性导电色浆,其特征是,所述的分散剂为聚羚酸胺盐溶液。
5. 如权利要求1所述的水性导电色浆,其特征是,所述的防腐杀菌剂为异噻唑啉酮。
6. 如权利要求1所述的水性导电色浆,其特征是,所述的消泡剂是以疏水化合物为载体的矿物油溶液。
7. 如权利要求1所述的水性导电色浆,其特征是,所述的碳黑粉为纳米级材料。