CN101215435A - 适用于热固性粉末涂料的远红外粉剂及其制备方法 - Google Patents
适用于热固性粉末涂料的远红外粉剂及其制备方法 Download PDFInfo
- Publication number
- CN101215435A CN101215435A CNA2007101165302A CN200710116530A CN101215435A CN 101215435 A CN101215435 A CN 101215435A CN A2007101165302 A CNA2007101165302 A CN A2007101165302A CN 200710116530 A CN200710116530 A CN 200710116530A CN 101215435 A CN101215435 A CN 101215435A
- Authority
- CN
- China
- Prior art keywords
- far infrared
- infrared powder
- powder
- thermosetting
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种适用于热固性粉末涂料的远红外粉剂及其制备方法,属于热固性粉末涂料的添加剂技术领域,其重量组成为:远红外粉料100%,外加2~3%的硼铝钛偶联剂,其中,远红外粉料的重量百分组成为:氧化锆15~25%、高岭土30~40%、电气石5~8%和余量的氢氧化铝,与热固性粉末涂料的溶合性好,并增强了热固性粉末涂料的性能和应用效果;将硼铝钛偶联剂加入到远红外粉料中搅拌,控制温度为125~140℃,搅拌速度750~1200转/分钟,时间8~15分钟,然后冷却即得远红外粉剂,制备方法简单易行、科学合理。
Description
技术领域
本发明涉及一种适用于热固性粉末涂料的远红外粉剂及其制备方法,属于热固性粉末涂料的添加剂技术领域。
背景技术
远红外技术的推广应用使人们获得了很多益处,各种远红外保健产品层出不穷,有远红外保健被、保健褥、保健衣服等,有远红外保健治疗仪、保健带等,有远红外保健涂料、油漆等,……,要制备远红外热固性粉末涂料,如果直接将远红外粉料直接添加到热固性粉末涂料中,由于有机基料与无机填料根本无法融合,造成无机填料成颗粒状悬浮于表面,轻轻一蹭即可脱落,直接影响了热固性粉末涂料的性能和应用效果。
发明内容
本发明的目的在于提供一种适用于热固性粉末涂料的远红外粉剂,与热固性粉末涂料的溶合性好,并增强了热固性粉末涂料的性能和应用效果;本发明同时提供了其简单易行、科学合理的制备方法。
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加2~3%的硼铝钛偶联剂。
其中,远红外粉料的重量百分组成为:氧化锆15~25%、高岭土30~40%、电气石5~8%和余量的氢氧化铝,红外发射率大于0.9,红外线的波长为8-14μm,与人体吸收的波段要求相匹配。
本发明简单易行、科学合理的制备方法如下:
将购买的硼铝钛偶联剂粉料加入到远红外粉料中搅拌,控制温度为125~140℃,搅拌速度750~1200转/分钟,时间8~15分钟,然后冷却即得远红外粉剂。
最好,首先将远红外粉料加热后再加入硼铝钛偶联剂,如加热到115±5℃,再加入硼铝钛偶联剂。加入硼铝钛偶联剂后,可边搅拌边升温,直至到125~140℃,也可以直接在温度达到125~140℃时加入硼铝钛偶联剂。
本发明适用于热固性粉末涂料的远红外粉剂,通过加入硼铝钛偶联剂进行改性,使其与热固性粉末涂料有了很好的溶合性,保证了热固性粉末涂料的性能和应用效果,如提高流平度、增加附着力等。应用时,按照外加重量比5-8%的比例加入到热固性粉末涂料中,混合均匀即可;本发明制备方法简单易行、科学合理。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加2.5%的硼铝钛偶联剂,其中:远红外粉料的重量百分组成为:氧化锆20%、高岭土35%、电气石7%和余量的氢氧化铝。
本发明远红外粉剂的制备方法如下:
将远红外粉料加入到密封高速搅拌容器中,升温至115±2℃,再加入硼铝钛偶联剂,搅拌速度1000转/分钟,继续升温至13±2℃,保温10分钟,然后冷却即得远红外粉剂。
实施例2
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加2%的硼铝钛偶联剂,其中:远红外粉料的重量百分组成为:氧化锆25%、高岭土32%、电气石7%和余量的氢氧化铝。
本发明远红外粉剂的制备方法如下:
将远红外粉料加入到密封高速搅拌容器中,升温至116±2℃,再加入硼铝钛偶联剂,搅拌速度900转/分钟,继续升温至135±2℃,保温15分钟,然后冷却即得远红外粉剂。
实施例3
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加3%的硼铝钛偶联剂,其中:远红外粉料的重量百分组成为:氧化锆22%、高岭土36%、电气石5%和余量的氢氧化铝。
本发明远红外粉剂的制备方法如下:
将远红外粉料加入到密封高速搅拌容器中,升温至118±2℃,再加入硼铝钛偶联剂,搅拌速度1100转/分钟,继续升温至128±2℃,保温8分钟,然后冷却即得远红外粉剂。
实施例4
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加2.6%的硼铝钛偶联剂,其中:远红外粉料的重量百分组成为:氧化锆18%、高岭土37%、电气石6%和余量的氢氧化铝。
本发明远红外粉剂的制备方法如下:
将远红外粉料加入到密封高速搅拌容器中,升温至113±2℃,再加入硼铝钛偶联剂,搅拌速度800转/分钟,继续升温至122±2℃,保温13分钟,然后冷却即得远红外粉剂。
实施例5
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加2.2%的硼铝钛偶联剂,其中:远红外粉料的重量百分组成为:氧化锆21%、高岭土38%、电气石8%和余量的氢氧化铝。
本发明远红外粉剂的制备方法如下:
将远红外粉料加入到密封高速搅拌容器中,升温至130±2℃,再加入硼铝钛偶联剂,搅拌速度950转/分钟,保温12分钟,然后冷却即得远红外粉剂。
实施例6
本发明所述的适用于热固性粉末涂料的远红外粉剂,其重量组成为:远红外粉料100%,外加2.7%的硼铝钛偶联剂,其中:远红外粉料的重量百分组成为:氧化锆13%、高岭土35%、电气石7%和余量的氢氧化铝。
本发明远红外粉剂的制备方法如下:
将远红外粉料加入到密封高速搅拌容器中,升温至130±2℃,再加入硼铝钛偶联剂,搅拌速度1000转/分钟,保温13分钟,然后冷却即得远红外粉剂。
Claims (5)
1.一种适用于热固性粉末涂料的远红外粉剂,其特征在于重量组成为:
远红外粉料100%,外加2~3%的硼铝钛偶联剂。
2.根据权利要求1所述的适用于热固性粉末涂料的远红外粉剂,其特征在于远红外粉料的重量百分组成为:氧化锆15~25%、高岭土30~40%、电气石5~8%和余量的氢氧化铝。
3.根据权利要求1所述的适用于热固性粉末涂料的远红外粉剂的制备方法,其特征在于将硼铝钛偶联剂加入到远红外粉料中搅拌,控制温度为125~140℃,搅拌速度750~1200转/分钟,时间8~15分钟,然后冷却即得远红外粉剂。
4.根据权利要求3所述的适用于热固性粉末涂料的远红外粉剂的制备方法,其特征在于首先将远红外粉料加热后再加入硼铝钛偶联剂。
5.根据权利要求4所述的适用于热固性粉末涂料的远红外粉剂的制备方法,其特征在于将远红外粉料加热到115±5℃,再加入硼铝钛偶联剂。