CN101200799A - 钢铁表面中低温高耐蚀黑色磷化液 - Google Patents

钢铁表面中低温高耐蚀黑色磷化液 Download PDF

Info

Publication number
CN101200799A
CN101200799A CNA2006101051843A CN200610105184A CN101200799A CN 101200799 A CN101200799 A CN 101200799A CN A2006101051843 A CNA2006101051843 A CN A2006101051843A CN 200610105184 A CN200610105184 A CN 200610105184A CN 101200799 A CN101200799 A CN 101200799A
Authority
CN
China
Prior art keywords
phosphating
steel surface
temperature high
high corrosion
corrosion resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2006101051843A
Other languages
English (en)
Other versions
CN101200799B (zh
Inventor
杨通
董晟全
陈山川
李高宏
梁艳峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian Technological University
Original Assignee
Xian Technological University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian Technological University filed Critical Xian Technological University
Priority to CN2006101051843A priority Critical patent/CN101200799B/zh
Publication of CN101200799A publication Critical patent/CN101200799A/zh
Application granted granted Critical
Publication of CN101200799B publication Critical patent/CN101200799B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种钢铁表面中低温高耐蚀黑色磷化液，其特征是在1升磷化液中含有磷酸二氢锰40－50g/L、硝酸锌60－70g/L、硝酸镍1－2g/L、醋酸(36％)3－4ml/L、柠檬酸铵2－3g/L、钼酸铋1－2g/L，其余为水。本磷化液在60－65℃下成膜20分钟就可生成18－22μm的磷化膜。本发明磷化温度低，能耗小，沉渣少，并且可减少污染，保护环境，磷化膜均匀致密，外观色泽感官性状良好，特别是耐蚀性符合国家有关标准。

Description

钢铁表面中低温高耐蚀黑色磷化液
技术领域
本发明属于金属表面处理技术领域，尤其是涉及一种钢铁表面中低温高耐蚀黑色磷化液。
背景技术
磷化工艺是以磷酸盐溶液对金属基体表面进行处理，在其表面形成一层附着牢固的转化膜层的工艺。氧化碱性发黑工艺是采用硝酸钠高温(120-140℃)氧化体系，在工件表面生成蓝黑色四氧化三铁为主的氧化膜的方法。
长期以来，在表面处理领域中，相当数量的钢铁工件通过磷化和氧化处理，以提高钢铁表面的防护和装饰性能。由于磷化膜色泽不如氧化膜，而耐腐蚀性又优于氧化膜，致使钢铁表面经磷化或氧化处理形成的化学转化膜其防护性能和装饰性能难以兼顾。采用黑色磷化既可以保证膜层的耐蚀性，又具有一定的装饰性，而且这种膜层还具有吸光、吸热、绝缘、耐磨等优点。因此，该技术在机械、兵器、航空、仪器、仪表、汽车等领域有着广泛的应用前景。
中国专利申请中有较多关于磷化液的发明，但由于配方中所用成分的不同，耐蚀磷化温度一般要在75-90℃时才能进行，能源消耗较大，对环境污染较重，磷化过程沉渣也多，生产成本也高。而最主要的是磷化膜的厚度不能满足工艺要求，耐腐蚀性差，磷化膜色泽欠佳，难以用于实际生产。
发明内容
本发明要解决的问题是为克服现有技术中存在的不足，提供一种能降低化温度、减少沉渣量、改善磷化膜性能和外观色泽、降低能源消耗、减小环境污染的钢铁表面中低温高耐蚀黑色磷化液。
实现本发明的技术解决方案在于：在1升磷化液中含有
磷酸二氢锰   40-50g/L    硝酸锌   60-70g/L
硝酸镍       1-2g/L      醋酸     3-4ml/L
柠檬酸铵     2-3g/L      钼酸铋   1-2g/L
其余为水。
其进一步技术解决方案是：在1升的磷化液中含有
磷酸二氢锰    47g/L     硝酸锌   66g/L
硝酸镍        1.6g/L    醋酸     2ml/L
柠檬酸铵      2.5g/L    钼酸铋   1g/L
其余为水。
所说的醋酸浓度为36％。
本发明在基本磷化液组成的基础上，研究了各种促进剂对磷化膜的影响，用正交设计实验，寻找出了最佳组合促进剂；研究了各种络合剂对减少沉渣的影响，在保证磷化膜质量的前提下，寻找对环境友好的络合剂，减少磷化沉渣，减小环境污染，延长了磷化液的使用寿命。同时，还研究了各种促黑剂对膜层色泽和质量的影响，以及不同温度和时间对磷化膜生成的影响。所产生的积极效果是：
1、锌锰离子比例合适，生成的磷酸盐沉淀致密均匀，钼酸根和铋离子在溶液中形成深色磷钼杂多酸盐和铋盐沉积在金属表面，可得到均匀致密的深黑色磷化膜，外观色泽感官性状良好。
2、本发明所用水为自来水，与其他磷化液中所用去离子水相比，方便而且成本低廉。
3、本磷化液在60-65℃条件下即可生成高耐蚀性磷化膜，大大降低了能耗。
4、由本磷化液生成的磷化膜通过硫酸点滴实验耐蚀时间大于5分钟，高与国家标准3分钟，具有较好的耐蚀性。
5、沉渣大量减少，改善了工作条件，对环境的污染也大大减少。
本发明所用成分易得，配置简单，使用方便，具有很好的社会效益和经济效益。
具体实施方式
本发明的磷化液中含有：
磷酸二氢锰   40-50g/L     硝酸锌   60-70g/L
硝酸镍       1-2g/L       醋酸     3-4ml/L
柠檬酸铵     2-3g/L       钼酸铋   1-2g/L
再用自来水稀释至1升即可。
还可以使用以下配比：
磷酸二氢锰    47g/L     硝酸锌   66g/L
硝酸镍        1.6g/L    醋酸     2ml/L
柠檬酸铵      2.5g/L    钼酸铋   1g/L
同样用水稀释至1升。
以上两例中所说醋酸的浓度均为36％。
经过实际应用，在进行磷化处理时，只需将钢铁工件浸入60-65℃的磷化液，控制成膜时间为20分钟，就能在工件表面生成18-22μm的磷化膜。

Claims (3)

1.一种钢铁表面中低温高耐蚀黑色磷化液，其特征是在1升磷化液中含有：
磷酸二氢锰  40-50g/L    硝酸锌    60-70g/L
硝酸镍      1-2g/L      醋酸      3-4ml/L
柠檬酸铵    2-3g/L      钼酸铋    1-2g/L
其余为水。
2.如权利要求1所述的钢铁表面中低温高耐蚀黑色磷化液，其特征是在1升的磷化液中含有：
磷酸二氢锰    47g/L     硝酸锌    66g/L
硝酸镍        1.6g/L    醋酸      2ml/L
柠檬酸铵      2.5g/L    钼酸铋    1g/L
其余为水。
3.如权利要求1或2所述的钢铁表面中低温高耐蚀黑色磷化液，其特征是所说的醋酸浓度为36％。
CN2006101051843A 2006-12-15 2006-12-15 钢铁表面中低温高耐蚀黑色磷化液 Expired - Fee Related CN101200799B (zh)