CN101191006A - Controllable solidifying type technologic clay sculpture material - Google Patents
Controllable solidifying type technologic clay sculpture material Download PDFInfo
- Publication number
- CN101191006A CN101191006A CNA2006101296821A CN200610129682A CN101191006A CN 101191006 A CN101191006 A CN 101191006A CN A2006101296821 A CNA2006101296821 A CN A2006101296821A CN 200610129682 A CN200610129682 A CN 200610129682A CN 101191006 A CN101191006 A CN 101191006A
- Authority
- CN
- China
- Prior art keywords
- clay sculpture
- component
- technologic
- sculpture material
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a controllable and cured type technique clay sculpture material, which adopts epoxy resin, PVC paste resin, talc powder and light calcium carbonate as raw materials. The raw materials are mixed evenly and then stirred into putty shape composition 1; curing agent, the PVC paste resin and the talc powder are mixed evenly and stirred into semi-transparent paste, in which the light calcium carbonate is added, thus obtaining composition 2. The two compositions are mixed evenly in accordance with a certain ratio, thus obtaining the controllable and cured type technique clay sculpture material. The invention is characterized in that: the invention not only has the plasticity (being moulded into different shapes randomly) of the traditional technique clay sculpture material (clay), but also has long storing time; besides, the cured time can be controlled (a plurality of hours or a plurality of days) under low temperature (below 0 DEG C); the invention is characterized by constructability, innocuity, adjustable hardness of products and extremely high impact resistance (being uneasy to be broken), etc. The invention is the technique clay sculpture material with excellent comprehensive property.
Description
Technical field
The present invention relates to a kind of controllable solidifying type technologic clay sculpture material, belong to material science.
Background technology
The clay sculpture artwork is of a great variety, with a long history, is the art form that China people love, and has strong place of china characteristic.Traditional clay sculpture material is raw material with earth, adds auxiliary agent, and water is regulated viscosity, has characteristics with low cost.But because traditional clay sculpture material time of drying long (generally needing several days time even longer) easily causes artwork distortion, the heap moulded to collapse, large-scale clay sculpture goods are all the more so.And traditional clay sculpture material is medium with water, can not operate (freezing below 0 ℃) under the cold condition, thereby limit its use.
Synthetic materials has advantages such as intensity height, ageing resistance is strong, set time is adjustable.According to clay sculpture goods characteristics and performance requriements, the development and operation temperature range is wide, set time is adjustable and the novel process clay sculpture material of superior performance has important Practical significance.
Summary of the invention
With Resins, epoxy, solidifying agent, pvc resin paste grade, talcum powder and light calcium carbonate etc. is raw material, and uniform mixing, stirring by a certain percentage promptly gets controllable solidifying type technology carving material.Except that the plasticity-with traditional technology clay sculpture material (mud) (can arbitrarily mould different shape), also have and to control that (several hours to several days), low temperature (below 0 ℃) can be constructed, nontoxic, goods hardness can be in harmonious proportion high shock resistance characteristics such as (being difficult for breaking into pieces) set time.It is a kind of technologic clay sculpture material of excellent combination property.
Embodiment
Example 1 is stuck with paste resins with 30 parts of PVC and is mixed through stirring with 100 parts of Resins, epoxy and be into translucent pasty state, adds 80 parts of talcum powder while stirring, and system is puttylike nian substantially, rubs 24 parts of flanging adding light calcium carbonates as first component with the back.30 parts of PVC are stuck with paste resins mix through stirring with 100 parts of Resins, epoxy and be into translucent pasty state, add 80 parts of talcum powder while stirring, system is puttylike nian substantially, rubs 24 parts of flanging adding light calcium carbonates as first component with the back.35 parts of PVC are stuck with paste resin and fully stirring of 100 parts of solidifying agent (651#), be uniformly mixed into translucent pasty state, add 50 parts of talcum powder and 70 parts of light calcium carbonates while stirring as second component.Above-mentioned two components pack room temperature (10 ℃-40 ℃) respectively and store, and validity period is 60 days.During use first component and second component can be used by 1: 1 uniform mixing of quality, best duration of service is for mixing the back after 15-30 minute (viscosity is more moderate).
Claims (9)
1. controllable solidifying type technologic clay sculpture material.With Resins, epoxy, solidifying agent, pvc resin paste grade, talcum powder and light calcium carbonate etc. is raw material, and uniform mixing, stirring by a certain percentage promptly gets controllable solidifying type technology carving material.Except that the plasticity-with traditional technology clay sculpture material (mud) (can arbitrarily mould different shape), also have period of storage long (60 days), set time and can control that (several hours to several days), low temperature (below 0 ℃) can be constructed, nontoxic, goods hardness can be in harmonious proportion high shock resistance characteristics such as (being difficult for breaking into pieces).It is a kind of technologic clay sculpture material of excellent combination property.
2. by the described controllable solidifying type technologic clay sculpture material of claim 1, it is characterized in that 100 parts of Resins, epoxy (E-51), PVC sticks with paste resin (PB1302) 30 parts, 80 parts of talcum powder and 24 parts of raw materials as first component of light calcium carbonate.
3. by described controllable solidifying type technologic clay sculpture material first component raw material of claim 2, it is characterized in that the PVC that will accurately take by weighing sticks with paste resin and adds fully stirring in the Resins, epoxy, be uniformly mixed into translucent mashed prod.Add talcum powder while stirring, the system for the treatment of is puttylike nian substantially, rubs flanging with the back and adds light calcium carbonate as first component.
4. by the described controllable solidifying type technologic clay sculpture material of claim 1, it is characterized in that 100 parts in solidifying agent (651#), PVC sticks with paste resin (PB1302) 35 parts, 50 parts of talcum powder and 70 parts of raw materials as second component of light calcium carbonate.
5. press the raw material of described controllable solidifying type technologic clay sculpture material second component of claim 4, it is characterized in that the PVC that will accurately take by weighing sticks with paste resin and solidifying agent (651#) fully stirs, be uniformly mixed into translucent pasty state, add talcum powder and light calcium carbonate while stirring as second component.
6. pack respectively in room temperature (10 ℃-40 ℃) by claim 3 and described first component of claim 5 and second component and store, validity period is 60 days.
7. can use by 1: 1 uniform mixing of quality in use by described first component of claim 6 and second component, best duration of service is for mixing the back after 15-30 minute (viscosity is more moderate).
8. by the described controllable solidifying type technologic clay sculpture material of claim 1, it is characterized in that by changing the relative consumption of first component and second component, can regulate the set time (from several hours to several days) of clay sculpture craftwork, to adapt to clay sculpture time or variation of temperature.
9. by the described controllable solidifying type technologic clay sculpture material of claim 1, it is characterized in that except that the plasticity-with traditional technology clay sculpture material (mud) (can arbitrarily mould different shape) having also that period of storage is long, can control that (several hours to several days), low temperature (below 0 ℃) can be constructed, nontoxic, goods hardness can be in harmonious proportion high shock resistance characteristics such as (being difficult for breaking into pieces) set time.