CN101162189B - 一种热塑性塑料样品制备方法 - Google Patents
一种热塑性塑料样品制备方法 Download PDFInfo
- Publication number
- CN101162189B CN101162189B CN200610096685A CN200610096685A CN101162189B CN 101162189 B CN101162189 B CN 101162189B CN 200610096685 A CN200610096685 A CN 200610096685A CN 200610096685 A CN200610096685 A CN 200610096685A CN 101162189 B CN101162189 B CN 101162189B
- Authority
- CN
- China
- Prior art keywords
- sample
- spatula
- thermoplastic plastics
- sample preparation
- stereotyped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种热塑性塑料样品制备方法,本方法使用工具简单、操作方法简便、特点是不会破坏样品分子结构,根据需要一次操作可制备出不同厚度的试样,关键是该方法对人体安全,本发明的方法是将样品置于一金属刮铲(1)上,通过加热器(2)加热金属刮铲(1),间接加热样品(3),当样品(3)被加热至熔融状态时,刮铲(1)携此样品(3)于一固定的平板(4)上,刮铲(1)平面与平板(4)呈锐角状,靠近平板(4)的刮铲边沿(1-1)与平板(4)留有一线形狭缝,夹容于刮铲(1)与平板(4)间的熔融态样品(3),被手持移动的刮铲(1)刮蹭出厚度等同于线形狭缝尺寸的薄膜状试样,刮铲移动时变换狭缝尺寸可制备出不同H厚度的试样。
Description
技术领域:本发明涉及一种热塑性塑料样品制备方法,具体地说是制备供红外光谱仪器分析测绘使用的一种热塑性塑料样品制备方法。
背景技术:要获得一张高质量的光谱图,除了仪器本身的因素外,样品制备方法在红外光谱测绘技术中占有重要的地位,如果样品处理方法不恰当,即使仪器的性能再好也得不到满意的红外光谱图,这一点对于固体样品的测绘尤为重要。作为固体样品相当数量的热塑性塑料样品目前大多采用薄膜法或压片法制备,化学工业出版社《红外光谱法》(1979.10)中公开了薄膜法的制备方法:一种是直接加热熔融样品然后涂制或压制成膜、另一种则是把样品制成溶液,第一种方法由于直接加热样品,受热的不均匀很容易使塑料组织结构发生变化,操作不好时还会使样品部分碳化,不但会造成绘制的光谱图失真,还有可能释放出有害气体,损害人的身体健康;另外制备试样所使用的工具品种多,特别是采用高价的盐窗加热样品,操作不好很容易损坏,至使制备成本增高,为得一完整的谱图需制备不同厚度试样时,该方法操作极为繁琐不便;而采用第二种由溶液来制膜的方法,最麻烦的是溶剂的除去,有时为了除去残留的溶剂干扰,往往需要在真空烘箱内烤数小时之久,此法不经济,同时也不安全,因为大部分溶剂都是对人体有害的,在制备试样时不可避免的会被人体吸入而损害健康。
发明内容:本发明的目的是克服以上制备方法的不足,提供一种使用工具简单、操作方法简便、又不会破坏样品分子结构,根据需要一次操作可制备出不同厚度的试样,本发明的方法是将样品置于一金属刮铲上,通过加热器加热金属刮铲,间接加热样品,当样品被加热至熔融状态时,刮铲携此样品于一固定的平板上,刮铲平面与平板呈锐角状,靠近平板的刮铲边沿与平板留有一线形狭缝,夹容于刮铲与平板间的熔融态样品,被手持移动的刮铲刮蹭出厚度等同于线形狭缝尺寸的薄膜状试样,刮铲移动时变换狭缝尺寸可制备出不同厚度的试样。
上述的金属刮铲1,头部为扁平长方形状,其两侧边沿1-1和1-2平直光滑;而加热器2采用普通酒精灯5,所述样品3取米粒大小,最大不要超出刮铲两侧边沿1-1、1-2,而所述的固定的平板4的表面最好经过抛光处理。
本发明的有益效果是:使用工具简单、操作方法简便、又不会破坏样品分子结构,一次操作可制备出不同厚度的试样,最关键是该方法对人体安全。
附图说明:
附图1为本发明所使用的工具刮铲结构示意图;
附图2为本发明加热操作原理图;
附图3为本发明刮蹭操作原理图。
下面将结合附图对本发明作进一步说明,并给出实施例。
实施例如图1、图2、图3所示,本发明所述热塑性塑料样品制备方法是将米粒大小的样品3置于一头部为扁平长方形状的金属刮铲1上,其两侧边沿1-1和1-2平直光滑,样品3不要超出刮铲两侧边沿1-1、1-2,通过普通酒精灯5加热金属刮铲1,间接加热样品3,当样品被加热至熔融状态时,刮铲携此样品3于一固定的表面经过抛光处理的平板4上,刮铲1平面与平板4呈锐角状,靠近平板4的刮铲边沿1-1与平板4留有一线形狭缝,夹容于刮铲1与平板4间的熔融态样品3,被手持移动的刮铲1刮蹭出厚度等同于线形狭缝尺寸的薄膜状试样,刮铲1移动时变换狭缝尺寸可制备出不同H厚度的试样.
Claims (5)
1.一种热塑性塑料样品制备方法,其特征是,将样品(3)置于一金属刮铲(1)上,通过加热器(2)加热金属刮铲,间接加热样品(3),当样品被加热至熔融状态时,刮铲携此样品(3)于一固定的平板(4)上,刮铲(1)平面与平板(4)呈锐角状,靠近平板(4)的刮铲边沿(1-1)与平板(4)留有一线形狭缝,夹容于刮铲(1)与平板(4)间的熔融态样品(3),被手持移动的刮铲(1)刮蹭出厚度等同于线形狭缝尺寸的薄膜状试样,刮铲(1)移动时变换狭缝尺寸可制备出不同H厚度的试样。
2.根据权利要求1所述的一种热塑性塑料样品制备方法,其特征是,所述的金属刮铲(1),头部为扁平长方形状,其两侧边沿(1-1、1-2)平直光滑。
3.根据权利要求1或2所述的一种热塑性塑料样品制备方法,其特征是,所述加热器(2)为普通酒精灯(5)。
4.根据权利要求1或2所述的一种热塑性塑料样品制备方法,其特征是,所述样品(3)取米粒大小,最大不要超出刮铲两侧边沿(1-1、1-2)。
5.根据权利要求1或2所述的一种热塑性塑料样品制备方法,其特征是,所述的固定的平板(4)的表面经过抛光处理。