CN101161737A - 水性仿幕墙金属光泽漆 - Google Patents
水性仿幕墙金属光泽漆 Download PDFInfo
- Publication number
- CN101161737A CN101161737A CNA2006101171582A CN200610117158A CN101161737A CN 101161737 A CN101161737 A CN 101161737A CN A2006101171582 A CNA2006101171582 A CN A2006101171582A CN 200610117158 A CN200610117158 A CN 200610117158A CN 101161737 A CN101161737 A CN 101161737A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- percent
- imitating
- class
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性仿幕墙金属光泽漆,该漆的主要组分及其重量配比为:水性树脂40%~80%、消泡剂0.05%~0.8%、分散剂0.05%~1.0%、颜料5%~35%、增稠剂0.1%~1%、防缩边剂0.1%~1%、流平剂0.1%~1%、防冻剂1%~10%、抗菌剂0.5%~5%、防霉防藻剂0.5%~5%以及水5%~40%。本发明的水性金属光泽漆可涂装于建筑外墙、内墙等水泥制品表面,对墙体高装饰性,达到与铝塑板一般的装饰效果,并且装饰分割缝与板面间浑然一体,具有高效率防霉防藻、具防水透气的呼吸功能、成本低、金属质感强烈,装饰效果佳且对环境无污染,高抗污、高耐候性。
Description
技术领域
本发明涉及一种水性仿幕墙(或称仿铝塑板)金属光泽漆,尤其涉及一种水性氟碳树脂仿幕墙(或称仿铝塑板)金属光泽漆。
背景技术
普通水性涂料用于外墙不能达到仿铝塑板幕墙的高装饰效果,普通涂料颜色单调,没有生机,溶剂型涂料装饰效果好但不环保,如仿高级装饰材料的外墙涂料及施工方法(CN01125008.9)公开的技术。
发明内容
本发明要解决的技术问题在于提供一种水性仿幕墙金属光泽漆,以克服现有技术存在的上述缺陷。
本发明水性仿幕墙金属光泽漆的主要组分及其重量配比为:固体含量为45%~55%的水性树脂40%~80%、消泡剂0.05%~0.8%、分散剂0.5%~2%、颜料5%~35%、增稠剂0.1%~1%、防缩边剂0.1%~1%、流平剂0.1%~1%、定向剂5~20%、防冻剂1%~10%、抗菌剂0.5%~5%、防霉防藻剂0.5%~5%以及水5%~40%。
当该漆的组分中不含消光剂时制得的漆为亮光漆,当需配制哑光漆时,还需加入重量比为0~15%的消光剂,所说的消光剂选自未经表面处理的微粉化二氧化硅,如美国GRACE公司的C803、C805、C807、C809等中的一种。
优选的各组分及其重量配比为:固体含量为45%~55%的水性氟碳树脂52.5%、消泡剂0.2%、分散剂0.5%、金属效果颜料9.7%、增稠剂0.5%、防缩边剂0.8%、流平剂0.3%、定向剂6%、抗粘污剂4.5%、防冻剂4%、抗菌剂1%以及防霉防藻剂3%水20%。
所述水性水性树脂是水性氟碳树脂,其化学名称为聚四氟乙烯丙烯酸酯共聚物乳液或六氟丙烯酸丁酯与有机硅共聚物乳液,可采用日本DAIKIN公司的产品350E氟碳乳液,沈阳佳雪集团的氟硅乳液601D。
所述消泡剂为聚硅氧烷-聚醚共聚物乳液类、聚丙二醇类、聚乙二醇-憎水固体-聚硅氧烷混合物类、矿物油基类或其混合物;所说的聚硅氧烷-聚醚共聚物乳液类可采用德国迪高化工有限公司的TEGO805;所说的聚丙二醇类可采用德国巴斯夫化工有限公司生产的Pluriol P 2000;所说的聚乙二醇-憎水固体-聚硅氧烷混合物类可采用德国毕克化学(亚太)私人有限公司生产的BYK024;矿物油基类可采用深圳市海川化工有限公司生产的Foamster309A;
所述分散剂为聚丙烯酸铵盐类、改性聚丙烯酸溶液类、改性聚羧酸盐类或它们的混合物;所述聚丙烯酸铵盐类可采用深圳市海川化工有限公司生产的Hydropalat 640A;改性聚丙烯酸溶液类可采用德国迪高化工有限公司生产的TEGO Dispers750W;改性聚羧酸盐类可采用德国巴斯夫化工有限公司生产的Sokalan PA30CL;
所述颜料包括无机颜料、有机颜料或金属效果颜料或其混合物,无机颜料如透明氧化铁红、铁黄,碳黑等,有机颜料如永固紫、酞菁蓝、DPP橙,金属效果颜料可采用德国ECKART公司的HYDROLAN系列水性铝浆或德国MERK公司的高耐候系列珠光粉。金属效果颜料是在人工合成的氧化铝基材上进行处理的新型材料,通过高科技的结晶化处理,这种人工合成的氧化铝便能得到更加完美平滑的表面和狭窄的粒径分布,同时在这种基材上还包裹了反射性极强的金属氧化物,使其有闪烁效果,并且在水中可以稳定分散,其粒径为5~30μm。效果颜料还包括由天然云母薄片包裹金属氧化物(如氧化铁、二氧化钛等)薄层制成,通过光的反射、折射和干涉效应的叠加形成独特的颜色和光泽,其粒径为5~60μm,可采用MERK公司生产的牌号为Xirallic以氧化铝为基材的高彩度水晶效应颜料系列和Iriodin100银白系列的产品;
所述增稠剂为非离子聚氨酯缔合型类、碱溶胀乳液非缔合型类、疏水碱溶胀乳液缔合型类或其混合物,非离子聚氨酯缔合型类可采用深圳明佳科技有限公司生产的PU40;碱溶胀乳液非缔合型类可采用美国罗门哈斯公司生产的RM-2020、ACRYSOL ASE-60;疏水碱溶胀乳液缔合型类可采用美国罗门哈斯公司生产的ACRYSOL DR-1;
所述防缩边剂为聚硅氧烷-聚醚共聚物类,可采用德国迪高化工有限公司生产的TEGO245;
所述流平剂为交联型有机硅聚醚丙烯酸酯类共聚物、二甲基聚硅氧烷乳液,聚硅氧烷-聚醚共聚物类可采用德国迪高化工有限公司生产的TEGOGlide450;二甲基聚硅氧烷乳液可采用TEGO Glide482;
所说的定向剂选自水性乙酸丁酸纤维素(CAB),可采用美国EASTMAN公司的CMCAB-641-0.5或CMCAB-641-0.2;
所述抗粘污剂为有机物改性纳米二氧化硅类或其混合物,可采用北京首创公司的水性纳米抗污剂NZW-1(化学名称是纳米材料金属氧化物制成均匀稳定、纳米尺寸含量大于95%的纳米胶体),也可采用深圳国达科技纳米材料中心生产的牌号为居安仕纳米防污剂的产品;
所述防冻剂为丙二醇或乙二醇或它们的混合物;
所述抗菌剂为异噻唑啉酮类抗菌剂、TiO2作载体的纳米氯化银离子类抗菌剂、银离子类抗菌剂或它们的混合物;异噻唑啉酮类抗菌剂可采用日本SR商事株式会社或鞍山市裕原塑胶抗菌剂公司生产的牌号为长福明牌IOR-250无机抗菌剂的产品,银离子类抗菌剂可采用鞍山市裕原塑胶抗菌剂公司生产的牌号为长福明牌IOR-350无机抗菌剂的产品;
防霉防藻剂选自低环境影响类三嗪衍生物(如敌草农、氯[二氯苯氧基]苯酚等)和DCOIT类(异噻唑啉酮)或它们的混合物;三嗪衍生物可采用Clariant公司生产的牌号为Nipacide DFS的产品;DCOIT类可采用Clariant公司生产的牌号为Nipacide DFZ的产品;
本发明的水性仿幕墙(或称仿铝塑板)金属光泽漆可分为银灰色(原色)、调色两大类,调色漆需要在上述组分中加入0~15%的高耐候、高透明水性色浆,所说的水性色浆选自BASF的XFAST系列中高透明、高耐候的颜料。
本发明的水性金属光泽漆可涂装于建筑外墙、内墙等水泥制品表面,形成金属光泽涂膜,对墙体高装饰性,达到与铝塑板一般的装饰效果,并且装饰分割缝与板面间浑然一体,减少了外挂铝塑板和填缝胶间结合不牢造成的渗水对墙体的破坏,其高效率防霉防藻、具防水透气的呼吸功能、成本低、金属质感强烈,装饰效果佳且对环境无污染,高抗污、高耐候性,可广泛应用于现代高要求建筑物的外墙涂装和酒店、办公室的内墙装饰装修。
具体实施方式
实施例1~4
实施例中,所采用的原料如下:
实施例1 | 实施例2 | 实施例3 | 实施例4 | |
水性树脂 | 水性氟碳树脂 | 水性氟碳树脂 | 水性氟碳树脂 | 水性氟硅树脂 |
消泡剂 | BYK024 | Pluriol P 2000 | TEGO805 | Foamster309A |
分散剂 | Hydropalat 640A | TEGO Dispers750W | Sokalan PA30CL | Sokalan PA30CL |
色浆 | BASF的XFAST | BASF的XFAST | BASF的XFAST | BASF的XFAST |
效果颜料 | HYDROLAN系列水性铝浆 | Xirallic水晶效应颜料 | Xirallic水晶效应颜料 | Iriodin100珠光粉 |
增稠剂 | PU40 | RM-2020 | ACRYSOL DR-1 | ACRYSOL DR-1 |
防缩边剂 | TEGO245 | TEGO245 | TEGO245 | TEGO245 |
流平剂 | TEGO Glide450 | TEGO Glide450 | TEGO Glide482 | TEGO Glide482 |
定向剂 | CMCAB-641-0.5 | CMCAB-641-0.2 | CMCAB-641-0.2 | CMCAB-641-0.2 |
防冻剂 | 丙二醇 | 丙二醇 | 乙二醇 | 乙二醇 |
抗菌剂 | 异噻唑啉酮类 | 银离子类抗菌剂 | 纳米氯化银离子类 | 银离子类 |
防霉防藻剂 | 类三嗪衍生物 | DCOIT | 类三嗪衍生物 | 类三嗪衍生物 |
本发明水性仿幕墙(或称仿铝塑板)金属光泽漆中具体采用的组分及其重量配比为:
实施例1:
水性氟碳树脂(固体含量:45%)为55%、消泡剂为0.2%、分散剂为0.4%、金属效果颜料为16%、增稠剂为0.3%、防缩边剂为0.3%、流平剂为0.5%、定向剂为质量浓度为8%的水溶液6%、抗粘污剂为4%、防冻剂为4%、抗菌剂1%、防霉防藻剂为2%以及水10.3%。
实施例2:
水性氟碳树脂(固体含量:50%)为52.5%、消泡剂为0.2%、分散剂为0.5%、金属效果颜料为9.7%、增稠剂为0.5%、定向剂为质量浓度为8%的溶液8%、防缩边剂为0.8%、流平剂为0.3%、抗粘污剂4.5%、防冻剂为4%、抗菌剂为1%、防霉防藻剂3%以及水15%。
实施例3:
水性氟碳树脂(固体含量:50%)为60.5%、消泡剂为0.2%、分散剂为0.5%、金属效果颜料为10%、增稠剂为0.5%、定向剂为质量浓度为15%的溶液15%、防缩边剂为0.5%、流平剂为0.3%、抗粘污剂4.5%、防冻剂为4%、抗菌剂为1%、防霉防藻剂3%以及水0%。
实施例4:
水性氟硅树脂(固体含量:50%)为55.5%、消泡剂为0.2%、分散剂为0.5%、金属效果颜料为15%、增稠剂为0.5%、定向剂为质量浓度为10%的溶液10%、防缩边剂为0.5%、流平剂为0.3%、抗粘污剂4.5%、防冻剂为4%、抗菌剂为1%、防霉防藻剂3%以及水5%。
其中实施例2为最佳配方。
配制时,将水性树脂和防冻剂、消泡剂、分散剂、流平剂、增稠剂等各种涂料助剂充分分散后,加入抗菌剂分散均匀即可。涂装施工时,可根据具体情况加入适量的水调节粘度,再用喷涂的方法将漆涂建筑物墙面、水泥制品表面使其全面封闭即可。
实施例3与实施例4与实施例1和实施例2相同。
经检测,本发明的水性仿幕墙(或称仿铝塑板)金属光泽漆的主要质量技术指标如下:
Claims (10)
1.一种水性仿幕墙金属光泽漆,其特征在于,主要组分及其重量配比为:固体含量为45~55%的水性树脂40%~80%、消泡剂0.05%~0.8%、分散剂0.5%~2%、颜料5%~35%、增稠剂0.1%~1%、防缩边剂0.1%~1%、流平剂0.1%~1%、定向剂5~20%、防冻剂1%~10%、抗菌剂0.5%~5%、防霉防藻剂0.5%~5%以及水5%~40%。
2.根据权利要求1所述的水性仿幕墙金属光泽漆,其特征在于,还包括重量比为0~15%的消光剂。
3.根据权利要求1所述的水性仿幕墙金属光泽漆,其特征在于,各组分及其重量配比为:固体含量为45~55%的水性氟碳树脂52.5%、消泡剂0.2%、分散剂0.5%、金属效果颜料9.7%、增稠剂0.5%、防缩边剂0.8%、流平剂0.3%、定向剂6%、抗粘污剂4.5%、防冻剂4%、抗菌剂1%以及防霉防藻剂和3%水20%。
4.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,所述水性水性树脂是水性氟碳树脂。
5.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,所述消泡剂为聚硅氧烷-聚醚共聚物乳液类、聚丙二醇类、聚乙二醇-憎水固体-聚硅氧烷混合物类、矿物油基类或其混合物。
6.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,所述分散剂为聚丙烯酸铵盐类、改性聚丙烯酸溶液类、改性聚羧酸盐类或它们的混合物。
7.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,所述颜料包括无机颜料、有机颜料或金属效果颜料或其混合物,无机颜料选自透明氧化铁红、铁黄和碳黑等,有机颜料选自永固紫、酞菁蓝、DPP橙,金属效果颜料选自水性铝浆、珠光粉或由天然云母薄片包裹金属氧化物薄层制成,其粒径为5~60μm。
8.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,所述增稠剂为非离子聚氨酯缔合型类、碱溶胀乳液非缔合型类、疏水碱溶胀乳液缔合型类或其混合物。
9.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,所述防缩边剂为聚硅氧烷-聚醚共聚物乳液,所述流平剂为交联型聚硅氧烷聚醚丙烯酸酯类共聚物、所说的定向剂选自水性乙酸丁酸纤维素;所述抗粘污剂为有机物改性纳米二氧化硅类或其混合物;所述防冻剂为丙二醇或乙二醇或它们的混合物;所述抗菌剂为异噻唑啉酮类抗菌剂、TiO2作载体的纳米氯化银离子类抗菌剂、银离子类抗菌剂或它们的混合物;防霉防藻剂选自低环境影响类三嗪衍生物和异噻唑啉酮或它们的混合物。
10.根据权利要求1,2或3所述的水性仿幕墙金属光泽漆,其特征在于,还包括0~15%的透明水性色浆。