CN101144136A - 一种含钒高强度耐腐蚀钢筋用钢及其生产工艺 - Google Patents
一种含钒高强度耐腐蚀钢筋用钢及其生产工艺 Download PDFInfo
- Publication number
- CN101144136A CN101144136A CNA2007101335977A CN200710133597A CN101144136A CN 101144136 A CN101144136 A CN 101144136A CN A2007101335977 A CNA2007101335977 A CN A2007101335977A CN 200710133597 A CN200710133597 A CN 200710133597A CN 101144136 A CN101144136 A CN 101144136A
- Authority
- CN
- China
- Prior art keywords
- steel
- corrosion
- percent
- temperature
- strength corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
盐雾试验 | 周浸试验 | |
试验设备 | FQY010型盐雾箱 | F1-65型周浸试验机 |
试验标准 | GB10125-97 | TB/T2375-93 |
腐蚀介质 | 5% NaCl | 0.01MNaHSO3,3L/天补加0.02MNaHSO3 |
PH值 | 6.5~7.2 | 4.4~4.8 |
温度(℃) | 35±2 | 45±2 |
相对湿度,% | 60~80 | |
时间(h) | 96 | 96 |
实施例1 | 实施例2 | 实施例3 | |
盐雾试验 | 46 | 52 | 44 |
周浸试验 | 80 | 76 | 82 |
Rel,MPa | 450/464/458 | 447/447/458 | 445/450/448 |
Rm,MPa | 640/638/634 | 634/624/632 | 640/640/635 |
A,% | 20/22/21 | 20/21/21 | 19/21/20 |
Claims (3)