CN101122756B - 黑色墨粉及其制备方法 - Google Patents
黑色墨粉及其制备方法 Download PDFInfo
- Publication number
- CN101122756B CN101122756B CN2007101321476A CN200710132147A CN101122756B CN 101122756 B CN101122756 B CN 101122756B CN 2007101321476 A CN2007101321476 A CN 2007101321476A CN 200710132147 A CN200710132147 A CN 200710132147A CN 101122756 B CN101122756 B CN 101122756B
- Authority
- CN
- China
- Prior art keywords
- black
- wax
- black ink
- emulsion polymerization
- granular material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开一种黑色墨粉及其制备方法。具体说是彩色复印机、彩色打印机、彩色传真机和彩色印刷机用黑色墨粉及其制备方法。它是用乳胶聚合高分子树脂、黑色颜料、黑色磁粉、电荷调节剂、蜡、水性分散剂、二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷等原料,先将其中的乳胶聚合高分子树脂、电荷调节剂、黑色颜料、黑色磁粉、水性分散剂和蜡放在一起,搅拌均匀,制成混合溶液。再用喷雾干燥机在160~300℃的温度下将上述混合溶液喷雾干燥成颗粒状物料。之后,对上述颗粒状物料进行筛选,并加入二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷,经均匀混合而制成。该黑色墨粉,不仅生产成本低,而且不会对环境造成污染。
Description
技术领域
本发明涉及一种墨粉及其制备方法。具体说是彩色复印机、彩色打印机、彩色传真机和彩色印刷机用黑色墨粉及其制备方法。
背景技术
目前,彩色复印机、彩色打印机、彩色传真机和彩色印刷机上使用的黑色墨粉都是乳液聚合墨粉。这种乳液聚合墨粉主要由乳液、颜料和交联剂等其它辅料而制成。其制备方法是,先将乳液、颜料和交联剂等其它辅料放在一起,经均匀搅拌,制成颗粒状物料。然后,加酸和洗涤剂对颗粒状物料进行清洗,洗去颗粒状物料上的浮料。之后,对经清洗过的颗粒状物料进行干燥处理。最后,在经干燥处理过的颗粒状物料中加入二氧化硅等辅料,并均匀混合而制成。由于这种黑色墨粉在生产过程中需要用大量的清水来进行清洗,且每生产一吨产品就需50~100吨清水,不仅水资源浪费严重、生产成本较高,而且清洗后的费水排放出来,会对环境造成污染。
发明内容
本发明要解决的问题是提供一种黑色墨粉。这种黑色墨粉,不仅生产成本低,而且不会对环境造成污染。
本发明要解决的另一个问题是提供一种黑色墨粉的制备方法。
为解决上述问题,采取以下技术方案:
本发明的黑色墨粉特点是含有以下重量份的原料:
乳胶聚合高分子树脂70~96份;
黑色颜料0.5~10份;
黑色磁粉0~11份;
电荷调节剂3~10份;
蜡0~5份;
水性分散剂0~2份;
二氧化硅0.05~0.6份;
六甲基二硅氮烷0~3份;
二甲基二氯硅烷0~3份;
其中:所说电荷调节剂是金属水杨酸络合物或金属偶氮络合物;所说的蜡是聚丙烯蜡、聚乙烯蜡或石蜡中的任意一种;所说水性分散剂是亚甲基二荼磺酸钠或甲基荼磺酸甲醛。
本发明的黑色墨粉的制备方法含有以下步骤:
先将乳胶聚合高分子树脂、电荷调节剂、黑色颜料、黑色磁粉、水性分散剂和蜡放在一起,搅拌均匀,制成混合溶液;
再用喷雾干燥机在160~300℃的温度下将上述混合溶液喷雾干燥成颗粒状物料;
之后,对上述颗粒状物料进行筛选,除去粒径大于13微米、小于1微米的颗粒;
最后,将经筛选过的颗粒状物料投入混合器中,并加入二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷,经均匀混合,制成黑色墨粉。
采取以上方案,具有以下优点:
由于本发明的黑色墨粉含有乳胶聚合高分子树脂、黑色颜料、黑色磁粉、电荷调节剂、蜡、水性分散剂、二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷等原料,而且采用喷雾干燥方法制成,生产过程中不用清洗,不仅可避免水资源的浪费、降低了生产成本,而且没有费水排出、避免了费水对环境带来的污染。
具体实施方式
第一个实施例
选取96份的乳胶聚合高分子树脂、0.2份的黑色颜料、3份的电荷调节剂、2份的二氧化硅;其中:所说乳胶聚合高分子树脂为无锡西神日化用品厂产品;所说电荷调节剂是金属水杨酸络合物;
先将乳胶聚合高分子树脂、电荷调节剂和黑色颜料放在一起,搅拌均匀,制成混合溶液;
再用喷雾干燥机在250℃的温度下将上述混合溶液喷雾干燥成颗粒状物料;
之后,对上述颗粒状物料进行筛选,除去粒径大于13微米、小于1微米的颗粒;
最后,将经筛选过的颗粒状物料投入混合器中,并加入二氧化硅,经均匀混合,制成黑色墨粉。
第二个实施例
选取83份的乳胶聚合高分子树脂、6份的黑色颜料、7份的黑色磁粉、7份的电荷调节剂、1份的蜡、1.2份的水性分散剂、0.05份的二氧化硅、3份的六甲基二硅氮烷和3份的二甲基二氯硅烷。其中:所说乳胶聚合高分子树脂是无锡西神日化用品厂的产品;所说电荷调节剂是金属偶氮络合物;所说的蜡是聚丙烯蜡;所说水性分散剂是亚甲基二荼磺酸钠;
先将乳胶聚合高分子树脂、电荷调节剂、黑色颜料、黑色磁粉、水性分散剂和蜡放在一起,搅拌均匀,制成混合溶液;
再用喷雾干燥机在160℃的温度下将上述混合溶液喷雾干燥成颗粒状物料;
之后,对上述颗粒状物料进行筛选,除去粒径大于13微米、小于1微米的颗粒;
最后,将经筛选过的颗粒状物料投入混合器中,并加入二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷,经均匀混合,制成黑色墨粉。
第三个实施例
选取70份的乳胶聚合高分子树脂、10份的黑色颜料、11份的黑色磁粉、10份的电荷调节剂、5份的蜡、2份的水性分散剂、0.6份的二氧化硅、1.5份的六甲基二硅氮烷和2份的二甲基二氯硅烷。其中:所说乳胶聚合高分子树脂是无锡西神日化用品厂的产品;所说电荷调节剂是金属水杨酸络合物;所说的蜡是聚乙烯蜡;所说水性分散剂是甲基荼磺酸甲醛;
先将乳胶聚合高分子树脂、电荷调节剂、黑色颜料、黑色磁粉、水性分散剂和蜡放在一起,搅拌均匀,制成混合溶液;
再用喷雾干燥机在300℃的温度下将上述混合溶液喷雾干燥成颗粒状物料;
之后,对上述颗粒状物料进行筛选,除去粒径大于13微米、小于1微米的颗粒;
最后,将经筛选过的颗粒状物料投入混合器中,并加入二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷,经均匀混合,制成黑色墨粉。
Claims (1)
1.一种黑色墨粉的制备方法,所述黑色墨粉含有以下重量份的原料:
乳胶聚合高分子树脂70~96份;
黑色颜料0.5~10份;
黑色磁粉0~11份;
电荷调节剂3~10份;
蜡0~5份;
水性分散剂0~2份;
二氧化硅0.05~0.6份;
六甲基二硅氮烷0~3份;
二甲基二氯硅烷0~3份;
其中:所说电荷调节剂是金属水杨酸络合物或金属偶氮络合物;所说的蜡是聚丙烯蜡、聚乙烯蜡或石蜡中的任意一种;所说水性分散剂是亚甲基二荼磺酸钠或甲基荼磺酸甲醛;
所述的制备方法包括以下步骤:
先将乳胶聚合高分子树脂、电荷调节剂、黑色颜料、黑色磁粉、水性分散剂和蜡放在一起,搅拌均匀,制成混合溶液;
再用喷雾干燥机在160~300℃的温度下将上述混合溶液喷雾干燥成颗粒状物料;
之后,对上述颗粒状物料进行筛选,除去粒径大于13微米、小于1微米的颗粒;
最后,将经筛选过的颗粒状物料投入混合器中,并加入二氧化硅、六甲基二硅氮烷和二甲基二氯硅烷,经均匀混合,制成黑色墨粉。