CN101121860B - 一种无铬耐指纹涂料 - Google Patents

一种无铬耐指纹涂料 Download PDF

Info

Publication number
CN101121860B
CN101121860B CN200710131837XA CN200710131837A CN101121860B CN 101121860 B CN101121860 B CN 101121860B CN 200710131837X A CN200710131837X A CN 200710131837XA CN 200710131837 A CN200710131837 A CN 200710131837A CN 101121860 B CN101121860 B CN 101121860B
Authority
CN
China
Prior art keywords
percent
water
fingerprint
chromium
resistant coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN200710131837XA
Other languages
English (en)
Other versions
CN101121860A (zh
Inventor
高新田
马金
庄建林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU LANLING POLYMER MATERIAL CO Ltd
Original Assignee
JIANGSU LANLING POLYMER MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU LANLING POLYMER MATERIAL CO Ltd filed Critical JIANGSU LANLING POLYMER MATERIAL CO Ltd
Priority to CN200710131837XA priority Critical patent/CN101121860B/zh
Publication of CN101121860A publication Critical patent/CN101121860A/zh
Application granted granted Critical
Publication of CN101121860B publication Critical patent/CN101121860B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明为解决现有的含铬耐指纹涂料在配制、仓储、运输使用过程中对环境产生一定的危害，特别是铬对环境造成的污染问题，本发明涉及的化学组分为：水性聚氨酯树脂40～70wt％，二氧化硅溶胶4～8wt％，水性聚四氟乙烯蜡浆10～20wt％，去离子水20～40wt％，EFTOP EF-112 0.2～0.3wt％，乙二醇2～3wt％，Asekahate B-10190.5～0.7wt％，在反应釜中投入水性聚氨酯树脂，边搅拌边加入二氧化硅，水性聚四氟乙烯蜡浆，再加入成膜助剂，然后向反应釜中投入其他助剂，最后向反应釜中加入去离子水，再持续搅拌15～30分钟，即得到产品无铬耐指纹涂料。

Description

一种无铬耐指纹涂料
技术领域
本发明涉及一种涂料组合物，尤其是一种制造耐指纹钢板的耐指纹涂料。
背景技术
目前，随着人们对生活质量的要求越来越高，不仅是要所使用的生活用品美观，更要求其环保无危害。随着汽车、家电、办公用品等的不断更新，对钢板的要求也越来越高，耐指纹钢板就是一种升级换代产品、高附加值表面处理产品，与一般裸露的钢板相比，它不仅提高了钢板的耐腐蚀性，还有许多新的性能如耐指纹性、涂装性和导电性等。现有的技术中耐指纹钢板处理是对基材线进行钝化处理后涂覆一层1～3微米的有机薄膜，所用的化学处理剂分别是铬酸盐系的钝化剂和水性有机涂料，但这类涂料在配制、仓储、运输使用过程对环境有一定的危害，特别是铬酸盐对环境有较大的污染。
此外，已公布的一些国内外的专利中，如欧洲专利申请EP156437A1公开的是一种“水基涂料、涂覆金属基板的方法和得到的金属基板”，是使用一种粘接剂和至少2种润滑剂，其中至少有一种为大量锌粉的无机物，在焊接时产生锌雾气，对人体有害，并影响焊接部位的寿命；另外欧洲专利申请EP780452A2公开的一种“水性涂料”，它直接采用环氧改性丙烯酸树脂为成膜剂，但该涂料为容器使用，是采用后涂层，对于需要预涂层处理的钢板并不适用；在国内，上海宝山钢铁(集团)公司和上海罗思化学建材有限公司在1994年6月15日申请专利(CN94112200.X)一种耐指纹钢板的生产方法，并于1996年3月20日公开(CN1118790)，他介绍了一种耐指纹钢板的生产方法，是利用一种以改性聚丙烯酸酯乳液为主，添加有机硅溶胶、成膜助剂及水组成的水性高分子有机涂料。
发明内容
本发明的针对现有的含铬耐指纹涂料在配制、仓储、运输使用过程中对环境产生一定的危害，特别是铬对环境的污染的问题而研发。
本发明是一种无铬耐指纹涂料，其主要化学成分为水性聚氨酯树脂40～70wt％，二氧化硅溶胶4～8wt％，水性聚四氟乙烯蜡浆10～20wt％，去离子水10～40wt％，润湿剂EFTOP EF-112 0.2～0.3wt％，乙二醇2～3wt％，消泡剂Adeka NATEB-1019 0.5～0.7wt％。
本发明的制备工艺如下：在反应釜中投入水性聚氨酯树脂，边搅拌边加入二氧化硅溶胶，水性聚四氟乙烯蜡浆，再加入成膜助剂，然后向反应釜中投入其他助剂，最后向反应釜中加入去离子水，再持续搅拌15～30分钟，即得到产品无铬耐指纹涂料。
本发明中的基料使用水性聚氨酯树脂代替了一般耐指纹涂料使用的水性丙烯酸树脂，改善了使用水性丙烯酸树脂涂料会出现的热粘冷脆的现象。
本发明中所的润湿剂EFTOP EF-112是由日本JEMCO株式会社生产。
本发明中所的消泡剂Adeka NATE B-1019是由日本ADEKA株式会社生产的。
本发明适用于涂敷在热镀锌钢板、电镀锌钢板、冷轧钢板表面，形成一层耐指纹保护膜，从而制成耐指纹钢板，适用于连续镀锌涂敷的高速生产线线进行连续辊涂。
本发明是水性无铬体系，组分中不含有对环境有污染的金属离子，本发明可采用浸涂、喷涂、辊涂等方式涂装于热镀锌钢板、电镀锌钢板、冷轧钢板表面上，固化时间短，只需3～5秒，涂装后可满足镀锌钢板所需的硬韧性、耐蚀性、耐酸性、耐碱性、耐热性、重涂性及成型不脆化、不回粘的要求，并可大大提高上述各种钢板的耐指纹性。
具体实施方式
实例一
一种优选的耐指纹涂料的具体成分和配比如下：
  组分  重量(g)  备注
  水性聚氨酯树脂  600
  二氧化硅水性溶胶  70
  水性聚四氟乙烯蜡浆  100
  去离子水  203
  EFtop EF-112  2  日本JEMCO株式会社生产
  乙二醇  20
  Adeka NATE B-1019  5  日本ADEKA株式会社生产
相反应釜中投加600g水性聚氨酯树脂，边搅拌边加入70g二氧化硅水性溶胶，100g水性聚四氟乙烯蜡浆，再加入20g乙二醇，然后向反应釜中投入EFTOPEF-112 2g和Adeka NATE B-1019 5g，最后向反应釜中加入203g去离子水，再持续搅拌15分钟，即得到产品无铬耐指纹涂料1号。
实例二
一种耐指纹涂料的具体成分和配比如下：
  组分   重量(g)  备注
  水性聚氨酯树脂   1000
  二氧化硅水性溶胶   120
  水性聚四氟乙烯蜡浆   300
  组分   重量(g)  备注
  去离子水   500
EFtop EF-112 6 日本JEMCO株式会社生产
  乙二醇   60
  Adeka NATE B-1019   14  日本ADEKA株式会社生产
向反应釜中投加1000g水性聚氨酯树脂，边搅拌边加入120g二氧化硅水性溶胶，300g水性聚四氟乙烯蜡浆，再加入60g乙二醇，然后向反应釜中投入EFTOPEF-112 2g和Adeka NATE B-1019 6g，最后向反应釜中加入500g去离子水，再持续搅拌15分钟，即得到产品无铬耐指纹涂料2号。
实例三
将实例一和实例二中配制的无铬耐指纹涂料进行全性能检测，检测结果如下：
  编号   项目  无铬耐指纹涂料1号  无铬耐指纹涂料2号   指标
  1   粘度  7  10   8±3cps(25℃)
  2   细度  9  6   ≤10μm
  3   溶剂组成  去离子水  去离子水   去离子水
  4   清洗剂  去离子水  去离子水   去离子水
  5   重量固体份  23.4％  24.5％   25±2(％)
  6   体积固体份  24.8％  25.1％   24±2(％)
  7   湿膜比重  1.06  1.04   1.03±0.05
  8   干膜比重  1.09  1.11   1.07±0.05
  9   干膜厚度  0.9  1.2   1±0.5μm
  10   储存期  6个月  6个月   6个月
  11   固化温度(PMT)  89℃  78℃   70-110℃
  12   固化时间  5秒  5秒   3-5秒
  编号   项目  无铬耐指纹涂料1号  无铬耐指纹涂料2号   指标
  13   PH值  9.8  10.1   9.5-10.5
  14   划格附着力试验  0  0   0级
  15   耐指纹性a  无指纹残留  无指纹残留   优良
  16   重涂性b  优  优   优良
  17   盐雾试验c  81小时  79小时   72小时
备注：a以大拇指压印，看有无留下指纹痕迹；
b上涂聚酯烤漆，做划格附着力试验，0级为最好；
c黑锈白锈面积5％以下。

Claims (1)

1.一种无铬耐指纹涂料，其特征在于其化学组分含量：水性聚氨酯树脂40～70wt％，二氧化硅溶胶4～8wt％，水性聚四氟乙烯蜡浆10～20wt％，去离子水10～40wt％，润湿剂EFTOP EF-112 0.2～0.3wt％，乙二醇2～3wt％，消泡剂AsekahateB-1019 0.5～0.7wt％。
CN200710131837XA 2007-09-07 2007-09-07 一种无铬耐指纹涂料 Active CN101121860B (zh)