CN101117534A - 聚氨酯防水涂料生产工艺 - Google Patents
聚氨酯防水涂料生产工艺 Download PDFInfo
- Publication number
- CN101117534A CN101117534A CNA2006100151558A CN200610015155A CN101117534A CN 101117534 A CN101117534 A CN 101117534A CN A2006100151558 A CNA2006100151558 A CN A2006100151558A CN 200610015155 A CN200610015155 A CN 200610015155A CN 101117534 A CN101117534 A CN 101117534A
- Authority
- CN
- China
- Prior art keywords
- percent
- temperature
- hour
- hours
- proof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种聚氨酯防水涂料生产工艺，在一釜内计量投入30％聚醚并加热40℃，升温达到要求后加入计量的8％异氰酸酯，然后搅拌，温度升至85℃进行保温反应2小时，石油沥青20％，增溶助剂10％，石粉26％，低粘度油6％，催化剂0.5％加入另一釜内，升温105℃，再进行真空脱水2小时；从两釜内分别取样，混合后于85℃，保温半小时后，降温至50℃，将两釜内物料混合，搅拌半小时后计量包装。本发明具有以下优点：施工简便、防水效果好、无挥发性溶剂、无毒无污染、工艺简单、易于控制、贮存期长，有利于环境保护。
Description
技术领域
本发明涉及一种聚氨酯防水涂料生产工艺。
背景技术
目前，聚氨酯防水涂料基本上都是双组份溶剂型产品，其在施工时配料中掺入挥发性溶剂，使用容易引起火灾，不利环境保护。
发明内容
本发明的目的在于克服上述的缺陷，提供一种聚氨酯防水涂料生产工艺。
本发明的技术方案是：一种聚氨酯防水涂料生产工艺，其特征在于：以大分子量的异氰酸酯和大分子量的聚醚合成的聚氨酯预聚体做为主体材料，通过掺加石油沥青、增溶助剂、石粉、低粘度油类、增塑剂、催化剂等辅助材料合成的一种湿固化型涂料。先合成低粘度的聚氨酯预聚体，异氰酸酯和聚醚的当量比控制在大于3：用6％低粘度油质稀释剂来稀释由于预聚体与辅料掺和增加的粘度。
本发明具有以下优点：施工简便、防水效果好、无挥发性溶剂、无毒无污染、工艺简单、易于控制、贮存期长，有利于环境保护。
具体实施方式
实施例：一种聚氨酯防水涂料生产工艺，在一釜内计量投入30％聚醚并加热40℃，升温达到要求后加入计量的8％异氰酸酯，然后搅拌，温度升至85℃进行保温反应2小时，石油沥青20％，增溶助剂10％，石粉26％，低粘度油6％，催化剂0.5％加入另一釜内，升温105℃，再进行真空脱水2小时；从两釜内分别取样，混合后于85℃，保温半小时后，降温至50℃，将两釜内物料混合，搅拌半小时后计量包装。
Claims (1)
1.一种聚氨酯防水涂料生产工艺，其特征在于：在一釜内计量投入30％聚醚并加热40℃，升温达到要求后加入计量的8％异氰酸酯，然后搅拌，温度升至85℃进行保温反应2小时，石油沥青20％，增溶助剂10％，石粉26％，低粘度油6％，催化剂0.5％加入另一釜内，升温105℃，再进行真空脱水2小时；从两釜内分别取样，混合后于85℃，保温半小时后，降温至50℃，将两釜内物料混合，搅拌半小时后计量包装。