CN101117464A - 一种镁橄榄石质中间包涂料及其制备方法 - Google Patents

一种镁橄榄石质中间包涂料及其制备方法 Download PDF

Info

Publication number
CN101117464A
CN101117464A CNA2007100531123A CN200710053112A CN101117464A CN 101117464 A CN101117464 A CN 101117464A CN A2007100531123 A CNA2007100531123 A CN A2007100531123A CN 200710053112 A CN200710053112 A CN 200710053112A CN 101117464 A CN101117464 A CN 101117464A
Authority
CN
China
Prior art keywords
forsterite
percent
particle diameter
tundish
magnesia
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007100531123A
Other languages
English (en)
Other versions
CN100532470C (zh
Inventor
祝洪喜
邓承继
白晨
葛山
石生德
庞伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University of Science and Engineering WUSE
Original Assignee
Wuhan University of Science and Engineering WUSE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Science and Engineering WUSE filed Critical Wuhan University of Science and Engineering WUSE
Priority to CNB2007100531123A priority Critical patent/CN100532470C/zh
Publication of CN101117464A publication Critical patent/CN101117464A/zh
Application granted granted Critical
Publication of CN100532470C publication Critical patent/CN100532470C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种镁橄榄石质中间包用耐火涂料及其制备方法。所采用的技术方案是：将20～50wt％的镁橄榄石砂、25～55wt％的镁橄榄石熟料、15～30wt％的镁砂细粉、5～15wt％的镁钙砂细粉和1～5wt％的粘土混合，外加上述配料0～0.5wt％的有机纤维、0.5～2.0wt％的六偏磷酸钠和0.3～1.0wt％的三聚磷酸钠，经搅拌机混合制成，使用时加水搅拌即可。本发明以镁橄榄石为基料，所制备的产品具有耐高温性好、价格低廉、不污染钢水、耐用性好、对人体没有不利影响、使用方便的特点。

Description

一种镁橄榄石质中间包涂料及其制备方法
技术领域
本发明属于以镁橄榄石砂为基料的耐火材料领域。尤其涉及一种镁橄榄石质中间包涂料及其制备方法。
背景技术
炼钢工业中连铸技术的快速发展和广泛应用，浇钢连铸取代了传统的模铸浇钢，中间包是连铸的关键设备，中间包工作层耐火涂料用量很大。但中间包用耐火涂料绝大多数是用镁质原料制备的，而镁质矿产资源较少，镁质原料日益紧张，采用其他原料取代镁质原料制备中间包用耐火涂料势在必然。
为此，国内外很多厂家都在寻求采用其他原料取代镁质原料制备中间包用耐火涂料。为节约镁质原料，有的厂家采用了白云石和镁砂作为主要原料制备中间包用耐火涂料(CN1459346，CN1074635)，但是，白云石容易水化并产生较大体积膨胀，涂料的体积安定性不好。采用镁砂加铬铁矿砂生产的中间包涂料的体积安定性好(CN1060302)，但铬精矿砂的价格昂贵，成本太高，而且氧化铬在高温下会挥发出六价铬，对人体有害。镁橄榄石砂的价格低、耐高温性好，是制备中间包涂料的较好原料，少数厂家采用了镁橄榄石砂参与配料制备中间包涂料(CN1459345)，但选用原料种类较多，镁橄榄石砂的实际加入量有限。
发明内容
本发明的任务是提供一种耐高温性好、价格低廉、不污染钢水、耐用性好、对人体没有不利影响的镁橄榄石质中间包用耐火涂料及其制备方法。
为实现上述任务，本发明所采用的技术方案是：将20～50wt％的镁橄榄石砂、25～55wt％的镁橄榄石熟料、15～30wt％的镁砂细粉、5～15wt％的镁钙砂细粉和1～5wt％的粘土细粉混合，外加0～0.5wt％的有机纤维、0.5～2.0wt％的六偏磷酸钠和0.3～1.0wt％的三聚磷酸钠，经搅拌机混合均匀、分袋包装，使用时加水搅拌。其中：
镁橄榄石砂的MgO含量≥41.0wt％、粒径为0～3mm，镁橄榄石熟料的MgO含量≥43.0wt％、粒径为0～3mm，镁砂细粉的MgO含量≥93.0wt％、粒径为0～0.074mm，镁钙砂细粉的MgO含量≥95.0wt％、粒径为0～0.074mm，粘土细粉的Al2O3含量≥30.0wt％、粒径为0～0.074mm。
有机纤维为纸纤维、木质纤维、聚乙烯纤维和聚丙烯纤维中的一种或一种以上。
由于采用上述技术方案，本发明以镁橄榄石为基料，所制备的镁橄榄石质中间包用耐火涂料具有耐高温性好、价格低廉、不污染钢水、耐用性好、对人体没有不利影响的特点。
具体实施方式
下面结合实施例对本发明作进一步的描述：
实施例1
一种镁橄榄石质中间包用耐火涂料及其制备方法。将35～50wt％的镁橄榄石砂、25～45wt％的镁橄榄石熟料、15～20wt％的镁砂细粉、7～15wt％的镁钙砂细粉和2～5wt％的粘土混合，外加0.5wt％的纸纤维、0.5～1.5wt％的六偏磷酸钠和0.3～1.0wt％的三聚磷酸钠，经搅拌机混合均匀、分袋包装，使用时加水搅拌即可施工应用。
其中：镁橄榄石砂的MgO含量≥41.0wt％、粒径为0～3mm，镁橄榄石熟料的MgO含量≥43.0wt％、粒径为0～3mm，镁砂细粉的MgO含量≥93.0wt％、粒径为0～0.074mm，镁钙砂细粉的MgO含量≥95.0wt％、粒径为0～0.074mm，粘土细粉的Al2O3含量≥30.0wt％、粒径为0～0.074mm。
实施例2
一种镁橄榄石质中间包用耐火涂料及其制备方法。将20～35wt％的镁橄榄石砂、35～55wt％的镁橄榄石熟料、18～25wt％的镁砂细粉、5～10wt％的镁钙砂细粉和1～3wt％的粘土混合，外加0.5～1.0wt％的六偏磷酸钠和0.3～1.0wt％的三聚磷酸钠，经搅拌机混合均匀，然后分袋包装，使用时加水搅拌即可施工应用。
其中：镁橄榄石砂的MgO含量≥41.0wt％、粒径为0～3mm，镁橄榄石熟料的MgO含量≥43.0wt％、粒径为0～3mm，镁砂细粉的MgO含量≥93.0wt％、粒径为0～0.074mm，镁钙砂细粉的MgO含量≥95.0wt％、粒径为0～0.074mm，粘土细粉的Al2O3含量≥30.0wt％、粒径为0～0.074mm。
实施例3
一种镁橄榄石质中间包用耐火涂料及其制备方法。将20～30wt％的镁橄榄石砂、30～45wt％的镁橄榄石熟料、25～30wt％的镁砂细粉、5～10wt％的镁钙砂细粉和1～3wt％的粘土混合，外加0.1wt％的聚乙烯纤维、0.5～1.5wt％的六偏磷酸钠和0.3～0.8wt％的三聚磷酸钠，按上述配料比配料，经搅拌机混合均匀，然后分袋包装，使用时加水搅拌即可施工应用。
其中：镁橄榄石砂的MgO含量≥41.0wt％、粒径为0～3mm，镁橄榄石熟料的MgO含量≥43.0wt％、粒径为0～3mm，镁砂细粉的MgO含量≥93.0wt％、粒径为0～0.074mm，镁钙砂细粉的MgO含量≥95.0wt％、粒径为0～0.074mm，粘土细粉的Al2O3含量≥30.0wt％、粒径为0～0.074mm。
本具体实施方式以镁橄榄石砂为基料，所制备的镁橄榄石质中间包用耐火涂料具有耐高温性好、价格低廉、不污染钢水、耐用性好、对人体没有不利影响、使用方便的特点。

Claims (4)

1.一种镁橄榄石质中间包用耐火涂料的制备方法，其特征在于将20～50wt％的镁橄榄石砂、25～55wt％的镁橄榄石熟料、15～30wt％的镁砂细粉、5～15wt％的镁钙砂细粉和1～5wt％的粘土细粉混合，外加0～0.5wt％的有机纤维、0.5～2.0wt％的六偏磷酸钠和0.3～1.0wt％的三聚磷酸钠，经搅拌机混合均匀、分袋包装，使用时加水搅拌。
2.根据权利要求1所述的镁橄榄石质中间包用耐火涂料的制备方法，其特征在于所述镁橄榄石砂的MgO含量≥41.0wt％、粒径为0～3mm，镁橄榄石熟料的MgO含量≥43.0wt％、粒径为0～3mm，镁砂细粉的MgO含量≥93.0wt％、粒径为0～0.074mm，镁钙砂细粉的MgO含量≥95.0wt％、粒径为0～0.074mm，粘土细粉的Al2O3含量≥30.0wt％、粒径为0～0.074mm。
3.根据权利要求1所述的镁橄榄石质中间包用耐火涂料的制备方法，其特征在于所述的有机纤维为纸纤维、木质纤维、聚乙烯纤维和聚丙烯纤维中的一种或一种以上。
4.根据权利要求1～3项中任一项所述的镁橄榄石质中间包用耐火涂料的制备方法所制备的镁橄榄石质中间包用耐火涂料。
CNB2007100531123A 2007-09-03 2007-09-03 一种镁橄榄石质中间包涂料及其制备方法 Expired - Fee Related CN100532470C (zh)