CN101113623A - 一种添加煤渣的镁渣砖及其制备方法 - Google Patents
一种添加煤渣的镁渣砖及其制备方法 Download PDFInfo
- Publication number
- CN101113623A CN101113623A CNA2006102007443A CN200610200744A CN101113623A CN 101113623 A CN101113623 A CN 101113623A CN A2006102007443 A CNA2006102007443 A CN A2006102007443A CN 200610200744 A CN200610200744 A CN 200610200744A CN 101113623 A CN101113623 A CN 101113623A
- Authority
- CN
- China
- Prior art keywords
- slag
- cinder
- interpolation
- parts
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了添加煤渣的镁渣砖及其制备方法，它是用下述重量配比的原料：镁还原渣60～80份、碎石10～25份、石膏或/和石灰1～15份，煤渣5～25份，将镁还原渣用蒸汽蒸1～3小时或加水睏料1－5天后再与其它原料加水混合、压制成型，干燥后制成。本发明采用炼镁过程中产生的大量镁还原渣为主要原料，加入适当配料，制成建筑用砖，既减轻了工业废渣对环境的污染，又为建筑工程增加了新材料。本发明配方合理，制作方法易于掌握，生产周期短，制出的砖强度在25MPa以上，可达到国家建筑用砖的标准。
Description
技术领域
本发明涉及一种添加煤渣的镁渣砖及其制备方法，属于建筑材料领域。
背景技术
在工业炼镁过程中会产生大量的镁还原渣，燃煤炉窑也会产生大量的煤渣。这些镁还原渣和煤渣都是不能随便倾倒的废弃物，它们会破坏生态环境和生态平衡。目前用工业废渣为主要原料制砖的方法中，基本上是以粉煤灰为主要原料。虽然也有用镁渣制砖的方法，由于制作方法自身的缺陷，制砖效果并不理想，且生产周期长，并未应用于实际中。
发明内容
本发明的目的在于，提供一种添加煤渣的镁渣砖及其制备方法。该方法采用炼镁过程中产生的镁还原渣和工业炉窑中含煤燃料燃烧产生的煤渣为主要原料，制成高强度的建筑用砖，其制作方法易于掌握，配方合理，生产周期短，砖的强度更高，减少工业废料对环境的污染，有利于废料的再利用。
本发明的技术方案：添加煤渣的镁渣砖，它是用下述重量配比的原料加水制成；
镁还原渣60～80份， 碎石 10～25份，
石膏或/和石灰1～15份， 煤渣 5～25份。
上述的高强度镁渣砖，它是用下述重量配比的原料加水制成；
镁还原渣70～80份， 碎石 17～23份，
石膏或/和石灰5～13份， 煤渣 10～20份。
上述的添加煤渣的镁渣砖中，所述的碎石是粒径不超过10mm的天然石料或工业废渣。
上述的添加煤渣的镁渣砖中，所述的碎石是粒径不超过7mm的石灰石、高炉矿渣或磷渣
前述的添加煤渣的镁渣砖中，所述的石膏是天然石膏、磷石膏或工业副产品脱硫石膏。
前述的添加煤渣的镁渣砖中，所述的石灰是能生成氢氧化钙的生石灰或电石渣。
前述的添加煤渣的镁渣砖中，所述的煤渣是煤气炉炉渣、燃煤炉窑的煤渣。
前述的添加煤渣的镁渣砖的制备方法，按下述步骤制作；
a、将镁还原渣用蒸汽蒸1-3小时或加水睏料1-5天，得A品；
b、将A品与其它原料加水混匀，压制成砖坯，干燥后得成品。
与现有技术相比，本发明提供了一种添加煤渣的镁渣砖及其制备方法。本发明以炼镁过程中产生的大量镁还原渣和工业炉窑中含煤燃料燃烧产生的煤渣为主要原料，经配料和采用适宜的制备方法，制成建筑用砖。既减轻了工业废渣对环境的污染，又为建筑工程增加了新材料。本发明配方合理，制作方法易于掌握，制出的砖强度很高(可达到20MPa以上)，达到国家建筑用砖的标准。具有易于生产、生产周期短、生产成本低、产品效果好的特点。
具体实施方式
实施例1。按下述步骤制作添加煤渣的镁渣砖。
a、将650Kg的镁还原渣用蒸汽蒸2小时，得A品；
b、将A品与150Kg的碎石、50Kg的石膏和100Kg的煤渣加水混匀，压制成砖坯，干燥后得成品。
镁还原渣可用皮江法炼镁过程中产生的镁还原渣或其它方法获得的镁还原渣、碎石作为骨料，比较好地是用粒径不超过7mm的石灰石、高炉矿渣或磷渣，也可用其它的天然石料或工业废渣。石膏可用磷石膏、天然石膏或工业副产品脱硫石膏。煤渣可用煤气炉炉渣、燃煤炉窑的煤渣。用蒸汽蒸镁还原渣可以提高砖的强度和缩短生产时间。
实施例2。按下述步骤制作高强度镁渣砖。
a、将700Kg的镁还原渣用蒸汽蒸2小时，得A品；
b、将A品与190Kg的碎石、80Kg的石膏、120Kg的煤渣加水混匀，压制成砖坯，干燥后得成品。
Claims (8)
1.一种添加煤渣的镁渣砖，其特征在于：它是用下述重量配比的原料加水制成；
镁还原渣60～80份 ， 碎石10～25份，
石膏或/和石灰1～15份，煤渣5～25份。
2.根据权利要求1所述的添加煤渣的镁渣砖，其特征在于：它是用下述重量配比的原料加水制成；
镁还原渣70～80份， 碎石17～23份，
石膏或/和石灰5～13份， 煤渣10～20份。
3.根据权利要求2所述的添加煤渣的镁渣砖，其特征在于：所述的碎石是粒径不超过10mm的天然石料或工业废渣。
4.根据权利要求3所述的添加煤渣的镁渣砖，其特征在于：所述的碎石是粒径不超过7mm的石灰石、高炉矿渣或磷渣。
5.根据权利要求2所述的添加煤渣的镁渣砖，其特征在于：所述的石膏是天然石膏、磷石膏或工业副产品脱硫石膏。
6.根据权利要求2所述的添加煤渣的镁渣砖，其特征在于：所述的石灰是能生成氢氧化钙的生石灰或电石渣。
7.根据权利要求2所述的添加煤渣的镁渣砖，其特征在于：所述的煤渣是煤气炉炉渣、燃煤炉窑的煤渣。
8.如权利要求1至7中任一权利要求所述的添加煤渣的镁渣砖的制备方法，其特征在于：按下述步骤制作；
a、将镁还原渣用蒸汽蒸1-3小时或加水睏料1-5天，得A品；
b、将A品与其它原料加水混匀，压制成砖坯，干燥后得成品。