CN101100574A - Low-lead rust-preventive pigment - Google Patents
Low-lead rust-preventive pigment Download PDFInfo
- Publication number
- CN101100574A CN101100574A CNA2007100352797A CN200710035279A CN101100574A CN 101100574 A CN101100574 A CN 101100574A CN A2007100352797 A CNA2007100352797 A CN A2007100352797A CN 200710035279 A CN200710035279 A CN 200710035279A CN 101100574 A CN101100574 A CN 101100574A
- Authority
- CN
- China
- Prior art keywords
- rust
- lead
- red
- low
- medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A low-lead antirust pigment consists of Fast Red 1-10 wt%, permanent orange 0.1-10 wt%, medium chrome yellow 1-10 wt%, titanium pigment 1-10 wt% and filler. It costs low, saves fast red usage, and has less lead and no environmental pollution.
Description
Technical field
The present invention relates to a kind of rust-stabilising pigment.
Background technology
Red lead powder is a kind of plumbiferous rust-stabilising pigment, the present rust-inhibiting paint of producing with red lead powder, the content of red lead powder reaches more than 60%, be a kind of high plumbiferous rust-inhibiting paint, because the plumbous heavy metal that belongs to, price is also more expensive, the use height of red lead powder, both increased production cost, in the production use, also caused pollution, direct labor's health had been caused very big harm environment.
Summary of the invention
The purpose of this invention is to provide the low rust-stabilising pigment of a kind of lead tolerance.
The objective of the invention is to realize in the following way: a kind of low-lead rust-preventive pigment, this rust-stabilising pigment contain following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%.
A kind of low-lead rust-preventive pigment, this rust-stabilising pigment contain following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%
Phosphoric acid salt 15-30%.
A kind of low-lead rust-preventive pigment, this rust-stabilising pigment contain following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%
Red lead powder 5-25%.
A kind of low-lead rust-preventive pigment, this rust-stabilising pigment contain following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%
Phosphoric acid salt 15-25%
Red lead powder 5-15%.
The present invention has following beneficial effect, and the one, do not use or reduced the usage quantity of red lead powder, the lead tolerance of the rust-stabilising pigment of production reduces greatly; The 2nd, because lead is a kind of more expensive metal, the price of red lead powder need not or reduce the usage quantity of red lead powder also than higher, also greatly reduces production cost of products; The 3rd, reduced pollution to environment, also alleviated harm to the direct labor.
Embodiment
The present invention will be further described below in conjunction with embodiment:
Embodiment 1
A kind of low-lead rust-preventive pigment is got the red of 1.5Kg, and 0.5Kg's is solid forever orange, the medium chrome yellow medium yellow of 5Kg, the titanium dioxide of 8Kg, the zinc phosphate of 30Kg, the barium sulfate of 55Kg is as stopping composition, add ball mill successively, ball milling 3-5 hour, moisture content≤1%, 325 screen residue≤1%, packaging final prod, color are shallow orange.
Embodiment 2
A kind of low-lead rust-preventive pigment is got the red of 2Kg, and 1Kg's is solid forever orange, the medium chrome yellow medium yellow of 8Kg, the titanium dioxide of 5Kg, the zinc phosphate of 30Kg, the lime carbonate of 54Kg is as stopping composition, add ball mill successively, ball milling 3-5 hour, moisture content≤1%, 325 screen residue≤1%, packaging final prod, color are orange.
Embodiment 3
A kind of low-lead rust-preventive pigment is got the red of 5Kg, and 3Kg's is solid forever orange, the medium chrome yellow medium yellow of 4Kg, the titanium dioxide of 8Kg, red lead powder 20Kg's, the lime carbonate of 60Kg is as stopping composition, add ball mill successively, ball milling 3-5 hour, moisture content≤1%, 325 screen residue≤1%, packaging final prod, color are orange.
Embodiment 4
A kind of low-lead rust-preventive pigment is got the red of 5Kg, and 3Kg's is solid forever orange, the medium chrome yellow medium yellow of 5Kg, the titanium dioxide of 5Kg, the zinc phosphate of 22Kg, red lead powder 8Kg, the barium sulfate of 52Kg adds ball mill successively as stopping composition, ball milling 3-5 hour, moisture content≤1%, 325 screen residues≤1%, packaging final prod, color is dark orange.
Claims (4)
1, a kind of low-lead rust-preventive pigment is characterized in that this rust-stabilising pigment contains following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%.
2, a kind of low-lead rust-preventive pigment according to claim 1 is characterized in that this rust-stabilising pigment contains following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%
Phosphoric acid salt 15-30%.
3, a kind of low-lead rust-preventive pigment according to claim 1 is characterized in that this rust-stabilising pigment contains following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%
Red lead powder 5-25%.
4, a kind of low-lead rust-preventive pigment according to claim 1 is characterized in that this rust-stabilising pigment contains following weight percent component:
Red 1-10%
Solid forever orange 0.1-10%
Medium chrome yellow medium yellow 1-10%
Titanium dioxide 1-10%
Phosphoric acid salt 15-25%
Red lead powder 5-15%.