CN101760050A - Compound iron oxide red rust resisting pigment - Google Patents
Compound iron oxide red rust resisting pigment Download PDFInfo
- Publication number
- CN101760050A CN101760050A CN200910226710A CN200910226710A CN101760050A CN 101760050 A CN101760050 A CN 101760050A CN 200910226710 A CN200910226710 A CN 200910226710A CN 200910226710 A CN200910226710 A CN 200910226710A CN 101760050 A CN101760050 A CN 101760050A
- Authority
- CN
- China
- Prior art keywords
- rust
- oxide red
- iron oxide
- pigment
- rust resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a compound iron oxide red rust resisting pigment, which contains the following components in percentage by weight: 20-80 percent of ferric oxide and 20-80 percent of iron phosphate. The invention has the following advantages that: firstly, the invention integrates the chemical rust resisting characteristics of iron oxide red physical shielding rust resistance and phosphates, has strong weather resistance and good rust resistance and is particularly suitable for metal rust resistance in relatively-severe environment; secondly, the invention can utilize industrial waste residue so as to save resources and reduce the production cost; and in addition, the no pollution generates in the production process and products have no toxicity and are green and environment-friendly.
Description
Technical field
The present invention relates to a kind of rust-stabilising pigment.
Background technology
Ferric oxide also claims iron oxide red, has stable in properties, the non-discoloring characteristics of high temperature, and as coating, good weatherability has certain rust inhibition, and it is antirust to belong to physical shielding, generally is used for more rudimentary pigment; And phosphate-based rust-stabilising pigment, it is antirust to belong to chemistry, have nontoxic, nuisanceless, the characteristics of environmental protection, at present main usefulness be zinc phosphate, zinc phosphate rust-preventive pigment one is the price height; The 2nd, it is not fine being used for the relatively more abominable metal rust preventing effect of environment for use.
Summary of the invention
The purpose of this invention is to provide a kind of iron oxide red composite antirust pigment.
The objective of the invention is to realize in the following way: a kind of compound iron oxide red rust resisting pigment, this rust-stabilising pigment contain following weight percent component:
Ferric oxide 20-80%
Tertiary iron phosphate 20-80%.
This rust-stabilising pigment contains following weight percent component:
Ferric oxide 20-75%
Tertiary iron phosphate 20-75%
Tinting material 1-20%.
This rust-stabilising pigment is made up of following weight percent component:
Ferric oxide 20-75%
Tertiary iron phosphate 20-75%
Tinting material 1-20%
Coupling auxiliary agent 1-5%.
The present invention has following beneficial effect, and the one, combine the antirust characteristics of the antirust and phosphatic chemistry of iron oxide red physical shielding, weathering resistance is strong, and favorable rust preventing effect is adapted to the more abominable metal rust preventing of environment for use especially; The 2nd, can utilize industrial residue, economize on resources, reduce production costs; Production process is pollution-free, and product is nontoxic, environmental protection.
Embodiment
The invention will be further described below in conjunction with embodiment;
One, embodiment 1:
Ferric oxide, tertiary iron phosphate are dried to moisture content respectively less than 1%, behind ferric oxide with 60% and 40% the tertiary iron phosphate thorough mixing, are crushed to greater than 325 orders.If the use industrial residue, ferric oxide, tertiary iron phosphate content are more than 60%.
Two, embodiment 2:
For tinctorial yield, vividness and the hiding rare that improves pigment, in pigment, add the tinting material of 1-20%.
Three, embodiment 3:
For wettability and the dispersiveness that improves pigment, in pigment, add the silane coupling agent of 1-5%.
Claims (3)
1. compound iron oxide red rust resisting pigment, it is characterized in that: this rust-stabilising pigment contains following weight percent component:
Ferric oxide 20-80%
Tertiary iron phosphate 20-80%.
2. a kind of compound iron oxide red rust resisting pigment according to claim 1 is characterized in that: this rust-stabilising pigment contains following weight percent component:
Ferric oxide 20-75%
Tertiary iron phosphate 20-75%
Tinting material 1-20%.
3. a kind of compound iron oxide red rust resisting pigment according to claim 1 is characterized in that: this rust-stabilising pigment is made up of following weight percent component:
Ferric oxide 20-75%
Tertiary iron phosphate 20-75%
Tinting material 1-20%
Coupling auxiliary agent 1-5%.