CN101099971A - Waste polymerizing treatment method - Google Patents
Waste polymerizing treatment method Download PDFInfo
- Publication number
- CN101099971A CN101099971A CNA2007101057933A CN200710105793A CN101099971A CN 101099971 A CN101099971 A CN 101099971A CN A2007101057933 A CNA2007101057933 A CN A2007101057933A CN 200710105793 A CN200710105793 A CN 200710105793A CN 101099971 A CN101099971 A CN 101099971A
- Authority
- CN
- China
- Prior art keywords
- waste
- hydroxide
- harmless
- processing method
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Scope | Use |
Building structural materials | The high strength structure material reclaims use discarded object building products road maintenance (comprising under the low temperature environment) sealant fire prevention isolated material inorganic bond in a large number in building and other industrial circle |
Solid waste is handled | The solid that pollutes, the any poisonous metal of the processing of liquid and mud, the low-activity discarded object, the chemical stabilization of nuke rubbish and physics seal contaminated fragment admittedly, the high efficiente callback of sealing up for safekeeping of metal and nonmetal equipment utilizes discarded object (flyash, the ore waste residue, metal debris, wood chip, cullet, junked tire or the like) |
The petroleum and natural gas drilling well | Super steady/fixed lateral drilling well fixing of sealing the banded separation layer probing of agent hole admittedly with high-strength cement fragment, landwaste |
Bioceramic | The ceramic material for dental applications artifical bone uses ceramic material |
Refractory material | But the fire prevention of injection mo(u)lding, fire proofing casting large scale crucible and assembly |
Parameter name | Performance parameter | Remarks |
Density | 1.7-2.0g/cc | Can change with filler and additive |
Porosity | The outward appearance porosity is about 0, and there is the minute quantity hole inside | But the people is for causing hole |
Compression strength | 8000-12000psi(55-83MPa) | Can change with filler and additive |
Bending strength | 900-1600psi(6.2-11MPa) | Interpolation fiber etc. can strengthen bending strength |
Section toughness | 0.3-1 | Add fiber, whisker etc. and can strengthen toughness |
Water stability | Stable in the PH3.5-11 scope | |
Thermal coefficient of expansion | About 10 -5/C 0 | Change with additive |
Anti-flammability | The adhesive anti-flammability is fabulous | Also have a good flame even mix with wood chip |
Heat endurance | The adhesive heat endurance is fabulous | The finished product heat endurance may be influenced by additive |
Anti-penetrating property of the width of cloth | Anti-penetrating property of the width of cloth (Beta, Gamma ray etc.) is strong | |
The filler type | Any slag or other industry/domestic refuse | |
Adhesive and filler ratio | The adhesive of 7.5%-50%, remainder is a filler | |
Water consumption | Use half of binder wt generally speaking | Very sensitive to additive and granularity thereof |
Molding time | A few minutes were by several hours | A small amount of interpolation five can change shaping speed |
Slurry viscosity before the moulding | The 200-1000 centipoise | Can change viscosity by adding specific additive |
Heat production | Exothermic process can solidify at low temperatures | Can be by the preliminary treatment control thermal discharge of additive |
The pH value scope of slurry | By highly acid to neutral solution | The pH value of product is about 8 |
Molding process | Casting, extruding, spraying | Can regulate according to forming process and form |
Surface texturisation | From smooth to coarse | Depend on mould |
Color | Pure adhesive porcelain is a white | Can change its color with pigment by adding pottery |
Change in size during curing molding | Slightly microdilatancy | Can be according to complicated mold shape moulding |
Production equipment | Concrete production equipment commonly used | With the outer tight bonding of any material of plastics |
Cost | More conventional water mixes slightly expensive, but superior performance |
Claims (11)