CN101089063A - 一种热塑性丙烯酸油漆 - Google Patents

一种热塑性丙烯酸油漆 Download PDF

Info

Publication number
CN101089063A
CN101089063A CN 200610044779 CN200610044779A CN101089063A CN 101089063 A CN101089063 A CN 101089063A CN 200610044779 CN200610044779 CN 200610044779 CN 200610044779 A CN200610044779 A CN 200610044779A CN 101089063 A CN101089063 A CN 101089063A
Authority
CN
China
Prior art keywords
thermoplastic acrylic
paint
solvent
pigment
weight proportion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610044779
Other languages
English (en)
Inventor
郎需东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200610044779 priority Critical patent/CN101089063A/zh
Publication of CN101089063A publication Critical patent/CN101089063A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种热塑性丙烯酸油漆，油漆的组份包括：热塑性丙烯酸树脂、颜料、助剂、溶剂，热塑性丙烯酸油漆的生产方法包括以下步骤：将热塑性丙烯酸树脂、颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散，将经过搅拌、分散的油漆使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um，在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌，获得热塑性丙烯酸油漆，与普通油漆相比，具有使用方便、耐候性强、成本低、附着力更强的优点，本发明具有较高的市场推广价值。

Description

一种热塑性丙烯酸油漆
技术领域
本发明涉及一种油漆，具体的说，涉及一种热塑性丙烯酸油漆。
背景技术
目前，市场上使用的工业涂料中，普通醇酸漆在天气变热时会变软，其耐候性比较差，双组份聚酯漆的附着力比较强，但其在使用时必须兑加固化剂，使用后若有剩余，则剩余部分很快会固化而无法使用，浪费较大，而且价格较高，热塑性丙烯酸油漆的耐候性比较强，使用时无需兑加固化剂，所以，热塑性丙烯酸漆得到了广泛的应用，但普通热塑性丙烯酸漆的附着力比较差，容易脱落。
发明内容
本发明的目的是提供一种使用方便、耐候性强、成本低、附着力强的热塑性丙烯酸油漆。
为实现上述目的，本发明采用如下的技术方案：一种热塑性丙烯酸油漆，其特征是：所述油漆的组份包括：
热塑性丙烯酸树脂、颜料、助剂、溶剂。
以下为上述技术方案的改进：
所述油漆各成份的重量配比为：
热塑性丙烯酸树脂75～85％、颜料2.5～20％、助剂0.5～0.7％、溶剂4.3～12％。
所述油漆各成份的重量配比为：
热塑性丙烯酸树脂77～83％、颜料5.5～16％、助剂0.5～0.7％、溶剂6.3～11％。
所述油漆各成份的重量配比为：
热塑性丙烯酸树脂79～81％、颜料9～13％、助剂0.5～0.7％、溶剂7.3～95％。
所述油漆各成份的重量配比为：
热塑性丙烯酸树脂80％、颜料11％、助剂0.6％、溶剂8.4％。
所述助剂包括消泡剂、分散剂、流平剂。
所述溶剂包括醋酸丁脂、CAC。
一种热塑性丙烯酸油漆的生产方法包括以下步骤：
(1)将热塑性丙烯酸树脂、颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散；
(2)将经过搅拌、分散的混合物使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um；
(3)在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌、混匀，获得热塑性丙烯酸油漆。
本发明采用以上技术方案，与普通油漆相比，具有使用方便、耐候性强、成本低、附着力更强的优点，本发明具有较高的市场推广价值。
具体实施例
实施例1：一种热塑性丙烯酸油漆，包括：热塑性丙烯酸树脂、红色颜料、助剂、溶剂，助剂包括台湾德谦化学公司生产的消泡剂SJ-236、分散剂SJ-101、流平剂SJ-311，溶剂包括醋酸丁脂、CAC即乙二醇乙醚醋酸酯，油漆各成份的重量配比为：热塑性丙烯酸树脂78％、红色颜料17％、助剂0.5％、溶剂4.5％。
热塑性丙烯酸油漆的生产方法包括以下步骤：
(1)将热塑性丙烯酸树脂、红色颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散；
(2)将经过搅拌、分散的混合物使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um；
(3)在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌、混匀，获得热塑性丙烯酸油漆。
实施例2：一种热塑性丙烯酸油漆，包括：热塑性丙烯酸树脂、红色颜料、助剂、溶剂，助剂包括台湾德谦化学公司生产的消泡剂SJ-241、分散剂SJ-103、流平剂SJ-325，溶剂包括醋酸丁脂、CAC即乙二醇乙醚醋酸酯，油漆各成份的重量配比为：热塑性丙烯酸树脂80％、绿色颜料12.45％、助剂0.55％、溶剂7％。
热塑性丙烯酸油漆的生产方法包括以下步骤：
(1)将热塑性丙烯酸树脂、绿色颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散；
(2)将经过搅拌、分散的混合物使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um；
(3)在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌、混匀，获得热塑性丙烯酸油漆。
实施例3：一种热塑性丙烯酸油漆，包括：热塑性丙烯酸树脂、红色颜料、助剂、溶剂，助剂包括台湾德谦化学公司生产的消泡剂SJ-252、分散剂SJ-112、流平剂SJ-326，溶剂包括醋酸丁脂、CAC即乙二醇乙醚醋酸酯，油漆各成份的重量配比为：热塑性丙烯酸树脂82％、兰色颜料8.4％、助剂0.6％、溶剂9％。
所述热塑性丙烯酸油漆的生产方法包括以下步骤：
(1)将热塑性丙烯酸树脂、兰色颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散；
(2)将经过搅拌、分散的混合物使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um；
(3)在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌、混匀，获得热塑性丙烯酸油漆。
实施例4：一种热塑性丙烯酸油漆，包括：热塑性丙烯酸树脂、红色颜料、助剂、溶剂，助剂包括台湾德谦化学公司生产的消泡剂SJ-253、分散剂SJ-123S、流平剂SJ-328，溶剂包括醋酸丁脂、CAC即乙二醇乙醚醋酸酯，油漆各成份的重量配比为：热塑性丙烯酸树脂84％、所需颜色的颜料4.35％、助剂0.65％、溶剂11％。
所述热塑性丙烯酸油漆的生产方法包括以下步骤：
(1)将热塑性丙烯酸树脂、所需颜色的颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散；
(2)将经过搅拌、分散的混合物使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um；
(3)在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌、混匀，获得热塑性丙烯酸油漆。

Claims (8)

1、一种热塑性丙烯酸油漆，其特征是：所述油漆的组份包括：
热塑性丙烯酸树脂、颜料、助剂、溶剂。
2、如权利要求1所述的一种热塑性丙烯酸油漆，其特征是：所述油漆各成份的重量配比为：
热塑性丙烯酸树脂75～85％、颜料2.5～20％、助剂0.5～0.7％、溶剂4.3～12％。
3、如权利要求2所述的一种热塑性丙烯酸油漆，其特征是：所述油漆各成份的重量配比为：
热塑性丙烯酸树脂77～83％、颜料5.5～16％、助剂0.5～0.7％、溶剂6.3～11％。
4、如权利要求3所述的一种热塑性丙烯酸油漆，其特征是：所述油漆各成份的重量配比为：
热塑性丙烯酸树脂79～81％、颜料9～13％、助剂0.5～0.7％、溶剂7.3～9.5％。
5、如权利要求4所述的一种热塑性丙烯酸油漆，其特征是：所述油漆各成份的重量配比为：
热塑性丙烯酸树脂80％、颜料11％、助剂0.6％、溶剂8.4％。
6、如权利要求5所述的一种热塑性丙烯酸油漆，其特征是：所述助剂包括消泡剂、分散剂、流平剂。
7、如权利要求6所述的一种热塑性丙烯酸油漆，其特征是：所述溶剂包括醋酸丁脂、CAC。
8、一种热塑性丙烯酸油漆的生产方法，其特征是：所述生产方法包括以下步骤：
(1)将热塑性丙烯酸树脂、颜料、分散剂按照重量配比放置于拉缸内，使用高速分散机搅拌、分散；
(2)将经过搅拌、分散的混合物使用沙磨机研磨，至细度达到要求，其中面漆颗粒小于或等于20um，底漆颗粒小于或等于30um；
(3)在研磨后的油漆内按照重量配比添加消泡剂、流平剂、溶剂，使用高速分散机搅拌、混匀，获得热塑性丙烯酸油漆。
CN 200610044779 2006-06-15 2006-06-15 一种热塑性丙烯酸油漆 Pending CN101089063A (zh)