CN101054612B - 长寿型铁水预处理脱硫喷枪 - Google Patents

长寿型铁水预处理脱硫喷枪 Download PDF

Info

Publication number
CN101054612B
CN101054612B CN2006100792059A CN200610079205A CN101054612B CN 101054612 B CN101054612 B CN 101054612B CN 2006100792059 A CN2006100792059 A CN 2006100792059A CN 200610079205 A CN200610079205 A CN 200610079205A CN 101054612 B CN101054612 B CN 101054612B
Authority
CN
China
Prior art keywords
molten iron
pipeline
long life
iron pretreatment
spraying gun
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2006100792059A
Other languages
English (en)
Other versions
CN101054612A (zh
Inventor
刘东业
亚历山大罗夫·维克多·亚历山大罗维奇
舍甫钦柯·阿纳托里·费多罗维奇
巴什马科夫·亚历山大·米哈依洛维奇
杨嘉瑞
应理智
刘欣雨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YINGKOU DSMK TECHNOLOGY DEVELOPMENT CO., LTD.
Original Assignee
刘东业
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 刘东业 filed Critical 刘东业
Priority to CN2006100792059A priority Critical patent/CN101054612B/zh
Publication of CN101054612A publication Critical patent/CN101054612A/zh
Application granted granted Critical
Publication of CN101054612B publication Critical patent/CN101054612B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属黑色冶金范畴，具体涉及在铁水包中对铁水进行炉外处理的长寿型铁水预处理脱硫喷枪，其特点是，含有：管道(1)、枪本体(2)、位于管道(1)外侧的耐火材料层(4)、附在管道(1)外又置于耐火材料层(4)内的骨架(3)；所述管道(1)经骨架(3)与耐火材料层(4)配接；所述耐火材料层(4)以重量百分含量计含有：颗粒状尖晶石40～80；细粉状尖晶石5～30；细粉状赛隆1～10；细粉状蓝晶石2～10；辅助原料1～5；添加剂0.01～0.4。

Description

长寿型铁水预处理脱硫喷枪
技术领域
本发明属黑色冶金范畴，具体涉及在铁水包中对铁水进行炉外处理的长寿型铁水预处理脱硫喷枪。
背景技术
当今钢铁工业仍然是以高炉转炉长流程工艺为主流，钢产量约占总产量的70％，但其工艺在不断发展，随着分步炼钢的出现，转炉炼钢工序已分解成铁水预处理、转炉冶炼、炉外精练三个阶段，将炼钢的各种化学反应由过去在一个转炉内进行而分解到三个阶段来完成，各种化学反应在其最佳的条件下进行，结果是提高了生产率，降低了生产成本，获得了质量更加纯净的钢，满足了各种工业对钢质的更高要求。铁水预处理除特殊要求脱硅脱磷或提取一些特殊元素如钒钛和铌外，一般主要是对铁水脱硫。
脱硫喷枪是脱硫装置中的主要部件之一，喷枪寿命的长短直接影响铁水脱硫效果及铁水脱硫成本。
发明内容
本发明的目的旨在克服现有技术的不足之处而提供一种使用寿命长，体积稳定性好，中温强度高的长寿型铁水预处理脱硫喷枪。
本发明的技术解决方案可依如下方式实现：
一种长寿型铁水预处理脱硫喷枪，它含有：管道、枪本体、位于管道外侧的耐火材料层、附在管道外又置于耐火材料层内的骨架；所述管道经骨架与耐火材料层配接；所述耐火材料层以重量百分含量计含有：
颗粒状尖晶石    40～80
细粉状尖晶石    5～30
细粉状赛隆      1～10
细粉状蓝晶石    2～10
辅助原料        1～5
添加剂          0.01～0.4。
本发明所述管道内配有内管。所述管道的端口可配有耐火套管。所述管道的出口可设计成喇叭口结构。
本发明所述管道及内管的出口处可采用弯曲结构。
作为一种优选方案，本发明所述内管的出口处可为可拆装结构，其端口喷嘴与所述内管封接。
本发明在所述喷嘴的外部配有耐火套管。
本发明所述辅助原料以重量份计含有：
无机非金属微粉     1～4
无机结合剂         1～3。
其中所述添加剂可含有减水剂、防爆剂、增塑剂。
而其中所述无机结合剂为纯铝酸钙，减水剂为萘系磺酸盐、防爆剂为金属铝粉、增塑剂为羧甲基纤维素。
本发明对现有喷枪的耐材配方进行了实质性改进，其使用寿命长，体积稳定性好，中温强度高，本发明的主要特点如下：
1)以往技术比较注重常温(110℃×24h)强度和高温(1500℃×3h)强度，而本发明除保持上述两温度段强度外，还注重中温(1100℃×3h)强度，也就是说整个温度(常温、中温、高温)范围均能保持较高的强度(耐压≥100MPa)。
2)以往技术是常温、中温体积稳定，高温略重收缩，本专利产品在整个使用温度范围内，体积均比较稳定，高温线变化率±0.1％，急冷急热性(1100℃水冷)≥60次。
3)使用寿命≥100次。
附图说明
下面结合附图和具体实施方式对本发明作进一步说明。
图1为本发明的一种实施方式结构示意图；
图2为本发明的另一种实施方式结构示意图；
图3为本发明的第三种实施方式结构示意图；
图4为本发明的第四种实施方式结构示意图。
具体实施方式
实施例1
如图1所示，长寿型铁水预处理脱硫喷枪，它含有：管道1、枪本体2、位于管道1外侧的耐火材料层4、附在管道1外又置于耐火材料层4内的骨架3；所述管道1经骨架3与耐火材料层4配接；所述耐火材料层4以重量百分含量计含有：
颗粒状尖晶石    70
细粉状尖晶石    10
细粉状赛隆      10
细粉状蓝晶石    5
辅助原料        4.8
添加剂          0.2。
本发明所述管道1内可配有内管6(如图3)。本发明所述管道1的端口配有耐火套管5(如图2)。本发明所述管道1的出口为喇叭口结构。所述管道1及内管6的出口处可采用弯曲结构(如图4)。所述管道1的出口处为可拆装结构，其端口喷嘴7与所述内管6封接。在所述喷嘴7的外部配有耐火套管8(如图4)。所述辅助原料含有：无机非金属微粉(起促进烧结作用)、无机结合剂；无机非金属微粉与无机结合剂的重量比为1∶1。所述添加剂含有：减水剂、防爆剂、增塑剂。所述无机结合剂为纯铝酸钙，减水剂为萘系磺酸盐、防爆剂为金属铝粉、增塑剂为羧甲基纤维素。减水剂、防爆剂及增塑剂的用量可根据实际需要进行任意调配。
实施例2
本发明在机械结构上与实施例1相同而耐火材料层4还可采用如下组分(以重量百分含量计)：
颗粒状尖晶石    62
细粉状尖晶石    17
细粉状赛隆      8
细粉状蓝晶石    8
辅助原料        4.7
添加剂          0.3。
所述辅助原料含有：无机非金属微粉(起促进烧结作用)、无机结合剂；无机非金属微粉与无机结合剂的重量比为1∶1。所述添加剂含有：减水剂、防爆剂、增塑剂。所述无机结合剂为纯铝酸钙，减水剂为萘系磺酸盐、防爆剂为金属铝粉、增塑剂为羧甲基纤维素。减水剂、防爆剂及增塑剂的用量可根据实际需要进行任意调配。
上述耐火材料层的生产工艺过程为：
1)对主原料进行称量；
2)对辅助原料及添加剂进行称量后进行预混合；
3)将步骤1)及步骤2)的物料加水混合、成型、养生；
4)对步骤3)所得产品进行热处理、包装。
本发明长寿型铁水预处理脱硫喷枪的工作方式按下述实现：
喷枪下潜进入铁水到必要深度。打开给料器，通过喷注系统把籽粒镁送入喷枪内管6，继而通过可更换喷嘴7送到铁水中。喷入必需的剂量后停止吹送，把喷枪提离熔体，关闭载气。

Claims (7)

1.一种长寿型铁水预处理脱硫喷枪，其特征在于，含有：管道(1)、枪本体(2)、位于管道(1)外侧的耐火材料层(4)、附在管道(1)外又置于耐火材料层(4)内的骨架(3)；所述管道(1)经骨架(3)与耐火材料层(4)配接；所述耐火材料层(4)以重量百分含量计含有：
颗粒状尖晶石          40～80
细粉状尖晶石          5～30
细粉状赛隆            1～10
细粉状蓝晶石          2～10
辅助原料              1～5
添加剂                0.01～0.4；
所述辅助原料以重量份计含有：
无机非金属微粉        1～4；
无机结合剂            1～3；
所述添加剂含有减水剂、防爆剂、增塑剂；所述无机结合剂为纯铝酸钙，减水剂为萘系磺酸盐，防爆剂为金属铝粉，增塑剂为羧甲基纤维素；所述无机非金属微粉起促进烧结作用。
2.根据权利要求1所述长寿型铁水预处理脱硫喷枪，其特征在于：所述管道(1)内配有内管(6)。
3.根据权利要求1所述长寿型铁水预处理脱硫喷枪，其特征在于：所述管道(1)的端口配有耐火套管(5)。
4.根据权利要求1或2所述长寿型铁水预处理脱硫喷枪，其特征在于：所述管道(1)的出口为喇叭口结构。
5.根据权利要求2所述长寿型铁水预处理脱硫喷枪，其特征在于：所述管道(1)及内管(6)的出口处采用弯曲结构。
6.根据权利要求5所述长寿型铁水预处理脱硫喷枪，其特征在于：所述内管(6)的出口处为可拆装结构，其端口喷嘴(7)与所述内管(6)封接。
7.根据权利要求6所述长寿型铁水预处理脱硫喷枪，其特征在于：在所述喷嘴(7)的外部配有耐火套管(8)。
CN2006100792059A 2006-04-15 2006-04-15 长寿型铁水预处理脱硫喷枪 Expired - Fee Related CN101054612B (zh)