CN101045838A - 丝网印刷制备电解镍扣极板绝缘层的油墨 - Google Patents
丝网印刷制备电解镍扣极板绝缘层的油墨 Download PDFInfo
- Publication number
- CN101045838A CN101045838A CN 200610156306 CN200610156306A CN101045838A CN 101045838 A CN101045838 A CN 101045838A CN 200610156306 CN200610156306 CN 200610156306 CN 200610156306 A CN200610156306 A CN 200610156306A CN 101045838 A CN101045838 A CN 101045838A
- Authority
- CN
- China
- Prior art keywords
- electrolytic
- ink
- nickle
- printing ink
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种丝网印刷制备电解镍扣极板绝缘层的油墨，其特征在于该油墨含有重量比为10％～15％的低分子量环氧树脂E－51；20％～25％的氨基树脂585；30％～35％的蓖麻油醇酸树脂947；30％～35％的钛白粉R－930；0.5％～1.0％的有机膨润土；0.1％～0.5％的对甲苯磺酸；0.1％～0.3％的甲基硅油H－201；其细度小于20μm，用二甲苯调整黏度为3.5Pa.s～4.5Pa.s。该丝网油墨具有良好的印刷适性、较低的交联固化温度和较快的固化速度、附着力强、耐电解介质、绝缘性能好等特点，具有原料易得，工艺简单，适应性强，生产率高等特点，适合大规模工业生产。
Description
技术领域
丝网印刷制备电解镍扣极板绝缘层的油墨，涉及一种丝网油墨，特别是一种用于电解镍扣极板绝缘层印刷的丝网油墨。
背景技术
通过环氧树脂、氨基树脂、豆油醇酸树脂的三拼复合路线制备的油墨主要以平板印刷方式用于各种铁制品的印刷，以丝网印刷方式应用的并不多见，尤其在电化学冶炼中采用丝网印刷方式形成电解极板绝缘层更为少见。在电解镍扣生产中人们对电解极板绝缘层的制备进行的多种尝试中，在电解镍扣极板上丝网印刷上具有良好的印刷适性、较低的交联固化温度和较快的固化速度、附着力强、耐电解介质、印刷墨层厚、交联密度高、绝缘性能好等特点绝缘层的是一种全新的尝试。为此，寻求一种新的满足电解镍扣极板绝缘层制造要求的丝网油墨是必须的。
发明内容
本发明的目的就是为了提供一种具有良好的印刷适性、较低的交联固化温度和较快的固化速度、附着力强、耐电解介质、印刷墨层厚、交联密度高、绝缘性能好等特点丝网印刷制备电解镍扣极板绝缘层的油墨。
本发明的目的是通过以下技术方案实现的。
丝网印刷制备电解镍扣极板绝缘层的油墨，其特征在于该油墨含有重量比为10％～15％的低分子量环氧树脂E-51；20％～25％的氨基树脂585；30％～35％的蓖麻油醇酸树脂947；30％～35％的钛白粉R-930；0.5％～1.0％的有机膨润土；0.1％～0.5％的对甲苯磺酸；0.1％～0.3％的甲基硅油H-201；其细度小于20μm，用二甲苯调整黏度为3.5Pa.s～4.5Pa.s。
本发明的丝网印刷制备电解镍扣极板绝缘层的油墨，采用低分子量环氧树脂、氨基树脂、蓖麻油醇酸树脂为成膜物质，结合颜料与包括触变剂、流平剂、催干剂的助剂经分散研磨，得到适合丝网印刷的、满足电解镍扣绝缘层使用要求的单组分烘干型丝网油墨，固化温度为120℃～150℃，固化时间为3min～5min。
制备时按油墨配方量称取环氧树脂、氨基树脂、蓖麻油醇酸树脂、颜料与专用助剂(触变剂、流平剂、催干剂)，投入预分散容器中，搅拌使颜料粉体润湿并使体系初步分散。将预分散的物料送入三辊机中进行研磨，保持研磨料温低于30℃，以二甲苯调整黏度，当细度低于20μm、黏度为3.5Pa.s时即为合格，得到适合丝网印刷的、满足电解镍扣绝缘层使用要求的单组分烘干型丝网油墨。
本发明的优点在于该丝网油墨用于电解镍扣极板绝缘层的丝网印刷具有良好的印刷适性、较低的交联固化温度和较快的固化速度、附着力强、耐电解介质、印刷墨层厚、交联密度高、绝缘性能好等特点；该丝网油墨原料易得，工艺简单，适应性强，生产率高，适合大规模工业生产；该丝网油墨满足电解镍扣极板绝缘层的丝网印刷，具有重要的实用价值。
具体实施方式
丝网印刷制备电解镍扣极板绝缘层的油墨，该油墨含有重量比为10％～15％的低分子量环氧树脂E-51；20％～25％的氨基树脂585；30％～35％的蓖麻油醇酸树脂947；30％～35％的钛白粉R-930；0.5％～1.0％的有机膨润土；0.1％～0.5％的对甲苯磺酸；0.1％～0.3％的甲基硅油H-201；其细度小于20μm，用二甲苯调整黏度为3.5Pa.s～4.5Pa.s。
实施例1
准确称取蓖麻油醇酸树脂330.0g、环氧树脂142.8g、氨基树脂237.2g、钛白颜料280g、触变剂10g、流平剂1.2g、催干剂0.2g，将上述物料依次加入预分散容器中，用玻璃棒搅拌使固体粉料润湿达到初期预分散，然后，将预分散的物料在三辊机上进行研磨，研磨三道测细度小于20μm，用二甲苯调整黏度为3.5Pa.s，即得电解镍扣极板丝网印刷油墨。固化温度为120℃，固化时间为3min。丝网印刷制备的电解镍扣极板绝缘层效果好。
实施例2
准确称取蓖麻油醇酸树脂280.0g、环氧树脂192.8g、氨基树脂287.2g、钛白颜料230g、触变剂15g、流平剂1.0g、催干剂0.5g，将上述物料依次加入预分散容器中，用玻璃棒搅拌使固体粉料润湿达到初期预分散，然后，将预分散的物料在三辊机上进行研磨，研磨三道测细度小于20μm，用二甲苯调整黏度为4.5Pa.s，即得电解镍扣极板丝网印刷油墨。固化温度为150℃，固化时间为3min。丝网印刷制备的电解镍扣极板绝缘层效果好。
实施例3
准确称取蓖麻油醇酸树脂450.0g、环氧树脂140.8g、氨基树脂280.2g、钛白颜料320g、触变剂22.0g、流平剂2.0g、催干剂1.0g，将上述物料依次加入预分散容器中，用玻璃棒搅拌使固体粉料润湿达到初期预分散，然后，将预分散的物料在三辊机上进行研磨，研磨三道测细度小于20μm，用二甲苯调整黏度为4.5Pa.s，即得电解镍扣极板丝网印刷油墨。固化温度为120℃，固化时间为3min。丝网印刷制备的电解镍扣极板绝缘层效果好。
Claims (1)
1.丝网印刷制备电解镍扣极板绝缘层的油墨，其特征在于该油墨含有重量比为10％～15％的低分子量环氧树脂E-51；20％～25％的氨基树脂585；30％～35％的蓖麻油醇酸树脂947；30％～35％的钛白粉R-930；0.5％～1.0％的有机膨润土；0.1％～0.5％的对甲苯磺酸；0.1％～0.3％的甲基硅油H-201；其细度小于20μm，用二甲苯调整黏度为3.5Pa.s～4.5Pa.s。