CN101029281A - 清洁剂及其制备方法 - Google Patents

清洁剂及其制备方法 Download PDF

Info

Publication number
CN101029281A
CN101029281A CN 200710013785 CN200710013785A CN101029281A CN 101029281 A CN101029281 A CN 101029281A CN 200710013785 CN200710013785 CN 200710013785 CN 200710013785 A CN200710013785 A CN 200710013785A CN 101029281 A CN101029281 A CN 101029281A
Authority
CN
China
Prior art keywords
aeo
sanitising agent
stablizer
acetyl chloride
propionyl chloride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200710013785
Other languages
English (en)
Other versions
CN101029281B (zh
Inventor
李泽潜
殷立全
杨西军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2007100137856A priority Critical patent/CN101029281B/zh
Publication of CN101029281A publication Critical patent/CN101029281A/zh
Application granted granted Critical
Publication of CN101029281B publication Critical patent/CN101029281B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明为清洁剂及其制备方法，属于精细化工技术领域，特点是由AEO－9，AEO－7，乙酰氯，丙酰氯，NaHCO3和稳定剂按一定重量比制作而成，其制备方法是在反应釜内注入AEO－9和AEO－7混合物，加热后滴入乙酰氯和丙酰氯的混合液，经升温熟化反应、减压脱气、降温后加入稳定剂，用NaHCO3调节pH值，自然降温即可。各反应物支链相互渗透，互相连接，形成高分子量，多官能团，长链结构的共聚物，满足清洁、广泛、高效产品要求。

Description

清洁剂及其制备方法
技术领域
本发明属于工业化学品精细化工技术领域，特别是一种非离子表面活性清洁剂，本发明还涉及该产品的制备方法。
背景技术
发展高效、环保、常温的清洁剂，一直是清洁剂行业科研攻关的方向。一些科技发达国家近年均投入数以千万美元的科研经费，用于该项目的研究和开发。特别是工业清洗，如大型军事武器、大中型机械设备、航空、航海、冶金、矿山、化工、机电等行业，小到日常汽车修理，空调清洁，设备保养以及各种民用金属、非金属物件，卫生用具，门窗等的清洁去污等领域，都离不开清洁剂。每年在清洁行业(包括工业和民用)的消费额数以百亿计，且随着工业化程度的提高，呈逐年上升趋势。传统清洁剂目前大量使用的汽油、煤油、柴油、三氯乙烷等有机溶剂，存在清洗效率低，有环境污染、有腐蚀性、使用不方便等缺点，而且使用不安全、不方便，对人体有害，对环境污染。工业设备清洗使用尚可，而在民用方面却难以让人们接受。
发明内容
本发明的目的在于提供一种月桂醇聚氧乙烯醚(AE0-9、AE0--7)与乙酰氯、丙酰氯反应生成的复合酯类清洁剂，广泛、高效、环保。
本发明还涉及该种清洁剂的制备方法。
本发明是这样实现的：
清洁剂，其特征在于它是由下述重量配比的原料制作而成：AE0-9：450-500，AE0-7：350-430，乙酰氯：75-85，丙酰氯：88-93，NaHCO3：1--1.5和稳定剂：0.1-0.5。
制备上述清洁剂的方法，其特征在于：反应釜加热干燥后，注入AE0-9和AE0-7混合物，加热，滴入乙酰氯和丙酰氯的混合液，滴加完毕后，升温熟化反应，减压脱气，降温后加入稳定剂，用NaHCO3调PH值，自然降温。
本发明采用上述方案后，各反应物支链相互渗透，互相连接，形成高分子量，多官能团，长链结构的共聚物，满足清洁、广泛、高效、环保的要求。并具有如下技术效果：
(1)本发明清洁剂是一种无毒、无污染、无刺激性的非离子表面活性剂，能与其它无机、有机溶剂相混合、兼溶性强。
(2)无泡且具有抑泡、消泡等功能。
(3多支链、多官能团相互渗透，作用加强，每个分子具有两种亲水基和两个亲油基。中间亲水，两头亲油，无论是氧原子，还是羟基都具有与水分子生成氢键的能力。
(4)单体滴加发挥了单体贮藏所的作用，利用率高，质量稳定。
(5)抗静电能力强，在产品使用过程中多官能团，使动磨擦因数和静磨擦因数大幅度改变，使去污作用效果明显。
(6)适用范围广泛可用于航空、船舶、车辆、机电、冶金、油田、化工、纺织、民用等领域的金属件、陶瓷、玻璃、水泥制品、塑料制品、木制品、纺织品等。
(7)适应性强。常温、低温、高温均可使用，运用超声波清洗效果更佳。
具体实施方式
下面结合实施例对本发明作详细说明。
一、配方(Kg)
配方1：
AE0-9                    45.9
AE0-7                    38
乙酰氯                   7.5
丙酰氯                   9.2
NaHCO3               1
稳定剂                0.1
配方2：
AE0-9                 49.9
AE0-7                 43
乙酰氯                8.5
丙酰氯                8.8
NaHCO3               1.5
稳定剂                0.5
所述稳定剂可采用聚乙烯醇，也可采用MS-1与聚乙烯醇的混合物。
二、制备方法
按配方比取AE0-9和AE0-7充分混和后，备用；
乙酰氯和丙酰氯混合加入计量槽中，备用；
反应釜蒸汽加热干燥后，注入AE0-9和AE0-7混合物，加热至50℃左右；
慢慢滴入乙酰氯和丙酰氯的混合液，控制滴加速度，时间在45分钟以上；
滴加完毕，升温至82℃左右，熟化反应2.5小时；
测其折光率，达到1.4571-1.4575规定的范围后，减压脱气1小时，降温至60℃；
加入稳定剂；
用NaHCO3调PH值至7--8，自然降温40℃左右出料；
上述配料与若干去离子水混合即成为不同浓度的清洁剂。
三、产品特性
本清洁剂是由非离子表面活性剂和各种高效有机、无机化工助剂混制化合而成，浅黄色液体，性能平和稳定，按比例溶解于水后，即可对各种污染的油污进行清洗，去污能力远远超过于汽油(每千克相当于30千克汽油的清洗去污能力)，清洗成本仅为汽油的四分之一。该清洗剂适于金属件、非金属件、油漆、陶瓷、玻璃、水泥制品、木制品、塑料制环境无污染，对人体无毒害作用，属防锈型产品，对金属物件还具有相当的防锈功能。包装、运输、使用、贮存方便，而且可循环使用。
四、技术指标
1、外观：浅黄色油状液体
2、PH值：7-8(3％水溶液、25℃)
3、清洁力：≥85(3％水溶液60℃)
4、泡沫性能：≤80mm(50±150℃)
5、漂洗性能：(不锈钢片)无清洁剂残留物
五、质量对比
为验证本发明产品的技术效果，与珠海产CS-12进行了对比试验，试验结果如下：
  指标名称   CS-12   本发明产品
  清洁力   75   85
  泡沫能力   68   79
  漂洗性能   少量   无
结论：本发明产品的各项技术指标均高于CS-12产品。

Claims (6)

1、清洁剂，其特征在于它是由下述重量配比的原料制作而成：
AEO-9    450-500
AEO-7    350-430
乙酰氯   75-85
丙酰氯   88-93
NaHCO3  1--1.5
稳定剂   0.1-0.5。
2、根据权利要求1所述的清洁剂，其特征在于所述原料的重量配比为：
AEO-9    45.9
AEO-7    38
乙酰氯   7.5
丙酰氯   9.2
NaHCO3  1
稳定剂   0.1。
3、根据权利要求1或2所述的清洁剂，其特征在于所述稳定剂采用聚乙烯醇。
4、制备权利要求1所述的清洁剂的方法，其特征在于：反应釜加热干燥后，注入AEO-9和AEO-7混合物，加热，滴入乙酰氯和丙酰氯的混合液，滴加完毕后，升温熟化反应，减压脱气，降温后加入稳定剂，用NaHCO3调PH值，自然降温。
5、根据权利要求4所述的制备清洁剂的方法，其特征在于：AEO-9和AEO-7混合物的加热温度为50--60℃。
6、根据权利要求4或5所述的制备清洁剂的方法，其特征在于：熟化反应的温度为80--90℃，时间为2-3小时。
CN2007100137856A 2007-03-11 2007-03-11 清洁剂 Expired - Fee Related CN101029281B (zh)