CN101024878A - Environment-protection brightening type chemical nickel-plating additive - Google Patents
Environment-protection brightening type chemical nickel-plating additive Download PDFInfo
- Publication number
- CN101024878A CN101024878A CN 200610147751 CN200610147751A CN101024878A CN 101024878 A CN101024878 A CN 101024878A CN 200610147751 CN200610147751 CN 200610147751 CN 200610147751 A CN200610147751 A CN 200610147751A CN 101024878 A CN101024878 A CN 101024878A
- Authority
- CN
- China
- Prior art keywords
- plating
- agent
- environment
- chemical nickel
- type chemical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an environmental protection bright chemical nickel plating additive, belonging to the field of metal material surface strengthened protection and decoration technique, comprising complexing agent, stabilizer, brightening agent, surface active agent, and buffering agent, where the complexing agent is composed of one or more of the sodium citrate, lactic acid and malic acid; the brightening agent is composed of one or more of the cystine, bluestone and PESS. And it has advantages of environmental protection, use convenience, low cost, wide applications, convenience of storage and transportation; and the working plating solution prepared with it has stronger deep plating and uniform plating abilities, and the deposited coating has lower porosity, compact and fully bright.
Description
Technical field
The present invention relates to a kind of chemical nickel-plating additive, relate in particular to a kind of environment-protection brightening type chemical nickel-plating additive; Belong to metal material surface enhanced protection and decoration technique field.
Background technology
Electroless plating is to utilize appropriate reductant, the solution metal ion is restored, and be deposited on a kind of chemical treating process through the plating piece surface of catalytic activation.For the nickel process under the acidic conditions, can represent with following two reaction formula:
[NiL]
2++2e
-→Ni+L
2Ni+7H
2PO
2 -+H
2O-7e
-→5H
2PO
3 -+2Ni-P+2H
2↑+2H
+
In recent years, electroless plating comes into one's own industrial day by day as a kind of process for treating surface, and its range of application has covered industrial every field.The continuous development of chemical nickel plating ascribes this technology to and has favorable manufacturability, chemical Ni-plating layer has unique physics, chemistry and mechanical property, and processing unit is simple, be easy to control and grasp, coating is evenly smooth, be applicable to the complicated shape part, environmentally friendly, these all are that electroplating technology is not available.
At present, chemical nickel-plating liquid is commercialization all, typical commercial chemistry nickel-plating liquid by main salt (single nickel salt), reductive agent (sodium hypophosphite), buffer reagent (sodium-acetate), and multiple complexing agent, stablizer, brightening agent, wetting agent, pH value adjust concentrated solution A, B, the C liquid that agent etc. is formed, open cylinder by A, B liquid, A, C liquid are added, its operating procedure is extremely strict, stores and also extremely inconvenience of transportation.
Chinese patent application (200410036014.5) relates to a kind of chemical nickel plating composite additive, and this composite additive is made up of stablizers such as accelerators such as buffer reagents such as complexing agents such as citric acid, sodium acetate, Succinic Acid, thiocarbamides; Though it has avoided macromethod to adjust the trouble of multiple composition, use more convenient; But do not contain brightening agent and tensio-active agent in this composite additive, coating is easy to generate pin hole, and porosity is bigger; The solidity to corrosion of coating and ornamental all relatively poor; And the use of stablizer thiocarbamide, having reduced the coating passivation ability, its intensive adsorption makes coating hole occur easily.
Summary of the invention
The existing operating procedure of commercial chemistry nickel-plating liquid that the present invention is directed to prior art is extremely strict, store and transport also extremely inconvenient defective a kind of environment-protection brightening type chemical nickel-plating additive is provided, but the work plating bath self-catalyzed deposition under operational condition with this chemical nickel-plating additive preparation goes out densification, light, uniform nickel phosphorus base binary alloy plating, easy to use, be convenient to store and transportation;
The present invention also is easy to generate pin hole at the chemical nickel plating composite additive of prior art, and the coating porosity is bigger; The solidity to corrosion of coating and ornamental all relatively poor defective provide a kind of formation of eliminating the coating pin hole, reduce the coating porosity, improve coating performance, improve the solidity to corrosion and the ornamental environment-protection brightening type chemical nickel-plating additive of coating.
Above-mentioned technical problem of the present invention is implemented by the following technical programs: a kind of environment-protection brightening type chemical nickel-plating additive, and every premium on currency solution of this additive comprises the composition of following weight:
Complexing agent: 300~600g; Stablizer: 0.3~1g;
Brightening agent: 2~10g; Tensio-active agent: 0.1~0.5g;
Buffer reagent: 250~500g;
Wherein said complexing agent is grouped into by one or more one-tenth in Trisodium Citrate, lactic acid, the oxysuccinic acid; Described stablizer is grouped into by one or both one-tenth in Potassium Iodate, the Sulfothiorine; Described brightening agent is grouped into by one or more one-tenth in Gelucystine, copper sulfate, the PESS; Described tensio-active agent is grouped into by one or more one-tenth in sodium lauryl sulphate, Sodium dodecylbenzene sulfonate, the n-octyl sodium sulfate.Environment-protection brightening type chemical nickel-plating additive of the present invention comprises complexing agent, stablizer, brightening agent, tensio-active agent and buffer reagent; Wherein tensio-active agent can quicken the discharging of hydrogen in the work plating bath, reduces the formation of pin hole, thereby reduces the coating porosity; And the adding of brightening agent can be so that the surface of coating be complete bright, and appearance property is better; The compound use of two kinds of compositions can be eliminated the formation of coating pin hole, reduces the coating porosity, improves coating performance, the solidity to corrosion of raising coating and ornamental.Be compounded to form environment-protection brightening type chemical nickel-plating additive of the present invention with the multiple material of complexing agent, stablizer, brightening agent, tensio-active agent and buffer reagent; When preparation work plating bath, only need add on a small quantity, under operational condition, can go out densification, light, uniform nickel phosphorus base binary alloy plating by self-catalyzed deposition.
In above-mentioned environment-protection brightening type chemical nickel-plating additive, described buffer reagent is a sodium-acetate.
In above-mentioned environment-protection brightening type chemical nickel-plating additive, described complexing agent is a compound complex agent, and this compound complex agent is made up of Trisodium Citrate, lactic acid, oxysuccinic acid; Every premium on currency solution of described additive comprises lactic acid 200-500 milliliter, Trisodium Citrate 50-200 gram, oxysuccinic acid 50-200 gram.Adopt compound complex agent can with Ni
2+Form polynary ligand, favourable to bath stability and life cycle, and higher sedimentation velocity and stable phosphorus content are arranged.
In above-mentioned environment-protection brightening type chemical nickel-plating additive, described stablizer is an one package stabilizer, and this one package stabilizer is made up of Potassium Iodate, Sulfothiorine; Every premium on currency solution of described additive comprises Potassium Iodate 0.2-0.5 gram, Sulfothiorine 0.1+0.4 gram.
In above-mentioned environment-protection brightening type chemical nickel-plating additive, described brightening agent is a composite brightening agent, this composite brightening agent is made up of Gelucystine, copper sulfate, PESS, and every premium on currency solution of wherein said additive comprises Gelucystine 0.05-0.2 gram, copper sulfate 0.5-3 gram, PESS 1-5ml.It is by being adsorbed on the micro cathode district of catalytic surface that the present invention adopts composite brightening agent, the surface tension at interface is reduced, hydrogen is easy to separate out, it is careful to help crystallization, particularly the metal ion in the composite brightening agent participates in codeposition, stoped growing up of Ni-P crystal grain, prior art is not added the coating surface big rise and fall of brightening agent, often surpass 300nm, and the surface cell size is inhomogeneous, after adding composite brightening agent of the present invention, surface undulation has only about 50nm, and structure cell is even, and the coating that therefore adopts composite brightening agent of the present invention and obtained is smooth, the light porosity is low, thickness is even, has obviously improved the glossiness and the solidity to corrosion of coating surface.Complicated shape had excellent all platings and covering power.
Environment-protection brightening type chemical nickel-plating additive of the present invention is prepared by the following method:
Volume by the preparation environment-protection brightening type chemical nickel-plating additive calculates the weight of required complexing agent, stablizer, brightening agent, tensio-active agent and buffer reagent and carries out weighing;
With mentioned component with deionized water or dissolved in distilled water;
Various composition uniform mixing with after the dissolving add deionized water or distilled water to prescribed volume; Filter out the impurity in the composition in case of necessity.
In addition, the present invention also provides the application of environment-protection brightening type chemical nickel-plating additive in electroless plating; The consumption of wherein said environment-protection brightening type chemical nickel-plating additive is to add 10~20 milliliters in every liter of plating bath.
Concrete use is: will select the qualified product that meet national standard for use as solution, single nickel salt, sodium hypophosphite that single nickel salt, the sodium hypophosphite of main salt, reductive agent is mixed with 500 grams per liter concentration respectively;
In the coating bath of cleaning, add half deionized water or clean water of prescribed volume, the above-mentioned solution of dissolved is added coating bath successively by the concentration of single nickel salt 20-30 grams per liter, sodium hypophosphite 20-35 grams per liter under stirring condition;
Add environment-protection brightening type chemical nickel-plating additive 10-20 milliliter of the present invention/liter, add deionized water or distilled water to prescribed volume, remove by filter impurity in case of necessity;
Adjust plating under pH value can be warming up to 82~88 ℃ to 4.0-5.1 the condition with sodium hydroxide or ammoniacal liquor or glacial acetic acid; Plating bath can constantly be added continuous plating by consumption.
Therefore, the present invention has the following advantages:
1, environment-protection brightening type chemical nickel-plating additive of the present invention need not have toxic heavy metal ion used as stabilizers, brightening agents such as lead, cadmium, therefore adds the coating environmental protection that this additive deposits, and can reach the ROHS of European Union standard.
Go out densification, full light, nickel phosphorus base binary alloy plating uniformly but 2, adopt environment-protection brightening type chemical nickel-plating additive of the present invention to add in the work plating bath of preparation not only self-catalyzed deposition to, and it is stronger to add dark plating, the covering power of work plating bath of preparation to.
3, environment-protection brightening type chemical nickel-plating additive of the present invention is not only easy to use, and the few cost of addition is low; And be convenient to store and transportation.
4, adopt environment-protection brightening type chemical nickel-plating additive of the present invention can reduce the formation of coating pin hole, reduce the coating porosity, improve coating performance, the coating outward appearance reaches full light, thereby improves its solidity to corrosion and ornamental.
5, environment-protection brightening type chemical nickel-plating additive of the present invention has changed the sales mode of traditional chemical nickel-plating liquid, can be at coating surfaces such as iron, aluminium, copper; Can be widely used in food machinery, mould, cooker, hot-water heating valve, stitch machine, vapour rub accessory, electronic product etc.
Embodiment
Below be specific embodiments of the invention, technical scheme of the present invention is further described, but the present invention is not limited to these embodiment.
Embodiment 1:
300 milliliters of lactic acid, Trisodium Citrate 50 grams, oxysuccinic acid 50 grams, Potassium Iodate 0.4 gram, Sulfothiorine 0.1 gram, Gelucystine 0.05 gram, copper sulfate 0.5 gram, 5 milliliters of PESSs, sodium lauryl sulphate 0.4 restrain in taking by weighing in the required every liter of additive of ratio of prescription, sodium-acetate 400 restrains and puts into container adding deionized water respectively it is dissolved, composition after the above-mentioned dissolving is mixed, add deionized water to required volume, promptly make the environment-protection brightening type chemical nickel-plating additive of embodiment 1.
The comparative example 1
Put into container adding deionized water respectively for 60 milligrams it is dissolved in taking by weighing tartrate 100 grams, oxysuccinic acid 100 grams, lactic acid 100g, Succinic Acid 50g, molybdenum oxide 60mg, potassiumiodide in the required every liter of additive of ratio of prescription, composition after the above-mentioned dissolving is mixed, add deionized water to required volume, promptly make comparative example 1 environment-protection brightening type chemical nickel-plating additive.
Application Example 1
Select for use the single nickel salt, the sodium hypophosphite that meet national standard to be mixed with the solution of 500 grams per liter concentration; In the coating bath of cleaning, add half deionized water of prescribed volume, the above-mentioned solution of dissolved is added to coating bath successively by the concentration of single nickel salt 25 grams per liters, sodium hypophosphite 25 grams per liters, and stirs; 10 milliliters/liter of the environment-protection brightening type chemical nickel-plating additives of adding embodiment 1 add deionized water to prescribed volume, remove by filter impurity in case of necessity; Adjust plating under the condition that pH value to 4.6 ± 2 can be warming up to 85 ± 3 ℃; Plating bath can constantly be added continuous plating by consumption, and sedimentation velocity is 15~25um/h in the plating process, and plating bath can recycle 12 cycles continuously; Coating is the base binary alloy plating of non-crystalline state, non magnetic, phosphorus content 7-9wt% after the plating, and its performance is as shown in table 1.
Contrast Application Example 1
The environment-protection brightening type chemical nickel-plating additive of the foregoing description 1 is changed into comparative example 1 environment-protection brightening type chemical nickel-plating additive, other condition is with Application Example 1, sedimentation velocity is 15~25um/h in the plating process, and plating bath can recycle 12 cycles continuously; Coating is the base binary alloy plating of non-crystalline state, non magnetic, phosphorus content 7-9wt% after the plating, and its performance is as shown in table 1.
Table 1: the performance of coating is as follows under two kinds of embodiments
As can be seen from Table 1, the environment-protection brightening type chemical nickel-plating additive of the embodiment of the invention 1 adds the sedimentary nickel phosphorus of work plating bath base binary alloy plating to and has higher compactness, outward appearance is light entirely, and bonding force is stronger, and hardness is higher to have solidity to corrosion and decorate properties preferably.
Embodiment 2:
200 milliliters of lactic acid, Trisodium Citrate 50 grams, oxysuccinic acid 50 grams, Potassium Iodate 0.2 gram, Sulfothiorine 0.2 gram, Gelucystine 0.1 gram, copper sulfate 1 gram, 3 milliliters of PESSs, Sodium dodecylbenzene sulfonate 0.2 restrain in taking by weighing in the required every liter of additive of ratio of prescription, sodium-acetate 350 restrains and puts into container adding deionized water respectively it is dissolved, composition after the above-mentioned dissolving is mixed, add deionized water to required volume, promptly make the environment-protection brightening type chemical nickel-plating additive of embodiment 2.
Application Example 2
Select for use the single nickel salt, the sodium hypophosphite that meet national standard to be mixed with the solution of 500 grams per liter concentration; In the coating bath of cleaning, add half deionized water of prescribed volume, the above-mentioned solution of dissolved is added to coating bath successively by the concentration of single nickel salt 20 grams per liters, sodium hypophosphite 20 grams per liters, and stirs; 20 milliliters/liter of the environment-protection brightening type chemical nickel-plating additives of adding embodiment 1 add deionized water to prescribed volume, remove by filter impurity in case of necessity; Adjust plating under the condition that pH value to 4.4 ± 2 can be warming up to 85 ± 3 ℃; Plating bath can constantly be added continuous plating by consumption, and sedimentation velocity is 15~20um/h in the plating process, and plating bath can recycle 10 cycles continuously; Coating is the base binary alloy plating of non-crystalline state, non magnetic, phosphorus content 8-10wt% after the plating, and its performance is as shown in table 2.
Embodiment 3:
50 milliliters of lactic acid, Trisodium Citrate 200 grams, oxysuccinic acid 100 grams, Potassium Iodate 0.3 gram, Sulfothiorine 0.1 gram, Gelucystine 0.1 gram, copper sulfate 1.5 grams, 4 milliliters of PESSs, n-octyl sodium sulfate 0.3 restrain in taking by weighing in the required every liter of additive of ratio of prescription, sodium-acetate 300 restrains and puts into container adding deionized water respectively it is dissolved, composition after the above-mentioned dissolving is mixed, add deionized water to required volume, promptly make the environment-protection brightening type chemical nickel-plating additive of embodiment 3.
Application Example 3
Select for use the single nickel salt, the sodium hypophosphite that meet national standard to be mixed with the solution of 500 grams per liter concentration; In the coating bath of cleaning, add half deionized water of prescribed volume, the above-mentioned solution of dissolved is added to coating bath successively by the concentration of single nickel salt 24 grams per liters, sodium hypophosphite 21 grams per liters, and stirs; 10 milliliters/liter of the environment-protection brightening type chemical nickel-plating additives of adding embodiment 1 add deionized water to prescribed volume, remove by filter impurity in case of necessity; Adjust plating under the condition that pH value to 4.2 ± 2 can be warming up to 85 ± 3 ℃; Plating bath can constantly be added continuous plating by consumption, and sedimentation velocity is 15~20um/h in the plating process, and plating bath can recycle 10 cycles continuously; Coating is the base binary alloy plating of non-crystalline state, non magnetic, phosphorus content 9-11wt% after the plating, and its performance is as shown in table 2.
Table 2: the performance of coating is as follows under two kinds of embodiments
As can be seen from Table 2: the environment-protection brightening type chemical nickel-plating additive of the embodiment of the invention 2~3 adds the sedimentary nickel phosphorus of work plating bath base binary alloy plating to and also has higher compactness, outward appearance is light entirely, bonding force is stronger, and hardness is higher to have solidity to corrosion and decorate properties preferably.
Specific embodiment described in the present invention only is that the present invention's spirit is illustrated.The technician of the technical field of the invention can make various modifications or replenishes or adopt similar mode to substitute described specific embodiment, but can't depart from spirit of the present invention or surmount the defined scope of appended claims.
Although the present invention has been made detailed explanation and has quoted some specific exampless as proof, to those skilled in the art, only otherwise leave that the spirit and scope of the present invention can be done various variations or correction is obvious.
Claims (7)
1, a kind of environment-protection brightening type chemical nickel-plating additive is characterized in that, every premium on currency solution of this additive comprises the composition of following weight:
Complexing agent: 300~600g; Stablizer: 0.3~1g;
Brightening agent: 2~10g; Tensio-active agent: 0.1~0.5g;
Buffer reagent: 250~500g;
Wherein said complexing agent is grouped into by one or more one-tenth in Trisodium Citrate, lactic acid, the oxysuccinic acid; Described stablizer is grouped into by one or both one-tenth in Potassium Iodate, the Sulfothiorine; Described brightening agent is grouped into by one or more one-tenth in Gelucystine, copper sulfate, the PESS; Described tensio-active agent is grouped into by one or more one-tenth in sodium lauryl sulphate, Sodium dodecylbenzene sulfonate, the n-octyl sodium sulfate.
2, environment-protection brightening type chemical nickel-plating additive according to claim 1 is characterized in that, described buffer reagent is a sodium-acetate.
3, environment-protection brightening type chemical nickel-plating additive according to claim 1 and 2 is characterized in that, described complexing agent is a compound complex agent, and this compound complex agent is made up of Trisodium Citrate, lactic acid, oxysuccinic acid; Every premium on currency solution of described additive comprises lactic acid 200-500 milliliter, Trisodium Citrate 50-200 gram, oxysuccinic acid 50-200 gram.
4, environment-protection brightening type chemical nickel-plating additive according to claim 1 and 2 is characterized in that, described stablizer is an one package stabilizer, and this one package stabilizer is made up of Potassium Iodate, Sulfothiorine; Every premium on currency solution of described additive comprises Potassium Iodate 0.2-0.5 gram, Sulfothiorine 0.1-0.4 gram.
5, environment-protection brightening type chemical nickel-plating additive according to claim 1 and 2, it is characterized in that, described brightening agent is a composite brightening agent, this composite brightening agent is made up of Gelucystine, copper sulfate, PESS, and every premium on currency solution of wherein said additive comprises Gelucystine 0.05-0.2 gram, copper sulfate 0.5-3 gram, PESS 1-5ml.
6, the application of a kind of environment-protection brightening type chemical nickel-plating additive as claimed in claim 1 in electroless plating.
7, application according to claim 6 is characterized in that, the consumption of described environment-protection brightening type chemical nickel-plating additive is to add 10~20 milliliters in every liter of plating bath.