CN101024361A - Tiffany glass making method - Google Patents
Tiffany glass making method Download PDFInfo
- Publication number
- CN101024361A CN101024361A CN 200710026565 CN200710026565A CN101024361A CN 101024361 A CN101024361 A CN 101024361A CN 200710026565 CN200710026565 CN 200710026565 CN 200710026565 A CN200710026565 A CN 200710026565A CN 101024361 A CN101024361 A CN 101024361A
- Authority
- CN
- China
- Prior art keywords
- glass
- supreme
- tiffany
- preparation
- glassware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to Tiffany glass manufacturing method. It aims to solve the problem of complex processing for using the Tiffany as decorating material in existing technology. This method is simple and practical. Its detail can be seen in the specification.
Description
Technical field
The present invention relates to decoration material field, more particularly, relate to a kind of preparation method of Tiffany glass.
Background technology
The all Buddhist nuns of Supreme Being are as a kind of ornament materials, with its surperficial distinctive skin texture and beautiful color, favored by the consumer, at home and abroad, be widely applied in building occupancy, all use all Buddhist nuns of Supreme Being always as external some church and civil buildings and decorated, Tiffany glass demonstrates unique decorative effect under the irradiation of light.The all Buddhist nuns of Supreme Being also are widely used aspect lamp decoration product.The application of all Buddhist nuns of Supreme Being aspect lamp decoration product is based on American-European style, promptly the form with scolding tin is fixed on all Buddhist nuns of Supreme Being on the light fixture as additional the decoration on the copper cash model support, light fixture with all Buddhist nuns of Supreme Being as the printing opacity main body, simple and tasteful on style, but its processing technology is very complicated, and some gently moving design flexible that are beyond expression can't satisfy growing design requirement.
Summary of the invention
An object of the present invention is to solving in the above-mentioned prior art all Buddhist nuns of Supreme Being very complicated as the ornament materials processing technology, some gently moving design flexible are beyond expression, can't satisfy the problem of growing design requirement, a kind of preparation method of Tiffany glass is provided.
For achieving the above object, technical scheme of the present invention provides a kind of preparation method of Tiffany glass, and this method technology is as follows:
A. glassware is processed processing;
C. with all Buddhist nun's cutting formings of Supreme Being;
D. allocate glue;
E. even spreading glue on all Buddhist nuns of Supreme Being is bonded at glassware through that face that the A step processes, and exerts pressure, and 2-10 minute, preferred 3 minutes, gets final product.
The all Buddhist nuns of Supreme Being are through the water under high pressure cutting forming
Between A step and C step, can also establish the B1 step: all Buddhist nuns of glass and Supreme Being carry out curved processing.
It is consistent that glass and all Buddhist nuns of Supreme Being carry out the radian that curved is processed to form.
Between B1 step and C step, can also establish the B2 step: carry out decal paper technology by prior art.
In the described A step glassware processed and be treated to technologies such as boundary of the prior art sheet, water cut, bore, mill.
650 degrees centigrade of curved temperature, 680 degrees centigrade of glass curved temperature.
Described allotment glue is A glue: B glue is 1: 1, mixes preferred 25 ℃ down at 20-30 ℃.
AB glue manufacturer imperial crown adhesive article Vietnam subsidiary factory, address: Dongguan City Humen town.
The light pressure of exerting pressure in the described E step get final product, there is no particular restriction, and be generally all passable from being pressed onto with have gentle hands not in the pressure limit that glass and all Buddhist nuns of Supreme Being can be crushed, preferably 5-6 Pascal.
Method of the present invention is equally applicable to all Buddhist nuns of Supreme Being and is adhesive in body surfaces such as aluminum component, ironware, ligneous piece, light source surface, plastic parts, merchant wire.
The present invention is with respect to the beneficial effect of prior art: the inventive method is produced on all Buddhist nun's goods of the Supreme Being technology and has been carried out great simplification, and the quality of product is better, not only can remain with the elegant and graceful of all Buddhist nun's goods of original Supreme Being, and can show some gently moving design flexible, processing in detail is also more lively, multi-level product can be set, and, the fraction defective of product can be controlled in below 3%, PR welding technique for fixing is more than high ten times, energy resource consumption is few, can not produce harmful substance, more helps environmental protection.
The specific embodiment
Further specify the present invention below in conjunction with embodiment, but not as a limitation of the invention.
Embodiment 1
A. glassware is processed processing, edging after the prior art water under high pressure cuts behind the decal paper sanding that sprays paint, carries out curved and handles;
C. all Buddhist nuns of Supreme Being are cut off through the prior art water under high pressure and be slit into shape, carry out curved and handle, all Buddhist nun's curveds of Supreme Being radian is consistent with the glass radian;
D. allocate glue, the AB glue that imperial crown adhesive article Vietnam subsidiary factory is produced mixes under 25 ℃ with 1: 1 ratio;
E. even spreading glue on all Buddhist nuns of Supreme Being is bonded at glassware through that face that the A step processes, the 5-6 Pascal that exerts pressure, and not removable dislocation in 3 minutes, exert pressure got final product in 8 minutes.
650 ℃ of curved temperature, 680 ℃ of glass curved temperature.
But the Tiffany glass heatproof does not come off for 200 ℃.
Claims (6)
1. the preparation method of a Tiffany glass, this method technology is as follows:
A. glassware is processed processing
C. with all Buddhist nun's cutting formings of Supreme Being;
D. allocate glue;
E. even spreading glue on all Buddhist nuns of Supreme Being is bonded at glassware through that face that the A step processes, and exerts pressure, and 2-10 minute, preferred 3 minutes, gets final product.
2. according to the preparation method of the described Tiffany glass of claim 1, it is characterized in that, between A step and C step, can also establish the B1 step: all Buddhist nuns of glass and Supreme Being carry out curved processing.
3. according to the preparation method of the described Tiffany glass of claim 2, it is characterized in that it is consistent that glass and all Buddhist nuns of Supreme Being carry out the radian that curved is processed to form.
4. according to the preparation method of the described Tiffany glass of claim 1, it is characterized in that, between B1 step and C step, can also establish the B2 step: carry out decal paper technology by prior art.
5. according to the preparation method of the described Tiffany glass of claim 1, it is characterized in that, in the described A step glassware processed and be treated to technologies such as boundary of the prior art sheet, water cut, bore, mill.
6. according to the preparation method of the described Tiffany glass of claim 1, it is characterized in that described cutting forming is the water under high pressure cutting forming.