CN103465713B - A kind of processing technology of inlaying mother-of-pearl inlay - Google Patents
A kind of processing technology of inlaying mother-of-pearl inlay Download PDFInfo
- Publication number
- CN103465713B CN103465713B CN201310429545.XA CN201310429545A CN103465713B CN 103465713 B CN103465713 B CN 103465713B CN 201310429545 A CN201310429545 A CN 201310429545A CN 103465713 B CN103465713 B CN 103465713B
- Authority
- CN
- China
- Prior art keywords
- mother
- shell
- pearl inlay
- inlaying
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of processing technology of inlaying mother-of-pearl inlay, comprise the following steps: shell, awabi sheet or spiral shell shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern; The surface of polishing for inlaying mother-of-pearl inlay body; Gained patterned surfaces is applied glue, is pasted onto on body; After 22 ~ 26 hours, with hot water, pattern for subsequent use is washed off; After moisture content is dry, with liquid honing, and spray paint first and be baked to 130 ~ 150 DEG C, taking-up cools completely; After polishing, baking of again spraying paint arrives finished product 3 times repeatedly.The technique that the present invention inlays mother-of-pearl inlay is simple, and pattern part lines are lively, life-like, overcome the defect that existing process is stiff, stiff.
Description
Technical field
The present invention relates to the technology field making ornament, particularly a kind of processing technology of inlaying mother-of-pearl inlay.
Background technology
Mother-of-pearl inlay, also known as " Luo Dian ", " spiral shell is filled out ", " coin is embedding ", " fall in freshwater mussel ", " bank spiral shell " and " sieve coin ", also have in history and be " coin spiral shell ", it is Chinese distinctive art rarity.So-called " mother-of-pearl inlay ", refers to and grinds into the thin slices such as personage, birds and flowers, geometric figure or word with spiral shell shell and sea cowry, be embedded in the general name of the decoration technology on implements surface according to picture needs.Because mother-of-pearl inlay is a kind of natural thing, outward appearance natural beauty, having ferocious visual effect, is therefore also a kind of modal traditional decoration art, is widely used on lacquerware, furniture, musical instrument, screen, box casket, basin dish, woodcarving and relevant handicraft.
Traditional mother-of-pearl inlay mosaic technology: execute flax silk on the surface of wood paint thing, execute cinder, paste cotton paper, execute thin ash, execute pitch-dark multipass, inlay mother-of-pearl inlay (the spiral shell freshwater mussel cut out and gold and silver, colored stone sheet), cover pitch-dark multipass, polishing pushes away light again, until mother-of-pearl inlay exposes, become plane.Though present this technology has improvement, but still there is complex process, handicraft surface poor flatness, there is stiff, stiff defect in pattern.
Summary of the invention
The invention provides a kind of processing technology of inlaying mother-of-pearl inlay, solve existingly inlay mother-of-pearl inlay complex process, there is stiff, stiff defect in pattern.
Technical scheme of the present invention is achieved in that a kind of processing technology of inlaying mother-of-pearl inlay, comprises the following steps:
1) shell, awabi sheet or spiral shell shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern;
2) surface of polishing for inlaying mother-of-pearl inlay body;
3) step 1 gained patterned surfaces is applied glue, be pasted onto on body;
4), after 22 ~ 26 hours, with hot water, pattern for subsequent use is washed off;
5) after moisture content is dry, with liquid honing, and spray paint first and be baked to 130 ~ 150 DEG C, taking-up cools completely;
6), after polishing, baking of again spraying paint arrives finished product 3 times repeatedly.
Wherein, preferably, described is porcelain utensil for inlaying mother-of-pearl inlay body.
Wherein, preferably, described porcelain utensil is porcelain dish or porcelain vase.
Wherein, preferably, in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 0.02 ~ 0.07mm.
Wherein, preferably, in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 1 ~ 5mm.
Wherein, preferably, the glue in described step 3 is resistant to elevated temperatures super glue.
Wherein, preferably, the temperature of the hot water in described step 4 is more than 80 DEG C.
Wherein, preferably, described step 6 also comprises the step be plotted to by seven color powder on mother-of-pearl inlay before again spraying paint.
The present invention has following beneficial effect:
1. the present invention inlays the technique of mother-of-pearl inlay simply, and when mother-of-pearl inlay thinner thickness, form the smooth light face that does not have concave-convex sense, shell pattern part lines are lively, life-like, overcome the defect that existing process is stiff, stiff.
2., when the part that the mother-of-pearl inlay adopted is the thickest reaches 4 ~ 5mm, the mother-of-pearl inlay adopting the method for this technique to inlay reaches the artistic effect of embossment.
3. porcelain (porcelain dish, porcelain vase) the institute drawing case had now is Freehandhand-drawing and draws (high temperature) or pattern stickup (low temperature), forms through baking.And porcelain utensil mother-of-pearl inlay technique is pattern shell raw material and awabi thin slice formed, can be combined and difficult drop-off with porcelain utensil preferably, be the another new form of expression of porcelain product.
Detailed description of the invention
Be clearly and completely described the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
The present embodiment inlays mother-of-pearl inlay on porcelain vase, and it inlays the processing technology of mother-of-pearl inlay, comprises the following steps:
1) shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern; Wherein, shell thickness is 1 ~ 5mm, and it is according to the needs of composition, and thin and thick distributes.
2) surface of polishing porcelain vase;
3) step 1 gained patterned surfaces is coated super glue, be pasted onto on porcelain vase;
4), after 22 hours, with 80 DEG C of hot water, pattern for subsequent use is washed off;
5) after moisture content is dry, with liquid honing, and spray paint first and be baked to 150 DEG C, taking-up cools completely;
6) after polishing, by the method for artificial Freehandhand-drawing, needed to be plotted on the shell of porcelain vase by seven color powder according to composition, baking of again spraying paint arrives finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that step of spraying paint adopts is varnish.
Adopt this process to be mounted on porcelain vase by mother-of-pearl inlay, the porcelain vase made, because shell thickness is thicker, porcelain vase surface irregularity after spraying paint, reaches the effect of embossment, and its pattern is more lively.
Embodiment 2
The present embodiment inlays mother-of-pearl inlay on porcelain vase, and it inlays the processing technology of mother-of-pearl inlay, comprises the following steps:
1) the awabi sheet through being polished to being pasted onto on pattern for subsequent use, making it to become pattern; Wherein, the thickness of awabi sheet is 0.02 ~ 0.07mm.
2) surface of polishing porcelain vase;
3) step 1 gained patterned surfaces is coated super glue, be pasted onto on porcelain vase;
4), after 24 hours, with 90 DEG C of hot water, pattern for subsequent use is washed off;
5) after moisture content is dry, with liquid honing, and spray paint first and be baked to 140 DEG C, taking-up cools completely;
6) after polishing, by the method for artificial Freehandhand-drawing, needed to be plotted on the awabi thin slice of porcelain vase by seven color powder according to composition, baking of again spraying paint arrives finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that step of spraying paint adopts is varnish.
Adopt the porcelain vase that this process is made, its surface forms the smooth light face that does not have concave-convex sense, and pattern part lines are lively, life-like, overcome the defect that existing process is stiff, stiff.
Embodiment 3
The present embodiment inlays mother-of-pearl inlay on porcelain dish, and it inlays the processing technology of mother-of-pearl inlay, comprises the following steps:
1) shell, awabi sheet or spiral shell shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern; Wherein, the thickness of above-mentioned mother-of-pearl inlay is 0.02 ~ 0.07mm.
2) surface of polishing porcelain dish;
3) step 1 gained patterned surfaces is coated super glue, be pasted onto on porcelain dish;
4), after 24 hours, with 95 DEG C of hot water, pattern for subsequent use is washed off;
5) after porcelain dish moisture content is dry, with liquid honing, and spray paint first and be baked to 130 DEG C, taking-up cools completely;
6) after polishing, by the method for artificial Freehandhand-drawing, baking of again spraying paint arrives finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that step of spraying paint adopts is varnish.
Adopt the porcelain dish that this process is made, its surface forms the smooth light face that does not have concave-convex sense, and pattern part lines are lively, life-like, overcome the defect that existing process is stiff, stiff.
Embodiment 4
The present embodiment inlays mother-of-pearl inlay at wooden bottle, and it inlays the processing technology of mother-of-pearl inlay, comprises the following steps:
1) shell, awabi sheet or spiral shell shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern; Wherein, the thickness of above-mentioned mother-of-pearl inlay is 0.02 ~ 0.07mm.
2) to polish the surface of wooden bottle;
3) step 1 gained patterned surfaces is coated super glue, be pasted onto on wooden bottle;
4), after 24 hours, with 85 DEG C of hot water, pattern for subsequent use is washed off;
5) after moisture content is dry, with liquid honing, and spray paint first and be baked to 130 DEG C, taking-up cools completely;
6) after polishing, by the method for artificial Freehandhand-drawing, baking of again spraying paint arrives finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that step of spraying paint adopts is varnish.
The wooden bottle adopting this process to make, its surface forms the smooth light face that does not have concave-convex sense, and pattern part lines are lively, life-like, overcome the defect that existing process is stiff, stiff.
Embodiment 5
The present embodiment inlays mother-of-pearl inlay on wooden bodiless lacquer bottle, and it inlays the processing technology of mother-of-pearl inlay, comprises the following steps:
1) shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern; Wherein, the thickness of above-mentioned mother-of-pearl inlay is 1 ~ 5mm.
2) surface of polishing porcelain dish;
3) step 1 gained patterned surfaces is coated super glue, be pasted onto on wooden bodiless lacquer bottle;
4), after 24 hours, with 80 DEG C of hot water, pattern for subsequent use is washed off;
5) after porcelain utensil moisture content is dry, with liquid honing, and spray paint first and be baked to 130 DEG C, taking-up cools completely;
6) after polishing, by the method for artificial Freehandhand-drawing, baking of again spraying paint arrives finished product 3 times repeatedly.
Glue used in the present embodiment is 502 super glue, and the paint that step of spraying paint adopts is varnish.
The wooden bottle adopting this process to make, its surface forms the smooth light face that does not have concave-convex sense, and pattern part lines are lively, life-like, overcome the defect that existing process is stiff, stiff.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. inlay a processing technology for mother-of-pearl inlay, it is characterized in that, comprise the following steps:
1) shell, awabi sheet or spiral shell shell through being polished to being pasted onto on pattern for subsequent use, making it to become pattern;
2) surface of polishing for inlaying mother-of-pearl inlay body;
3) step 1 gained patterned surfaces is applied glue, be pasted onto on body;
4), after 22 ~ 26 hours, with hot water, pattern for subsequent use is washed off;
5) after moisture content is dry, with liquid honing, and spray paint first and be baked to 130 ~ 150 DEG C, taking-up cools completely;
6), after polishing, baking of again spraying paint arrives finished product 3 times repeatedly;
Described is porcelain utensil for inlaying mother-of-pearl inlay body;
In described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 0.02 ~ 0.07mm;
Or in described step 1, the thickness of the shell be polished to, awabi sheet or spiral shell shell is 1 ~ 5mm.
2. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, is characterized in that: described porcelain utensil is porcelain dish or porcelain vase.
3. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, is characterized in that: the glue in described step 3 is resistant to elevated temperatures super glue.
4. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, is characterized in that: the temperature of the hot water in described step 4 is more than 80 DEG C.
5. a kind of processing technology of inlaying mother-of-pearl inlay according to claim 1, is characterized in that: also comprise the step be plotted to by seven color powder on mother-of-pearl inlay before again spraying paint in described step 6.