CN100464935C - Gas-protected special steel bar welding method and fixture

Info

Publication number: CN100464935C
Application number: CNB031116663A
Authority: CN
Inventors: 梁满堂
Original assignee: Individual
Current assignee: Individual
Priority date: 2003-05-15
Filing date: 2003-05-15
Publication date: 2009-03-04
Anticipated expiration: 2023-05-15
Also published as: CN1548263A

Abstract

The gas-protected welding process of special steel bar includes cleaning the welded parts of the steel bar, welding and other steps, and features the fixtures set at two ends near the welded part to regulate welding interval and concentricity, connecting part with the same size as the steel bar to be welded, gas-protected arc welding machine and welding rod adopted and natural cooling after welding. Compared with available technology, the present invention has the advantages of convenient welding, high efficiency, high welding quality, high welding point strength, welding seam capable of being bent by 90 deg, etc.

Description

Deformed bar gas shield weld jig

Technical field

The invention belongs to a kind of weld jig, particularly a kind of deformed bar gas shield weld jig.

Background technology

Following several method is mainly adopted in welding at the building trade deformed bar: mechanical connection method, electric ingot process, butt welding process, gas crimping method and overlap welding method.Wherein, the mechanical connection method is mainly used in diameter and exists

The deformed bar welding that 25mm is above, and

The deformed bar of the above specification of 25mm adopts other method then can't weld, and this welding method costs an arm and a leg; Electric ingot process is mainly used in the construction of shear wall, column aspect, and it is confined to

The following vertical deformed bar of 25mm welds, and can not be used for the deformed bar welding of level; Butt welding process is mainly used in

The level welding of the following deformed bar of 25mm, the deficiency of existence is: produce fluctuation as electric current and then do not weld, influence welding quality; Gas crimping method is mainly used in diameter and exists

The deformed bar welding that 25mm is following needs preheating during welding, also will carry out grinding process after the welding, and the intensity of its weld is lower than the intensity of mother metal; The overlap welding method is faced with superseded because exist can not bending resistance and problem such as welding efficiency is low at present.Above-mentioned various welding method also exists shortcomings such as can not construct for a short time in the space, arrangement of reinforcement finishes to construct, fixing back, reinforcing bar two ends mid portion can not weld.

Summary of the invention

The purpose of this invention is to provide a kind of deformed bar gas shield weld jig; easy construction; the efficient height; can satisfy the butt welding requirement of different size deformed bar, welding quality is good, and the intensity of weld is better than the intensity of mother metal; can be crooked after the welding; the flexibility that possesses skills, the energy is saved in the restriction that place and deformed bar welded condition are not welded in construction.

The objective of the invention is to be achieved through the following technical solutions:

Anchor clamps provided by the invention include clamp, it is characterized in that at the balladeur train one end stationary clamp that is fixedly connected, and assembling sliding clip in the other end chute of balladeur train, sliding clip is connected in and can be screwed on the adjustment screw rod of back-outing, and has been screwed the location jackscrew on two clamps; Connecting rack on balladeur train is installed on support and is adjusted screw, adjusts screw and is screwedly mounted on the sliding clip.

The present invention and prior art relatively have following advantage: easy construction, the efficient height, can satisfy the butt welding requirement of different size deformed bar, welding quality is good, and the intensity of weld is better than the intensity of mother metal, and welding back weld seam can crooked 90 °, flexibility possesses skills, the restriction that place and deformed bar specification and welded condition are not welded in construction, the little highly versatile of place capacity is saved the energy.

Description of drawings

Fig. 1-Fig. 6 is a welding step schematic diagram of the present invention.

Fig. 7-Figure 12 is welding wire piles up scolder in welded gaps a process schematic diagram.

Figure 13 is the clamp structure schematic diagram.

Figure 14 is a stationary clamp part-structure schematic diagram.

Figure 15 is a sliding clip part-structure schematic diagram.

Figure 16 is the state diagram of gas arc welding wire welding welding seam.

Figure 17 is that deformed bar is at weld assembling connector schematic diagram.

Figure 18-Figure 22 is the structural representation of different shape connector.

Figure 23 is a welding position hardness test result schematic diagram.

Figure 24 is a welding position extension test result schematic diagram.

The specific embodiment

See Fig. 1-Fig. 6, welding step is as follows:

1, the corrosion of the end face of deformed

bar

1,9 welding positions and periphery, oil stain, cement mortar etc. are removed;

2, the deformed bar 1 of an end is loaded onto the stationary clamp 8 of anchor clamps, by jackscrew 7 (see figure 1) that is fixed, the deformed bar of the other end is adorned 9 sliding clips 6 of loading onto anchor clamps, be fixed by jackscrew 7, and, adjust the concentricity (see figure 3)s by adjusting screw 5 by turning adjustment screw rod 3 adjustment weld gap (see figure 2)s.

3, be positioned at the inboard fixed installation of anchor clamps connector 11 (seeing Fig. 4, Figure 17) in the welding position of deformed bar.

4, use co3 gas arc welding to meet sb. at the airport and welding wire 15 welded seam (seeing Fig. 5, Figure 16), fully melt by the weld seam of yaw welding wire 15 earlier left and right sides deformed bar, be welded to connect the deformed bar weld seam (see figure 7) of part 11 bottoms, begin two layers of continuous weldings, three layers then successively from the bottom ..., (see that Fig. 8-Figure 11), last scolder 12 heaps are high above deformed bar diameter (seeing Figure 12) to outside with scolder 12 is overlapping.

5, weld job finish after naturally cooling unload the lower clamp (see figure 6).

See Fig. 1,13-15, clamp structure is as follows: at the balladeur train 4 one ends stationary clamp 8 that is fixedly connected, be screwed location jackscrew 7 on the stationary clamp 8, the other end of balladeur train 4 is provided with chute 2, and assembling sliding clips 6 in the chute 2 are screwed location jackscrew 7 on the sliding clip 6.Sliding clip 6 is rotatably connected in and can be screwed on the adjustment screw rod of back-outing 3, adjusts screw rod 3 and is screwedly mounted on the hold-down nut 13 of balladeur train 4 ends, in the outer end of adjusting screw rod 3 rocking handle 10 is housed.Shaking rocking handle 10 slides adjustment screw rod 3 drive sliding clips 6 in chute 2.Connecting rack 14 on balladeur train 4, install to adjust screw 5 on support 14, adjust screw 5 and are screwedly mounted on the sliding clip 6, turn deformed bar 1 concentricity in the deformed bar 9 adjusted in the screw 5 fine-tuning sliding clips 6 and the stationary clamp 8.

Connector 11 can adopt following several structure: see Figure 18, connector 11 is half garden arc of sheet material processing, is provided with the arc ditch 16 of outside bulging in the middle of it, and the inboard width of arc ditch 16 and the degree of depth are respectively 6-10 millimeters and 3-5 millimeters.See Figure 19, connector is provided with positioning boss 17 on the arc ditch end face of connector body on the basis of said structure, and the width of positioning boss 17 is 10-20 millimeters.See Figure 20, connector is half a garden arc of sheet material processing, and half garden arc end face of connector body is provided with locating slot 18, and the width of locating slot 18 is 10-20 millimeters.See Figure 21,22, groove shapes or angle steel shape can be adopted in the cross section of connector body.

The Vickers hardness of deformed bar welding of the present invention and hot strength machinery performance test results are seen Figure 23, Figure 24.In Figure 23, the test point of round dot is surperficial more than 2 millimeters, and the test point of blockage is that the surface is below 2 millimeters.

Claims

1, a kind of anchor clamps, it includes clamp, it is characterized in that: at the balladeur train one end stationary clamp that is fixedly connected, assembling sliding clip in the other end chute of balladeur train, sliding clip is connected in and can be screwed on the adjustment screw rod of back-outing, and has been screwed the location jackscrew on two clamps; Connecting rack on balladeur train is installed on support and is adjusted screw, adjusts screw and is screwedly mounted on the sliding clip.