CN100462326C - Medicine, wine package container - Google Patents
Medicine, wine package container Download PDFInfo
- Publication number
- CN100462326C CN100462326C CNB2007100485892A CN200710048589A CN100462326C CN 100462326 C CN100462326 C CN 100462326C CN B2007100485892 A CNB2007100485892 A CN B2007100485892A CN 200710048589 A CN200710048589 A CN 200710048589A CN 100462326 C CN100462326 C CN 100462326C
- Authority
- CN
- China
- Prior art keywords
- feldspar
- hunan
- porcelain
- glaze
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A medicine or wine packing container able to shield light and heat is composed of a ceramic body and the enameled external and/or internal surface layers of said ceramic body. Said ceramic body is prepared from quartz sand (15-25 Wt%), Wangcang feldspar (10-20), Hunan argil, changsha clay (8-15) and Hunan feldspar. Said enamel is prepared from Hunan feldspar (48-58 Wt%), silica (20-24), calcite (10-14), argil (4-10) and talc powder (8-12).
Description
Technical field:
The present invention is relevant with packaging vessel, and is especially relevant with medicine class, wine package container.
Background technology:
Existing medicine bottle mainly is to adopt non-toxic plastic to make, and the easy property of adstante febre strange taste is unfavorable for HUMAN HEALTH.The bottle that existing employing glass is made can not lucifuge, heat, and wine is perishable.Leaded in its glaze of employing ceramic package container, be unfavorable for HUMAN HEALTH.
Summary of the invention:
The objective of the invention is in order to overcome above deficiency, provide a kind of and can reduce cost, can lucifuge, heat, prolonged preservation can guarantee the quality of medicine or wine, safety is beneficial to medicine class, the wine package container of HUMAN HEALTH.
The object of the present invention is achieved like this:
Medicine class of the present invention, wine package container comprise the porcelain body that porcelain makes and are compound in the porcelain body and/or the glaze of being made by glaze of outside, make the porcelain of porcelain body and are made up of following raw materials according by weight percentage:
Quartz sand 15～25%,
Wangcang feldspar 10～20%,
Hunan white clay 25～35%,
Changsha soil 8～15%,
Hunan feldspar 20～30%,
The above-mentioned overglaze glaze of making is made up of following raw materials according by weight percentage:
Hunan feldspar 48～58%,
Silica 20～24%,
Calcite 10～14%,
White clay 4～10%,
Talcum powder 8～12%.
Quartz sand in the porcelain of the present invention has been the effect of skeleton, and the Wangcang feldspar plays bonding, increases brightness and whiteness, and the Hunan clay plays bonding and increases whiteness, and Changsha soil plays anticracking, and Hunan feldspar works to increase carclazyte.Hunan feldspar plays bonding and increases whiteness in the glaze of the present invention, and silica plays skeleton, and calcite plays a part to increase transparency and brightness, and white clay plays bonding and increases whiteness, the effect of the gentle anticracking of talcum powder landing.
Packaging vessel of the present invention adopts the existent method preparation.
Raw material among the present invention can solve nearby, reduces production costs.Unleaded in the glaze, safety is beneficial to HUMAN HEALTH.Lucifuge, heat, medicine, particularly wine undergo no deterioration, and long quality-guarantee period strengthens pure, the perfume of distinguishing the flavor of of vinosity.
Description of drawings:
Fig. 1 is a structural representation of the present invention.
Fig. 2 is another structural representation of the present invention.
Fig. 3 is the present invention's structural representation again.
Embodiment:
Embodiment 1:
Fig. 1 has provided the embodiment of the invention 1 packaging container structure figure.Referring to Fig. 1, the porcelain body 1 of the band mouth 4 that packaging vessel of the present invention is made by porcelain and be compound in the inside and outside glaze 2,3 that the glaze of 1 inside and outside of porcelain body makes respectively and the lid 5 that cooperates with mouth is formed.
Present embodiment 1 is made the porcelain of porcelain body and is made up of following raw materials according by weight percentage:
Quartz sand 20%,
Wangcang feldspar 15%,
Hunan white clay 32%,
Changsha soil 8%,
Hunan feldspar 25%,
Present embodiment 1 is made the overglaze glaze and is made up of following raw materials according by weight percentage:
Hunan feldspar 58%,
Silica 20%,
Calcite 10%,
White clay 4%,
Talcum powder 8%.
With various raw materials divide the name of an article to store up, various raw material must not load in mixture, misloading, proportioning by porcelain and glaze is carried out formula combination, send into the ball mill fine grinding with conveying belt respectively again after the combination, make its granularity reach 0.004 millimeter (200 order), put into respectively again that porcelain stops stock tank, glaze stops stock tank.After porcelain was deposited one day, the stable porcelain slurry of formation was by TCTLY wet type electric magnetic iron remover, can remove metal-powder and oxide compounds thereof such as contained, iron, cobalt, nickel, avoided product molten spot of black and fusion hole to occur, guaranteed that whiteness is transparent.With TC8Q variable embolism pump delivery porcelain slurry, the slip casting machine shaping (being shaped) of being in the milk with plaster mould, be shaped the back by carrying out sand milling after TC3G chain type drying machine (circulating) drying, adopt glazing machine (the glaze slurry that glaze stops in the stock tank is conveyed in the glazing machine through the TC8Q Variable plunger pump) glazing behind the sand milling, reenter the broadband tunnel furnace (as wide 1.8 meters, long 100 meters), through kiln three bands; Preheating zone, thermal zone, low temperate zone, institute goes out finished product through screening, and salable product are used for applique, reenter decorating firing kiln, and through 800-900 ℃ of decoration firings, kiln discharge---is checked and accepted---packing---warehouse-in.
Present embodiment 1 packaging vessel can be made different shape, can be used for adorning wine, also can be used for the powder charge product.
Embodiment 2:
Fig. 2 has provided the embodiment of the invention 2 packaging container structure figure.The embodiment of the invention 2 packaging container structures basic with embodiment 1 with, not existing together is glaze in not having, the porcelain of making porcelain body is different with the proportioning of formation overglaze glaze.
The porcelain of the porcelain body that present embodiment 2 is made is made up of following raw materials according by weight percentage:
Quartz sand 15%,
Wangcang feldspar 15%,
Hunan white clay 30%,
Changsha soil 10%,
Hunan feldspar 30%,
Present embodiment 2 is made the overglaze glaze and is made up of following raw materials according by weight percentage:
Hunan feldspar 48%,
Silica 22%,
Calcite 12%,
White clay 8%,
Talcum powder 10%.
Present embodiment 2 making methods are with embodiment 1.
Embodiment 3:
Fig. 3 has provided the embodiment of the invention 3 packaging container structure figure.Present embodiment 3 packaging container structures are basic and embodiment 1 is same.Not existing together is not have outer glaze, and the porcelain of making porcelain body is different with the proportioning that forms glaze and glaze.
The porcelain of the porcelain body that present embodiment 3 is made is made up of following raw materials according by weight percentage:
Quartz sand 25%,
Wangcang feldspar 10%,
Hunan white clay 35%,
Changsha soil 10%,
Hunan feldspar 20%,
Hunan feldspar 52%,
Silica 20%,
Calcite 12%,
White clay 6%,
Talcum powder 10%.
The making method of present embodiment 3 packaging vessels is with embodiment 1.
The various embodiments described above are that foregoing of the present invention is further described, but this should be interpreted as that the scope of the above-mentioned theme of the present invention only limits to the foregoing description.All technology that realizes based on foregoing all belong to scope of the present invention.
Claims (1)
1. medicine class, wine package container is characterized in that comprising the porcelain body that porcelain is made and are compound in the porcelain body and/or the glaze of being made by glaze of outside, make the porcelain of porcelain body and are made up of following raw materials according by weight percentage:
Quartz sand 15～25%,
Wangcang feldspar 10～20%,
Hunan white clay 25～35%,
Changsha soil 8～15%,
Hunan feldspar 20～30%,
The above-mentioned overglaze glaze of making is made up of following raw materials according by weight percentage:
Hunan feldspar 48～58%,
Silica 20～24%,
Calcite 10～14%,
White clay 4～10%,
Talcum powder 8～12%.