CN100455697C - 一种马氏体不锈钢活塞环的着色方法 - Google Patents

一种马氏体不锈钢活塞环的着色方法 Download PDF

Info

Publication number
CN100455697C
CN100455697C CNB2005101207289A CN200510120728A CN100455697C CN 100455697 C CN100455697 C CN 100455697C CN B2005101207289 A CNB2005101207289 A CN B2005101207289A CN 200510120728 A CN200510120728 A CN 200510120728A CN 100455697 C CN100455697 C CN 100455697C
Authority
CN
China
Prior art keywords
piston ring
stainless steel
martensite stainless
process furnace
steel piston
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005101207289A
Other languages
English (en)
Other versions
CN1793413A (zh
Inventor
揭晓华
卢国辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong University of Technology
Original Assignee
Guangdong University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong University of Technology filed Critical Guangdong University of Technology
Priority to CNB2005101207289A priority Critical patent/CN100455697C/zh
Publication of CN1793413A publication Critical patent/CN1793413A/zh
Application granted granted Critical
Publication of CN100455697C publication Critical patent/CN100455697C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是一种马氏体不锈钢活塞环的着色方法。包括如下步骤：1)悬挂活塞环；2)清洗活塞环；3)将活塞环进行液体喷砂处理；4)清水漂洗活塞环；5)用热水清洗活塞环；6)吹干活塞环；7)清洗后的活塞环以悬挂方式置于加热炉中加热，同时滴入蒸馏水，经不同温度加热保温，可获得不同颜色的致密氧化膜；8)将活塞环从加热炉中取出。本发明由于采用直接氧化法在不锈钢活塞环表面形成彩色膜的着色方法，本发明没有污染，而且颜色控制简单，操作方便。本发明是一种方便实用的马氏体不锈钢活塞环的着色方法。

Description

一种马氏体不锈钢活塞环的着色方法
1、技术领域：
本发明是一种马氏体不锈钢活塞环的着色方法，特别是一种马氏体不锈钢活塞环的着色方法。
2、背景技术：
随着人们生活水平的提高，摩托车在国内的销售和使用正以成倍的速度增长。而活塞环是摩托车内燃机的主要零件和易损件，在使用过程中，活塞环很易磨损，磨损后导致发动机性能大大下降，出现气密性差、拉缸、发动机无力等现象，从而使油耗增加，功率降低，严重影响发动机的正常运转。因此，国内外都很重视提高活塞环寿命的研究，并在活塞环材质和表面加工及表面强化处理方面做了大量工作。目前市面上不少活塞环是采用马氏体不锈钢来制造的，主要是利用其减振性好的特点，不锈钢活塞环热处理后再加不同的着色处理工艺，可以获得艳丽的彩色膜，这些彩色膜是由金属氧化物组成的，它们即起到美观作用，又起到防锈和减摩作用。
不锈钢的着色研究起始于1927年，从那时起，人们对彩色不锈钢一直进行着不懈的研究，不锈钢的着色方法很多，但主要研究方法可以分为两大类：化学着色法和电化学着色法，其中研究最多的是化学法，也就是INCO法，它是把不锈钢浸入化学着色液中，通过化学自发反应而在不锈钢表面形成一种彩色膜，这种方法在实际生产中已得到了应用，但是由于这种方法污染较为严重，而且颜色控制手段复杂，不易操作，尤其对于马氏体不锈钢来说，着色难度更大，所以现在国内外业内人士开始了一些其它新方法的探索，力图改变以上这些不足。
3、发明内容：
本发明的目的在于克服上述缺点而提供一种采用直接氧化法在马氏体不锈钢活塞环表面形成彩色膜的着色方法。本发明没有污染，而且颜色控制简单，操作方便。
本发明马氏体不锈钢活塞环的着色方法，包括如下步骤：
1)悬挂活塞环；
2)清洗活塞环；
3)将活塞环进行液体喷砂处理；
4)清水漂洗活塞环；
5)用热水清洗活塞环；
6)吹干活塞环；
7)清洗后的活塞环以悬挂方式置于加热炉中加热，同时滴入蒸馏水，经不同温度加热保温，可获得不同颜色的致密氧化膜；
8)将活塞环从加热炉中取出。
上述活塞环在加热炉中的加热温度为300℃～430℃。
上述滴入蒸馏水速度为8～12滴/分钟。
上述活塞环在加热炉中的加热时间为50～60分钟。
上述液体喷砂处理所用材料是石英砂，石英砂粒度为350目～450目。
本发明由于采用直接氧化法在马氏体不锈钢活塞环表面形成彩色膜的着色方法，本发明没有污染，而且颜色控制简单，操作方便。本发明是一种方便实用的马氏体不锈钢活塞环的着色方法。
4、具体实施方式：
实施例1：
本发明马氏体不锈钢活塞环的着色方法，包括如下步骤：
1)悬挂活塞环，本实施例中，活塞环所用材料为6Cr13Mo马氏体不锈钢；
2)清洗活塞环；
3)将活塞环进行液体喷砂处理，其目的是清理活塞环表面，并有良好的机械活化作用；液体喷砂处理所用材料是石英砂，石英砂粒度为350目～450目，本实施例中，石英砂的粒度为400目。
4)清水漂洗活塞环；
5)用热水清洗活塞环；
6)吹干活塞环；
7)清洗后的活塞环以悬挂方式置于加热炉中加热，活塞环在加热炉中的加热温度为300℃～430℃，加热时间为50～60分钟。另外，在加热过程中同时滴入蒸馏水，经不同温度加热保温，可获得不同颜色的致密氧化膜；氧化过程滴入蒸馏水的作用是改变活塞环的氧化触媒，使氧化膜均匀致密。上述滴入蒸馏水速度为8～12滴/分钟。本实施例中，活塞环在加热炉中的加热温度为380℃，加热时间为55分钟。滴入蒸馏水速度为10滴/分钟。
8)将活塞环从加热炉中取出，活塞环可获得金黄色氧化膜。
实施例2：
本发明马氏体不锈钢活塞环的着色方法与实施例1相同，不同之处在于活塞环在加热炉中的加热温度为400℃，活塞环可获天蓝色氧化膜。

Claims (4)

1、一种马氏体不锈钢活塞环的着色方法，其特征在于包括如下步骤：
1)悬挂活塞环；
2)清洗活塞环；
3)将活塞环进行液体喷砂处理；
4)清水漂洗活塞环；
5)用热水清洗活塞环；
6)吹干活塞环；
7)清洗后的活塞环以悬挂方式置于加热炉中加热，同时滴入蒸馏水，经不同温度加热保温，可获得不同颜色的致密氧化膜；
8)将活塞环从加热炉中取出。
2、根据权利要求1所述的马氏体不锈钢活塞环的着色方法，其特征在于上述活塞环在加热炉中的加热温度为300℃～430℃。
3、根据权利要求1所述的马氏体不锈钢活塞环的着色方法，其特征在于上述滴入蒸馏水速度为8～12滴/分钟。
4、根据权利要求1所述的马氏体不锈钢活塞环的着色方法，其特征在于上述活塞环在加热炉中的加热时间为50～60分钟。
CNB2005101207289A 2005-12-19 2005-12-19 一种马氏体不锈钢活塞环的着色方法 Expired - Fee Related CN100455697C (zh)