CN100434379C - 调节玻璃的熔融和成型温度的方法以及由此方法制备的玻璃制品 - Google Patents
调节玻璃的熔融和成型温度的方法以及由此方法制备的玻璃制品 Download PDFInfo
- Publication number
- CN100434379C CN100434379C CNB028039696A CN02803969A CN100434379C CN 100434379 C CN100434379 C CN 100434379C CN B028039696 A CNB028039696 A CN B028039696A CN 02803969 A CN02803969 A CN 02803969A CN 100434379 C CN100434379 C CN 100434379C
- Authority
- CN
- China
- Prior art keywords
- cao
- mgo
- glass
- composition
- glass composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
组分 | 重量百分数 |
SiO<sub>2</sub> | 70-75 |
Na<sub>2</sub>O | 12-15 |
K<sub>2</sub>O | 0-2 |
CaO | >9 |
MgO | <4 |
Al<sub>2</sub>O<sub>3</sub> | 0-2 |
SO<sub>3</sub> | 0-1 |
Fe<sub>2</sub>O<sub>3</sub> | 0-2 |
SiO<sub>2</sub>+Al<sub>2</sub>O<sub>3</sub> | ≥70 |
Na<sub>2</sub>O+K<sub>2</sub>O | 12-15 |
CaO+MgO | 12-13.5 |
CaO/MgO | 2-5 |
组分 | 组合物1 | 组合物2 |
SiO<sub>2</sub> | 72.53 | 72.89 |
Na<sub>2</sub>O | 13.79 | 13.9 |
K<sub>2</sub>O | 0.02 | 0 |
CaO | ≥9.1 | ≥10 |
MgO | ≤4 | ≤3 |
Al<sub>2</sub>O<sub>3</sub> | 0.03 | 0.03 |
SO<sub>3</sub> | 0.2 | 0.2 |
Fe<sub>2</sub>O<sub>3</sub> | 0.5 | 0.1 |
SiO<sub>2</sub>+Al<sub>2</sub>O<sub>3</sub> | 72.56 | 72.91-73.01 |
Na<sub>2</sub>O+K<sub>2</sub>O | 13.81 | 13.9 |
CaO+MgO | 12.85 | 12.69-12.8 |
组分 | 重量百分数 |
SiO<sub>2</sub> | 72.53±0.1 |
Na<sub>2</sub>O | 13.79±0.1 |
K<sub>2</sub>O | 0.02±01 |
Al<sub>2</sub>O<sub>3</sub> | 0.03±.01 |
SO<sub>3</sub> | 0.2±.01 |
Fe<sub>2</sub>O<sub>3</sub> | 0.5±.01 |
SiO<sub>2</sub>+Al<sub>2</sub>O<sub>3</sub> | 72.56±0.1 |
Na<sub>2</sub>O+K<sub>2</sub>O | 13.81±0.1 |
CaO+MgO | 12.85±.05 |
组分 | 重量百分数 |
SiO<sub>2</sub> | 72.89±0.1 |
Na<sub>2</sub>O | 13.9±0.1 |
K<sub>2</sub>O | 0 |
Al<sub>2</sub>O<sub>3</sub> | 0.02±0.01 |
SO<sub>3</sub> | 0.2±.01 |
Fe<sub>2</sub>O<sub>3</sub> | 0.1±.01 |
SiO<sub>2</sub>+Al<sub>2</sub>O<sub>3</sub> | 72.91±0.1 |
Na<sub>2</sub>O+K<sub>2</sub>O | 13.9±0.1 |
CaO+MgO | 12.8±.11 |
组分 | 重量百分数 |
SiO<sub>2</sub> | 72.80 |
Na<sub>2</sub>O | 13.90 |
K<sub>2</sub>O | 0.03 |
Fe<sub>2</sub>O<sub>3</sub> | 0.10 |
CaO+MgO | 12.74 |
组分 | 重量百分数 |
SiO<sub>2</sub> | 72.41 |
Na<sub>2</sub>O | 13.78 |
Al<sub>2</sub>O<sub>3</sub> | 0.16 |
Fe<sub>2</sub>O<sub>3</sub> | 0.48 |
CaO+MgO | 12.84 |
组分 | 重量百分数 |
SiO<sub>2</sub> | 72.56 |
Na<sub>2</sub>O+K<sub>2</sub>O | 13.85 |
Fe<sub>2</sub>O<sub>3</sub> | 0.49 |
CaO+MgO | 12.89 |
Claims (18)