CN100412018C - 太阳能光电效应玻璃 - Google Patents

太阳能光电效应玻璃 Download PDF

Info

Publication number
CN100412018C
CN100412018C CNB2006100379564A CN200610037956A CN100412018C CN 100412018 C CN100412018 C CN 100412018C CN B2006100379564 A CNB2006100379564 A CN B2006100379564A CN 200610037956 A CN200610037956 A CN 200610037956A CN 100412018 C CN100412018 C CN 100412018C
Authority
CN
China
Prior art keywords
glass
coating
magnesium fluoride
present
glass substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2006100379564A
Other languages
English (en)
Other versions
CN1807319A (zh
Inventor
林金锡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou Almaden Stock Co., Ltd.
Original Assignee
CHANGZHOU YAMADUN TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU YAMADUN TECHNOLOGY Co Ltd filed Critical CHANGZHOU YAMADUN TECHNOLOGY Co Ltd
Priority to CNB2006100379564A priority Critical patent/CN100412018C/zh
Publication of CN1807319A publication Critical patent/CN1807319A/zh
Application granted granted Critical
Publication of CN100412018C publication Critical patent/CN100412018C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种太阳能光电转换玻璃，特别涉及一种可应用于太阳能电池上的太阳能光电效应玻璃，它包括玻璃基片和涂覆在玻璃基片上面的涂层，所述玻璃基片上面的涂层由氧化锆和氟化镁组成，它们的重量百分比为氧化锆25%～38%，氟化镁62%～75%。本发明的优点是：(1)透光率高。涂层玻璃在300mm～800mm之间的透光率比未涂层的透光率增加2%以上；(2)自清洁能力强。其优良的憎水性和表面防静电的凹凸状的微观结构使灰尘无法粘附在上面；(3)使用寿命长。玻璃表面的涂层硬度大，耐久度好，可达到20年以上，使玻璃得到了有效的保护，从而也降低了使用成本；(4)具有抗菌防霉及远红外功能。

Description

太阳能光电效应玻璃
技术领域
本发明涉及一种太阳能光电转换玻璃，特别涉及一种可应用于太阳能电池上的太阳能光电效应玻璃。
背景技术
目前，公知的太阳能光电转换依靠的是太阳能电池组件中的硅片，硅片有很好的吸光作用，随着人门对太阳能电池组件的不断改进，太阳能电池组件中的硅片的光电转化效率在目前的工艺制作水平上已达到了极限，要想再提高太阳能电池的光电转换效率已成为一个难题。同时由于太阳能电池的工作场所多设置在环境恶劣的室外，造成太阳能电池组件表面易脏，且脏后又很难清洁。我们知道的解决太阳能电池光电转换效率的方法其中之一是，提高太阳能电池光电组件中作为封盖材料的玻璃基片的透光率，从而来达提高整个太阳能电池相对光电转化效率的目的。普通的玻璃很难做到，因为它含铁量高，达不到作为太阳能电池玻璃基片的性能要求；人们尝试着采用一种普通超白玻璃，这种玻璃含铁量低，但它是采用浮法工艺生产出来的，表面平滑光洁，存在反射率过高的缺点，做太阳能电池玻璃基片有一定不足之处；还有一种普通超白玻璃，它是采用压延工艺生产的，它的缺点是透光不透视，对做太阳能电池玻璃基片也有缺点。目前性能比较好的是一种表面均匀分布点状花纹的超白玻璃，它的含铁量低，折射性好，但是自清洁性能差。上述的几种玻璃基片除了存在着上述的缺陷外，都存在着难清洁的问题。因而目前要想找到一种透光率高，又易清洁的玻璃基片一直是一个难题。
发明内容
本发明的目的是针对现有技术的不足，提供一种透光性高，使光电转换效率更高，又易清洗的太阳能光电效应玻璃。
实现上述目的的技术方案是：一种太阳能光电效应玻璃，它包括玻璃基片和涂覆在玻璃基片上面的涂层，所述玻璃基片上面的涂层由氧化锆和氟化镁组成，它们的重量百分比为氧化锆25％～38％，氟化镁62％～75％，涂层中氧化锆和氟化镁是平均粒径在50nm，厚度在10μm的纳米材料。
采用本发明所述的高效太阳能光电效应玻璃，具有以下优点：(1)透光率高。由于涂层是氧化锆和氟化镁两种成分热熔混合而成，涂层中氧化锆和氟化镁是平均粒径在50nm，厚度在10μm的纳米材料，因而透光率高，涂层玻璃在300mm～800mm之间的透光率比未涂层的透光率增加2％以上，也就是把太阳能电池的光电相对转化效率提高了2％以上，透光率的增加在实际应用上意味着具有更高的经济价值、技术价值和社会价值，是一种高效太阳能光电效应玻璃；(2)自清洁能力强。由于玻璃表面是运用纳米材料形成的涂层，模仿了荷叶结构，其优良的憎水性和表面防静电的凹凸状的微观结构使灰尘无法粘附在上面，在雨水的自然冲刷下即可保持玻璃表面的清洁，达到了自动清洁的目的，这种优点对于置于大自然恶劣环境中的太阳能电池是一个重大的技术进步；(3)使用寿命长。玻璃表面的涂层硬度大，耐久度好，可达到20年以上，使玻璃得到了有效的保护，延长了玻璃的使用寿命，从而也降低了使用成本；(4)具有抗菌防霉及远红外功能。由于此涂层玻璃散热性能好，因而可以避免太阳能电池组件的热衰减。
具体实施方式
下面通过实施例对本发明作进一步详细的说明。
实施例一
一种太阳能光电效应玻璃，它包括玻璃基片和涂覆在玻璃基片上面的涂层，所述玻璃基片上面的涂层由氧化锆和氟化镁组成，它们的重量百分比为氧化锆25％，氟化镁75％。
实施例二
一种太阳能光电效应玻璃，它包括玻璃基片和涂覆在玻璃基片上面的涂层，所述玻璃基片上面的涂层由氧化锆和氟化镁组成，它们的重量百分比为氧化锆38％，氟化镁62％。
实施例三
一种太阳能光电效应玻璃，它包括玻璃基片和涂覆在玻璃基片上面的涂层，所述玻璃基片上面的涂层由氧化锆和氟化镁组成，它们的重量百分比为氧化锆30％，氟化镁70％。
在上述的各实施例中，可选用含铁量低、透视性好、表面均匀分布点状花纹的超白玻璃，运用上述各配方中的比例将氧化锆和氟化镁两种成分热熔混合，做成涂层，运用特殊的工艺将涂料喷涂在超白玻璃上，然后在300℃温度下烘烤20分钟，涂层与玻璃间就形成了硅氧键，从而使两者牢固地形成一体。

Claims (4)

1. 一种太阳能光电效应玻璃，它包括玻璃基片和涂覆在玻璃基片上面的涂层，其特征在于：所述玻璃基片上面的涂层由氧化锆和氟化镁组成，它们的重量百分比为氧化锆25％～38％，氟化镁62％～75％，涂层中氧化锆和氟化镁是平均粒径在50nm，厚度在10μm的纳米材料。
2. 根据权利要求1所述的太阳能光电效应玻璃，其特征在于：所述氧化锆和氟化镁的重量百分比为氧化锆25％，氟化镁75％。
3. 根据权利要求1所述的太阳能光电效应玻璃，其特征在于：所述氧化锆和氟化镁的重量百分比为氧化锆38％，氟化镁62％。
4. 根据权利要求1所述的太阳能光电效应玻璃，其特征在于：所述氧化锆和氟化镁的重量百分比为氧化锆30％，氟化镁70％。
CNB2006100379564A 2006-01-24 2006-01-24 太阳能光电效应玻璃 Active CN100412018C (zh)