CN100406603C - 冷轧带肋钢筋专用母材的制备方法 - Google Patents

冷轧带肋钢筋专用母材的制备方法 Download PDF

Info

Publication number
CN100406603C
CN100406603C CNB2004100795039A CN200410079503A CN100406603C CN 100406603 C CN100406603 C CN 100406603C CN B2004100795039 A CNB2004100795039 A CN B2004100795039A CN 200410079503 A CN200410079503 A CN 200410079503A CN 100406603 C CN100406603 C CN 100406603C
Authority
CN
China
Prior art keywords
ribs
rolling
parent metal
temperature
cold rolled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100795039A
Other languages
English (en)
Other versions
CN1760395A (zh
Inventor
苏鹤洲
张卫强
王志雄
宾石函
李金柱
杨顺武
邓家木
李志敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNMING STEELS CO Ltd
Original Assignee
KUNMING STEELS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNMING STEELS CO Ltd filed Critical KUNMING STEELS CO Ltd
Priority to CNB2004100795039A priority Critical patent/CN100406603C/zh
Publication of CN1760395A publication Critical patent/CN1760395A/zh
Application granted granted Critical
Publication of CN100406603C publication Critical patent/CN100406603C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种冷轧带肋钢筋专用母材的制备方法，其特征在于它将化学成分如下的钢材：C 0.14—0.22wt%、Si 0.10—0.30wt%、Mn 0.40—0.65wt%、S≤0.035wt%、P≤0.035wt%，其余为Fe以及不可避免的不纯物，进行轧制，使生产出来的冷轧带肋钢筋专用母材，具有外形尺寸精度高、表面质量好，强度级别和规格齐全，通条性能稳定，生产成本低等特点，在轧制过程中不易断线，能够保证产品在冷加工过程中的稳定性，减少生产事故，显著提高冷轧带肋钢筋性能的合格率，有效提高了工程建设技术水平和工程质量，减少了原材料的消耗，降低了工程造价，创造了可观的社会效益。

Description

冷轧带肋钢筋专用母材的制备方法
技术领域
本发明涉及一种冷轧带肋钢筋专用母材的制备方法，属于金属材料的设计与制造技术领域。
背景技术
冷轧带肋钢筋是二十世纪八十年代开始引入我国的一种新型高效建筑钢材，具有强度高，与混凝土的握裹力强，能节约钢材和水泥等特点。如在现浇混凝土板中，使用冷轧带肋钢筋可节约钢材30％以上；在预应力混凝土构件中，使用冷轧带肋钢筋后，可节约水泥50kg/m3～80kg/m3，并能显著提高混凝土质量，因此应用较为广泛。但现有的冷轧带肋钢筋所使用的原料大多是建筑用低碳热轧盘条，在使用过程中存在以下问题：1)热轧盘条质量不好，线材表面氧化铁皮厚，尺寸公差较大，直接影响冷轧带肋钢筋的轧制合格率。2)盘条的化学成分波动大且S、P含量高、易偏析并含有夹杂物，使得线材在拉拔过程中常常因成分偏析或夹杂物含量高而导致断裂，既影响冷轧带肋钢筋的生产产量，又影响冷轧带肋钢筋的产品质量。3)盘条的通条性能不均匀，使冷轧带肋钢筋在正常的生产条件下，会出现一段合格一段不合格的现象。4)建筑用低碳热轧盘条不能满足生产不同强度级别的冷轧带肋钢筋的需要。由于上述不足，使得冷轧带肋钢筋的合格率较低，直接影响其产量和质量，因此，有必要对现有技术进行改进。
发明内容
本发明的目的在于提供一种性能稳定，产品合格率高，通条性能好，生产成本低，强度级别与规格齐全，精度高、质量好的冷轧带肋钢筋专用母材的制备方法。
本发明通过下列技术方案实现：一种冷轧带肋钢筋专用母材的制备方法，其特征在于它将化学成分如下的钢材：C 0.14-0.22wt％、Si 0.10-0.30wt％、Mn 0.40-0.65wt％、S≤0.035wt％、P≤0.035wt％，其余为Fe以及不可避免的不纯物，通过下列工艺轧制：将上述钢坯送入温度为1000～1150℃的加热炉中加热至铸坯温度达950～1050℃时开轧，经粗轧、中轧、预精轧各6道次后，在800～920℃温度下进行精轧，精轧后在880～940℃温度下吐丝成圈，以辊速为0.20～0.50m/s的速度在辊道上，先使盘条温度由850～900℃冷却至700～800℃，再使盘条由600～700℃冷却至400～500℃，再进行集卷，即可获得母材产品。还可用现有其它轧制工艺制得。
本发明具有下列优点和效果：采用上述方案生产出来的冷轧带肋钢筋专用母材，具有以下优点；1、专用母材的外形尺寸精度高、表面质量好，能够保证产品在冷加工过程中的稳定性，减少生产事故。2、专用母材的通条性能稳定，能显著提高冷轧带肋钢筋性能的合格率，降低生产成本。3、专用母材的强度级别和规格齐全，可以满足生产厂家生产不同强度级别和规格的冷轧带肋钢筋。4、用专用母材生产出来的冷轧带肋钢筋，有效提高了工程建设技术水平和工程质量，减少了原材料的消耗，降低了工程造价，创造了可观的社会效益。
具体实施方式
下面结合实施例对本发明做进一步描述。
实施例1
取下列化学成分的钢材：C 0.14wt％、Si 0.10wt％、Mn 0.40wt％、S≤0.035wt％、P≤0.035wt％，其余为Fe以及不可避免的不纯物。经下列工艺轧制得冷轧带肋钢筋专用母材：将所述钢坯送入温度为1000～1150℃的加热炉中加热至铸坯温度达950～1050℃时开轧，经粗轧6道次、中轧6道次、预精轧6道次后，在800～920℃温度下进行精轧，精轧后在880～940℃温度下吐丝成圈，送入辊道上，辊速为0.20～0.50m/s，开启风机，使盘条温度由850～900℃冷却至700～800℃，开启风机及辊道上所有罩盖，使盘条由600～700℃冷却至400～500℃，再进行集卷，即可获得牌号为TS460L的母材。
实施例2
取下列化学成分的钢坯：C 0.22wt％、Si 0.30wt％、Mn 0.65wt％、S≤0.035wt％、P≤0.035wt％，其余为Fe以及不可避免的不纯物，并按与实施例1相同的轧制工艺轧制得冷轧带肋钢筋专用母材。
实施例3
取下列化学成分的钢坯：C 0.18wt％、Si 0.20wt％、Mn 0.55wt％、S≤0.035wt％、P≤0.035wt％，其余为Fe以及不可避免的不纯物，并按与实施例1相同的轧制工艺轧制得冷轧带肋钢筋专用母材。

Claims (1)

1.一种冷轧带肋钢筋专用母材的制备方法，其特征在于它将化学成分如下的钢材：C0.14-0.22wt％、Si0.10-0.30wt％、Mn0.400.65wt％、S≤0.035wt％、P≤0.035wt％，其余为Fe以及不可避免的不纯物；通过下列工艺轧制而成：将上述钢坯送入温度为1000～1150℃的加热炉中加热至铸坯温度达950～1050℃时开轧，经粗轧、中轧、预精轧各6道次后，在800～920℃温度下进行精轧，精轧后在880～940℃温度下吐丝成圈，以辊速为0.20～0.50m/s的速度在辊道上，先使盘条温度由850～900℃冷却至700～800℃，再使盘条由600～700℃冷却至400～500℃，再进行集卷，即可获得母材产品。
CNB2004100795039A 2004-10-12 2004-10-12 冷轧带肋钢筋专用母材的制备方法 Expired - Fee Related CN100406603C (zh)