CN100405904C - 表面应用的抗菌地毯处理 - Google Patents
表面应用的抗菌地毯处理 Download PDFInfo
- Publication number
- CN100405904C CN100405904C CNB038245507A CN03824550A CN100405904C CN 100405904 C CN100405904 C CN 100405904C CN B038245507 A CNB038245507 A CN B038245507A CN 03824550 A CN03824550 A CN 03824550A CN 100405904 C CN100405904 C CN 100405904C
- Authority
- CN
- China
- Prior art keywords
- antimicrobial
- solid
- floor coverings
- carpet
- goods
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供了含有嵌入到目标纤维中以赋予其耐用抗菌整理的固体抗菌颗粒的表面抗菌地面遮盖物处理。这种表面处理包括特定的抗菌金属离子基固体化合物，例如银离子交换化合物，(例如，包括磷酸银锆、银沸石和/或银玻璃)，其在液体介质中存在或者与另一种固体处理相混合。这种处理还任选包括耐污剂、防止泥土再沉积的化合物和液体、表面活性剂、抗静电剂及类似物质的组合物，从而赋予目标地毯产品其它特性。因此，这种地毯处理赋予地毯簇绒表面和绒头本身极好的抗菌特性。此外，发现应用这种金属离子基固体抗菌剂，使得目标地毯产品在真空处理后具有使抗菌活性和/或进一步洗涤后的耐用性增强的能力。
Description
技术领域
本发明涉及含有嵌入到目标纤维中以赋予其耐用抗菌整理的固体抗菌颗粒的表面抗菌地面遮盖物处理。这种表面处理包括特定的抗菌金属离子基固体化合物，例如银离子交换化合物，(例如，包括磷酸银锆、银沸石和/或银玻璃)，其在液体介质中存在或者与另一种固体处理相混合。这种处理还任选包括耐污剂、防止泥土再沉积的化合物和液体、表面活性剂、抗静电剂及类似物质的组合物，从而赋予目标地毯产品其它特性。因此，这种地毯处理赋予地毯簇绒表面和绒头本身极好的抗菌特性。此外，发现应用这种金属离子基固体抗菌剂，使得目标地毯产品在真空处理后具有使抗菌活性和/或进一步洗涤后的耐用性增强的能力。
技术背景
以下列出的所有美国专利，全部并入本文以供参考。
近年来，对于来自潜在日常暴露的细菌污染物所带来的危险已经引起了极大的关注。其中相关的值得注意的例子包括快餐店夹生牛肉中发现的大肠杆菌的某些菌株引起的食物中毒的致命结果；夹生的和未清洗的家禽食物制品中的沙门氏菌污染引起的疾病；以及由金黄葡萄球菌、克雷白氏肺炎菌、酵母菌和其它单细胞生物引起的疾病和皮肤感染。随着该领域中消费者利益的增加，制造商已经开始在各种日常用品和制品引入抗菌剂。例如，某些品牌的聚丙烯切菜板、液体皂等都含有抗菌化合物。这类制品中最流行的抗菌剂是三氯生(triclosan)。尽管在液体或某种聚合介质中加入这种化合物已经相对简单，但其它底物，包括织物和纤维表面的其它基层中，已经证实是不太合用的。此外，三氯生含有经离解后可能会在基层表面释放的氯离子。这种离子对于人类具有潜在的危险性，这是由于接触和在环境污水中会导致皮肤刺激等。另外，有时有害细菌具有对三氯生的杀菌性能逐渐形成免疫的能力。而且，已证实用三氯生进行表面处理也是无效的，因为这种化合物具有高度水溶性并且当暴露在足够量的湿气中时容易被除去。
地毯，特别是地毯的绒头部分(例如设计用于与行人鞋类接触的部分，例如簇绒纤维、割绒纤维、毛圈绒头纤维等)，非常容易被细菌、真菌和其它类型微生物污染物所感染。当行人以穿鞋、赤脚等方式在这种表面上行走时，不必说液体溢流物、碎屑以及其它细菌和真菌滋养物的可能性相对较高，细菌和真菌的传播也很有可能，更不必说助长了这种微生物的维持和生长。某些例如蒸汽清洁法的清洁方法，经过一段时间后，通过在地毯表面部分维持使滋养物生长的水环境以及因此导致的微生物后续的维持和生长，也很可能使这种微生物的生长速度加快。尽管可以通过这种清洁过程中的高温曝露对细菌或真菌造成妨碍，一旦温度水平回复正常，这种微生物可以从休眠中回复过来。将抗菌剂应用到地毯底布上以防止粘接失效和由此导致的绒头部分与底布本身的分层剥离。此外，也出现了一些应用在地毯绒头部分上的抗菌剂，包括Scholla等人的美国专利第5,096,747号，其公开了同时应用耐污和抗菌化合物进行处理的地毯。尽管专利权所有人公开了阴离子和/或非离子型抗菌剂，例如，优选戊二醛、Microban X-580(异丙醇、对二异丁基苯氧基乙氧基溴络合物、和正辛基二环庚烷二羰基酰亚胺、胡椒基丁醚、和除虫菊酯)、和磷酸；在此专利中任何一处都没有提及金属基无机抗菌剂，更不用说金属离子基无机抗菌剂。这种现有技术的抗菌剂可能具有缺陷，例如缺乏长期功效(因此为了保持高抗菌性能水平需要重复进行处理)以及潜在的细菌免疫。此外，美国专利第5,503,840号公布了利用具有镀层(银、铜、铝、二氧化硅和壬二酸二辛酯)的硫酸钡颗粒作为抗菌剂用于地毯纤维和纱线中，而非作为表面应用。因此，为地毯簇绒表面和制品提供短期和长期有效的、耐用及持久的表面应用抗菌剂，是长期以来的需要。
近来，已经开发和利用了含特定金属离子的(例如含Ag+的)无机杀菌剂(例如离子交换化合物，例如磷酸锆、玻璃和/或沸石化合物)作为用于不同基层和表面之上和之中的抗菌剂。这些类型的抗菌剂由于其具有以下能力是高度理想的：提供抗菌活性效力，同时不用害怕细菌或真菌对其免疫，更不用说其不具有能够提供有害刺激和潜在讨厌气味的高度氧化部分和侧基(例如氯基化合物)，而且通常这些固体颗粒操作的容易性，使这些化合物有望在许多不同介质中应用。具体的说，这种杀菌剂适合结合在塑料组合物和纤维中以便提供具有内在抗菌特性的日常和消耗产品。尽管这些银基剂提供了极好的、耐用的抗菌性能，到目前为止不存在学说指出或明确建议应用这些无机化合物作为地毯绒头纤维上存在的耐用表面涂覆剂。如果考虑到在任意表面上提供固体颗粒耐用表面涂覆剂的困难这并不令人惊奇，更不用说在特定的地毯簇绒表面和纤维上。这种固体微粒向这种地毯簇绒结构的底部沉降的倾向，以及由此看来无法提供遍及此纤维(即，同时在上部、中部和底部)的有效抗菌性能，妨碍了这种处理的尝试。因此在这种高度期望的抗菌制剂得到有效地应用之前，需要改善保护的不均匀性。到目前为止，这种障碍尚未被克服，因此不允许在地毯簇绒结构中广泛应用这些抗菌剂。
发明内容
因此本发明的一个目的是提供一种在清洁或清洁后的步骤中用含金属离子的耐用抗菌处理对地面遮盖物制品的地毯绒头部分有效地进行处理的简单方式。本发明的另一个目的是提供一种用含抗菌金属离子的耐用抗菌处理对地面遮盖物的地毯绒头部分有效地进行处理的简单方式，其中的抗菌处理还赋予其抗真菌和减少气味的特性。
因此，本发明包括一种对地面遮盖物制品进行抗菌处理的表面应用的方法，包括以下步骤
(a)提供含有固体抗菌剂和至少一种选自表面活性剂、含脲-甲醛的粉末、熔凝硅石及其任意混合物的其它化合物的固体或液体处理组合物；
(b)提供地面遮盖物制品；以及
(c)使步骤“a”所述处理组合物与步骤“b”所述地面遮盖物制品相接触；
其中，在根据AATCC检测方法138进行至少2次标准地毯洗涤处理后，所述处理组合物赋予所述地面遮盖物制品的抗菌剂水平，经AATCC检测方法100-1999进行24小时的曝光检测所测量出的对克雷白氏肺炎菌的杀死率对数(log kill rate)至少是1.0，优选大于1.5，更优选大于2.0。本发明也包括上述方法中的不同处理组合物。以上提到的洗涤耐久性测试是标准化的，由于本领域的普通技术人员可以很好地掌握该技术，其不是本发明所必需的或对本发明的限制。这种检测方法仅仅提供了一个标准，在根据此标准进行的两次洗涤过程中，经本发明处理的地毯地面遮盖物制品不会丧失过高程度的抗菌效力。
残留固体抗菌剂的有效量可以通过任何标准方法进行测量，例如，感应耦合等离子体法(ICP)、X-射线荧光法(XRF)或原子吸收(AA)分光光度分析法。然而，同样优选对与抗菌性能有关的这种表面应用地毯处理的耐用性(即地毯簇绒表面处理的保持力)进行测量。因此，经过有效的抗菌处理后，在根据AATCC检测方法138进行两次标准洗涤过程后，如上面所提到的根据AATCC检测方法100-1999曝光24小时后显示的对克雷白氏肺炎菌的杀死率对数，至少为1.0和更大，其显示了残留的和/或仍然具有抗菌效力的最小可接受性能的合适的和必需的固体抗菌剂量。该杀死率对数优选大于1.2，更优选1.5，最优选至少为2.0。此外，经过最少次洗涤过程后，该杀死率对数表示以上提到的预期耐用性。
现有技术中任何一处均没有公布、利用或明确推荐这种特殊处理的地毯地面遮盖物或其制造方法。在最近的技术中，上面提到的Scholla等人提出某些液体抗菌剂与某些耐污整理剂同时作为地毯簇绒结构的潜在共同添加剂。没有固体抗菌剂被提及或明确推荐，更不用说含金属离子的固体抗菌剂，更不用说含银离子的抗菌化合物。所有其它的现有技术均讨论了在纤维中(其可以包括地毯纤维)挤压的固体抗菌剂赋予目标地面遮盖物制品以抗菌特性。然而，没有任何一处提到或暗示以上广泛说明的耐用表面处理。
任何标准的地毯纱线或纤维可以用作本申请内进行表面处理的基层。因此，天然纤维(棉、羊毛等)或合成纤维(聚酯、聚酰胺、聚烯烃等)可以独自构成目标基层，或与合成纤维、天然纤维或这两种类型的混纺形成任意组合或混合物而构成目标基层。对于合成类型，本发明可以使用，例如但是不限于，聚烯烃，例如聚乙烯、聚丙烯和聚丁烯；卤代聚合物，例如聚氯乙烯；聚酯，例如聚乙烯对苯二酸酯、聚酯/聚醚；聚酰胺，例如尼龙6和尼龙6，6；聚氨酯；以及这些单体任意结合的均聚物、共聚物或三聚物等。特别优选尼龙6、尼龙6，6、聚丙烯、和聚乙烯对苯二酸酯(一种聚酯)。此外，目标纤维中可以含有复合添加剂，可以用任何数量的不同材料(包括那些在下面更详细列出的)进行预涂覆，和/或可以用任何类型的着色剂(例如聚(氧化烯化的)着色剂)、以及颜料、染料、淡色(tints)等进行染色或着色，从而为最终使用者提供其它的美学特征。其它添加剂也可以存在于目标纤维或纱线之上和/或之中，其包括抗静电剂、增艳处理化合物、成核剂、抗氧化剂、UV稳定剂、填料、耐久定形整理剂、柔软剂、润滑剂、固化促进剂等。本发明的纤维特别需要的任选和补足的整理剂是泥土释放剂或抗再沉积剂，其改善了地毯绒头纱线和纤维(例如SCOTCHGUARD)的疏水性和除尘度。此外，其它潜在添加剂和/或整理剂可以包括防护剂碳氟化合物及其衍生物、硅酮、蜡、及其它类似的防水材料。
优选具体的处理含有至少一种类型的含金属离子的固体颗粒或其混合物。术语“金属”包括任何这种历史上已了解的周期表成员(包括过渡金属，例如但是不限于银、锌、铜、镍、铁、镁、锰、钒、金、钴、铂等，以及包括但是不限于铝、锡、钙、镁、锑、铋等的其它类型金属)。更优选本发明中所使用的金属是通常被称为过渡金属的那些。过渡金属中，更优选的金属是银、锌、金、铜、镍、锰和铁。最优选银和锌。这些金属在目标地毯绒头基层上提供最全面的所需特性，例如优选抗菌、抗真菌和/或减少气味的特性，可靠的着色性，良好的耐光性以及最重要的洗涤耐久性。
优选本发明的含金属离子的化合物是由可由美利肯公司获得的商标为ALPHASAN
的抗菌磷酸银锆，尽管任何含银抗菌化合物均可用作该优选种类的添加剂或替代物，这些含银抗菌化合物包括，例如(仅仅作为一些例子)，可由Sinanen(品川燃料公司)获得的商标为ZEOMIC
的银取代沸石，或可由Ishizuka Glass(石塚硝子株式会社)获得的商标为IONPURE
的银取代玻璃。也优选这种化合物是氧化锌、蓖麻醇酸锌、氯化锌和硫酸锌。以上提到的其它金属也可以使用；然而，从性能的观点来看优选银和锌；无论如何，最优选含银离子型。一般来说，这种金属化合物的加入量为具体的处理组合物总重的大约0.01至60％；更优选大约0.05至大约50wt.％；最优选大约0.1至大约50wt.％(取决于目标用途；对于液体来说，该量很低，因为在液体处理过程中具有传递足够量抗菌剂的能力，而在固体混合物中该量相对大，因为与目标簇绒表面相接触的固体量较低；因此对于固体表面应用，初始混合物中相对高的抗菌剂量在使用过程中传递足够的抗菌水平)。因此，经由液体(例如洗涤剂)或固体介质传递向目标基层加入含金属离子的化合物作为活性物，加入量为绒头纤维重量(owff)的100至15,000ppm，更优选150至大约14,000ppm，进一步优选175至13,000ppm，最优选200与12,000ppm之间(转化为owff重量百分比大约是0.02至1.2％)。这一比例提供了涉及清洗耐久性、电绝缘性、和总成本的最佳抗菌和/或减少气味的性能，更不用说经过进一步和/或未来的真空处理或其它清洁过程后，其具有最大的潜力使嵌入到目标纤维中的量保持充足。含有任何必要的粘合剂、粘合物、增稠剂等的处理自身加入到基层中的量为a)每平方码大约0.01至约大8.0盎司，或者b)大约0.1至大约20％owff。其它可能的化合物是，同样不限于，银基材料，例如可由DuPont(杜邦公司)获得的AMP
T558和MICROFREE，以及可由Johnson Mathey(约翰逊·马斯公司)获得的JMAC
如果处理组合物是液体，固体抗菌剂可以悬浮、分散、或仅仅存在于含有表面活性剂的液体介质中。液体介质在本质上应当相对容易挥发以便在与目标地面遮盖物制品相接触时容易蒸发。因此，液体介质(或赋形剂)可以选自水、短链醇(例如甲醇、乙醇、异丙醇、丁醇)等。表面活性剂可以选自一般种类的阴离子表面活性剂、阳离子表面活性剂、两性表面活性剂、非离子表面活性剂、两性离子表面活性剂及其任意混合物。这种表面活性剂用于帮助允许使固体抗菌剂与目标地面遮盖物制品的纤维有效地良好接触，不限于任何科学理论，我们相信这是为了耐久性目的而使固体抗菌化合物易于嵌入目标纤维。尽管任何类型的表面活性剂或多种表面活性剂可以用于这种处理组合物，优选表面活性剂在本质上是氟化的。已经发现这种氟化表面活性剂使上面提到的抗菌剂与纤维之间的有效接触成为可能，并且还可能为经处理后的纤维提供某种程度的水和/或其它液体防护性。因此，具体的说，可不受限制使用的是可由DuPont(杜邦公司)获得的商标为ZONYL
7的那些氟化表面活性剂，或者其它类型的氟化表面活性剂，例如可由3M公司获得的那些。表面活性剂应当以总处理组合物的0.001至25wt.％的量存在；更优选大约0.01至大约10wt.％。表面活性剂也可以帮助固体抗菌剂在液体介质(或赋形剂)中实现分散；然而，某些表面活性剂的存在比例可能不够高，不足以提供这种效力，或者仅仅是不含有为长久保持这种分散体而允许适当混合的侧基。因此，处理组合物可能是现成可使用的，或者可能需要进行混合或振荡以便有效地使合适量的所需固体抗菌剂进入待应用(通过喷雾、涂敷、雾化或其它类似方法)的分散体区域内。此外，表面活性剂本身可能在液体介质(或赋形剂)中形成悬浮液。分散体、悬浮液或仅仅是液体组合物，可以进一步含有其它添加剂，例如粘度调节剂、抗静电剂等，以便为应用的目的提供所需性能，或为待处理纤维提供更多的整理或性能。
同样，或者除了这种表面活性剂组分之外，可以在液体处理组合物中使用熔融硅石分散体。已经发现这种硅石提供了使固体抗菌剂与目标纤维的接触增强的类似能力，同时还提供了一定程度的防止泥土再沉积的性能。因此为了加强抗菌性能和防止泥土再沉积性能的目的，可以同时在此分散体中应用熔融硅石和固体抗菌剂。在这种情况下，熔融硅石可以总处理组合物的大约0.1至大约35wt.％的量存在。同上，可以存在另外的添加剂(粘度调节剂等)。此外，熔融硅石/固体抗菌剂液体组合物可以是分散体形式(特别是如果还存在表面活性剂时)、悬浮体形式、或仅仅是如上的液体形式也可以。
潜在优选地，尽管不是必需地，用于应用在目标地面遮盖物制品上的处理组合物的液体形式是洗涤剂。因此，当与目标表面相接触时，这种液体组合物中的表面活性剂或多种表面活性剂会产生其中也存在固体抗菌剂的泡沫(froth)、泡沫(foam)或肥皂泡沫(sud)。因此，这种洗涤剂使得清洁用和/或处理用表面活性剂组分以及固体抗菌剂化合物得以极好地进行渗透，以便如上所述使固体化合物易于嵌入目标纤维中。在这些潜在优选的地毯洗涤剂组合物中，优选表面活性剂在本质上是阴离子的(例如长链脂肪酸钠盐，作为一个具体非限定性例子的月桂基硫酸钠)，尽管也可以加入氟化表面活性剂以赋予目标纤维上述性能。这种洗涤剂可以作为气悬体(其中有典型的推进剂存在)使用，或者作为粘性液体使用，该粘性液体经过在目标地面遮盖物制品之上和之中的搅动，以使这种清洁/消毒洗涤剂组合物产生所需的泡沫(foam)、泡沫(froth)和/或肥皂泡沫。洗涤剂也可以含有上面所提到的表面活性剂组分的溶剂，例如水、短链醇及类似物质，其在这种地毯洗涤剂组合物是典型的。通常，这种组合物中的表面活性剂量应当是总组合物的大约0.1至大约50wt.％；更优选大约0.5至大约30wt.％；最优选大约1.0至大15wt.％之间。
本发明处理组合物的固体形式包括熔融硅石与固体抗菌剂的混合物，或者，更优选固体抗菌剂与脲-甲醛聚合粉末(例如，可由Milliken& Company(美利肯公司)获得的商标为CAPTURE
的粉末)的组合。在这种情况下，熔融硅石或CAPTURE
粉末构成混合物的主要部分，其含量至少为95wt.％。每一种类型的混合物均可以用完全干燥的形式使用或者在目标纤维的预湿润后使用。无论何种情况，固体组合物或者有助于防止泥土的再沉积(熔融硅石)，或者有助于将泥土和其它颗粒吸入随后可以通过真空处理从绒头纤维中除去从而得到比以前更干净的地面遮盖物制品的粉末中(CAPTURE
)。在这种情况下，非常令人惊奇的是，被脲-甲醛聚合物吸附的固体抗菌剂似乎不如被目标纤维(特别是合成纤维)吸附并且嵌入其中的多。此外，如下面所提到的，在不向目标纤维上施加任何另外的抗菌处理的情况下，甚至在经过一定持续时间后，所使用的固体抗菌剂在仅仅进行了真空处理后将显示出对目标地面遮盖物制品的簇绒表面的增强的效力。同样，这一结果是非常令人惊奇的，但是，不限于任何科学理论，我们相信这一结果是由于固体抗菌化合物可能存在于地面遮盖制品纤维部分本身的底部，而经真空处理后这种化合物移动到靠近其表面的地方而并没有完全被真空处理除去。
如上所述的术语“地面遮盖物”，是用于概括任意含有绒头纤维并且用于覆盖人们要在其上行走的表面的标准制品。因此，地毯(阔幅地毯、方块地毯及类似物品)和地垫(室外、室内及类似物品)是本发明关注的主要制品。术语“绒头纤维部分”包括任何在地面遮盖物中使用的标准纤维及其合成物。仅作为例子，尼龙纤维、聚乙烯纤维、聚丙烯纤维、棉纤维、聚乙烯基乙酸酯纤维及类似纤维，可以通过织物(例如任何类型的机织、非机织或针织织物，其中的纤维类型例如前文中列出的那些)形成簇绒，该织物刚好是术语“基底部分(primary backingportion)所包含的内容。此外，绒头纤维部分可以是单纤维丝、芯鞘纤维及类似物，或可以作为毛圈绒头、割绒或任意其它类型的地毯面。
最初，在与任何其它组分结合之前，绒头纤维部分通过与基底布进行缝合、簇绒、钉合及类似方法形成复合材料，随后其可以简单的粘附到另外的部分上。另外可选地，基底布可以与第二基层织物相接触，随后可以在基底布上通过针织制造绒头纤维部分。基本上，制造本发明的地面遮盖物制品存在着任意数量的选择。在Higgins等人的美国专利第5,929,145号、第5,948,500号、第5,545,276号、和第5,540,968号中公布了地毯和方块地毯制品的例子。在Kerr的美国专利第5,902,662号、Kerr等人的第5,928,446号和Nagahama等人的第5,305,565号中存在着地垫制品的例子。优选使用乳胶将绒头纤维部分粘合到第二基层上以形成稳定的复合材料。如需要，该乳胶可以含有抗菌剂。
术语第二基层部分(secondary backing portion)规定得相当广泛，因为关于这种组分的重要问题是与处于该层和基底布之间的本发明的乳胶之间的接触。因而，这种第二层可以是任意标准地毯或地垫基层、或中间层。因此，如果其是地毯，第二基层可以是聚烯烃织物、或者是聚氨酯泡沫(为了缓冲目的)或仅仅是聚氨酯泡沫所附着的织物层。如果其是地垫，第二基层很可能是固体橡胶或泡沫橡胶的薄片，尽管，同样，这一基层可以是处于基底布和外层之间的织物、橡胶等的中间层。
根据AATCC测试方法100-1999，特定金属离子基固体抗菌剂应当在24小时后表现出可接受的杀死率对数。这种可接受的杀死率对数水平下所检测到的金黄葡萄球菌比基线至少高0.1。或者，如果其杀死率对数大于未处理(也就是说，不加入固体无机抗菌剂)绒头纤维(例如与对照的、不含抗菌剂的纤维的杀死率对数相比高了0.5)，将存在可接受的水平。对于金黄葡萄球菌，优选该杀死率对数比基线至少高0.3，更优选0.5，最优选1.0。当然，这种杀死率对数的上限远远高于基线，处于5.0的数量级(99.999％杀死率)。因此，任何处于中间的比率，当然也是可接受的。另一方面，只要这种测量结果优于相关的未处理纤维的记录值，对于此发明来说杀死率对数是负数也是可接受的。在这种情况下，目标地毯绒头纤维中存在的抗菌物质至少表现出对于细菌生长的阻碍。
这些可选的纤维处理的优选实施方案在下面进行更详细的讨论。
具体实施方式
本发明范围内特别优选的处理的例子在下面提出。
液体处理组合物
优选的含抗菌剂的处理制剂，根据下表将所有组分混合在一起进行配制。使用这种特定制剂进行表面处理的制造也在下面表格中提及。
实施例1
含阴离子表面活性剂的洗涤剂组合物
组分 加入量(wt.％)
月桂基硫酸钠 1
水 平衡量
抗菌剂 (如下面列出)
实施例2
含氟化表面活性剂的喷雾组合物
组分 加入量(wt.％)
ZONYL8300 10
水 平衡量
抗菌剂 (如下面列出)
固体处理组合物
优选的含抗菌剂的处理制剂，根据下表将所有组分混合在一起进行配制。使用这种特定制剂进行表面处理的制造也在下面表格中提及。
实施例3
脲-甲醛混合物
组分 加入量(wt.％)
CAPTURE
牌粉末 98
抗菌剂 2
实施例4
硅石混合物
组分 加入量(wt.％)
硅石(Aerosol 130) 50
抗菌剂 50
实施例5
脲-甲醛/硅石混合物
组分 加入量(wt.％)
CAPTURE
牌粉末 96
硅石(Aerosol 130) 2
抗菌剂 2
另一个实施例6中仅仅需要在抗菌剂中进行洗刷(在这种情况下，加入到目标地面遮盖物样品(尼龙方块地毯)中的ALPHASAN
RC5000的量为11,600ppm。还进行了根本不使用抗菌剂的对照处理。
随后，将以上液体和固体处理组合物分别应用在根据美国专利第5,540,968号和第5,545,276号的一般制造方法制造的典型加垫方块地毯制品上，并且在初始时、根据AATCC检测方法138进行随后的洗涤之后，以及在不对其应用任何另外的抗菌化合物的情况下进行随后的真空处理之后，检测其抗菌效力。
将应用在目标方块地毯绒头部分的抗菌剂量调节为均匀等差的水平，从绒头纤维重量(owff)的500ppm至达到11,600owff(从而对这些不同抗菌剂水平之间效力的差别进行检测，以及对在处理后真空处理步骤中除去的预期量进行补偿)。在24小时曝光后，在初始和随后进行2次根据AATCC测试方法138的洗涤处理后，对于克雷白氏肺炎菌的杀伤滤对数结果如下。
实验数据表1
聚酯方块地毯样品上对于克雷白氏肺炎菌的杀伤率对数
实施例 初始的或经
代码(上 抗菌剂(ppm owff) 杀伤率对数
真空处理的
述)
1 ALPHASAN
RC 5000(11,600) 初始 1.17
1 ALPHASANRC 5000(11,600) 真空处理后 2.15
(比较实施例)
1 无 初始 -0.26
1 无 真空处理后 -0.20
对照 无 初始 -0.68
实验数据表2
在尼龙方块地毯样品上对于克雷白氏肺炎菌的Log Kill Rates
初始的、经
实施例
洗涤的、或
代码(上 抗菌剂类型(ppm owff) 杀伤率对数
经真空处理
述)
后的
2 ALPHASANRC 5000(500) 初始 1.53
2 ALPHASAN
RC 5000(500) 经洗涤 1.27
2 ALPHASAN
RC 5000(2000) 初始 2.34
2 ALPHASAN
RC 5000(2000) 经洗涤 2.22
3 ALPHASAN
RC 5000(11,600) 初始 2.00
4 ALPHASAN
RC 5000(11,600) 初始 3.28
5 ALPHASANRC 5000(11,600) 初始 2.49
5 ALPHASANRC 5000(11,600) 经真空处理 3.41
6 ALPHASAN
RC 5000(11,600) 初始 1.56
6 ALPHASAN
RC 5000(11,600) 经真空处理 3.74
初始的、经
实施例
洗涤的、或
代码(上 抗菌剂类型(ppm owff) 杀伤率对数
经真空处理
述)
后的
(比较实施例)
2 无 初始 0.17
*进行了两次根据AATCC测试方法138的洗涤
因此，本发明的方法以及发明的抗菌处理组合物赋予目标地面遮盖物制品极好的耐用抗菌性能。
当然，以下权利要求的精神和范围中也包括本发明的许多可选择的实施方式和修改。
Claims (16)
1.一种对地面遮盖物制品表面应用抗菌处理的方法，包括以下步骤：
(a)提供含有含金属离子的无机固体抗菌剂和至少一种选自表面活性剂、含脲-甲醛的粉末、熔融硅石、氟化聚合物及其任意混合物的其它化合物的固体或液体处理组合物；
(b)提供地面遮盖物制品；以及
(c)使步骤“a”所述处理组合物与步骤“b”所述地面遮盖物制品相接触；
其中所述处理组合物赋予所述地面遮盖物制品的抗菌水平，测量为对于克雷白氏肺炎菌的杀死率对数，至少是1.0。
2.如权利要求1所述的方法，其中所述含金属离子的抗菌剂是银离子基化合物。
3.如权利要求2所述的方法，其中所述的银离子基化合物是银离子交换化合物。
4.如权利要求1所述的方法，其中所述处理组合物是液体。
5.如权利要求4所述的方法，其中所述液体是洗涤剂。
6.如权利要求4所述的方法，其中所述液体含有阴离子表面活性剂。
7.如权利要求1所述的方法，其中所述处理组合物是固体。
8.如权利要求7所述的方法，其中所述固体是熔融硅石/含金属离子的无机固体抗菌剂混合物。
9.如权利要求7所述的方法，其中所述固体是脲-甲醛聚合物/含金属离子的无机固体抗菌剂混合物。
10.如权利要求4所述的方法，其中所述液体是喷雾。
11.如权利要求10所述的方法，其中所述液体含有氟化表面活性剂。
12.一种固体抗菌地面遮盖物处理组合物，其含有至少一种选自脲-甲醛聚合物、熔融硅石及其任意混合物的组分，和至少一种含金属离子的无机固体抗菌化合物。
13.如权利要求12所述的组合物，其中所述含金属离子的抗菌剂是银离子基化合物。
14.如权利要求13所述的组合物，其中所述银离子基化合物是银离子交换化合物。
15.一种对地面遮盖物制品表面应用抗菌处理的方法，包括以下步骤：
(a)提供含有至少一种银基离子交换化合物的固体抗菌组合物；
(b)提供地面遮盖物制品；和
(c)使步骤“a”所述处理组合物与步骤“b”所述地面遮盖物制品相接触；
其中所述处理组合物赋予所述地面遮盖物制品的抗菌水平，测量为对于克雷白氏肺炎菌的杀死率对数，至少是1.0。
16.一种显示出测量为对第一级克雷白氏肺炎菌的杀伤率对数的初始抗菌水平的地毯制品，其中在对所述初始抗菌水平进行测量后不加入任何另外的抗菌化合物的情况下对所述地毯制品进行真空处理之后，与所述初始抗菌水平相比，所述地毯制品表现出的对克雷白氏肺炎菌的杀伤率对数得到了提高。