CN100400711C - 黑色金属气相缓蚀剂及其制备方法 - Google Patents
黑色金属气相缓蚀剂及其制备方法 Download PDFInfo
- Publication number
- CN100400711C CN100400711C CNB2006100195170A CN200610019517A CN100400711C CN 100400711 C CN100400711 C CN 100400711C CN B2006100195170 A CNB2006100195170 A CN B2006100195170A CN 200610019517 A CN200610019517 A CN 200610019517A CN 100400711 C CN100400711 C CN 100400711C
- Authority
- CN
- China
- Prior art keywords
- parts
- alcohol
- portions
- urea
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种对黑色金属及其制品进行防锈保护的环保型气相缓蚀剂及其制备方法。气相缓蚀剂包括有苯甲酸胺、苯甲酸钠、尿素、乌洛托品、肉桂酸、酒精和无离子水配制而成，其组分和含量按重量计为：苯甲酸胺1-2份，苯甲酸钠2-4份，尿素1.5-3份，乌洛托品1.5-3份，肉桂酸0.8-1.5份，酒精2.5-4.5份，无离子水30-60份。本发明的有益效果在于：1、制成的缓蚀液中有害物质的含量极低，因此在生产和使用过程中能够保持低污染，有利于环保，能达到欧盟的ROHS指令；2、防锈性能好，产品能达到QB1319-91标准；3、生产制备方法简便，原料价格较低，因而生产成本低，易于推广应用。
Description
技术领域
本发明涉及一种对黑色金属及其制品进行防锈保护的环保型气相缓蚀剂及其制备方法。
技术背景
气相防锈纸作为黑色金属及其制品的防锈防护包装材料已被广泛应用。气相防锈纸主要由纸张涂覆气相缓蚀剂构成，但现有的气相缓蚀剂大多含有亚硝酸盐、磷酸盐、六价铬等对人体及环境有害的物质，若减少其用量，往往防锈效果不理想；为解决上述问题，已提出采用植酸等物质来替代上述有害物质，但价格昂贵、生产成本升高，难以推广。
发明内容
本发明所要解决的技术问题是在于针对上述现有技术存在的不足而提供一种环保性能好、生产成本低、制备简便和防锈性能优良的黑色金属气相缓蚀剂及其制备方法。
本发明黑色金属气相缓蚀剂的技术方案为：由苯甲酸胺、苯甲酸钠、尿素、乌洛托品、肉桂酸、酒精和无离子水配制而成，其组分和含量按重量计为：
苯甲酸胺1-2份， 苯甲酸钠2-4份， 尿素1.5-3份， 乌洛托品1.5-3份，
肉桂酸0.8-1.5份，酒精2.5-4.5份， 无离子水30-60份。
本发明的制备方法技术方案如下：
按重量计取以下组分和含量的原料待用：
苯甲酸胺1-2份， 苯甲酸钠2-4份， 尿素1.5-3份， 乌洛托品1.5-3份，
肉桂酸0.8-1.5份，酒精2.5-4.5份， 无离子水30-60份；
先将组分中的肉桂酸用酒精溶解制成A溶液，备用；
将无离子水放入反应釜中，依次加入以上其余各组份并搅拌到充分溶解，为B溶液；再在B溶液中加入配制好的A溶液，并混合搅拌均匀；
用氨水调整混合液的pH值至9-10。
本发明使用时将以上制配好的缓蚀剂按剂量涂布于中性原纸上经70℃-110℃烘干即可。
本发明的黑色金属气相缓蚀剂按QB1319-91标准执行防锈性能检测，检测结果如下：
| 试验项目 | 试验结果 | 试验条件 |
| 气相防锈甄别试验 | 9周期无锈 | t：50℃±2℃；RH：约95％ |
| 动态接触湿热试验 | 9周期无锈 | t：49℃±1℃；RH：大于95％ |
| 气相缓蚀能力试验 | 9周期无锈 | t：40℃±1℃；RH：约90％ |
本发明的黑色金属气相缓蚀剂按国家相关标准执行环保指标性能检测，检查结果如下：
| 检测项目 | 检测结果 | 执行标准 |
| 亚硝酸盐含量 | ＜6.4mg/kg | GB/T5009.33-2003 |
| 磷酸盐含量 | ＜4.95mg/kg | GB/T5009.87-2003 |
| 六价铬及其化合物含量 | ＜0.1mg/kg | ROHS指令 |
| 铅及其化合物含量 | ＜0.42mg/kg | ROHS指令 |
| 汞及其化合物含量 | ＜0.1mg/kg | ROHS指令 |
| 镉及其化合物含量 | ＜0.1mg/kg | ROHS指令 |
| 多溴联苯(PBB)含量 | 未检出 | ROHS指令 |
| 多溴联苯醚(PBDE)含量 | 未检出 | ROHS指令 |
本发明的有益效果在于：1、制成的缓蚀液中有害物质的含量极低，因此在生产和使用过程中能够保持低污染，有利于环保，能达到欧盟的ROHS指令；2、防锈性能好，产品能达到QB1319-91标准；3、生产制备方法简便，原料价格较低，因而生产成本低，易于推广应用。
具体实施方式
以下进一步详细描述本发明的实施例。
实施例1：
1、按重量计取0.8份肉桂酸加2.5份酒精充分搅拌至溶解，为A溶液，备用；
2、按重量计取30份无离子水放入反应釜中，并依次加入苯甲酸胺1份、尿素1.5份、苯甲酸钠2份、乌洛托品1.5份，充分搅拌至完全溶解，为B溶液；
3、将配制好的A溶液加入配制好的B溶液中充分混合搅拌，配制成气相缓蚀剂；
4、用PH试纸测试气相缓蚀剂的PH值，并用氨水调整PH至9-10即可。
使用时，在中性原纸一面涂布该气相缓蚀剂15-25g/m2，经70℃-110℃烘干即可。
实施例2：
1、按重量计取1.2份肉桂酸加3.5份酒精充分搅拌至溶解，为A溶液，备用；
2、按重量计取45份无离子水放入反应釜中，并依次加入苯甲酸胺1.5份、尿素2.2份、苯甲酸钠3份、乌洛托品2.3份，充分搅拌至完全溶解，为B溶液；
3、将配制好的A溶液加入配制好的B溶液中充分混合搅拌，配制成气相缓蚀剂；
4、用PH试纸测试气相缓蚀剂的PH值，并用氨水调整PH至9-10即可。
实施例3：
1、按重量计取1.5份肉桂酸加4.5份酒精充分搅拌至溶解，为A溶液，备用；
2、按重量计取60份无离子水放入反应釜中，并依次加入苯甲酸胺2份、尿素3份、苯甲酸钠4份、乌洛托品3份，充分搅拌至完全溶解，为B溶液；
3、将配制好的A溶液加入配制好的B溶液中充分混合搅拌，配制成气相缓蚀剂；
4、用PH试纸测试气相缓蚀剂的PH值，并用氨水调整PH至9-10即可。
Claims (5)
1.一种黑色金属气相缓蚀剂，其特征在于由苯甲酸胺、苯甲酸钠、尿素、乌洛托品、肉桂酸、酒精和无离子水配制而成，其组分和含量按重量计为：
苯甲酸胺1-2份，苯甲酸钠2-4份，尿素1.5-3份，乌洛托品1.5-3份，肉桂酸0.8-1.5份，酒精2.5-4.5份，无离子水30-60份。
2.按权利要求1所述的黑色金属气相缓蚀剂，其特征在于其组分和含量按重量计为：
苯甲酸胺1份，苯甲酸钠2份，尿素1.5份，乌洛托品1.5份，肉桂酸0.8份，酒精2.5份，无离子水30份。
3.按权利要求1所述的黑色金属气相缓蚀剂，其特征在于其组分和含量按重量计为：
苯甲酸胺1.5份，苯甲酸钠3份，尿素2.2份，乌洛托品2.3份，肉桂酸1.2份，酒精3.5份，无离子水45份。
4.按权利要求1所述的黑色金属气相缓蚀剂，其特征在于其组分和含量按重量计为：
苯甲酸胺2份，苯甲酸钠4份，尿素3份，乌洛托品3份，肉桂酸1.5份，酒精4.5份，无离子水60份。
5.一种黑色金属气相缓蚀剂的制备方法，其特征在于按重量计取以下组分和含量的原料待用：
苯甲酸胺1-2份，苯甲酸钠2-4份，尿素1.5-3份，乌洛托品1.5-3份，肉桂酸0.8-1.5份，酒精2.5-4.5份，无离子水30-60份；
先将组分中的肉桂酸用酒精溶解制成A溶液，备用；
将无离子水放入反应釜中，依次加入以上其余各组份并搅拌到充分溶解，为B溶液；
再在B溶液中加入配制好的A溶液，并混合搅拌均匀；
用氨水调整混合液的pH值至9-10。