CN100554516C - 水基长效防锈剂 - Google Patents

水基长效防锈剂 Download PDF

Info

Publication number
CN100554516C
CN100554516C CNB2007100102471A CN200710010247A CN100554516C CN 100554516 C CN100554516 C CN 100554516C CN B2007100102471 A CNB2007100102471 A CN B2007100102471A CN 200710010247 A CN200710010247 A CN 200710010247A CN 100554516 C CN100554516 C CN 100554516C
Authority
CN
China
Prior art keywords
water
boric acid
rust
long
preventive agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2007100102471A
Other languages
English (en)
Other versions
CN101012563A (zh
Inventor
王明望
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Sandaaoke Chemistry Co Ltd
Original Assignee
Dalian Sandaaoke Chemistry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Sandaaoke Chemistry Co Ltd filed Critical Dalian Sandaaoke Chemistry Co Ltd
Priority to CNB2007100102471A priority Critical patent/CN100554516C/zh
Publication of CN101012563A publication Critical patent/CN101012563A/zh
Application granted granted Critical
Publication of CN100554516C publication Critical patent/CN100554516C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种水基长效防锈剂,由C8~C10羧酸盐(钠、钾或铵盐,5.0~30.0%)、乙醇胺(一、二或三乙醇胺,5.0~15.0%)、硼酸类(硼酸或硼酸铵,3.0~8.0%)聚乙二醇(8~10个乙二醇聚合度,0.0~5.0%)组成。产品呈淡黄色透明粘稠液体。防锈剂可在常温或加温下使原料溶于水中即可。防锈剂对一般碳钢、铸铁都有良好的防护效果。使用时不会在金属表面形成白斑,无流痕并保持金属面原有色泽;湿热试验周期4周以上无变化。防锈剂稳定性好,在高温和低温等条件下都能保持稳定,不分层、无沉淀。产品及原料安全,在配制和使用时对人体无损害、对环境无污染,是一种环保、无污染的长效金属防锈剂。

Description

水基长效防锈剂
技术领域:
本发明涉及的是金属材料(铁与铁合金)表面的化学处理的领域。 背景技术:
当前对金属材料(特别是对钢铁)表面的防锈处理,大量使用的水基 防锈剂是以亚硝酸盐为主剂复配而成的。虽然其防锈效果好、价格低廉, 但该类防锈剂有很多弊端: 一是这类防锈剂有很大的毒性,亚硝酸盐是很 强的致癌物质,对人体、对环境,都有很大危害。另外,由于是盐基物质, 使用后容易在金属表面形成白班,影响外观;对酸碱很敏感,对使用的工 作液的有效浓度也必须十分注意,否则将会起相反效果。非但不起防锈作 用,还会起腐蚀作用,被称为"危险型"防锈剂。并且对铸铁通常效果很 差。难以满足工艺要求。目前也出现了很多这类产品的替代品,但防锈期 一般很难与亚硝酸盐相比,通常用于工序间防锈。CN 1530463 (申请号 03111171)提供的非亚硝酸盐水基防锈剂,虽然摆脱了亚硝酸盐,但其使 用的原料品种之多和配制方法之复杂(分A、 B两组分,三次加热熔解、 反应),实际使用也存在许多不便。
发明内容:
针对现有技术存在的不足,本发明旨在提供一种不用亚硝酸盐、无污 染、配制简单、效果好的长效金属防锈剂。
本发明采用的技术方案是:用有机羧酸盐、硼酸盐、乙醇胺及聚乙二 醇等复配制而成。其所用的原料品种和配比(W%)为
C8〜C10羧酸盐 5.0〜30.0
乙醇胺 5.0〜15.0硼酸类 3. 0〜8. 0
聚乙二醇 0. 0〜5. 0
水 42. 0〜87.0
其中:C8〜C10的羧酸盐为其钾盐、钠盐或铵盐,以钠盐较好;乙醇 胺为一乙醇胺、二乙醇胺、三乙醇胺中1〜2种;硼酸类为硼酸或硼酸铵, 以硼酸为宜;聚乙二醇为8〜10个乙二醇聚合。实践看来,以下配方较好-C8〜C10羧酸盐 8. 0〜15. 0
三乙醇胺 3.0〜14.0
硼酸 3. 0〜6. 0
聚乙二醇 0.0〜5.0
水 60. 0〜85.0
防锈剂的配制非常简单,常温或加温使原料溶于水中即可。产品为淡 黄色粘稠液体。
与现有技术相比较,本发明的防锈剂对一般碳钢、铸铁都有良好的防
护效果。不会在被防锈金属表面形成白斑、无流痕、保持金属表面原有色
泽,湿热试验周期4周以上无变化。另外,本发明的溶液稳定性好,在高
温和低温等条件下都能保持稳定,不分层、无沉淀。产品及原料安全,在
配制和使用时对人体无损害、对环境无污染,是一种环保、无污染的长效
金属防锈剂。
以下用实施例对本发明作进一步的说明。 具体实施方式:
实例l按以下配方(W%)进行防锈剂的配制:
异辛酸钠 15. 0
三乙醇胺 8.0
硼酸 5.0
水 72.0
配制时在室温下将上述原料混合、搅拌均匀即成,产品为淡黄色粘稠 液体。置于25〜3(TC下5个月,不分层、无沉淀。对碳钢板材进行防锈处 理后保持金属表面原有色泽,湿热试验周期500h无变化。
实例2
按以下配方(W%)进行防锈剂的配制:
癸酸钠 25.0
三乙醇胺 12.0
硼酸 4.0
水 59.0
配制同上例。产品为淡黄色透明液体。置于35〜5(TC下3个月,不分 层、无沉淀。对碳钢板材进行防锈处理后保持金属表面原有色泽,湿热试 验周期4周无变化。
实例3
按以下配方(W%)进行防锈剂的配制: 壬酸钾 8.0
三乙醇胺 4.0 一乙醇胺: 4.0硼酸 4.0 水 80.0
配制同上例。产品为淡黄色透明液体。置于35〜5(TC下3个月,不分 层、无沉淀。对碳钢板材进行防锈处理后保持金属表面原有色泽,湿热试 验周期4周无变化。
实例4
按以下配方(W%)进行防锈剂的配制 辛酸钠 三乙醇胺
15.0 8.0 5.0 4.0 68.0
聚乙二醇 水
配制同上例。产品呈淡黄色透明粘稠液体。置于35〜5(TC下6个月, 不分层、无沉淀。对铸铁件进行防锈处理后保持金属表面原有色泽,湿热 试验周期4周无变化。
实例5
按以下配方(W%)进行防锈剂的配制 庚酸钠 三乙醇胺
聚乙二醇 水
28.0 14.0 7.0 2.0 49.0配制同上例。产品呈淡黄色透明粘稠液体。置于25〜35-C下4个月, 不分层、无沉淀。对薄板进行防锈处遒后保持金属表面原有色泽,湿热s 试验周期4周无变化。

Claims (3)

1、一种水基长效防锈剂,其特征在于由如下品种组分和重量百分配比组成: C8~C10羧酸盐 5.0~30.0 乙醇胺 5.0~15.0 硼酸类 3.0~8.0 聚乙二醇 0.0~5.0 水 42.0~87.0 其中:C8~C10的羧酸盐为其钾盐、钠盐或铵盐;乙醇胺为一乙醇胺、二乙醇胺、三乙醇胺中1~2种;硼酸类为硼酸或硼酸铵;聚乙二醇为8~10个乙二醇聚合度;产品为淡黄色粘稠液体。
2、根据权利要求1所述水基长效防锈剂,其特征在于所述组分中: C8〜C10羧酸盐为C8〜C10羧酸钠盐;乙醇胺为三乙醇胺;硼酸类为硼
3、根据权利要求1所述水基长效防锈剂,其特征在于由如下品种组分和重量百分配比组成:C8〜C10羧酸盐 8. 0〜15.0三乙醇胺 硼酸聚乙二醇 水
CNB2007100102471A 2007-02-01 2007-02-01 水基长效防锈剂 Expired - Fee Related CN100554516C (zh)