CN100395290C - 松散形无机防水材料添加剂及其制备方法 - Google Patents
松散形无机防水材料添加剂及其制备方法 Download PDFInfo
- Publication number
- CN100395290C CN100395290C CNB2005100128434A CN200510012843A CN100395290C CN 100395290 C CN100395290 C CN 100395290C CN B2005100128434 A CNB2005100128434 A CN B2005100128434A CN 200510012843 A CN200510012843 A CN 200510012843A CN 100395290 C CN100395290 C CN 100395290C
- Authority
- CN
- China
- Prior art keywords
- waterproof material
- parts
- additive
- water
- loose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种防水材料添加剂，具体是一种松散形无机防水材料添加剂及其制备方法。解决了现有技术中存在的有机防水材料容易老化，不耐低温，防水性能差的问题。是由下列物质按重量比制成，氟硅酸钠10～14份、硫酸铝1～3份、氢氧化钠2～4份、硅油8～12份、水60～80份。其制备方法是，将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到35～45度的水中，搅拌均匀即可。不仅可以有效阻止水份的渗透，但由于存在缝隙还有透气的功能。无机基料在添加本发明所述的防水添加剂后使用不收缩、不变形、不易老化、而且互补性强，它可以随着基面的变动而形变，实现动态防水，一定程度上解决了普通卷材由于屋顶变形而产生裂缝渗漏的问题。
Description
技术领域
本发明涉及一种防水材料添加剂，具体是一种松散形无机防水材料添加剂及其制备方法。
背景技术
我国的建筑防水材料从建国到90年代一直采用“三毡两油”，后来改为三毡四油的沥青玛蹄脂，在90年代后期对油毡进行了改性，变为现在的SBS防水卷材和APP防水卷材，它们都属于有机防水材料。有机防水材料最大的缺点是：耐侯性差，易老化，在低温时柔性很不稳定，而且在施工过程中容易产生大量的有害气体，特别是当防水卷材用于屋面后，在太阳光紫外线的照射下，沥青橡胶中的油份，脂胶会大量挥发掉，一段时间后沥青中只剩下沥青质，由于沥青质脆性大，在冬季气温降低时就会收缩干裂，屋面漏水大都由此引起。所以使用防水卷材要想实现长期的防水就必需频繁地更换防水层和不断地维修。增加了用户的日常支出。
发明内容
本发明为了解决现有技术中存在的有机防水材料容易老化，不耐低温，防水性能差的问题而提供了一种松散形无机防水材料添加剂及其制备方法。
本发明是由以下技术方案实现的，一种松散形无机防水材料添加，是由下列物质按重量比制成，氟硅酸钠10～14份、硫酸铝1～3份、氢氧化钠2～4份、硅油8～12份、水60～80份。
其制备方法是，将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到35～45度的水中，搅拌均匀即可。所取各个物质的量均按照上述重量比例称取。
上所述硅油为市场上出售的常规产品，至少可以选用江西省星火化工厂生产的羟基硅油。
将制备好的添加剂1份与无机基料10份混合并搅拌均匀，再在180～220℃烘干或晾干，即可制备出松散型防水材料。无机基料需要加工粉碎，粒径一般小于3mm。
其防水机理是对无机基料进行加工使其粒径变小呈松散状态，然后在一定条件下用本发明所述的添加剂进行处理，使添加剂渗入到松散的无机基料中形成一个密封的结构体，添加剂在无机基料颗粒的表面形成致密的凹凸不平的点，不仅可以有效阻止水份的渗透，但由于存在缝隙还有透气的功能。而且可以在无机基料表面产生“荷叶效应”使松散的无机基料颗粒之间产生拒水功能。无机基料在添加本发明所述的防水添加剂后使用不收缩、不变形、不易老化、而且互补性强，它可以随着基面的变动而形变，实现动态防水，一定程度上解决了普通卷材由于屋顶变形而产生裂缝渗漏的问题。
防水性能指标测试见表1
表1
通过实验分析研究，每平米用本发明所述的添加剂配制成的防水材料成本在20元左右，仅相当于防水寿命为5年的普通有机防水卷材的价格，而且一旦施工完成可以数十年内免于维修，从而节约了大量的维修费用，以30年计算每平米至少可节约防水费用四十元，具有很高的经济效益和社会效益。
所选用的无机基料可以是高岭土、煤矸石、矿山尾矿砂、钢渣、耐火材料废弃物等多种工业废渣，不但能废物再利用而且施工过程全在常温下进行，避免了普通卷材热铺带来的环境污染。
具体实施方式
实施例1，一种松散形无机防水材料添加剂，是由下列物质按重量比制成，氟硅酸钠10千克、硫酸铝1千克、氢氧化钠2千克、硅油8千克、水60千克。
其制备方法是，将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到35度的水中，搅拌均匀即可。
将制备好的添加剂1份与高岭土10份混合后放置与搅拌机中，并搅拌均匀，再在180℃烘干或晾干，即可制备出松散型防水材料。高岭土需要预先加工粉碎，粒径一般小于3mm。
实施例2，
一种松散形无机防水材料添加剂，是由下列物质按重量比制成，氟硅酸钠14千克、硫酸铝3千克、氢氧化钠4千克、硅油12千克、水80千克。
其制备方法是，将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到45度的水中，搅拌均匀即可。
将制备好的添加剂1份与矿山尾矿砂10份混合并搅拌均匀，再在220℃烘干或晾干，即可制备出松散型防水材料。矿山尾矿砂需要预先加工粉碎，粒径一般小于3mm。
实施例3，
一种松散形无机防水材料添加剂，是由下列物质按重量比制成，氟硅酸钠12千克、硫酸铝2千克、氢氧化钠3千克、硅油10千克、水73千克。
其制备方法是，将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到43度的水中，搅拌均匀即可。
将制备好的添加剂1份与废钢渣10份混合并搅拌均匀，再在200℃烘干或晾干，即可制备出松散型防水材料。废钢渣需要预先加工粉碎，粒径一般小于3mm。
Claims (4)
1.一种松散形无机防水材料添加剂，其特征在于：是由下列物质按重量比例制成，氟硅酸钠10～14份，硫酸铝1～3份、氢氧化钠2～4份、硅油8～12份、水60～80份。
2.根据权利要求1所述的松散形无机防水材料添加剂，其特征在于：是由下列物质按重量比例制成，氟硅酸钠12份，硫酸铝2份、氢氧化钠3份、硅油10份、水73份。
3.一种松散形无机防水材料添加剂的制备方法，其特征在于：将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到35～45度的水中，搅拌均匀即可，其中所选取的各个原料的重量比例为，氟硅酸钠10～14份，硫酸铝1～3份、氢氧化钠2～4份、硅油8～12份、水60～80份。
4.根据权利要求3所述的松散形无机防水材料添加剂的制备方法，其特征在于：将氟硅酸钠、硫酸铝、氢氧化钠、硅油、加入到43度的水中，搅拌均匀即可，其中所选取的各个原料的重量比例为，氟硅酸钠12份，硫酸铝2份、氢氧化钠3份、硅油10份、水73份。