CN106747496A - 一种轻质耐火型建筑用砖及其制备方法 - Google Patents

一种轻质耐火型建筑用砖及其制备方法 Download PDF

Info

Publication number
CN106747496A
CN106747496A CN201611069978.9A CN201611069978A CN106747496A CN 106747496 A CN106747496 A CN 106747496A CN 201611069978 A CN201611069978 A CN 201611069978A CN 106747496 A CN106747496 A CN 106747496A
Authority
CN
China
Prior art keywords
parts
light
building brick
type building
refractory type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611069978.9A
Other languages
English (en)
Inventor
刘西平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Dingniu Municipal Construction Co Ltd
Original Assignee
Kunshan Dingniu Municipal Construction Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Dingniu Municipal Construction Co Ltd filed Critical Kunshan Dingniu Municipal Construction Co Ltd
Priority to CN201611069978.9A priority Critical patent/CN106747496A/zh
Publication of CN106747496A publication Critical patent/CN106747496A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种轻质耐火型建筑用砖及其制备方法，所述轻质耐火型建筑用砖的原料为工业废渣40‑80份、建筑废料40‑80份、废水80‑120份、污泥10‑65份、粉煤灰10‑50份、河沙10‑40份、水泥10‑30份、黏土5‑30份和烧结助剂1‑20份，其中，所述河沙、所述水泥与所述黏土的重量比为2：1：1，所述烧结助剂占所述轻质耐火型建筑用砖的原料总重的1‑3％。本发明具有一定的强度和耐火的效果，以综合垃圾为原料，不仅对废物进行回收利用，节约了生产成本，而且达到环保的效果。

Description

一种轻质耐火型建筑用砖及其制备方法
技术领域
本发明属于建筑用砖技术领域，特别是涉及一种轻质耐火型建筑用砖。
背景技术
城镇化快速发展的同时也加大了城镇垃圾的增量，环境污染不断恶化，城镇发展中的建筑垃圾、工业垃圾、生活垃圾等综合垃圾的处理方式受到很多人的关注。目前对综合垃圾的处理方式为填埋、焚烧和堆肥等，然而填埋会导致垃圾中的重金属污染土壤和水资源；焚烧会污染大气环境，产生灰霾天气；堆肥需增加堆肥设备以及运行成本。随着民众环保意识的不断加强，寻找绿色环保的处理城镇发展中垃圾的技术具有重要的意义。
目前建筑用砖多以黏土砖为主，生产这种砖不仅需要耗费大量耕地，而且不利于环境的治理和建筑业发展。因此改进现有建筑用砖的造砖工艺具有极大的发展前景。
发明内容
本发明主要解决的技术问题是提供一种轻质耐火型建筑用砖及其制备方法，本发明的砖具有一定的强度和耐火的效果，以综合垃圾为原料，不仅对废物进行回收利用，节约了生产成本，而且达到环保的效果。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种轻质耐火型建筑用砖，所述轻质耐火型建筑用砖的原料为工业废渣40-80份、建筑废料40-80份、废水80-120份、污泥10-65份、粉煤灰10-50份、河沙10-40份、水泥10-30份、黏土5-30份和烧结助剂1-20份，其中，所述河沙、所述水泥与所述黏土的重量比为2：1：1，所述烧结助剂占所述轻质耐火型建筑用砖的原料总重的1-3％；
所述工业废渣为高炉渣、煤渣、电石渣、有色金属渣和钢渣中至少两种；
所述建筑废料为废瓦块、废塑料、废竹木、废砂浆和废石膏中至少两种；
所述废水为石油废水、电镀废水、印刷废水、造纸废水和采矿废水中至少两种。
进一步地说，所述原料按如下重量份数计：工业废渣50-70份、建筑废料50-70份、废水100-120份、污泥20-50份、粉煤灰15-30份、河沙20-40份、水泥10-20份、黏土10-20份和烧结助剂4-10份。
进一步地说，所述烧结助剂为氧化铝、氧化锂、氧化锌和二氧化硅中至少两种。
进一步地说，所述水泥为低碱硅酸盐水泥或普通硅酸盐水泥。
进一步地说，所述黏土为耐火黏土。
更进一步地说，所述耐火黏土的耐火度>1580℃。
进一步地说，所述污泥的含水率为95％。
进一步地说，所述粉煤灰的细度为60-70目。
进一步地说，所述河沙的细度为70-100目。
所述的一种轻质耐火型建筑用砖的制备方法，包括如下步骤：
步骤一：将工业废渣和建筑废料先加入破碎机中破碎，再置入研磨机中研磨，磨细至600-700目，得混合物A；
步骤二：将混合物A置入搅拌机中，再依次按比例加入河沙、水泥和黏土，常温300-400r/min转速下搅拌1-2h，得混合物B；
步骤三：在混合物B中加废水、污泥、粉煤灰和烧结助剂，常温500-700r/min转速下搅拌30-60min，得混合物C；
步骤四：将混合物C置入模具中压制成坯体，160-180℃温度下干燥60min；
步骤五：将坯体入窑煅烧，即得轻质耐火型建筑用砖。
本发明的有益效果至少具有以下几点：
1、本发明采用工业废渣、建筑废渣和废水等作为生产原料，大幅度降低了废料的排放，具有环保效果；
2、本发明的生产工艺流程简单、高效，降低人员的劳动强度和能源消耗；
3、本发明的轻质耐火型建筑用砖具有稳定性高、抗压强度高、轻质和耐热耐火的优点。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：一种轻质耐火型建筑用砖，所述轻质耐火型建筑用砖的原料为工业废渣67份、建筑废料50份、废水117份、污泥40份、粉煤灰15份、河沙40份、水泥20份、黏土20份和烧结助剂5份。
所述工业废渣为高炉渣、煤渣、电石渣、有色金属渣和钢渣中至少两种；
所述建筑废料为废瓦块、废塑料、废竹木、废砂浆和废石膏中至少两种；
所述废水为石油废水、电镀废水、印刷废水、造纸废水和采矿废水中至少两种。
所述烧结助剂为氧化铝和氧化锂，所述水泥为普通硅酸盐水泥，所述黏土为耐火黏土，所述耐火黏土的耐火度>1580℃，所述污泥的含水率为95％，所述粉煤灰的细度为65目，所述河沙的细度为80目。
实施例2：一种轻质耐火型建筑用砖，其余与实施例1相同，不同之处在于，所述轻质耐火型建筑用砖的原料为工业废渣50份、建筑废料70份、废水113份、污泥27份、粉煤灰20份、河沙30份、水泥15份、黏土15份和烧结助剂8份，所述烧结助剂为氧化铝、氧化锂和氧化锌，所述水泥为低碱硅酸盐水泥。
实施例3：一种轻质耐火型建筑用砖，其余与实施例1相同，不同之处在于，所述轻质耐火型建筑用砖的原料为工业废渣60份、建筑废料53份、废水100份、污泥20份、粉煤灰26份、河沙34份、水泥17份、黏土17份和烧结助剂7份，所述烧结助剂为氧化锂、氧化锌和二氧化硅，所述水泥为普通硅酸盐水泥。
实施例4：一种轻质耐火型建筑用砖，其余与实施例1相同，不同之处在于，所述轻质耐火型建筑用砖的原料为工业废渣64份、建筑废料62份、废水106份、污泥50份、粉煤灰19份、河沙20份、水泥10份、黏土10份和烧结助剂10份，所述烧结助剂为氧化铝、氧化锂、氧化锌和二氧化硅，所述水泥为低碱硅酸盐水泥。
实施例5：一种轻质耐火型建筑用砖，其余与实施例1相同，不同之处在于，所述轻质耐火型建筑用砖的原料为工业废渣53份、建筑废料60份、废水109份、污泥44份、粉煤灰30份、河沙28份、水泥14份、黏土14份和烧结助剂6份，所述烧结助剂为氧化铝、氧化锂和二氧化硅，所述水泥为低碱硅酸盐水泥。
实施例6：一种轻质耐火型建筑用砖，其余与实施例1相同，不同之处在于，所述轻质耐火型建筑用砖的原料为工业废渣70份、建筑废料59份、废水120份、污泥38份、粉煤灰22份、河沙38份、水泥19份、黏土19份和烧结助剂4份，所述烧结助剂为氧化锂和氧化锌，所述水泥为普通硅酸盐水泥。
所述的一种轻质耐火型建筑用砖的制备方法，包括如下步骤：
步骤一：将工业废渣和建筑废料先加入破碎机中破碎，再置入研磨机中研磨，磨细至600-700目，得混合物A；
步骤二：将混合物A置入搅拌机中，再依次按比例加入河沙、水泥和黏土，常温300-400r/min转速下搅拌1-2h，得混合物B；
步骤三：在混合物B中加废水、污泥、粉煤灰和烧结助剂，常温500-700r/min转速下搅拌30-60min，得混合物C；
步骤四：将混合物C置入模具中压制成坯体，160-180℃温度下干燥60min；
步骤五：将坯体入窑煅烧，即得轻质耐火型建筑用砖。
将上述实施例进行相关性能测试，并与普通建筑用砖进行对比，结果如表1：
表1：
由表1可知：本发明的轻质耐火型建筑用砖具有较好的抗压强度和耐火性，体积密度比普通建筑用砖要高，具有轻质性。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书所作的等效结构变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (10)

1.一种轻质耐火型建筑用砖，其特征在于：所述轻质耐火型建筑用砖的原料为工业废渣40-80份、建筑废料40-80份、废水80-120份、污泥10-65份、粉煤灰10-50份、河沙10-40份、水泥10-30份、黏土5-30份和烧结助剂1-20份，其中，所述河沙、所述水泥与所述黏土的重量比为2：1：1，所述烧结助剂占所述轻质耐火型建筑用砖的原料总重的1-3％；
所述工业废渣为高炉渣、煤渣、电石渣、有色金属渣和钢渣中至少两种；
所述建筑废料为废瓦块、废塑料、废竹木、废砂浆和废石膏中至少两种；
所述废水为石油废水、电镀废水、印刷废水、造纸废水和采矿废水中至少两种。
2.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述原料按如下重量份数计：工业废渣50-70份、建筑废料50-70份、废水100-120份、污泥20-50份、粉煤灰15-30份、河沙20-40份、水泥10-20份、黏土10-20份和烧结助剂4-10份。
3.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述烧结助剂为氧化铝、氧化锂、氧化锌和二氧化硅中至少两种。
4.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述水泥为低碱硅酸盐水泥或普通硅酸盐水泥。
5.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述黏土为耐火黏土。
6.根据权利要求5所述的一种轻质耐火型建筑用砖，其特征在于：所述耐火黏土的耐火度>1580℃。
7.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述污泥的含水率为95％。
8.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述粉煤灰的细度为60-70目。
9.根据权利要求1所述的一种轻质耐火型建筑用砖，其特征在于：所述河沙的细度为70-100目。
10.根据权利要求1所述的一种轻质耐火型建筑用砖的制备方法，其特征在于：包括如下步骤：
步骤一：将工业废渣和建筑废料先加入破碎机中破碎，再置入研磨机中研磨，磨细至600-700目，得混合物A；
步骤二：将混合物A置入搅拌机中，再依次按比例加入河沙、水泥和黏土，常温300-400r/min转速下搅拌1-2h，得混合物B；
步骤三：在混合物B中加废水、污泥、粉煤灰和烧结助剂，常温500-700r/min转速下搅拌30-60min，得混合物C；
步骤四：将混合物C置入模具中压制成坯体，160-180℃温度下干燥60min；
步骤五：将坯体入窑煅烧，即得轻质耐火型建筑用砖。
CN201611069978.9A 2016-11-29 2016-11-29 一种轻质耐火型建筑用砖及其制备方法 Pending CN106747496A (zh)