CN100385031C - 用直接还原铁生产微碳铝铁合金的制备方法 - Google Patents
用直接还原铁生产微碳铝铁合金的制备方法 Download PDFInfo
- Publication number
- CN100385031C CN100385031C CNB2006100463511A CN200610046351A CN100385031C CN 100385031 C CN100385031 C CN 100385031C CN B2006100463511 A CNB2006100463511 A CN B2006100463511A CN 200610046351 A CN200610046351 A CN 200610046351A CN 100385031 C CN100385031 C CN 100385031C
- Authority
- CN
- China
- Prior art keywords
- aluminum
- iron
- carbon
- percent
- ferroaluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种用直接还原铁生产微碳铝铁合金的制备方法，其特征在于：微碳铝铁合金是以直接还原铁和工业铝为原料，其制备方法是：(1)根据微碳铝铁合金的重量组成，将直接还原铁和工业铝按铝40-70%、铁30-60%的比率进行选料和配料；(2)在电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀；(3)根据铝铁比的不同，控制浇铸温度在1100-1250℃，并控制冷却过程。(4)得到的微碳铝铁合金的化学成分重量的百分比是：铝40-70%、铁30-60%，碳≤0.02%及少量杂质。本发明由于直接还原铁近乎无碳，可以制取含碳≤0.02%的微碳铝铁合金。工艺简单、使用范围广、不粉化，作为终脱氧剂，生产中可大大提高钢材质量。
Description
技术领域
本发明微碳铝铁合金是一种炼钢过程终脱氧使用的脱氧剂，涉及一种用直接还原铁生产微碳铝铁合金的制备方法。
背景技术
炼钢生产中生产具有高延展性、高冲压性的镇静钢，尤其是适用于生产冷轧钢板的低碳铝深冲钢时，使用金属铝作为终脱氧剂是目前钢铁企业保证和提高钢材质量的重要手段。伴随汽车工业的发展，对低碳铝深冲钢的需求量愈来愈多。为了降低炼钢生产成本，提高经济效益，减少脱氧过程中铝的消耗是重要环节。由于铝的比重小，与钢液的比重相差大，使铝在脱氧过程中的收得率很低且不稳定。开发高铝含量的含碳量低的铝铁合金代替金属铝是减少铝消耗、稳定操作的有效途径，但是铝铁合金脱氧剂置于大气下易粉化，以致无法使用，限制了其应用。
发明内容
本发明的目的是为炼钢生产提供了一种用直接还原铁生产微碳铝铁合金的制备方法，用该方法生产的微碳铝铁合金，完全可以取代金属铝作为炼钢脱氧剂。
本发明用直接还原铁生产微碳铝铁合金的制备方法内容简述：
本发明用直接还原铁生产微碳铝铁合金的制备方法，其特征在于：制备微碳铝铁合金是以直接还原铁和工业铝为原料，按下列工艺步骤完成的：
(1)根据微碳铝铁合金的化学成分组成，将直接还原铁和工业铝按重量比：铝40-70％、铁30-60％的比率进行选料和配料；
(2)在电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀；
(3)根据铝铁比的不同，控制浇铸温度在1100-1250℃，并控制冷却过程；
(4)得到的微碳铝铁合金的化学成分是：铝40-70％、铁30-60％，碳≤0.02％及少量杂质。
本发明是一种采用直接还原铁为原料制取微碳铝铁合金的新型复合脱氧剂的生产方法。由于直接还原铁近乎无碳，可以制取含碳极低(碳≤0.02％)的微碳铝铁合金，在炼钢过程中可以完全取代金属铝。具有：生产工艺简单、碳含量≤0.02％、使用范围广、不粉化的特点。经研究证明，铝铁的粉化机理是由于在铝铁合金的晶界，如含碳高容易富集AI4C3相发生水解，放出烃类气体产生应力导致合金破裂而使合金粉化。使用直接还原铁生产铝铁合金含碳量极低，可以避免合金粉化情况的发生。采用直接还原铁为原料制取的微碳铝铁合金作为终脱氧剂，在炼钢生产中可以大大提高钢材质量。
具体实施方式
本发明用直接还原铁生产微碳铝铁合金的制备方法是这样实现的，制备微碳铝铁合金是采用直接还原铁和工业铝为原料，根据微碳铝铁合金的化学成分组成，1、将直接还原铁和工业铝按：铝40％、直接还原铁60％进行配料。将原料放入电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀。控制浇铸温度在1100-1250℃，并控制冷却过程，得到的微碳铝铁合金。
2、将直接还原铁和工业铝按：铝50％、直接还原铁50％进行配料。将原料放入电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀。控制浇铸温度在1100-1250℃，并控制冷却过程，得到的微碳铝铁合金。
3、将直接还原铁和工业铝按：铝60％、直接还原铁40％进行配料。将原料放入电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀。控制浇铸温度在1100-1250℃，并控制冷却过程，得到的微碳铝铁合金。
4、将直接还原铁和工业铝按：铝70％、直接还原铁30％进行配料。将原料放入电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀。控制浇铸温度在1100-1250℃，并控制冷却过程，得到的微碳铝铁合金。将得到的微碳铝铁合金进行检测，其化学成分是：铝40-70％、铁30-60％，碳≤0.02％及少量杂质，完全符合国家标准要求。
Claims (1)
1.一种用直接还原铁生产微碳铝铁合金的制备方法，其特征在于：制备微碳铝铁合金是以直接还原铁和工业铝为原料，按下列工艺步骤完成的：
(1)根据微碳铝铁合金的成分组成，将直接还原铁和工业铝按重量：铝40-70％、铁30-60％的比率进行选料和配料；
(2)在电磁感应工频炉或中频炉内熔炼，利用电磁进行搅拌均匀；
(3)根据铝铁比的不同，控制浇铸温度在1100-1250℃，并控制冷却过程；
(4)得到的微碳铝铁合金的化学成分重量的百分比是：铝40-70％、铁30-60％，碳≤0.02％及少量杂质。