CN100384954C - 一种丙烯酸防水乳胶 - Google Patents
一种丙烯酸防水乳胶 Download PDFInfo
- Publication number
- CN100384954C CN100384954C CNB2004100233120A CN200410023312A CN100384954C CN 100384954 C CN100384954 C CN 100384954C CN B2004100233120 A CNB2004100233120 A CN B2004100233120A CN 200410023312 A CN200410023312 A CN 200410023312A CN 100384954 C CN100384954 C CN 100384954C
- Authority
- CN
- China
- Prior art keywords
- acrylic acid
- water
- proof
- resin
- latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种丙烯酸防水乳胶含有丙烯酸乳液、树脂涂层胶PBA、树脂2.D、醋酸乙脂、丙二醇、乙烯—醋酸乙烯共聚物，轻钙粉，其特征在于：各组成物的重量百分比含量分别为：丙烯酸乳液25-30%、树脂涂层胶PBA 15-20%、树脂2.D 12-18%、醋酸乙脂8-13%、丙二醇8-13%、乙烯—醋酸乙烯共聚物11-18%、轻钙粉4-5%。丙烯酸防水乳胶还可添加3%的异辛酸钙；在使用中根据施工要求加0-10%重量份的120#溶剂油。该丙烯酸防水乳胶既无毒又无害、具有良好的抗老化性能，尤其是能耐零下40度的低温，是一种适用地域十分广的新的丙烯酸防水乳胶。
Description
技术领域
本发明涉及一种丙烯酸防水乳胶，属防水涂料及生产方法类。
背景技术
以丙烯酸树脂为主要组成物的乳胶涂料是防水涂料中的一大系列，但目前市场普遍见到的丙烯酸树脂涂料，虽然组方比较简单，但由于在组方中一般都掺有二甲苯、甲苯、丙酮及甲醛等有害化合物。由于公知的环境保护原因，这种含有上述化合物的涂料，在使用期间会向自然空间释放出一些有害物。另外，以丙烯酸树脂为主的外墙涂料，虽然具有一定的防水、防腐、隔热、绝缘功能，但由于自然环境上的差异，尤其对我们这样一南北、东西幅远辽阔、温差和日照差别又十分巨大的国家来讲，目前市场上的丙烯酸树脂防水涂料，在使用的适用性上，尤其是在抗老化、抗冻裂、少污染方面仍然存在诸多不够理想的地方，很有必要进行创新改进。
技术内容
本发明的目的：旨在提供一种既无毒又无害的适用地域广的、且又具防水防腐、隔热抗冻、美化装饰等多种功能于一体的丙烯酸防水乳胶。
这种丙烯酸防水乳胶含有丙烯酸乳液、树脂涂层胶PBA、树脂2.D、醋酸乙脂、丙二醇、乙烯一醋酸乙烯共聚物，轻钙粉，其特征在于：各组成物的重量百分比含量分别为：丙烯酸乳液25-30％、树脂涂层胶PBA15-20％、树脂2.D 12-18％、醋酸乙脂8-13％、丙二醇8-13％、乙烯一醋酸乙烯共聚物11-18％、轻钙粉4-5％。
所述的丙烯酸防水乳胶，其组成物的最佳百分比含量分别是：丙烯酸乳液30％、树脂涂层胶PBA 18％、树脂2.D 12％、醋酸乙脂10％、丙二醇8％、乙烯一醋酸乙烯共聚物18％、轻钙粉4％。
所述的丙烯酸防水乳胶还可添加3％的异辛酸钙。
所述的丙烯酸防水乳胶，在使用中根据施工要求加0-10％重量份的120#溶剂油。
根据以上配方制作的丙烯酸防水乳胶，除具有一般丙烯酸防水乳胶的使用特性以外，由于其组成物中不含任何油性物，走出了传统丙烯酸防水涂料的界域系列，因此能保证本产品在生产、运输和施工中均不会含有或产生有毒、有害物质，是完全意义上的绿色防水涂料。由于组成物特殊的化学理化性能，在产品的粘结力、柔软性、成膜性，以及耐压性、耐磨性等方面都有明显的优点；并可加工成各种，便于美化和装修工程施工；尤其适合抗冻性要求较高的我国北方和西北寒冷地区建筑物的防水、防渗施工使用。
具体实施方式
以下给出本发明的组分实施例，并结合实施例进一步阐述本发明。
丙烯酸防水乳胶配剂(以重量百分比计)
| 名称 | 实施例1 | 实施例2 | 实施例3 |
| 组成物 | ％ | ％ | ％ |
| 丙烯酸乳液 | 25 | 27.5 | 30 |
| 树脂涂层胶PBA | 20 | 17.5 | 15 |
| 树脂2.D | 12 | 15 | 18 |
| 醋酸乙脂 | 8 | 10.5 | 13 |
| 丙二醇 | 13 | 10.5 | 8 |
| 乙烯一醋酸乙烯共聚物 | 18 | 14.5 | 11 |
| 轻钙粉(或力德粉) | 4 | 4.5 | 5 |
根据上述技术方案提供的这种丙烯酸防水乳胶，主要用于工民建筑物的外墙、屋面防水施工，下水道、隧道以及工业和国防施工中的类似工程的防水防渗。在实际运用中，可以根据施工场地的各种环境要求，如使用环境的温度、建筑物的类型，以及防水层所要求的涂刷厚度等对配方进行适度的调整。如需使乳胶组成各种颜色时，只要将配方中所用的轻钙粉用力德粉来替代；而后掺入选用的颜料即可。此外，由于各种不同场地、不同气温条件下，对施工时的防水乳胶的粘稠度要求也不一样，因此，本发明所述的丙烯酸防水乳胶在施工中遇有渗漏的施工面时，可以掺入3％的异辛酸钙。同时，如乳胶过浓影响涂刷时，也可以加入不超过10％重量份的120#溶剂油，稀释该乳胶以后再使用；以便获得较薄的涂膜效果。
此外，这种丙烯酸防水乳胶，之所以具有良好的粘结力，主要是加入了；树脂涂层胶PBA和树脂2.D，这两种树脂胶在配方中起着决定性作用；其中的醋酸乙脂是上述两种树脂胶理想的稀释剂；配方中的丙二醇既具有吸湿作用，同时又对防水胶的抗冻性起着十分关键作用。经本发明人实际使用表明，该防水乳胶在-40℃时仍具有十分理想的使用性能。
Claims (4)
1.一种丙烯酸防水乳胶含有丙烯酸乳液、树脂涂层胶PBA、树脂2.D、醋酸乙脂、丙二醇、乙烯一醋酸乙烯共聚物，轻钙粉，其特征在于：各组成物的重量百分比含量分别为：丙烯酸乳液 25-30％、树脂涂层胶PBA15-20％、树脂2.D 12-18％、醋酸乙脂8-13％、丙二醇8-13％、乙烯一醋酸乙烯共聚物11-18％、轻钙粉4-5％。
2.如权利要求1所述的一种丙烯酸防水乳胶，其特征在于：所述的丙烯酸防水乳胶，其组成物的百分比含量分别是：丙烯酸乳液30％、树脂涂层胶PBA 18％、树脂2.D 12％、醋酸乙脂10％、丙二醇8％、乙烯一醋酸乙烯共聚物18％、轻钙粉4％。
3.如权利要求1所述的一种丙烯酸防水乳胶，其特征在于：所述的丙烯酸防水乳胶还可添加3％的异辛酸钙。
4.如权利要求1所述的一种丙烯酸防水乳胶，其特征在于：所述的丙烯酸防水乳胶，在使用中根据施工要求加0-10％重量份的120#溶剂油。