CN100343194C - 一种可有效防有害电磁辐射的陶瓷粉及其制备方法 - Google Patents
一种可有效防有害电磁辐射的陶瓷粉及其制备方法 Download PDFInfo
- Publication number
- CN100343194C CN100343194C CNB2006100659194A CN200610065919A CN100343194C CN 100343194 C CN100343194 C CN 100343194C CN B2006100659194 A CNB2006100659194 A CN B2006100659194A CN 200610065919 A CN200610065919 A CN 200610065919A CN 100343194 C CN100343194 C CN 100343194C
- Authority
- CN
- China
- Prior art keywords
- ceramic powder
- powder
- far
- electromagnetic wave
- electromagnetic radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种将有害于人体的电磁辐射吸收并转换成对人体有益的远红外波的特种陶瓷粉及其制备方法。该陶瓷粉由粘土、千枚岩、电气石、钾长石、钠长石、钒钛矿石、氧化铜、粘合剂DK2001组成,经粉碎、过筛、混合、搅拌、造粒、烘干、烧结、粉碎成粉制得,也可调和成涂料。利用该陶瓷粉可将各种电器元件及设备工作状态下所产生的有害电磁辐射吸收转化成2-18μm的有益电磁辐射,以达到对人体保健的作用。
Description
技术领域
本发明涉及陶瓷粉及其制备方法,具体地说,是一种可有效防有害电磁辐射的陶瓷粉及其制备方法。
技术背景
目前,人们在充分享受电磁辐射带来的方便舒适的同时,也日渐感受到了它的负面效应。如电磁辐射曾造成导航系统、信息传输系统的失控。特别是近些年来,国内外媒体上屡屡报道的有关电磁辐射对人体有害,更是让人们感觉到了来自电磁辐射污染的威胁。
电磁污染是指天然的人为的各种电磁波的干扰及有害的电磁辐射。由于广播、电视、微波技术的发展,射频设备功率成倍增加,地面上的电磁辐射大幅度增加,目前已达到直接威胁人体健康的程度。
人为电磁污染源包括:脉冲放电,如火花放电;工频交变电磁场,如大功率电机、变压器、输电线附近等;射频电磁辐射,如广播、电视、微波通讯等。
我们日常生活中碰到的广播、电视效果突然变差,几乎都是电磁干扰造成的。此外,电磁污染还对人体健康造成伤害。
因此,目前迫切需要一种可有效防有害电磁辐射的材料及其制备方法。
发明内容
本发明克服了上述缺点,提出了一种可有效防有害电磁辐射的材料及其制备方法。
为了实现上述的发明目的,本发明的技术方案是:
一种用于有害电磁波转换的远红外陶瓷粉体,由下列重量百分比的原料,经粉碎、过筛、混合、搅拌、造粒、烘干、烧结、粉碎成粉制得:
粘土 10-15 千枚岩 10-25 电气石 40-60
钾长石 5-10 钠长石 5-10 钒钛矿石 5-10
氧化铜 5-10 粘合剂DK2001 10
所述的粘合剂DK2001由下述的重量百分比的原料组成:
酒精 10-30 硬脂酸丁酯 5-10 聚乙烯醇 30-50
乙基苯基乙二醇 5-10 甘油 5-10
所述的粘土含水量为25wt%。
所述的氧化铜为工业级。
该粉体为500-2000目。
用于有害电磁波转换的远红外陶瓷粉体的制备方法,包含以下步骤:
A.将原料中的粘土、千枚岩、电气石、钾长石、钠长石、钒钛矿石、氧化铜粉碎,过350目筛;
B.将步骤A中得到的粉料投入制丸机内,以粘合剂DK2001均匀喷洒后,制成3-8毫米的球体;
C.将步骤B中得到的球体干燥,使之含水量小于5%;
D.将步骤C中得到的球体投入烧结炉烧结成瓷,烧结温度大于等于1100℃,并粉碎成500-2000目的粉体。
所述的步骤D中,优选地,烧结温度为1200-1350℃。
远红外陶瓷粉体可以用于有害电磁波转换的原理是:含有氢键的双原子和多原子分子在2-1gμm的电磁辐射范围内有一个普遍吸收带,只是每一种物质按其结构不同在这个吸收带上有它自己的最高吸收峰和两个较高吸收峰。只要根据不同的受体,调整特种功能性陶瓷的发射峰即可最大限度的作用于受体,达到所作用的目的。
本发明的优点是:利用该陶瓷粉可将各种电器元件及设备工作状态下所产生的有害电磁辐射吸收转化成2-18μm的有益电磁辐射,以达到对人体保健的作用。
具体实施方式
以下给出具体的实施例来进一步说明。这些实施例的用意只是说明性的,而不应理解为对本发明的限制。
实施例1:粘合剂DK2001的制备
取酒精20kg,硬脂酸丁酯8kg,聚乙烯醇40kg,乙基苯基乙二醇8kg,甘油8kg。置于反应器中搅拌均匀即可。制备完毕后密封,存放于阴凉避光处。
实施例2
A.将原料中的25wt%粘土15kg、千枚岩10kg、电气石60kg、钾长石5kg、钠长石10kg、钒钛矿石5kg、工业级氧化铜10kg粉碎,过350目筛;
B.将步骤A中得到的粉料投入制丸机内,以10公斤粘合剂DK2001均匀喷洒后,制成8毫米的球体;
C.将步骤B中得到的球体干燥,使之含水量小于5%;
D.将步骤C中得到的球体投入烧结炉烧结成瓷,烧结温度为1350℃,并粉碎成2000目的粉体。
实施例3
A.将原料中的粘土10kg、千枚岩25kg、电气石40kg、钾长石10kg、钠长石5kg、钒钛矿石10kg、氧化铜5kg粉碎,过350目筛;
B.将步骤A中得到的粉料投入制丸机内,以粘合剂10公斤DK2001均匀喷洒后,制成3毫米的球体;
C.将步骤B中得到的球体干燥,使之含水量小于5%;
D.将步骤C中得到的球体投入烧结炉烧结成瓷,烧结温度为1200℃,并粉碎成500目的粉体。
实施例4
A.将原料中的粘土12kg、千枚岩20kg、电气石50kg、钾长石8kg、钠长石8kg、钒钛矿石8kg、氧化铜8kg粉碎,过350目筛;
B.将步骤A中得到的粉料投入制丸机内,以粘合剂10公斤DK2001均匀喷洒后,制成5毫米的球体;
C.将步骤B中得到的球体干燥,使之含水量小于5%;
D.将步骤C中得到的球体投入烧结炉烧结成瓷,烧结温度为1100℃,并粉碎成1000目的粉体。
以上对本发明所提供的用于有害电磁波转换的远红外陶瓷粉体进行了详细介绍,本文中应用了具体个例对本发明的原理及实施方式进行了阐述,以上实施例的说明只是用于帮助理解本发明的方法及其核心思想;同时,对于本领域的一般技术人员,依据本发明的思想,在具体实施方式及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制。
Claims (6)
1.一种用于有害电磁波转换的远红外陶瓷粉体,其特征在于,由下列重量百分比的原料,经粉碎、过筛、混合、搅拌、造粒、烘干、烧结、粉碎成粉制得:
粘土 10-15 千枚岩 10-25 电气石 40-60
钾长石 5-10 钠长石 5-10 钒钛矿石 5-10
氧化铜 5-10 粘合剂DK2001 10;
所述的粘合剂DK2001由下述的重量百分比的原料组成:
酒精 10-30 硬脂酸丁酯 5-10 聚乙烯醇 30-50
乙基苯基乙二醇 5-10 甘油 5-10。
2.根据权利要求1所述的用于有害电磁波转换的远红外陶瓷粉体,其特征在于:所述的粘土含水量为25wt%。
3.根据权利要求1所述的用于有害电磁波转换的远红外陶瓷粉体,其特征在于:所述的氧化铜为工业级。
4.根据权利要求1所述的用于有害电磁波转换的远红外陶瓷粉体,其特征在于:该粉体为500-2000目。
5.权利要求1所述的用于有害电磁波转换的远红外陶瓷粉体的制备方法,其特征在于,包含以下步骤:
A.将原料中的粘土、千枚岩、电气石、钾长石、钠长石、钒钛矿石、氧化铜粉碎,过350目筛;
B.将步骤A中得到的粉料投入制丸机内,以粘合剂DK2001均匀喷洒后,制成3-8毫米的球体;
C.将步骤B中得到的球体干燥,使之含水量小于5%;
D.将步骤C中得到的球体投入烧结炉烧结成瓷,烧结温度大于等于1100℃,并粉碎成500-2000目的粉体。
6.权利要求1所述的用于有害电磁波转换的远红外陶瓷粉体的制备方法,其特征在于:烧结温度为1200-1350℃。