CN100339535C - 一种降低硅橡胶涂层织物表面能的方法 - Google Patents

一种降低硅橡胶涂层织物表面能的方法 Download PDF

Info

Publication number
CN100339535C
CN100339535C CNB2005101013620A CN200510101362A CN100339535C CN 100339535 C CN100339535 C CN 100339535C CN B2005101013620 A CNB2005101013620 A CN B2005101013620A CN 200510101362 A CN200510101362 A CN 200510101362A CN 100339535 C CN100339535 C CN 100339535C
Authority
CN
China
Prior art keywords
silicon rubber
surface energy
fabric coated
fabric
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005101013620A
Other languages
English (en)
Other versions
CN1793486A (zh
Inventor
狄剑锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Xinfeng Technology Co ltd
Original Assignee
Wuyi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuyi University filed Critical Wuyi University
Priority to CNB2005101013620A priority Critical patent/CN100339535C/zh
Publication of CN1793486A publication Critical patent/CN1793486A/zh
Application granted granted Critical
Publication of CN100339535C publication Critical patent/CN100339535C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种降低硅橡胶涂层织物表面能的方法，其方法步骤如下：(1)配制浓度为100%的丙酮溶液或乙醇溶液或正庚烷溶液；(2)将硅橡胶涂层织物浸入步骤(1)所述的溶液内，并在10℃～30℃的温度下浸泡30～50分钟；(3)将经步骤(2)的硅橡胶涂层织物取出晾干，以目测织物表面没有水珠为准；本工艺方法使得硅橡胶涂层织物的表面能由30～40mJ/m2降低到15mJ/m2以下，而且稳定，不随时间变化而变化，使硅橡胶表面的拒水能力显著增强。对于建筑蓬用涂层织物来说，增强拒水能力，就可以有效防止表面漏水和积尘，保持表面的清洁，减少清洗的次数，延长使用寿命。

Description

一种降低硅橡胶涂层织物表面能的方法
技术领域
本发明涉及一种降低织物表面能的方法，特别是一种降低硅橡胶涂层织物表面能的方法。
背景技术
近年来，以纺织品为顶篷材料的大型建筑物越来越多，作为建筑篷用织物，要有很高的力学性能及良好的表面性能，要求拒水、拒油、抗污、防污、易于清洁等，这就必须具有较低的表面能，由于硅橡胶(聚二甲基硅氧烷)具有良好的物理力学性能，是一种很好的拒水材料，水在其表面上的接触角大于100°，其理论表面能为21mJ/m2。因此，硅橡胶涂层织物作为建筑篷用织物得到广泛应用。
但是硅橡胶涂层织物的表面能很不稳定，溶液在其表面的接触角随时间变长而快速下降；目前人们通常使用接触角来计算表面能，当一滴溶液的体积小于6μL时，就可忽略地球引力对其形状的影响，认为液滴呈标准圆的一部分，只要测量溶液在固体表面上的高度h以及和固体接触面的直径D，就可以使用公式θ＝2h/D计算接触角；人们使用甘油(丙三醇)和二碘甲烷进行测试，采用动态的测量方测量其在硅橡胶涂层的织物上的接触角，方法如下：用数码相机以60张/S的速率将液滴在硅橡胶涂层的织物上的变化情况拍摄下来，并输入计算机，由计算机计算其接触角，并计算表面能，从测试结果发现，甘油(丙三醇)的接触角在两分钟内降低20°～30°；而二碘甲烷减低30°～35°，表明硅橡胶涂层织物的表面能将上升到30～40mJ/m2。再用水和其它溶液进行测量，规律一致，从而表明这是硅橡胶涂层织物表面的普遍现象。这种现象使硅橡胶的实际表面能远远高于其理论值(21mJ/m2)，使其拒水的能力明显降低。
发明内容
为了克服现有技术的不足，本发明提供一种降低并稳定硅橡胶涂层织物的表面能，提高其拒水能力的方法。
本发明解决上述技术问题所采用的技术方案是：
(1)配制浓度为100％的丙酮溶液或乙醇溶液或正庚烷溶液；
(2)将硅橡胶涂层织物浸入步骤(1)所述的溶液内，并在10℃～30℃的温度下浸泡30～50分钟；
(3)将经步骤(2)的硅橡胶涂层织物取出晾干，以目测织物表面没有水珠为准。
本发明的有益效果是：本工艺方法使得硅橡胶涂层织物的表面能由30～40mJ/m2降低到15mJ/m2以下，而且稳定，不随时间变化而变化，使硅橡胶表面的拒水能力显著增强。对于建筑蓬用涂层织物来说，增强拒水能力，就可以有效防止表面漏水和积尘，保持表面的清洁，减少清洗的次数，延长使用寿命。
具体实施方式
一种降低硅橡胶涂层织物表面能的方法，其方法步骤如下：
(1)配制浓度为100％的丙酮溶液(表面能为23.7mJ/m2)
(2)将硅橡胶涂层织物浸入步骤(1)所述的溶液内，并在10℃～30℃的温度下浸泡40～50分钟；
实际操作时，由于温度越低，织物需要浸泡的时间就要越长，但是低表面能的溶液容易燃烧，所以应该尽量在低温下进行处理，最好是控制在20℃的温度下浸泡45分钟；
(3)将经步骤(2)的硅橡胶涂层织物取出晾干，由于低表面能溶液易于挥发，所以只要将其在空气中风干即可，其风干程度以目测织物表面没有水珠为准。
本工艺方法还可以使用乙醇溶液(表面能为23.7mJ/m2)，操作的时候，在10℃～30℃的温度下浸泡35～45分钟；最好是控制在20℃的温度下浸泡40分钟；或者，使用正庚烷溶液(表面能为19.8mJ/m2)，操作时，在10℃～30℃的温度下浸泡30～40分钟；最好控制在20℃的温度下浸泡35分钟；另外，由于低表面能溶液易于挥发，所以尽量在封闭的盒体中进行浸泡处理。
本工艺方法使得硅橡胶涂层织物的表面能由30～40mJ/m2降低到15mJ/m2以下，而且稳定，不随时间变化而变化，使硅橡胶表面的拒水能力显著增强。对于建筑蓬用涂层织物来说，增强拒水能力，就可以有效防止表面漏水和积尘，保持表面的清洁，减少清洗的次数，延长使用寿命，从而可以广泛应用于纺织行业中篷用硅橡胶涂层织物制备上。

Claims (6)

1.一种降低硅橡胶涂层织物表面能的方法，其方法步骤如下：
(1)配制浓度为100％的丙酮溶液；
(2)将硅橡胶涂层织物浸入步骤(1)所述的溶液内，并在10℃～30℃的温度下浸泡30～50分钟；
(3)将经步骤(2)的硅橡胶涂层织物取出晾干，以目测织物表面没有水珠为准。
2.根据权利要求1所述的一种降低硅橡胶涂层织物表面能的方法，其特征在于：步骤(2)所述的浸泡温度为20℃，浸泡时间为45分钟。
3.一种降低硅橡胶涂层织物表面能的方法，其方法步骤如下：
(1)配制浓度为100％的乙醇溶液；
(2)将硅橡胶涂层织物浸入步骤(1)所述的溶液内，并在10℃～30℃的温度下浸泡30～50分钟；
(3)将经步骤(2)的硅橡胶涂层织物取出晾干，以目测织物表面没有水珠为准。
4.根据权利要求3所述的一种降低硅橡胶涂层织物表面能的方法，其特征在于：步骤(2)所述的浸泡温度为20℃，浸泡时间为40分钟。
5.一种降低硅橡胶涂层织物表面能的方法，其方法步骤如下：
(1)配制浓度为100％的正庚烷溶液；
(2)将硅橡胶涂层织物浸入步骤(1)所述的溶液内，并在10℃～30℃的温度下浸泡30～50分钟；
(3)将经步骤(2)的硅橡胶涂层织物取出晾干，以目测织物表面没有水珠为准。
6.根据权利要求5所述的一种降低硅橡胶涂层织物表面能的方法，其特征在于：步骤(2)所述的浸泡温度为20℃，浸泡时间为35分钟。
CNB2005101013620A 2005-11-11 2005-11-11 一种降低硅橡胶涂层织物表面能的方法 Expired - Fee Related CN100339535C (zh)