CH714879B1 - Copper-based alloy for goldsmiths, jewellery, watches and products made from this alloy. - Google Patents
Copper-based alloy for goldsmiths, jewellery, watches and products made from this alloy. Download PDFInfo
- Publication number
- CH714879B1 CH714879B1 CH00463/18A CH4632018A CH714879B1 CH 714879 B1 CH714879 B1 CH 714879B1 CH 00463/18 A CH00463/18 A CH 00463/18A CH 4632018 A CH4632018 A CH 4632018A CH 714879 B1 CH714879 B1 CH 714879B1
- Authority
- CH
- Switzerland
- Prior art keywords
- weight
- total amount
- alloy
- copper
- gold
- Prior art date
Abstract
L'invention concerne un alliage pour un produit d'orfèvrerie, de bijouterie, d'horlogerie ou de produits similaires consistant en un mélange de cuivre d'un montant total de 50 à 90% en poids, de l'argent dans une quantité totale de 0,1 à 25% en poids, de l'or dans une quantité totale de 0,1 à 40% en poids et éventuellement un ou plusieurs autres composants choisis parmi le palladium, le zinc, le platine, l'iridium, le nickel, le fer et le silicium dans une quantité totale de 0,1 à 20% en poids.The invention relates to an alloy for a product of goldsmithery, jewellery, watchmaking or similar products consisting of a mixture of copper in a total amount of 50 to 90% by weight, silver in a total amount from 0.1 to 25% by weight, gold in a total amount of 0.1 to 40% by weight and optionally one or more other components chosen from palladium, zinc, platinum, iridium, nickel, iron and silicon in a total amount of 0.1 to 20% by weight.
Description
[0001] La présente invention se rapporte à un alliage pour un produit de l'orfèvrerie, la bijouterie, l'horlogerie ou un produit similaire consistant en un mélange de cuivre, d'argent et d'or voire d'autres composants. The present invention relates to an alloy for a goldsmith product, jewelry, watchmaking or a similar product consisting of a mixture of copper, silver and gold or even other components.
[0002] Des alliages comportant du cuivre en faible proportion sont régulièrement utilisés pour influencer sur la résistance et la couleur dudit alliage. [0002] Alloys comprising a small proportion of copper are regularly used to influence the strength and color of said alloy.
[0003] Par exemple, pour obtenir une couleur d'alliage jaune il convient de mélanger 75% d'or pur, 12,5% de cuivre et 12,5% d'argent. C'est ce qui explique que l'on peut voir sur le marché des bijoux en or jaune plus ou moins clairs. [0003] For example, to obtain a yellow alloy color, 75% pure gold, 12.5% copper and 12.5% silver should be mixed. This explains why we can see more or less clear yellow gold jewelery on the market.
[0004] Pour obtenir un alliage rosé, il convient de mélanger 75% d'or pur, 19% de cuivre rosette et 6% d'argent fin alors que pour une couleur d'alliage rouge il convient de mélanger 75% d'or pur, 25% de cuivre rosette. To obtain a pink alloy, it is necessary to mix 75% pure gold, 19% rosette copper and 6% fine silver, while for a red alloy color it is necessary to mix 75% gold. pure, 25% copper rosette.
[0005] L'or 9 carats comporte une teneur en or de cet alliage est de à 37,5% d'or fin. Par exemple pour de l'or jaune 9 carats il convient de mélanger 37,5% d'or fin, 12,1% d'argent, 44,4% de cuivre et 6% de zinc. Pour obtenir de l'or rouge 9 carats il convient de mélanger 37,5% d'or fin, 55% de cuivre et 7,5% d'argent alors que pour obtenir de l'or rose 9 carats il convient de mélanger 37,5% d'or fin, 42,5% de cuivre et 20% d'argent. 9 carat gold has a gold content of this alloy is 37.5% fine gold. For example, for 9 carat yellow gold, 37.5% fine gold, 12.1% silver, 44.4% copper and 6% zinc should be mixed. To obtain 9 carat red gold it is necessary to mix 37.5% fine gold, 55% copper and 7.5% silver while to obtain 9 carat pink gold it is necessary to mix 37 .5% fine gold, 42.5% copper and 20% silver.
[0006] En ce qui concerne l'or 9 carats, cet alliage, pauvre en or fin, peut devenir terne assez rapidement selon le procédé de fabrication choisi. Il peut être cassant et difficilement réparable par soudure lorsque l'alliage est peu qualitatif. [0006] With regard to 9 carat gold, this alloy, poor in fine gold, can become dull quite quickly depending on the manufacturing process chosen. It can be brittle and difficult to repair by welding when the alloy is of poor quality.
[0007] WO2012017299 décrit un alliage pour articles en or, bijoux ou produits similaires, composé d'or dans une quantité totale allant de 4 à 4,5 % en poids, d'argent dans une quantité totale allant de 35 à 68 % en poids, de palladium dans une quantité totale allant de 8 à 30 % en poids, d'au moins un élément choisi parmi l'iridium, le cuivre, le zinc, le nickel, et le silicium dans une quantité totale allant de 18 à 32 % en poids ou d'indium dans une quantité totale allant de 25 à 32 % en poids, et éventuellement au moins un autre constituant dans une quantité totale allant jusqu'à 3 % en poids. [0007] WO2012017299 describes an alloy for gold articles, jewelry or similar products, composed of gold in a total amount ranging from 4 to 4.5% by weight, silver in a total amount ranging from 35 to 68% by weight, of palladium in a total amount ranging from 8 to 30% by weight, of at least one element chosen from iridium, copper, zinc, nickel, and silicon in a total amount ranging from 18 to 32 % by weight or indium in a total amount ranging from 25 to 32% by weight, and optionally at least one other constituent in a total amount ranging up to 3% by weight.
[0008] Le but de la présente invention est de proposer un alliage qualitatif et résistant pour un produit d'orfèvrerie, de bijouterie, d'horlogerie ou un produit similaire, l'alliage présentant un compromis intéressant entre une couleur et un éclat d'un rouge cuivre répondant aux exigences esthétiques des produits précédemment cités, résistant à l'oxydation lors d'opérations de traitement thermiques, brasage, soudage, fusion et gravage laser et dont la déformabilité permet sa transformation sans risque de fissuration et qui soit économique à réaliser. The object of the present invention is to provide a qualitative and resistant alloy for a product of goldsmithery, jewelry, watchmaking or a similar product, the alloy having an interesting compromise between a color and a shine of a copper red that meets the aesthetic requirements of the products mentioned above, resistant to oxidation during heat treatment, brazing, welding, melting and laser engraving operations and whose deformability allows its transformation without risk of cracking and which is economical to produce .
[0009] Un autre but de la présente invention est de fournir un produit d'orfèvrerie, de bijouterie, d'horlogerie ou produit similaire d'un alliage riche en cuivre susceptible de procurer des bienfaits pour la santé lorsque le produit est porté par un utilisateur. Another object of the present invention is to provide a goldsmith's, jeweller's, watchmaker's or similar product of a copper-rich alloy capable of providing health benefits when the product is worn by a user.
[0010] La présente invention fournit un alliage pour l'orfèvrerie, la bijouterie, l'horlogerie ou un produit similaire consistant en un mélange de : Cuivre dans une quantité totale de 50 à 90% en poids, typiquement 75 à 85% ; Argent dans une quantité totale de 0,1 à 20% en poids, typiquement 5 à 15% ; Or dans une quantité totale de 0,1 à 40% en poids, et typiquement 5 à 15% ; éventuellement un ou plusieurs autres composants, choisis parmi le palladium, le zinc, le platine, l'iridium, le nickel, le fer et le silicium dans une quantité totale allant jusqu'à 20 % en poids, typiquement 5 à 15%.The present invention provides an alloy for goldsmithing, jewelry, watchmaking or a similar product consisting of a mixture of: Copper in a total amount of 50 to 90% by weight, typically 75 to 85%; Silver in a total amount of 0.1 to 20% by weight, typically 5 to 15%; Gold in a total amount of 0.1 to 40% by weight, and typically 5 to 15%; optionally one or more other components, chosen from palladium, zinc, platinum, iridium, nickel, iron and silicon in a total amount ranging up to 20% by weight, typically 5 to 15%.
[0011] Ces résultats sont prouvés par plusieurs études scientifiques dont l'une des plus célèbres a été conduite en Australie par les Docteurs Struthers et Scott. Leurs résultats ont clairement mis en évidence une diminution des douleurs arthritiques chez les patients les ayant portés. [0011] These results are proven by several scientific studies, one of the most famous of which was conducted in Australia by Doctors Struthers and Scott. Their results clearly demonstrated a reduction in arthritis pain in patients who wore them.
[0012] Dans un mode de réalisation de l'alliage de l'invention, le cuivre est dans une quantité totale de 50 à 60% en poids, l'argent est en quantité totale de 10 à 25% en poids et l'or en quantité totale de 10 à 25% en poids. In one embodiment of the alloy of the invention, the copper is in a total amount of 50 to 60% by weight, the silver is in a total amount of 10 to 25% by weight and the gold in total amount from 10 to 25% by weight.
[0013] Dans un autre mode de réalisation de l'alliage de l'invention, le cuivre est dans une quantité totale de 60 à 70% en poids, l'argent est en quantité totale de 10 à 20% en poids et l'or en quantité totale de 10 à 20% en poids. In another embodiment of the alloy of the invention, the copper is in a total amount of 60 to 70% by weight, the silver is in a total amount of 10 to 20% by weight and the gold in a total amount of 10 to 20% by weight.
[0014] Dans encore un autre mode de réalisation, le cuivre est dans une quantité totale de 70 à 80% en poids, l'argent est en quantité totale de 10 à 20% en poids et l'or en quantité totale de 10 à 20% en poids. In yet another embodiment, the copper is in a total amount of 70 to 80% by weight, the silver is in a total amount of 10 to 20% by weight and the gold in a total amount of 10 to 20% by weight.
[0015] Pour une coloration rouge prononcée de l'alliage, dans un autre mode de réalisation, le cuivre est dans une quantité totale de 80 à 90% en poids, l'argent est en quantité totale de 5 à 15% en poids et l'or en quantité totale de 5 à 15% en poids. [0015] For a pronounced red coloration of the alloy, in another embodiment, the copper is in a total amount of 80 to 90% by weight, the silver is in a total amount of 5 to 15% by weight and gold in total amount from 5 to 15% by weight.
[0016] L'alliage selon l'une des réalisations précédentes comprend en outre du palladium dans une quantité totale de 0,1 à 5% en poids, notamment comme seul élément optionnel. The alloy according to one of the preceding embodiments further comprises palladium in a total amount of 0.1 to 5% by weight, in particular as the only optional element.
[0017] Un alliage selon la présente invention, peut être utilisé dans la fabrication d'un article de bijouterie ou d'une pièce d'horlogerie voire même de composants horlogers, notamment destinés à être portés à fleur de la peau pour procurer des bienfaits de santé grâce à la forte concentration en cuivre. [0017] An alloy according to the present invention can be used in the manufacture of an article of jewelery or of a timepiece or even of watchmaking components, in particular intended to be worn flush with the skin to provide benefits health thanks to the high concentration of copper.
[0018] Une description détaillée d'un mode de réalisation de l'alliage de la présente invention va maintenant être donnée en référence à l'unique figure donnée uniquement à titre d'exemple et non limitatif. A detailed description of an embodiment of the alloy of the present invention will now be given with reference to the single figure given solely by way of example and not limiting.
[0019] Comme illustré, une montre-bracelet comporte une boite de montre 1 comportant un alliage selon l'invention composé par exemple de cuivre d'un montant total de 85% en poids, d'argent dans une quantité totale de 7.5% en poids et d'or dans une quantité totale de 7.5% en poids également. As illustrated, a wristwatch comprises a watch case 1 comprising an alloy according to the invention composed for example of copper in a total amount of 85% by weight, silver in a total amount of 7.5% in weight and gold in a total amount of 7.5% by weight also.
[0020] Cet alliage a une couleur rouge cuivre, En plus de présenter un intérêt esthétique, cet alliage présente toutes les caractéristiques essentielles pour répondre aux exigences normatives horlogères. En effet, le présent alliage répond aux normes actuellement en vigueur, dans l'industrie horlogère suisse, et notamment concernant des domaines aussi variés que la terminologie, la construction horlogère, les tests et exigences en matière d'antimagnétisme et la résistance à l'étanchéité et aux chocs. [0020] This alloy has a copper red color. In addition to presenting an aesthetic interest, this alloy has all the essential characteristics to meet the watchmaking normative requirements. Indeed, the present alloy meets the standards currently in force in the Swiss watch industry, and in particular concerning fields as varied as terminology, watch construction, tests and requirements in terms of antimagnetism and resistance to tightness and shocks.
[0021] Dans le présent exemple, non seulement la boite de montre 1 comporte une carrure composée de l'alliage selon la présente invention comportant par exemple du cuivre dans un montant total de 85% en poids, d'argent dans une quantité totale de 7.5% en poids et d'or dans une quantité totale de 7.5% en poids mais encore les aiguilles des heures 2 et des minutes 2' comportent le même alliage. [0021] In the present example, not only does the watch case 1 comprise a middle part composed of the alloy according to the present invention comprising, for example, copper in a total amount of 85% by weight, silver in a total amount of 7.5% by weight and gold in a total amount of 7.5% by weight but also the hour 2 and minute 2' hands comprise the same alloy.
[0022] De la même manière, la couronne de remontoir 3 et le cadran de montre 4 sont également réalisés dans l'alliage selon la présente invention. [0022] In the same way, the winding crown 3 and the watch dial 4 are also made of the alloy according to the present invention.
[0023] Dans une variante, tous les composants horlogers sont également dans cet alliage à forte concentration en cuivre ou n'importe quel alliage selon la présente invention. [0023] In a variant, all the watch components are also in this alloy with a high copper concentration or any alloy according to the present invention.
[0024] Lorsque la montre illustrée est portée pendant une période prolongée, la forte concentration de cuivre de ces composants est susceptible de procurer des bienfaits de la santé. [0024] When the illustrated watch is worn for an extended period, the high concentration of copper in these components is likely to provide health benefits.
Claims (10)