CA1058879A - Subsurface-fortified glass laminates - Google Patents
Subsurface-fortified glass laminatesInfo
- Publication number
- CA1058879A CA1058879A CA224,910A CA224910A CA1058879A CA 1058879 A CA1058879 A CA 1058879A CA 224910 A CA224910 A CA 224910A CA 1058879 A CA1058879 A CA 1058879A
- Authority
- CA
- Canada
- Prior art keywords
- subsurface
- layers
- stressed
- glass
- fortifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Links
- 239000005340 laminated glass Substances 0.000 title claims abstract description 33
- 239000011521 glass Substances 0.000 claims abstract description 82
- 239000010410 layer Substances 0.000 claims description 106
- 239000000203 mixture Substances 0.000 claims description 25
- KKCBUQHMOMHUOY-UHFFFAOYSA-N Na2O Inorganic materials [O-2].[Na+].[Na+] KKCBUQHMOMHUOY-UHFFFAOYSA-N 0.000 claims description 20
- 239000002344 surface layer Substances 0.000 claims description 20
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 16
- 239000012792 core layer Substances 0.000 claims description 14
- 239000000404 calcium aluminium silicate Substances 0.000 claims description 12
- 235000012215 calcium aluminium silicate Nutrition 0.000 claims description 12
- WNCYAPRTYDMSFP-UHFFFAOYSA-N calcium aluminosilicate Chemical compound [Al+3].[Al+3].[Ca+2].[O-][Si]([O-])=O.[O-][Si]([O-])=O.[O-][Si]([O-])=O.[O-][Si]([O-])=O WNCYAPRTYDMSFP-UHFFFAOYSA-N 0.000 claims description 12
- 229940078583 calcium aluminosilicate Drugs 0.000 claims description 12
- 229910001491 alkali aluminosilicate Inorganic materials 0.000 claims description 11
- CHWRSCGUEQEHOH-UHFFFAOYSA-N potassium oxide Chemical compound [O-2].[K+].[K+] CHWRSCGUEQEHOH-UHFFFAOYSA-N 0.000 claims description 11
- MCMNRKCIXSYSNV-UHFFFAOYSA-N Zirconium dioxide Chemical compound O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 claims description 8
- 229910052681 coesite Inorganic materials 0.000 claims description 8
- 229910052906 cristobalite Inorganic materials 0.000 claims description 8
- 239000000377 silicon dioxide Substances 0.000 claims description 8
- 235000012239 silicon dioxide Nutrition 0.000 claims description 8
- 229910052682 stishovite Inorganic materials 0.000 claims description 8
- 229910052905 tridymite Inorganic materials 0.000 claims description 8
- 229910000272 alkali metal oxide Inorganic materials 0.000 claims description 7
- NOTVAPJNGZMVSD-UHFFFAOYSA-N potassium monoxide Inorganic materials [K]O[K] NOTVAPJNGZMVSD-UHFFFAOYSA-N 0.000 claims description 7
- 229910001948 sodium oxide Inorganic materials 0.000 claims description 7
- FUJCRWPEOMXPAD-UHFFFAOYSA-N Li2O Inorganic materials [Li+].[Li+].[O-2] FUJCRWPEOMXPAD-UHFFFAOYSA-N 0.000 claims description 6
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 claims description 6
- XUCJHNOBJLKZNU-UHFFFAOYSA-M dilithium;hydroxide Chemical compound [Li+].[Li+].[OH-] XUCJHNOBJLKZNU-UHFFFAOYSA-M 0.000 claims description 6
- 239000011022 opal Substances 0.000 claims description 4
- 230000002269 spontaneous effect Effects 0.000 claims description 4
- KRHYYFGTRYWZRS-UHFFFAOYSA-M Fluoride anion Chemical compound [F-] KRHYYFGTRYWZRS-UHFFFAOYSA-M 0.000 claims description 3
- 230000003111 delayed effect Effects 0.000 abstract description 27
- 238000004519 manufacturing process Methods 0.000 abstract description 4
- 230000001747 exhibiting effect Effects 0.000 abstract description 3
- 238000013508 migration Methods 0.000 description 11
- 230000005012 migration Effects 0.000 description 11
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 description 10
- 229910052708 sodium Inorganic materials 0.000 description 10
- 239000011734 sodium Substances 0.000 description 10
- 239000003513 alkali Substances 0.000 description 9
- ZLMJMSJWJFRBEC-UHFFFAOYSA-N Potassium Chemical compound [K] ZLMJMSJWJFRBEC-UHFFFAOYSA-N 0.000 description 6
- 238000005299 abrasion Methods 0.000 description 6
- 230000006835 compression Effects 0.000 description 6
- 238000007906 compression Methods 0.000 description 6
- 150000002500 ions Chemical class 0.000 description 6
- 229910052700 potassium Inorganic materials 0.000 description 6
- 239000011591 potassium Substances 0.000 description 6
- HNPSIPDUKPIQMN-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical group O=[Si]=O.O=[Al]O[Al]=O HNPSIPDUKPIQMN-UHFFFAOYSA-N 0.000 description 5
- 239000012634 fragment Substances 0.000 description 5
- 238000012360 testing method Methods 0.000 description 5
- 229910052782 aluminium Inorganic materials 0.000 description 4
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 4
- 230000002547 anomalous effect Effects 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 239000002241 glass-ceramic Substances 0.000 description 3
- 238000009863 impact test Methods 0.000 description 3
- 230000009467 reduction Effects 0.000 description 3
- 229910001415 sodium ion Inorganic materials 0.000 description 3
- GOLCXWYRSKYTSP-UHFFFAOYSA-N Arsenious Acid Chemical compound O1[As]2O[As]1O2 GOLCXWYRSKYTSP-UHFFFAOYSA-N 0.000 description 2
- WCUXLLCKKVVCTQ-UHFFFAOYSA-M Potassium chloride Chemical compound [Cl-].[K+] WCUXLLCKKVVCTQ-UHFFFAOYSA-M 0.000 description 2
- FAPWRFPIFSIZLT-UHFFFAOYSA-M Sodium chloride Chemical compound [Na+].[Cl-] FAPWRFPIFSIZLT-UHFFFAOYSA-M 0.000 description 2
- 239000005347 annealed glass Substances 0.000 description 2
- 230000004888 barrier function Effects 0.000 description 2
- 238000001816 cooling Methods 0.000 description 2
- 230000003247 decreasing effect Effects 0.000 description 2
- 238000013461 design Methods 0.000 description 2
- 239000006025 fining agent Substances 0.000 description 2
- YBMRDBCBODYGJE-UHFFFAOYSA-N germanium dioxide Chemical compound O=[Ge]=O YBMRDBCBODYGJE-UHFFFAOYSA-N 0.000 description 2
- 238000011835 investigation Methods 0.000 description 2
- 238000005498 polishing Methods 0.000 description 2
- 238000005070 sampling Methods 0.000 description 2
- 230000035939 shock Effects 0.000 description 2
- 238000009966 trimming Methods 0.000 description 2
- UXVMQQNJUSDDNG-UHFFFAOYSA-L Calcium chloride Chemical compound [Cl-].[Cl-].[Ca+2] UXVMQQNJUSDDNG-UHFFFAOYSA-L 0.000 description 1
- VEXZGXHMUGYJMC-UHFFFAOYSA-M Chloride anion Chemical compound [Cl-] VEXZGXHMUGYJMC-UHFFFAOYSA-M 0.000 description 1
- 229910052779 Neodymium Inorganic materials 0.000 description 1
- FKNQFGJONOIPTF-UHFFFAOYSA-N Sodium cation Chemical compound [Na+] FKNQFGJONOIPTF-UHFFFAOYSA-N 0.000 description 1
- -1 Tio2 Chemical compound 0.000 description 1
- 239000005358 alkali aluminosilicate glass Substances 0.000 description 1
- 229910000287 alkaline earth metal oxide Inorganic materials 0.000 description 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 1
- 229910000323 aluminium silicate Inorganic materials 0.000 description 1
- 230000003466 anti-cipated effect Effects 0.000 description 1
- GHPGOEFPKIHBNM-UHFFFAOYSA-N antimony(3+);oxygen(2-) Chemical compound [O-2].[O-2].[O-2].[Sb+3].[Sb+3] GHPGOEFPKIHBNM-UHFFFAOYSA-N 0.000 description 1
- 239000002585 base Substances 0.000 description 1
- 239000001110 calcium chloride Substances 0.000 description 1
- 229910001628 calcium chloride Inorganic materials 0.000 description 1
- 235000011148 calcium chloride Nutrition 0.000 description 1
- 150000001768 cations Chemical class 0.000 description 1
- CETPSERCERDGAM-UHFFFAOYSA-N ceric oxide Chemical compound O=[Ce]=O CETPSERCERDGAM-UHFFFAOYSA-N 0.000 description 1
- 229910000422 cerium(IV) oxide Inorganic materials 0.000 description 1
- 229910052804 chromium Inorganic materials 0.000 description 1
- 239000003086 colorant Substances 0.000 description 1
- 239000000470 constituent Substances 0.000 description 1
- 229910052802 copper Inorganic materials 0.000 description 1
- 230000002596 correlated effect Effects 0.000 description 1
- 230000000875 corresponding effect Effects 0.000 description 1
- 229910052593 corundum Inorganic materials 0.000 description 1
- 230000007547 defect Effects 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 239000011121 hardwood Substances 0.000 description 1
- 229910052742 iron Inorganic materials 0.000 description 1
- 238000003475 lamination Methods 0.000 description 1
- MRELNEQAGSRDBK-UHFFFAOYSA-N lanthanum oxide Inorganic materials [O-2].[O-2].[O-2].[La+3].[La+3] MRELNEQAGSRDBK-UHFFFAOYSA-N 0.000 description 1
- 229910052748 manganese Inorganic materials 0.000 description 1
- 238000000034 method Methods 0.000 description 1
- 229910052759 nickel Inorganic materials 0.000 description 1
- KTUFCUMIWABKDW-UHFFFAOYSA-N oxo(oxolanthaniooxy)lanthanum Chemical compound O=[La]O[La]=O KTUFCUMIWABKDW-UHFFFAOYSA-N 0.000 description 1
- 230000000149 penetrating effect Effects 0.000 description 1
- 230000000704 physical effect Effects 0.000 description 1
- 239000001103 potassium chloride Substances 0.000 description 1
- 230000001902 propagating effect Effects 0.000 description 1
- 230000003763 resistance to breakage Effects 0.000 description 1
- 230000002441 reversible effect Effects 0.000 description 1
- 238000012552 review Methods 0.000 description 1
- 238000007665 sagging Methods 0.000 description 1
- 238000007493 shaping process Methods 0.000 description 1
- 239000011780 sodium chloride Substances 0.000 description 1
- 230000002459 sustained effect Effects 0.000 description 1
- 238000012956 testing procedure Methods 0.000 description 1
- 229910052723 transition metal Inorganic materials 0.000 description 1
- 150000003624 transition metals Chemical class 0.000 description 1
- 229910052720 vanadium Inorganic materials 0.000 description 1
- 229910001845 yogo sapphire Inorganic materials 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
- B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B23/00—Re-forming shaped glass
- C03B23/20—Uniting glass pieces by fusing without substantial reshaping
- C03B23/203—Uniting glass sheets
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
- C03C17/02—Surface treatment of glass, not in the form of fibres or filaments, by coating with glass
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C27/00—Joining pieces of glass to pieces of other inorganic material; Joining glass to glass other than by fusing
- C03C27/06—Joining glass to glass by processes other than fusing
- C03C27/10—Joining glass to glass by processes other than fusing with the aid of adhesive specially adapted for that purpose
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/23—Sheet including cover or casing
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
- Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
- Y10T428/2495—Thickness [relative or absolute]
- Y10T428/24967—Absolute thicknesses specified
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31—Surface property or characteristic of web, sheet or block
- Y10T428/315—Surface modified glass [e.g., tempered, strengthened, etc.]
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Ceramic Engineering (AREA)
- Glass Compositions (AREA)
- Joining Of Glass To Other Materials (AREA)
- Laminated Bodies (AREA)
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US05/478,584 US3958052A (en) | 1974-06-12 | 1974-06-12 | Subsurface-fortified glass laminates |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| CA1058879A true CA1058879A (en) | 1979-07-24 |
Family
ID=23900513
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CA224,910A Expired CA1058879A (en) | 1974-06-12 | 1975-04-17 | Subsurface-fortified glass laminates |
Country Status (5)
| Country | Link |
|---|---|
| US (1) | US3958052A (index.php) |
| CA (1) | CA1058879A (index.php) |
| DE (1) | DE2525234C2 (index.php) |
| FR (1) | FR2274573A1 (index.php) |
| GB (1) | GB1510025A (index.php) |
Families Citing this family (25)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US5013605A (en) * | 1988-08-11 | 1991-05-07 | Gritz David N | Cordierite-type glass-ceramic with controlled coloration |
| DE19816380C1 (de) * | 1998-04-11 | 1999-10-07 | Schott Glas | Cadmiumfreie, farbige Anlaufgläser auf Basis einer Glaskeramik, Verfahren zu deren Herstellung und ihre Verwendung |
| US6387510B1 (en) * | 1999-04-13 | 2002-05-14 | Asahi Glass Company, Limited | Glass for a data storage medium substrate and glass substrate for data storage media |
| US6776006B2 (en) * | 2000-10-13 | 2004-08-17 | Corning Incorporated | Method to avoid striae in EUV lithography mirrors |
| US7201965B2 (en) * | 2004-12-13 | 2007-04-10 | Corning Incorporated | Glass laminate substrate having enhanced impact and static loading resistance |
| US9302937B2 (en) * | 2010-05-14 | 2016-04-05 | Corning Incorporated | Damage-resistant glass articles and method |
| KR101747057B1 (ko) | 2010-06-29 | 2017-06-13 | 코닝 인코포레이티드 | 오버플로 하향인발 융합 공정을 사용해 공동인발하여 만들어진 다층 유리 시트 |
| CN103338926B (zh) * | 2010-11-30 | 2016-03-02 | 康宁股份有限公司 | 表面和中心区域处于压缩状态的玻璃 |
| TWI572480B (zh) | 2011-07-25 | 2017-03-01 | 康寧公司 | 經層壓及離子交換之強化玻璃疊層 |
| US9359251B2 (en) | 2012-02-29 | 2016-06-07 | Corning Incorporated | Ion exchanged glasses via non-error function compressive stress profiles |
| US11079309B2 (en) | 2013-07-26 | 2021-08-03 | Corning Incorporated | Strengthened glass articles having improved survivability |
| US9517968B2 (en) | 2014-02-24 | 2016-12-13 | Corning Incorporated | Strengthened glass with deep depth of compression |
| TWI729925B (zh) | 2014-06-19 | 2021-06-01 | 美商康寧公司 | 無易碎應力分布曲線的玻璃 |
| US11123959B2 (en) | 2014-10-07 | 2021-09-21 | Corning Incorporated | Glass article with determined stress profile and method of producing the same |
| CN117623625A (zh) | 2014-10-08 | 2024-03-01 | 康宁股份有限公司 | 包含金属氧化物浓度梯度的玻璃和玻璃陶瓷 |
| US10150698B2 (en) | 2014-10-31 | 2018-12-11 | Corning Incorporated | Strengthened glass with ultra deep depth of compression |
| CN115536270A (zh) | 2014-11-04 | 2022-12-30 | 康宁股份有限公司 | 深层非易碎应力曲线及其制造方法 |
| US11613103B2 (en) | 2015-07-21 | 2023-03-28 | Corning Incorporated | Glass articles exhibiting improved fracture performance |
| US10579106B2 (en) | 2015-07-21 | 2020-03-03 | Corning Incorporated | Glass articles exhibiting improved fracture performance |
| CN108137396B (zh) | 2015-10-14 | 2022-04-26 | 康宁股份有限公司 | 具有确定的应力分布的层压玻璃制品及其形成方法 |
| TWI739442B (zh) | 2015-12-11 | 2021-09-11 | 美商康寧公司 | 具有金屬氧化物濃度梯度之可熔融成形的玻璃基物件 |
| EP3904302A1 (en) | 2016-04-08 | 2021-11-03 | Corning Incorporated | Glass-based articles including a metal oxide concentration gradient |
| KR20200091500A (ko) | 2016-04-08 | 2020-07-30 | 코닝 인코포레이티드 | 두 영역을 포함하는 응력 프로파일을 포함하는 유리-계 물품, 및 제조 방법 |
| TW201806759A (zh) | 2016-05-09 | 2018-03-01 | 康寧公司 | 具有經控制的熱膨脹係數之玻璃積層以及彼之製造方法 |
| US11214515B2 (en) * | 2017-11-30 | 2022-01-04 | Corning Incorporated | Glass-based articles having stress profiles with high stored energy and methods of manufacture |
Family Cites Families (8)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE1496097A1 (de) * | 1963-11-21 | 1969-03-20 | Teeg Research Inc | Mehrschichtiger Glasgegenstand und Verfahren zu seiner Herstellung |
| US3218220A (en) * | 1964-11-20 | 1965-11-16 | Brockway Glass Co Inc | Strengthened glass article and method of producing same |
| US3597305A (en) * | 1968-06-06 | 1971-08-03 | Corning Glass Works | Subsurface fortified glass or glass-ceramic laminates |
| US3649440A (en) * | 1969-07-09 | 1972-03-14 | Corning Glass Works | Strengthened laminated glass bodies |
| US3737294A (en) * | 1970-08-28 | 1973-06-05 | Corning Glass Works | Method for making multi-layer laminated bodies |
| US3673049A (en) * | 1970-10-07 | 1972-06-27 | Corning Glass Works | Glass laminated bodies comprising a tensilely stressed core and a compressively stressed surface layer fused thereto |
| US3746526A (en) * | 1971-03-10 | 1973-07-17 | Corning Glass Works | Method for forming subsurface fortified laminates |
| US3778335A (en) * | 1971-09-02 | 1973-12-11 | Corning Glass Works | Sodium aluminosilicate glass article strengthened by a surface compressive stress layer |
-
1974
- 1974-06-12 US US05/478,584 patent/US3958052A/en not_active Expired - Lifetime
-
1975
- 1975-04-17 CA CA224,910A patent/CA1058879A/en not_active Expired
- 1975-05-23 GB GB22702/75A patent/GB1510025A/en not_active Expired
- 1975-06-06 DE DE2525234A patent/DE2525234C2/de not_active Expired
- 1975-06-11 FR FR7518250A patent/FR2274573A1/fr active Granted
Also Published As
| Publication number | Publication date |
|---|---|
| DE2525234C2 (de) | 1984-10-31 |
| FR2274573B1 (index.php) | 1982-06-18 |
| DE2525234A1 (de) | 1976-01-02 |
| FR2274573A1 (fr) | 1976-01-09 |
| US3958052A (en) | 1976-05-18 |
| GB1510025A (en) | 1978-05-10 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CA1058879A (en) | Subsurface-fortified glass laminates | |
| US3673049A (en) | Glass laminated bodies comprising a tensilely stressed core and a compressively stressed surface layer fused thereto | |
| US11767252B2 (en) | Chemically strengthened glass, and glass for chemical strengthening | |
| US20240228364A1 (en) | Transition metal-containing, ion exchangeable colored glasses | |
| US12017952B2 (en) | Chemically tempered glass | |
| US3597305A (en) | Subsurface fortified glass or glass-ceramic laminates | |
| US3746526A (en) | Method for forming subsurface fortified laminates | |
| EP3074357B1 (en) | Fast ion exchangeable glasses with high indentation threshold | |
| US8304078B2 (en) | Chemically strengthened lithium aluminosilicate glass having high strength effective to resist fracture upon flexing | |
| KR101903219B1 (ko) | 비-오차 함수 압축 응력 프로파일을 통한 이온 교환된 유리 | |
| DE69219824T2 (de) | Feuerwiderstandsfähige Verglasungsplatte | |
| US20180057392A1 (en) | Strengthened glass ii | |
| JPH0769669A (ja) | 防火安全板ガラス | |
| US20070157919A1 (en) | Tempered glass for thermal insulation | |
| CN105683118A (zh) | 用于化学强化的玻璃的局部退火的方法 | |
| JP6311704B2 (ja) | 建築窓用複層ガラス | |
| WO2017183381A1 (ja) | 車両用合わせガラス | |
| JP2004099370A (ja) | 防火ガラス | |
| US20220184926A1 (en) | Glass with unique fracture behavior for vehicle windshield | |
| US5876472A (en) | Method for producing a chemically pretensioned glass body | |
| US6770375B2 (en) | Glazing, which can be subjected to high levels of thermal stress and comprising a glass body | |
| JP2022145562A (ja) | 建築用窓板ガラス | |