BRPI1100351A2 - phosphorescent grout for joining floor coverings, walls and the like - Google Patents

Abstract

Phosphorescent joint for joining floor, wall and floor coverings. Designed by an epoxy grout with phosphorescence properties, that is, it has more brightness and phosphorescence than ordinary grouts, capable of emitting phosphorescence for up to 3 hours after the incidence of light, whose formulation, by weight, is as follows : Component A Resin (2); Epoxy resin in the proportion of 19.0%, with a variation of about 5%; Benzyl Alcohol in the proportion of 4.0%, with a variation of about 5%; Quartz Sand Silica 100 mesh in the proportion of 66.77%, with a variation of about 5%; Pyrogenic Silica in the proportion of 0.2%, with a variation of about 5%; Organic pigment in the proportion of 10.0%, with a variation of about 5%; Zinc sulphide in the proportion of 0,03%, with a variation of plus or minus 5%; Component B - Hardener (3): Curing Agent at a ratio of 20.0%, with a variation of plus or minus 5%; Quartz Sand Silica mesh 100 in the proportion of 75.0%, with a variation of about 5%; Water in the proportion of 5.0%, with a variation of about 5%.

Description

Phosphorescent joint for joining floors, walls and similar cladding "

The present patent for the privilege of invention, "Phosphorescent Grout for the joining of floor, wall and similar coatings", has as its object a practical and innovative phosphorescent grout, which belongs to the field of building articles, to be used more precisely for filling. of the executive joints resulting from the laying of cladding plates, such as ceramic plates, tiles, porcelain tiles, granites, glass blocks, polished stoneware, among others.

Portantof = in the patent application in question has its own luminescence grout specially designed and developed for great practicality and which has great advantages both in its use and in its manufacture.

It is also, the objective of this application, to present a phosphorescent joint for joining floor coverings, walls and the like with low costs for its industrial feasibility, but allied to the requirements of robustness, safety and utility practicality, thus offering the consumer public an option. In addition to the similar market, which, unlike the usual products, offers numerous possibilities and benefits to its users, becoming a product of great acceptance in the construction market.

As construction technicians know, grouting is a specific building material for filling the executive joints resulting from the laying of cladding boards on the wall or floor with the function of waterproofing the sides of the boards.

In the usual form it is composed of products such as: cement, mineral aggregates, pigments, cellulosic additive, hydrofuge additive and polymers, which receive water and properly homogenized become a creamy mortar, suitable to fill the joints between ceramic tiles, waterproofing them. at.

Currently grouts are available in various colors and for various types of applications, such as anti-mold, waterproofing, outdoor and indoor areas, etc. and the thickness of the application varies depending on the size of the workpiece and its use, and may vary from one to fifteen millimeters. The major drawback of grouts

Conventional resides, specifically in the fact that they do not present phosphorescence, that is, although they are found in the most varied colors and shades, in order to match the respective coatings, there is the disadvantage of not emitting their own light, a fact of extreme importance for signaling public places with low lighting.

It was thinking of these drawbacks that, after numerous researches and studies, the inventor, a person linked to the branch, created and developed the object of the present patent, idealizing a "Phosphorescent Gathering for Cladding, Walls and Similars" in which not only the Physical-chemical and functional qualities were considered in its design, but also ease of application, durability and constituent elements, which brought great advantages in their use without any burden.

Thus, the present patent has been designed to obtain a construction product with as few components as possible, conveniently configured and arranged to allow the "Phosphorescent Grouting Joint" to perform its functions efficiently and effectively. unmatched versatility without the drawbacks already mentioned. In this patent application,

a practical and innovative "Phosphorescent GATHER FOR FLOOR, WALL AND SIMILAR COVERING" .com- all-aesthetic-and-functional qualities, designed and developed according to the most modern techniques, thus enabling their most varied use, from residential use to commercial use in domestic areas.

It can be used for grouting ceramic tiles, tiles, porcelain tiles, granites, glass blocks, sandstone, etc., with a recommended joint thickness of 2 to 10 mm.

Its innovative formulation allows an excellent level of functionality to be achieved, offering a phosphorescent grout which has great durability and has been specially developed for safety marking and marking sites.

The configuration of the phosphorescent joint, object of the present patent, in its new constructive form, has the following technical characteristics: - Waterproof;

- Flexible for wide and thin joints;

- absolute hygiene;

- Fully washable;

- Anti-mold, does not stain;

- smooth texture;

- High durability;

- Easy and total cleaning;

- Phosphorescence.

It is to be understood as soon as the grout in

The question is extremely simple in its formulation and therefore easily feasible, however, excellent practical and? -functional results are obtained, offering an innovative composition over known models.

Idealized with properties of

Innovative luminescence, results in a harmonic finish, very peculiar aspect and above all characteristic, and besides the aesthetic aspect, the product stands out for its versatility and convenience of use.

Next, for better understanding and

understanding of what constitutes the "Phosphorescent Gathering for the joining of floors, walls and similar coatings", which is claimed here, are presented in the accompanying illustrative drawings:

FIG. 1 - Shows a perspective view

phosphorescent grout components being poured into a container for preparation before being applied to the joints of the floor or wallcoverings.

FIG. 2 - Shows a side perspective view of the phosphorescent joint components being mixed to form the final product to be applied to the joints of floor or wall coverings.

FIG. 3 - Shows a super-lateral perspective view of the phosphorescent joint being applied to the joints of floor or wall coverings.

FIG. 4 - Shows a top view of the phosphorescent joint applied to the joints of floor or wall coverings.

According to how much they illustrate the

Related Figures, "Phosphorescent Grout for Joining Flooring, Walls and Similar Coatings -", - the subject-matter of the present invention, is characterized essentially by its being an epoxy grout with phosphorescent properties. Phosphorescence is the ability of a chemical species to emit light even in the dark.

It is a grout that has more brightness and phosphorescence than ordinary grouts, has the ability to emit phosphorescence for up to 3 hours after the end of light incidence, and the duration of phosphorescence depends on the time of exposure to light. .

The phosphorescent grout (1) in question is a completely water-based product, free of any radioactive additive, formulated from epoxy resin, mineral fillers, additives, organic pigments and curing agent. two components, which are: the resin (2) and the said hardening component (3).

Their formulations comprise the following components by weight. Component A - Resin (2)

• Epoxy resin in the proportion of 19.0%, with a variation of about 5%.

• Benzyl Alcohol in the proportion of 4.0%, with a variation of more or less than 5%.

• Quartz Sand Silica 100 mesh at a ratio of 66.77%, with a variation of about 5%.

• 0.2% fumed silica, with a variation of about 5%.

• Organic pigment in the proportion of 10.0%, with a variation of about 5%.

• Zinc sulfide in the proportion of 0.03% 7 with a variation of about 5%.

Component B - Hardener (3)

• Curing Agent at a rate of 20.0%, with a flow rate of about 5%.

• Quartz Sand Silica 100 mesh at a ratio of 75.0%, with a variation of about 5%.

• Water in the proportion of 5.0%, with a variation of about 5%.

Phosphorescent grout (1) has been specially developed for demarcation sites and safety signs, and can be applied at the junction of ceramic tiles, tiles, porcelain, granite, glass block, polished stone, both in homes and commercial buildings, preferably indoors.

The recommended joint thickness is 2 to 10 mm.

For a better understanding, follow below the technical parameters of the phosphorescent grout (1).

• Phosphorescence: 2 to 3 hours duration.

· Permeability at 240 minutes: 0.0g / cm2.

• Consistency: Thixotropic Mass.

• Specific weight: 1.85 kg / l.

• Mixture: equal parts Solution plus

Hardener.

· Usage time after mixing: 30 minutes.

• Ideal application temperature: 25 ° C.

• Total cure: 7 days.

• Minimum release time-for use: ~ 2

days

Its application is extremely simple,

The resin mixture (2) plus the hardening component (3) must be used within 30 minutes, which can be applied to the joints of the coating plates (4) with the aid of a simple polymeric spatula (5) by pressing down. if grouting downwards (always towards the joint), without leaving empty spaces at the bottom of the joints.

Therefore, the present descriptive report deals with a new conception in phosphorescent grout, presenting, as we could evidence from the analysis performed and the figures shown, innumerable differences over the conventional products existing in the consumer market, besides completely different formative and functional technical characteristics. relevant to the state of the art. Because of the advantages it offers, as well as being truly innovative features that meet all the requirements of novelty and originality in the genre, this "Phosphorescent Gathering for FLOOR, WALL AND SIMILAR COVERING" meets the conditions necessary to deserve the privilege of invention.

Claims (5)

1. "Phosphorescent joint for joining of flooring, walls and the like", as understood by a filler product joints resulting from the laying of wall cladding, wall, floor and the like, whose function is to waterproof the sides of the boards, characterized by a phosphorescent grout (1), consisting of two components, called resin (2) and hardener (3 ), where the Resin component (1) consists of: Epoxy resin in the proportion of 19.0% by weight, with a variation of about 5%; Benzyl alcohol of 4,0% by weight with a variation of more than or less than -5% - Quartz Sand Silica 100 mesh of 66,77% by weight of a variation to more or less than 5%; Fumed silica in the proportion of 0,2% by weight, with a variation of more or less than 5%; Organic pigment in the proportion of 10,0% by weight, with a variation of more or less than 5%; Zinc sulphide in the proportion of 0,03% by weight, with a variation of plus or minus 5%; said hardening component (3) comprises: Curing Agent in the proportion of 20.0% by weight, with a variation of about 5%; Quartz Sand Silica mesh -100 in the proportion of 75,0% by weight, with a variation of more or less than 5%; Water of 5.0% by weight, with a variation of more or less than 5%.