BR112022011028A2 - Placa de aço/tira de aço multifásica de baixo grau de silício e baixo grau de carbono equivalente a gpa, e método de fabricação da mesma - Google Patents

Placa de aço/tira de aço multifásica de baixo grau de silício e baixo grau de carbono equivalente a gpa, e método de fabricação da mesma

Info

Publication number
BR112022011028A2
BR112022011028A2 BR112022011028A BR112022011028A BR112022011028A2 BR 112022011028 A2 BR112022011028 A2 BR 112022011028A2 BR 112022011028 A BR112022011028 A BR 112022011028A BR 112022011028 A BR112022011028 A BR 112022011028A BR 112022011028 A2 BR112022011028 A2 BR 112022011028A2
Authority
BR
Brazil
Prior art keywords
steel plate
low
hole
gpa
steel strip
Prior art date
Application number
BR112022011028A
Other languages
English (en)
Inventor
Zhang Hanlong
Sun Yiqiang
Mao Xinping
Wang Cheng
Zhang Yulong
Jin Xinyan
Wang Shuize
Wang Li
Original Assignee
Baoshan Iron & Steel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoshan Iron & Steel filed Critical Baoshan Iron & Steel
Publication of BR112022011028A2 publication Critical patent/BR112022011028A2/pt

Abstract

PLACA DE AÇO/TIRA DE AÇO MULTIFÁSICA DE BAIXO GRAU DE SILÍCIO E BAIXO GRAU DE CARBONO EQUIVALENTE A GPA, E MÉTODO DE FABRICAÇÃO DA MESMA. São reveladas uma placa de aço/tira de aço multifásica de baixo grau de silício e baixo grau de carbono equivalente a GPa e um método de fabricação para estas. A placa de aço/tira de aço compreende os seguintes componentes em porcentagem em peso: 0,03-0,07% de C, 0,1-0,5% de Si, 1,7-2,0% de Mn, P=0,02%, S=0,01%, N=0,01%, 0,01-0,05% de Al, 0,4-0,7% de Cr, 0,001-0,005% de B, e 0,07-0,15% de Ti, e também compreende um ou ambos de 0,15-0,4% de Mo ou 0,02-0,08% de Nb, sendo o restante Fe e outras impurezas inevitáveis; e, ao mesmo tempo, a placa de aço/tira de aço satisfaz: o teor de B*=0,001 disponível, o teor de B*=B-[Ti-3,4N-1,2(C-Nb/7,8)]/22, CE<0,58 disponível, e CE=C+Mn/6+(Cr+Mo+V)/5+(Si+Ni+Cu)/15. A placa de aço tem uma resistência à tração de =980 MPa e uma tensão de ruptura de =780 MPa, e a taxa de expansão do furo satisfaz: se um furo original é um furo perfurado, a taxa de expansão do furo é >50%; e se o furo original é um furo rebarbado, a taxa de expansão do furo é >60%. A placa de aço é usada principalmente na preparação de chassis de veículos e peças do sistema de suspensão.
BR112022011028A 2019-12-31 2020-12-30 Placa de aço/tira de aço multifásica de baixo grau de silício e baixo grau de carbono equivalente a gpa, e método de fabricação da mesma BR112022011028A2 (pt)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201911415229.0A CN113122769B (zh) 2019-12-31 2019-12-31 低硅低碳当量吉帕级复相钢板/钢带及其制造方法
PCT/CN2020/141310 WO2021136355A1 (zh) 2019-12-31 2020-12-30 低硅低碳当量吉帕级复相钢板/钢带及其制造方法

Publications (1)

Publication Number Publication Date
BR112022011028A2 true BR112022011028A2 (pt) 2022-08-16

Family

ID=76685947

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112022011028A BR112022011028A2 (pt) 2019-12-31 2020-12-30 Placa de aço/tira de aço multifásica de baixo grau de silício e baixo grau de carbono equivalente a gpa, e método de fabricação da mesma

Country Status (8)

Country Link
US (1) US20230049380A1 (pt)
EP (1) EP4086362A4 (pt)
JP (1) JP7439265B2 (pt)
KR (1) KR20220119639A (pt)
CN (1) CN113122769B (pt)
AU (1) AU2020418007A1 (pt)
BR (1) BR112022011028A2 (pt)
WO (1) WO2021136355A1 (pt)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20230069426A (ko) * 2021-11-12 2023-05-19 주식회사 포스코 굽힘성 및 신장 플랜지성이 우수한 초고강도 강판 및 이의 제조 방법
CN117344203A (zh) * 2022-06-27 2024-01-05 宝山钢铁股份有限公司 一种抗拉强度800Mpa级热轧复相钢及其制造方法

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4660315B2 (ja) * 2005-08-09 2011-03-30 新日本製鐵株式会社 靭性に優れた厚手高強度鋼板の製造方法及び靭性に優れた厚手高強度鋼板
CN101008066B (zh) * 2006-01-27 2010-05-12 宝山钢铁股份有限公司 抗拉强度高于1000MPa的热轧马氏体钢板及其制造方法
JP4088316B2 (ja) 2006-03-24 2008-05-21 株式会社神戸製鋼所 複合成形性に優れた高強度熱延鋼板
JP2007284712A (ja) * 2006-04-13 2007-11-01 Nippon Steel Corp 靭性に優れた厚手高強度鋼板の製造方法及び靭性に優れた厚手高強度鋼板
JP5483916B2 (ja) * 2009-03-27 2014-05-07 日新製鋼株式会社 曲げ性に優れた高強度合金化溶融亜鉛めっき鋼板
JP5391801B2 (ja) 2009-04-16 2014-01-15 新日鐵住金株式会社 溶融めっき熱延鋼板およびその製造方法
CN102251170A (zh) * 2010-05-19 2011-11-23 宝山钢铁股份有限公司 一种超高强度贝氏体钢及其制造方法
KR101575832B1 (ko) 2011-08-09 2015-12-08 신닛테츠스미킨 카부시키카이샤 저온에서의 충격 에너지 흡수 특성과 haz 내연화 특성이 우수한 고항복비 열연 강판 및 그 제조 방법
CN103305746B (zh) * 2012-03-14 2015-09-23 宝山钢铁股份有限公司 一种时效硬化薄带连铸低碳微合金高强钢带制造方法
JP5895780B2 (ja) * 2012-09-10 2016-03-30 新日鐵住金株式会社 大入熱溶接熱影響部靭性に優れた鋼板およびその製造方法
BR112015011302B1 (pt) 2013-02-26 2020-02-27 Nippon Steel Corporation Chapa de aço laminada a quente e seu processo para produção
EP3112488B1 (en) 2014-02-27 2019-05-08 JFE Steel Corporation High-strength hot-rolled steel sheet and manufacturing method therefor
CN104513930A (zh) * 2014-12-19 2015-04-15 宝山钢铁股份有限公司 弯曲和扩孔性能良好的超高强热轧复相钢板和钢带及其制造方法
CN106119702B (zh) * 2016-06-21 2018-10-02 宝山钢铁股份有限公司 一种980MPa级热轧高强度高扩孔钢及其制造方法
CN105950998B (zh) * 2016-07-11 2018-01-26 攀钢集团攀枝花钢铁研究院有限公司 一种1000MPa级低碳热镀锌双相钢及其制备方法
CN109642292B (zh) * 2016-08-31 2021-11-12 杰富意钢铁株式会社 高强度钢板及其制造方法
MX2019008649A (es) * 2017-01-20 2019-12-16 Thyssenkrupp Steel Europe Ag Producto de acero plano laminado en caliente que consiste en un acero de fase compleja con una microestructura y un metodo predominantemente bainitico para la fabricacion de un producto de acero plano.
US10900100B2 (en) * 2017-03-31 2021-01-26 Nippon Steel Corporation Hot rolled steel sheet
CN109023036B (zh) * 2017-06-12 2020-03-31 鞍钢股份有限公司 一种超高强热轧复相钢板及生产方法
CN108642379B (zh) * 2018-05-15 2020-07-24 首钢集团有限公司 一种抗拉强度1200MPa级冷轧双相钢及其制备方法

Also Published As

Publication number Publication date
CN113122769A (zh) 2021-07-16
CN113122769B (zh) 2022-06-28
WO2021136355A1 (zh) 2021-07-08
EP4086362A1 (en) 2022-11-09
JP7439265B2 (ja) 2024-02-27
EP4086362A4 (en) 2023-07-19
US20230049380A1 (en) 2023-02-16
JP2023509410A (ja) 2023-03-08
AU2020418007A1 (en) 2022-07-21
KR20220119639A (ko) 2022-08-30

Similar Documents

Publication Publication Date Title
BR112022011028A2 (pt) Placa de aço/tira de aço multifásica de baixo grau de silício e baixo grau de carbono equivalente a gpa, e método de fabricação da mesma
CA2754123C (en) Low alloy steel with a high yield strength and high sulphide stress cracking resistance
BRPI0517890A (pt) método de produção de chapas de aço austenìtico de ferro/carbono/manganês tendo resistência e caracterìsticas de alongamento muito altas e excelente homogeneidade
BRPI0614604B1 (pt) tubo sem costura soldável e processo para produzir o mesmo
JP2007031734A (ja) 耐遅れ破壊特性に優れた高強度ボルトおよびその製造方法
BR112013031500B8 (pt) chapa de aço laminada a frio revestida, processo de fabricação uma chapa laminada a frio e revestida processo de fabricação de uma peça por soldagem de pelo menos uma chapa laminada a frio revestida e uso de uma chapa de aço laminada a frio revestida
BR112014001589A2 (pt) chapa de aço de alta resistência e chapa de aço galvanizada de alta resistência excelente em conformabilidade e métodos de produção das mesmas
BR0314819A (pt) Tubo de aço sem costura de alta resistência, excelente em resistência à fratura por hidrogênio induzido e seu método de produção
EP3594374A1 (en) Austenitic abrasion-resistant steel sheet
SG151274A1 (en) A high-strength thick steel plate excellent in low temperature toughness at heat affected zone resulting from large heat input welding
BRPI0621704B1 (pt) Chapa de aço de alta resistência laminada a quente e método para produção da mesma
AU2018376037B2 (en) High-strength high-toughness and wear-resistant composite steel plate and manufacturing method therefor
BR112018015250A2 (pt) fio de aço plano de alta resistência exibindo resistência à quebra induzida por hidrogênio superior
JP6051031B2 (ja) 高力ボルト及びその製造方法
BR112022001623A2 (pt) Placa de aço de alta resistência para um tubo de linha resistente a ácido, método de produção da mesma, e tubo de aço de alta resistência
JP2018204110A (ja) 耐摩耗厚鋼板
BR0315696A (pt) Peça de aço de construção soldável, processo para a fabricação de uma peça de aço soldável e processo para a fabricação de uma chapa de aço soldável
BRPI0607524B1 (pt) aço e método de sua produção
BR112022010497A2 (pt) Placa de aço/tira de aço multifásica de ultra alta resistência de baixo custo e baixo carbono e método de fabricação da mesma
JP6017944B2 (ja) 高力ボルト及びその製造方法
BRPI1005394B1 (pt) Heat resistant steel for engine valves with high temperature resistance
BR112021026504A2 (pt) Material de aço adequado para uso em ambiente ácido
CN104651740A (zh) 一种高强韧150钢级钻杆材料及其制备方法
KR900016489A (ko) 마르에이징 강
CN104651741A (zh) 一种高强韧160钢级钻杆材料及其制备方法