AT232962B - Verfahren zur Entaschung von aus Naturgraphit geformten Körpern - Google Patents

Verfahren zur Entaschung von aus Naturgraphit geformten Körpern

Info

Publication number
AT232962B
AT232962B AT346161A AT346161A AT232962B AT 232962 B AT232962 B AT 232962B AT 346161 A AT346161 A AT 346161A AT 346161 A AT346161 A AT 346161A AT 232962 B AT232962 B AT 232962B
Authority
AT
Austria
Prior art keywords
sep
natural graphite
ash removal
bodies formed
ppm
Prior art date
Application number
AT346161A
Other languages
English (en)
Inventor
Erich Dipl Ing Dr Techn Fitzer
Erich Dr Techn Nedopil
Original Assignee
Siemens Planiawerke Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Siemens Planiawerke Ag filed Critical Siemens Planiawerke Ag
Application granted granted Critical
Publication of AT232962B publication Critical patent/AT232962B/de

Description


   <Desc/Clms Page number 1> 
 



  Verfahren zur Entaschung von aus Naturgraphit geformten Körpern 
 EMI1.1 
 

 <Desc/Clms Page number 2> 

 
 EMI2.1 
 
 EMI2.2 
 
<tb> 
<tb> vor <SEP> der <SEP> Reinigung <SEP> nach <SEP> der <SEP> Reinigung
<tb> Gesamtasche <SEP> 550 <SEP> ppm <SEP> 25 <SEP> ppm
<tb> Bor <SEP> 0, <SEP> 2 <SEP> ppm <SEP> 0,15 <SEP> ppm
<tb> Raumgewicht <SEP> 2,05 <SEP> g/cm3 <SEP> 1, <SEP> 96 <SEP> g/cm3
<tb> Druckfestigkeit <SEP> 150 <SEP> kg/cm2 <SEP> 6, <SEP> 0 <SEP> kg/cm' <SEP> 
<tb> Permeabilität <SEP> 1, <SEP> 8. <SEP> 10-6arcies <SEP> 6,3. <SEP> 10-6Darcies
<tb> 
 
Beispiel 2 :

   Ein aus mikrokristallinem Naturgraphit (erdigem Naturgraphit) bestehender kugelförmiger Fcrmkörper (70 mm Durchmesser), der mit Kunstharzbindung hergestellt und bei   1 0000C   verkokt 
 EMI2.3 
 

 <Desc/Clms Page number 3> 

 5   cm/min angewendet.   Die Erhitzung wurde bis auf 3   0000C   innerhalb von 4 1/2 h durchgeführt. Die Abkühlung erfolgte im CO-Gasstrom.

   Das Reinigungsergebnis ist aus nachstehenden Angaben ersichtlich : 
 EMI3.1 
 
<tb> 
<tb> vor <SEP> der <SEP> Reinigung <SEP> nach <SEP> der <SEP> Reinigung
<tb> Asche <SEP> 7500 <SEP> ppm <SEP> 13 <SEP> ppm
<tb> = <SEP> 0, <SEP> 75 <SEP> %
<tb> Bor <SEP> 8, <SEP> 65 <SEP> ppm <SEP> 0,08 <SEP> ppm
<tb> Raumgewicht <SEP> 1, <SEP> 95 <SEP> g/cm3 <SEP> 1, <SEP> 82 <SEP> gfcm3
<tb> Druckfestigkeit <SEP> 350 <SEP> kg/cm <SEP> 320 <SEP> 1 <SEP> ;/cm <SEP> 
<tb> Permeabilität <SEP> 6, <SEP> 1. <SEP> 10-6 <SEP> Darcies <SEP> 2, <SEP> 16. <SEP> 10 <SEP> Darcies <SEP> 
<tb> 
 
Der so gereinigte Probekörper wurde einer Vakuumdruckimprägnierung mit niedrig viskosem Kunstharz unterworfen und ergab nach der Verkokung folgende Werte bei   1     :

     
 EMI3.2 
 
<tb> 
<tb> Reinheit <SEP> die <SEP> gleiche
<tb> Raumgewicht <SEP> 1, <SEP> 95 <SEP> g/cm3 <SEP> 
<tb> Druckfestigkeit <SEP> 550 <SEP> kg/cm2
<tb> Permeabilität <SEP> 9. <SEP> 10-7 <SEP> Darcies
<tb> 
 
 EMI3.3
AT346161A 1960-05-06 1961-05-03 Verfahren zur Entaschung von aus Naturgraphit geformten Körpern AT232962B (de)