WO2024253075A1 - 全固体電池およびその製造方法 - Google Patents

全固体電池およびその製造方法 Download PDF

Info

Publication number
WO2024253075A1
WO2024253075A1 PCT/JP2024/020301 JP2024020301W WO2024253075A1 WO 2024253075 A1 WO2024253075 A1 WO 2024253075A1 JP 2024020301 W JP2024020301 W JP 2024020301W WO 2024253075 A1 WO2024253075 A1 WO 2024253075A1
Authority
WO
WIPO (PCT)
Prior art keywords
solid electrolyte
positive electrode
negative electrode
electrolyte layer
solid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2024/020301
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
春樹 上剃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maxell Ltd
Original Assignee
Maxell Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maxell Ltd filed Critical Maxell Ltd
Priority to JP2025526110A priority Critical patent/JPWO2024253075A1/ja
Publication of WO2024253075A1 publication Critical patent/WO2024253075A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Images

Classifications

    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Definitions

  • the present invention relates to a highly reliable all-solid-state battery and a manufacturing method.
  • lithium batteries particularly lithium ion batteries, that can meet this demand use lithium-containing composite oxides such as lithium cobalt oxide ( LiCoO2 ) and lithium nickel oxide ( LiNiO2 ) as the positive electrode active material, graphite or the like as the negative electrode active material, and an organic electrolyte solution containing an organic solvent and a lithium salt as the non-aqueous electrolyte.
  • lithium-containing composite oxides such as lithium cobalt oxide ( LiCoO2 ) and lithium nickel oxide ( LiNiO2 ) as the positive electrode active material, graphite or the like as the negative electrode active material, and an organic electrolyte solution containing an organic solvent and a lithium salt as the non-aqueous electrolyte.
  • lithium-ion batteries As devices that use lithium-ion batteries continue to develop, there is a demand for longer life, higher capacity, and higher energy density lithium-ion batteries, as well as a high demand for the reliability of these longer life, higher capacity, and higher energy density lithium-ion batteries.
  • the organic electrolyte used in lithium-ion batteries contains organic solvents, which are flammable substances, and so there is a possibility that the organic electrolyte may generate abnormal heat if an abnormality such as a short circuit occurs in the battery. Furthermore, with the recent trend toward higher energy density in lithium-ion batteries and an increasing amount of organic solvent in the organic electrolyte, there is a demand for even greater reliability in lithium-ion batteries.
  • all-solid-state lithium batteries (all-solid-state batteries) that do not use organic solvents are also being considered.
  • All-solid-state lithium batteries use a molded solid electrolyte that does not use organic solvents instead of the conventional organic solvent-based electrolyte, and are highly reliable with no risk of abnormal heat generation from the solid electrolyte. For this reason, there are high expectations for them, especially in product areas that require high-capacity secondary batteries.
  • Solid-state batteries are also highly reliable and environmentally resistant, and have a long lifespan, making them promising maintenance-free batteries that can contribute to social development while also continuing to contribute to safety and security.
  • Providing solid-state batteries to society can contribute to the achievement of Goal 3 (Ensure healthy lives and promote well-being for all at all ages), Goal 7 (Ensure access to affordable, reliable, sustainable and modern energy for all), Goal 11 (Make cities and human settlements inclusive, safe, resilient and sustainable), and Goal 12 (Ensure sustainable consumption and production patterns) out of the 17 Sustainable Development Goals (SDGs) established by the United Nations.
  • SDGs Sustainable Development Goals
  • Patent Document 1 proposes a secondary battery structure in which an insulating layer interposed between a positive electrode layer and a negative electrode layer is composed of an electrolyte layer and a polymer-rich layer that has more polymer than the electrolyte layer, and the electrolyte layer is disposed on the positive electrode layer and negative electrode layer side, in order to solve problems such as short circuits caused by the appearance of adhesion in secondary batteries that have electrolytes with low fluidity such as solid electrolytes.
  • Patent Documents 2 to 5 propose filling the voids in a porous substrate such as a nonwoven fabric with a solid electrolyte to produce a solid electrolyte sheet that combines lithium ion conductivity and strength, and using this solid electrolyte sheet to construct an all-solid-state secondary battery.
  • Patent Document 5 shows that by making the thickness of the porous substrate 70% or more of the overall thickness of the solid electrolyte sheet, the mechanical strength of the solid electrolyte sheet can be improved, and even if the area of the solid electrolyte sheet is increased, damage to the solid electrolyte and falling off of the solid electrolyte from the porous substrate can be prevented.
  • Patent Document 5 makes it possible, for example, to enlarge the size of an all-solid-state battery, thereby achieving a high capacity.
  • a positive electrode having a positive electrode mixture layer containing a positive electrode active material or a negative electrode having a negative electrode mixture layer containing a negative electrode active material is integrated with a solid electrolyte sheet having a porous substrate, for example, by pressure molding, cracks may occur in the solid electrolyte sheet, causing a short circuit in the battery, or the solid electrolyte sheet may peel off from the positive electrode or negative electrode due to insufficient bonding between the solid electrolyte sheet and the positive electrode or negative electrode. Therefore, in all-solid-state batteries having a solid electrolyte sheet as a solid electrolyte layer, there is a need to develop technology that suppresses the occurrence of such problems and increases reliability.
  • the present invention was made in consideration of the above circumstances, and its purpose is to provide a highly reliable all-solid-state battery and a method for manufacturing the same.
  • the all-solid-state battery of the present invention has an electrode body in which a positive electrode and a negative electrode are laminated with a solid electrolyte layer interposed therebetween, and the solid electrolyte layer has a porous substrate and is characterized in that it is a laminate of a solid electrolyte layer (I) having a portion protruding from the ends of the positive electrode and the negative electrode in a planar view, a solid electrolyte layer (II) joined to the positive electrode and having a smaller area in a planar view than the solid electrolyte layer (I), and a solid electrolyte layer (III) joined to the negative electrode and having a smaller area in a planar view than the solid electrolyte layer (I).
  • a solid electrolyte layer (I) having a portion protruding from the ends of the positive electrode and the negative electrode in a planar view
  • a solid electrolyte layer (II) joined to the positive electrode and having a smaller area in a planar
  • the manufacturing method of the all-solid-state battery of the present invention is a method for manufacturing an all-solid-state battery having an electrode body in which a positive electrode and a negative electrode are stacked with a solid electrolyte layer interposed therebetween, and the solid electrolyte layer is a laminate of a solid electrolyte layer (I) having a porous substrate, a solid electrolyte layer (II) bonded to the positive electrode, and a solid electrolyte layer (III) bonded to the negative electrode, and the manufacturing method includes the steps of: preparing a solid electrolyte sheet having a porous substrate and a solid electrolyte held by the porous substrate; preparing a positive electrode coated on one side with a solid electrolyte; preparing a negative electrode coated on one side with a solid electrolyte; attaching the positive electrode to one side of the solid electrolyte sheet so that the solid electrolyte covering the positive electrode is in contact with the one side of the solid electrolyte sheet; and attaching
  • the present invention provides a highly reliable all-solid-state battery and a method for manufacturing the same.
  • FIG. 1 is a cross-sectional view illustrating a schematic diagram of an example of an all-solid-state battery of the present invention.
  • the all-solid-state battery of the present invention has an electrode body in which a positive electrode and a negative electrode are stacked with a solid electrolyte layer interposed therebetween.
  • the solid electrolyte layer has the following solid electrolyte layer (I), solid electrolyte layer (II), and solid electrolyte layer (III), and is configured by stacking these three layers.
  • the solid electrolyte layer (I) has a porous substrate and has portions that protrude from the ends of the positive electrode and the negative electrode in a planar view.
  • the solid electrolyte layer (II) is joined to the positive electrode and has a smaller area in a planar view than the solid electrolyte layer (I).
  • the solid electrolyte layer (III) is joined to the negative electrode and has a smaller area in a planar view than the solid electrolyte layer (I).
  • FIG. 1 shows a cross-sectional view that shows a schematic example of an all-solid-state battery of the present invention.
  • the all-solid-state battery 10 shown in FIG. 1 has a positive electrode 20, a negative electrode 30, and a solid electrolyte layer 40 that is interposed between the positive electrode 20 and the negative electrode 30, enclosed within an exterior body formed of an exterior can 50, a sealing can 60, and a resin gasket 70 that is interposed between them.
  • the sealing can 60 fits into the opening of the exterior can 50 via a gasket 70, and the open end of the exterior can 50 is tightened inward, causing the gasket 70 to come into contact with the sealing can 60, sealing the opening of the exterior can 50 and creating an airtight structure inside the battery.
  • the outer can and the sealing can can be made of stainless steel or the like.
  • the gasket can be made of polypropylene, nylon, or other materials. If heat resistance is required for the battery's intended use, heat-resistant resins with melting points exceeding 240°C, such as fluororesins such as tetrafluoroethylene-perfluoroalkoxyethylene copolymer (PFA), polyphenylene ether (PPE), polysulfone (PSF), polyarylate (PAR), polyethersulfone (PES), polyphenylene sulfide (PPS), and polyetheretherketone (PEEK), can also be used. If the battery is used in an application that requires heat resistance, a glass hermetic seal can be used for the sealing.
  • PFA tetrafluoroethylene-perfluoroalkoxyethylene copolymer
  • PPE polyphenylene ether
  • PSF polysulfone
  • PAR polyarylate
  • PES polyethersulfone
  • PPS
  • the solid electrolyte layer 40 has a solid electrolyte layer (I) 41 having a porous substrate, a solid electrolyte layer (II) 42 joined to the positive electrode 20, and a solid electrolyte layer (III) 43 joined to the negative electrode 30.
  • the solid electrolyte sheet when forming an electrode body using a solid electrolyte sheet having a porous substrate, if the solid electrolyte sheet is bonded to the positive and negative electrodes by pressure molding, the bonding between the positive electrode (positive electrode mixture compact containing positive electrode active material or positive electrode mixture layer) and the negative electrode (negative electrode mixture compact containing negative electrode active material or negative electrode mixture layer) may be insufficient, or cracks may occur in the solid electrolyte sheet.
  • the solid electrolyte layer of the electrode body has a configuration having a solid electrolyte layer (I) containing a porous substrate and a solid electrolyte layer (II) and a solid electrolyte layer (III) arranged on both sides of the solid electrolyte layer (I), for example, a positive electrode having a solid electrolyte coating layer formed in advance on the solid electrolyte layer (I) side surface of the positive electrode mixture compact (positive electrode mixture layer) and a negative electrode having a solid electrolyte coating layer formed in advance on the solid electrolyte layer (I) side surface of the negative electrode mixture compact (negative electrode mixture layer) can be used, and the electrode body can be formed by pressing these coating layers on the solid electrolyte layer (I) side.
  • the solid electrolyte layer (II) and the solid electrolyte layer (III) are well bonded to the solid electrolyte layer (I), and excessive pressure on the solid electrolyte layer (I) (solid electrolyte sheet) can be avoided when applying pressure to form the electrode body.
  • the solid electrolyte layer of the all-solid-state battery is preferably such that the outer periphery of the solid electrolyte layer (I) protrudes from the ends of the positive and negative electrodes in a plan view of the electrode body (when viewed from above or below in FIG. 1), and the solid electrolyte layer (II) and the solid electrolyte layer (III) have a smaller area than the solid electrolyte layer (I) in a plan view.
  • the solid electrolyte layer (II) can be made to have an area equivalent to that of the positive electrode mixture compact (positive electrode mixture layer) of the positive electrode, and the solid electrolyte layer (III) can be made to have an area equivalent to that of the negative electrode mixture compact (negative electrode mixture layer) of the negative electrode. That is, the size of the solid electrolyte layer (II) can be made the same as that of the positive electrode (positive electrode mixture layer), and the size of the solid electrolyte layer (III) can be made the same as that of the negative electrode (negative electrode mixture layer).
  • the positive electrode mixture compact (positive electrode mixture layer) and the solid electrolyte layer (II), and the negative electrode mixture compact (negative electrode mixture layer) and the solid electrolyte layer (III) can be formed using a common mold (such as a metal mold), while the large-area solid electrolyte layer (I) can effectively prevent contact between the positive electrode and the negative electrode even if they are misaligned during assembly. Therefore, this action also makes it possible for the all-solid-state battery of the present invention to improve productivity and reliability.
  • the outer periphery of the solid electrolyte layer (I) protrudes from the ends of the positive electrode and the negative electrode over the entire circumference. In other words, it is preferable that the parts of the solid electrolyte layer (I) that protrude from the ends of the positive electrode and the negative electrode are formed in a ring shape.
  • the all-solid-state battery of the present invention includes primary batteries and secondary batteries.
  • Solid electrolyte layer (I) has a porous substrate, and at least a portion of the solid electrolyte constituting the solid electrolyte layer (I) is present in a state of being held inside the porous substrate.
  • the solid electrolyte layer (I) can be formed by using a solid electrolyte sheet obtained by filling the inside of a porous substrate with a solid electrolyte.
  • the porous substrate of the solid electrolyte sheet may be made of a fibrous material, such as woven fabric, nonwoven fabric, or mesh, with nonwoven fabric being the most preferred.
  • the fiber diameter of the fibrous material that constitutes the porous substrate is preferably 5 ⁇ m or less, and preferably 0.5 ⁇ m or more.
  • the material of the fibrous material is not particularly limited as long as it does not react with metallic lithium and has insulating properties.
  • resins such as polyolefins such as polypropylene and polyethylene; polystyrene; aramid; polyamide-imide; polyimide; nylon; polyesters such as polyethylene terephthalate (PET); polyarylate; cellulose and modified cellulose; etc.
  • Inorganic materials such as glass, alumina, silica, and zirconia may also be used.
  • a preferred material is polyarylate.
  • the fibrous material may be made of one or more of the materials listed above.
  • the porous substrate may be made of only fibrous materials of the same material, or may be made of a combination of two or more fibrous materials of different materials.
  • the basis weight of the porous substrate is preferably 10 g/m2 or less, and more preferably 8 g/ m2 or less , so as to hold a sufficient amount of solid electrolyte to ensure good lithium ion conductivity and good lithium dendrite growth inhibition function, and from the viewpoint of ensuring sufficient strength, is preferably 3 g/m2 or more, and more preferably 4 g/ m2 or more .
  • the solid electrolyte contained in the solid electrolyte sheet is not particularly limited as long as it has lithium ion conductivity.
  • sulfide-based solid electrolytes, hydride-based solid electrolytes, halide-based solid electrolytes, oxide-based solid electrolytes, etc. can be used.
  • Examples of sulfide-based solid electrolytes include particles of Li 2 S-P 2 S 5 , Li 2 S-SiS 2 , Li 2 S- P 2 S 5 -GeS 2 , and Li 2 S -B 2 S 3 based glass.
  • thio- LISICON type electrolytes which have been attracting attention in recent years for their high lithium ion conductivity , are also available .
  • M 2 is P or V
  • M 3 is Al
  • M 4 is Zn
  • M 5 is S or either S and O
  • X is F, Cl, Br or I, 0 ⁇ a ⁇ 3, 0 ⁇ b+c+d ⁇ 3, 0 ⁇ e ⁇ 3]
  • Examples of hydride-based solid electrolytes include LiBH 4 , solid solutions of LiBH 4 and the following alkali metal compounds (for example, those in which the molar ratio of LiBH 4 to the alkali metal compound is 1:1 to 20:1), etc.
  • Examples of the alkali metal compounds in the solid solutions include at least one selected from the group consisting of lithium halides (LiI, LiBr, LiF, LiCl, etc.), rubidium halides (RbI, RbBr, RbF, RbCl, etc.), cesium halides (CsI, CsBr, CsF, CsCl, etc.), lithium amide, rubidium amide, and cesium amide.
  • lithium halides LiI, LiBr, LiF, LiCl, etc.
  • rubidium halides RbI, RbBr, RbF, RbCl, etc.
  • cesium halides CsI, CsBr, CsF, Cs
  • Other known solid electrolytes that can be used include those described in, for example, WO 2020/070958 and WO 2020/070955.
  • oxide-based solid electrolytes examples include garnet-type Li 7 La 3 Zr 2 O 12 , NASICON-type Li 1+O Al 1+O Ti 2-O (PO 4 ) 3 and Li 1+p Al 1+p Ge 2-p (PO 4 ) 3 , and perovskite-type Li 3q La 2/3-q TiO 3 .
  • solid electrolyte only one of the above-mentioned examples may be used, or two or more may be used in combination.
  • sulfide-based solid electrolytes are preferred because of their high lithium ion conductivity, sulfide-based solid electrolytes containing Li and P are more preferred, and sulfide-based solid electrolytes having an argyrodite structure, which have particularly high lithium ion conductivity and high chemical stability, are even more preferred.
  • the solid electrolyte is preferably in the form of particles, and the size of the particles is preferably 5 ⁇ m or less, more preferably 2 ⁇ m or less, on average, from the viewpoint of improving the filling of the pores of the porous substrate and ensuring good lithium ion conductivity.
  • the size of the solid electrolyte particles is too small, there is a risk of reduced ease of handling.
  • the solid electrolyte particles are preferably bound with a binder in order to hold them well in the pores of the porous substrate and to adhere well to the surface of the porous substrate. In this case, however, a larger amount of binder is required, which may increase the resistance value. Therefore, the average particle size of the solid electrolyte particles is preferably 0.3 ⁇ m or more, more preferably 0.5 ⁇ m or more.
  • the average particle diameter of the solid electrolyte particles and other particles means the 50% diameter value (D50) in the volume-based integrated fraction when the integrated volume is determined from particles with small particle sizes using a particle size distribution measurement device (such as the Microtrack particle size distribution measurement device " HRA9320 " manufactured by Nikkiso Co., Ltd.).
  • the edges of the porous substrate may be exposed on the surface of the solid electrolyte sheet, but in this case, it is desirable that the solid electrolyte is exposed along with the edges of the porous substrate, in order to facilitate smoother movement of lithium ions between the positive and negative electrodes.
  • the surface of the solid electrolyte sheet and its vicinity may be composed only of the solid electrolyte (and a binder, etc., as described below), without the presence of a porous substrate.
  • the solid electrolyte sheet it is preferable to use a binder to bind the solid electrolyte, so as to maintain the solid electrolyte well within the pores of the porous substrate and to improve the adhesion of the solid electrolyte covering the surface of the porous substrate to the porous substrate, thereby improving the shape retention of the solid electrolyte sheet and also improving the adhesion to the solid electrolyte layer (II) and the solid electrolyte layer (III).
  • the binder for the solid electrolyte sheet is preferably one that does not react with the solid electrolyte, and at least one resin selected from the group consisting of butyl rubber, chloroprene rubber, acrylic resin, and fluororesin is preferably used.
  • the thickness of the solid electrolyte sheet is preferably 5 ⁇ m or more, more preferably 10 ⁇ m or more, from the viewpoint of optimizing the distance between the positive and negative electrodes of the battery using the solid electrolyte sheet and suppressing the occurrence of short circuits and increases in resistance, and is preferably 50 ⁇ m or less, more preferably 30 ⁇ m or less.
  • the thickness of the porous substrate is preferably 85% or less, and more preferably 80% or less, of the thickness of the solid electrolyte sheet, from the viewpoint of ensuring smooth movement of lithium ions on the positive electrode side and smooth movement of lithium ions on the negative electrode side, as well as better suppressing the precipitation of lithium dendrites that cause charging abnormalities, with the solid electrolyte covering the surface of the porous substrate having the above-mentioned thickness.
  • the porous substrate serves as a component for improving the shape retention of the solid electrolyte sheet, but if the ratio of the thickness of the porous substrate to the solid electrolyte sheet is too small, the shape retention of the solid electrolyte sheet may decrease. Furthermore, when the ratio of the thickness of the porous substrate to the solid electrolyte sheet is relatively large, the effect of smoothing the movement of lithium ions on the positive electrode side and the negative electrode side, as well as suppressing metal precipitation that causes charging abnormalities, becomes more pronounced. For these reasons, the thickness of the porous substrate is preferably 30% or more of the thickness of the solid electrolyte sheet, and more preferably 50% or more.
  • Specific thickness of the porous substrate is, for example, preferably 3 ⁇ m or more, more preferably 8 ⁇ m or more, and preferably 45 ⁇ m or less, more preferably 25 ⁇ m or less.
  • the proportion of the porous substrate in the solid electrolyte sheet is preferably 30% by volume or less, and more preferably 25% by volume or less, from the viewpoint of ensuring good lithium ion conductivity.
  • the proportion of the porous substrate in the solid electrolyte sheet is preferably 5% by volume or more, and more preferably 10% by volume or more.
  • the content of the binder in the solid electrolyte sheet is preferably 0.5 mass% or more, and more preferably 1 mass% or more, of the total amount of the solid electrolyte and binder, from the viewpoint of further improving the shape retention of the solid electrolyte sheet, and from the viewpoint of limiting the amount of the binder to some extent and suppressing the decrease in lithium ion conductivity, it is preferably 5 mass% or less, and more preferably 3 mass% or less.
  • the method for producing the solid electrolyte sheet it is preferable to produce it by a method that includes a step of dispersing the solid electrolyte and a binder used as necessary in a solvent to prepare a slurry for forming the solid electrolyte layer, and then filling the voids in the porous substrate with the slurries in a wet manner (filling step).
  • the voids in the porous substrate are filled with the slurries, while a coating of the slurries is formed on the surface of the porous substrate. This method improves the strength of the solid electrolyte sheet, making it easier to produce a large-area solid electrolyte sheet.
  • Screen printing, doctor blade, immersion, and other coating methods can be used to fill the voids in the porous substrate with a slurry containing a solid electrolyte, and to form a coating film of the slurry on the surface of the porous substrate.
  • the slurry is prepared by adding the solid electrolyte and, if necessary, a binder to a solvent and mixing them. It is preferable to select a solvent for the slurry that does not easily deteriorate the solid electrolyte.
  • a solvent for the slurry that does not easily deteriorate the solid electrolyte.
  • non-polar aprotic solvents such as hydrocarbon solvents such as hexane, heptane, octane, nonane, decane, decalin, toluene, and xylene.
  • an ultra-dehydrated solvent with a water content of 0.001 mass% (10 ppm) or less.
  • fluorine-based solvents such as “Vertrel (registered trademark)” manufactured by Mitsui DuPont Fluorochemicals, “Zeorolla (registered trademark)” manufactured by Nippon Zeon Co., Ltd., and “Novec (registered trademark)” manufactured by Sumitomo 3M Co., Ltd., as well as non-aqueous organic solvents such as dichloromethane and diethyl ether can also be used.
  • the solvent in the slurry is removed by drying, and a solid electrolyte sheet can be obtained by performing pressure molding as necessary.
  • the method for manufacturing the solid electrolyte sheet is not limited to the wet method.
  • the solid electrolyte or a mixture of the solid electrolyte and the binder may be filled in a dry manner, and then pressure molding may be performed.
  • a sheet obtained by molding the mixture of the solid electrolyte and the binder may be attached to the surface of a sheet in which the voids in the porous substrate are filled with the solid electrolyte.
  • the solid electrolyte layer (I) produced using the solid electrolyte sheet preferably has an outer periphery that protrudes from the positive electrode [positive electrode mixture compact (positive electrode mixture layer)] and the negative electrode [negative electrode mixture compact (negative electrode mixture layer)] in a plan view, and the width of the protruding portion [the length of the shortest distance from the end of the positive electrode mixture compact (positive electrode mixture layer) and the negative electrode mixture compact (negative electrode mixture layer) to the end of the solid electrolyte layer (I)] can be, for example, 1 ⁇ m to 1 mm.
  • Solid electrolyte layer (II) and solid electrolyte layer (III) contain a solid electrolyte.
  • Specific examples of the solid electrolyte include the same sulfide-based solid electrolyte, hydride-based solid electrolyte, halide-based solid electrolyte, and oxide-based solid electrolyte as those exemplified above for constituting the solid electrolyte layer (I).
  • solid electrolyte of the solid electrolyte layer (II) and the solid electrolyte layer (III) only one of the above-mentioned examples may be used, or two or more may be used in combination.
  • sulfide-based solid electrolytes are preferred because of their high lithium ion conductivity, sulfide-based solid electrolytes containing Li and P are more preferred, and sulfide-based solid electrolytes having an argyrodite structure, which have particularly high lithium ion conductivity and high chemical stability, are even more preferred.
  • the solid electrolyte contained in the solid electrolyte layer (I), the solid electrolyte contained in the solid electrolyte layer (II), and the solid electrolyte contained in the solid electrolyte layer (III) may be the same type in all layers, or the same type may be used in two of the three layers and a different type may be used in the remaining layer, or different types may be used in each layer.
  • the solid electrolyte contained in at least one of the solid electrolyte layers (II) and (III) may be a different type from the solid electrolyte contained in the solid electrolyte layer (I).
  • the solid electrolyte layer (II) and the solid electrolyte layer (III) may contain a binder.
  • the binder contained in the solid electrolyte layer (II) and the solid electrolyte layer (III) may be the same as the binder exemplified above as the binder that may be contained in the solid electrolyte layer (I).
  • the content is preferably 2 to 10 mass % (the remainder can be solid electrolyte).
  • the solid electrolyte layer (II) and the solid electrolyte layer (III) may not contain a binder, and may be formed, for example, only from a solid electrolyte (the binder content may be 0 mass %). Note that it is also possible to configure either one of the solid electrolyte layers (II) and (III) to contain no binder, and the other to contain a binder.
  • each of the solid electrolyte layer (II) and the solid electrolyte layer (III) is preferably 1 to 10 ⁇ m.
  • the thickness of the solid electrolyte layer (II) and the thickness of the solid electrolyte layer (III) may be the same or different.
  • the areas of the solid electrolyte layer (II) and the solid electrolyte layer (III) in a planar view can be smaller than the area of the solid electrolyte layer (I) in a planar view, and can be the same as, for example, the area of the positive electrode mixture compact (positive electrode mixture layer) and the area of the negative electrode mixture compact (negative electrode mixture layer).
  • the solid electrolyte layer (II) and the solid electrolyte layer (III) can be formed by arranging a solid electrolyte or the like in a layer on the surface of the solid electrolyte sheet, and then pressurizing the layer in a state in which the layer is overlaid with a positive electrode mixture compact (positive electrode mixture layer) or a negative electrode mixture compact (negative electrode mixture layer).
  • a previously formed positive electrode mixture compact (positive electrode mixture layer) or a negative electrode mixture compact (negative electrode mixture layer) as the base material, arrange a solid electrolyte or the like in a layer on one surface of the base material to cover one side with the solid electrolyte, and then pressurize the layer in a state in which the layer is overlaid with the solid electrolyte sheet.
  • the total thickness of the solid electrolyte layer [the total thickness of the solid electrolyte layer (I), the solid electrolyte layer (II) and the solid electrolyte layer (III)] is preferably 5 ⁇ m or more, more preferably 20 ⁇ m or more, and is preferably 100 ⁇ m or less, and more preferably 50 ⁇ m or less, from the viewpoint of optimizing the distance between the positive electrode and the negative electrode of the battery and suppressing the occurrence of a short circuit or an increase in resistance.
  • Examples of the positive electrode of the all-solid-state battery include a structure in which a layer (positive electrode mixture layer) made of a molded body of a positive electrode mixture containing a positive electrode active material and a solid electrolyte is formed on a current collector, a structure made of only a molded body of a positive electrode mixture (pellets, etc.), and a structure in which a positive electrode mixture containing a positive electrode active material and a solid electrolyte is filled into the pores of a conductive porous substrate.
  • the positive electrode active material can be the same as the positive electrode active material used in conventionally known non-aqueous electrolyte primary batteries.
  • manganese dioxide, lithium-containing manganese oxide e.g., LiMn 3 O 6 , or a composite oxide having the same crystal structure as manganese dioxide ( ⁇ -type, ⁇ -type, or a structure in which ⁇ -type and ⁇ -type are mixed, etc.
  • lithium-containing composite oxide such as Li a Ti 5/3 O 4 (4/3 ⁇ a ⁇ 7/3); vanadium oxide; niobium oxide; titanium oxide; sulfides such as iron disulfide; graphite fluoride; silver sulfides such as Ag 2 S; nickel oxides such as NiO 2 ; and the like.
  • the positive electrode active material may be the same as the positive electrode active material used in conventionally known non-aqueous electrolyte secondary batteries, etc.
  • a spinel-type lithium manganese composite oxide represented by LiMrMn2-rO4 (wherein M is at least one element selected from the group consisting of Li, Na, K, B, Mg, Ca, Sr, Ba, Ti, V, Cr, Zr, Fe, Co, Ni, Cu, Zn, Al, Sn, Sb, In, Nb, Ta, Mo, W, Y, Ru , and Rh, and 0 ⁇ r ⁇ 1)
  • LirMn (1-s-r) NisMtO (2-u) Fv a layered compound represented by LiCo 1-r M r O 2 (wherein M is at least one element selected from the group consisting of Co, Mg, Al, B, Ti, V, Cr, Fe, Cu, Zn, Zr, Mo, Sn,
  • the average particle size of the positive electrode active material is preferably 1 ⁇ m or more, more preferably 2 ⁇ m or more, and preferably 10 ⁇ m or less, more preferably 8 ⁇ m or less.
  • the positive electrode active material may be either primary particles or secondary particles formed by agglomeration of primary particles.
  • the positive electrode active material has a reaction suppression layer on its surface to suppress reaction with the solid electrolyte contained in the positive electrode.
  • the solid electrolyte may oxidize and form a resistive layer, which may reduce the ionic conductivity in the positive electrode.
  • the reaction suppression layer may be made of a material that has ion conductivity and can suppress the reaction between the particles of the electrode active material (positive electrode active material) and the solid electrolyte.
  • materials that can form the reaction suppression layer include oxides containing Li and at least one element selected from the group consisting of Nb, P, B, Si, Ge, Ti, Zr, Ta and W, more specifically, Nb-containing oxides such as LiNbO 3 , Li 3 PO 4 , Li 3 BO 3 , Li 2 SO 4 , Li 4 SiO 4 , Li 4 GeO 4 , LiTiO 3 , LiZrO 3 , Li 2 WO 4 and the like.
  • the reaction suppression layer may contain only one of these oxides, or may contain two or more of them, and further, a plurality of these oxides may form a composite compound.
  • these oxides it is preferable to use an Nb-containing oxide, and it is more preferable to use LiNbO3 .
  • the reaction suppression layer is preferably present on the surface in an amount of 0.1 to 1.0 parts by mass per 100 parts by mass of the positive electrode active material. This range allows for good suppression of the reaction between the positive electrode active material and the solid electrolyte.
  • Methods for forming a reaction suppression layer on the surface of the positive electrode active material include the sol-gel method, mechanofusion method, CVD method, PVD method, and ALD method.
  • the content of the positive electrode active material in the positive electrode mixture is preferably 60 to 85 mass % in order to increase the energy density of the all-solid-state battery.
  • the positive electrode mixture can contain a conductive assistant.
  • a conductive assistant include carbon materials such as graphite (natural graphite, artificial graphite), graphene, carbon black, carbon nanofibers, and carbon nanotubes.
  • carbon materials such as graphite (natural graphite, artificial graphite), graphene, carbon black, carbon nanofibers, and carbon nanotubes.
  • the conductive assistant when the conductive assistant is contained in the positive electrode mixture, the content is preferably 1.0 parts by mass or more, preferably 7.0 parts by mass or less, and more preferably 6.5 parts by mass or less, when the content of the positive electrode active material is 100 parts by mass.
  • the positive electrode mixture may contain a binder.
  • a binder is a fluororesin such as polyvinylidene fluoride (PVDF).
  • PVDF polyvinylidene fluoride
  • the positive electrode mixture may not contain a binder if good moldability can be ensured in forming the positive electrode without using a binder, such as when a sulfide-based solid electrolyte is contained in the positive electrode mixture (described later).
  • the positive electrode mixture requires a binder, its content is preferably 15% by mass or less, and more preferably 0.5% by mass or more. On the other hand, if the positive electrode mixture is moldable without a binder, its content is preferably 0.5% by mass or less, more preferably 0.3% by mass or less, and even more preferably 0% by mass (i.e., no binder is included).
  • the positive electrode mixture can contain a solid electrolyte.
  • the solid electrolyte contained in the positive electrode mixture is not particularly limited as long as it has lithium ion conductivity.
  • the sulfide-based solid electrolyte, hydride-based solid electrolyte, halide-based solid electrolyte, oxide-based solid electrolyte, etc., exemplified above as those usable in the solid electrolyte layer of the solid electrolyte sheet, can be used.
  • the average particle size of the solid electrolyte is preferably 0.1 ⁇ m or more, and more preferably 0.2 ⁇ m or more, from the viewpoint of reducing grain boundary resistance, while it is preferably 10 ⁇ m or less, and more preferably 5 ⁇ m or less, from the viewpoint of forming a sufficient contact interface between the active material and the solid electrolyte.
  • the content of the solid electrolyte in the positive electrode mixture is preferably 10 parts by mass or more, and more preferably 15 parts by mass or more, when the content of the positive electrode active material is 100 parts by mass.
  • the content of solid electrolyte in the positive electrode mixture is preferably 65 parts by mass or less, and more preferably 60 parts by mass or less, when the content of the positive electrode active material is 100 parts by mass.
  • the current collector can be a metal foil such as aluminum or stainless steel; a sheet-like conductive porous substrate such as punched metal, net, expanded metal, or foamed metal; or a carbon sheet.
  • a foamed metal porous body As the sheet-like conductive porous substrate, it is preferable to use a foamed metal porous body.
  • a specific example of a foamed metal porous body is "Celmet (registered trademark)" by Sumitomo Electric Industries, Ltd.
  • the positive electrode can be manufactured by applying a positive electrode mixture-containing composition (paste, slurry, etc.) made by dispersing a positive electrode active material and a solid electrolyte, as well as conductive additives and binders, which are added as necessary, in a solvent, to a current collector, drying the composition, and then, if necessary, subjecting the composition to pressure molding, such as calendaring, to form a positive electrode mixture compact (positive electrode mixture layer) on the surface of the current collector.
  • a positive electrode mixture-containing composition paste, slurry, etc.
  • a positive electrode active material and a solid electrolyte as well as conductive additives and binders, which are added as necessary, in a solvent
  • NMP N-methyl-2-pyrrolidone
  • the positive electrode mixture compact may be formed by compressing the positive electrode mixture prepared by mixing the positive electrode active material and solid electrolyte with conductive additives and binders, which are added as necessary, by pressure molding or the like.
  • the positive electrode mixture compact obtained by such a method can be used as a positive electrode as is, as described above, or it can be used as a positive electrode after being bonded to a current collector by pressing or the like.
  • the thickness of the positive electrode mixture compact (positive electrode mixture layer) formed using the solvent-containing positive electrode mixture-containing composition is preferably 10 to 1000 ⁇ m.
  • the thickness of the positive electrode mixture compact obtained by pressure molding is preferably 0.15 to 4 mm.
  • the thickness of the positive electrode current collector is preferably 0.01 to 0.1 mm.
  • the positive electrode can be manufactured, for example, by filling the pores of the conductive porous substrate with the positive electrode mixture-containing composition, drying it, and then, if necessary, subjecting it to pressure molding such as calendaring.
  • a positive electrode mixture that does not contain a solvent and contains a positive electrode active material, a solid electrolyte, a conductive assistant, a binder, etc., may be dry-filled into the pores of a conductive porous substrate, and the positive electrode may be pressure-molded, such as by calendaring, as necessary, to produce a positive electrode.
  • the thickness is preferably 30 to 4000 ⁇ m.
  • the negative electrode of the all-solid-state battery has, for example, a molded body of a negative electrode mixture containing a negative electrode active material, a lithium sheet, or a lithium alloy sheet. Also, a conductive porous substrate having a negative electrode mixture containing a negative electrode active material filled in its pores can be used as the negative electrode.
  • examples include a structure in which a layer of a molded product of the negative electrode mixture (negative electrode mixture layer) is formed on a current collector, and a structure consisting only of a molded product of the negative electrode mixture (such as a pellet).
  • negative electrode active materials include carbon materials such as graphite, lithium titanium oxides (lithium titanate, etc.), simple substances containing elements such as Si and Sn, compounds (oxides, etc.), and alloys thereof. Lithium metal and lithium alloys (lithium-aluminum alloy, lithium-indium alloy, etc.) can also be used as negative electrode active materials.
  • the content of the negative electrode active material in the negative electrode mixture is preferably 40 to 80 mass % in order to increase the energy density of the battery.
  • the negative electrode mixture may contain a conductive additive. Specific examples include the same conductive additives as those exemplified above as those that may be contained in the positive electrode mixture.
  • the content of the conductive additive in the negative electrode mixture is preferably 10 to 30 parts by mass when the content of the negative electrode active material is 100 parts by mass.
  • the negative electrode mixture may contain a binder.
  • a binder Specific examples include the same binders as those exemplified above as those that may be contained in the positive electrode mixture. Note that, for example, in the case where the negative electrode mixture contains a sulfide-based solid electrolyte (described later), if good moldability can be ensured in forming the negative electrode mixture layer without using a binder, the negative electrode mixture may not need to contain a binder.
  • the negative electrode mixture requires a binder, its content is preferably 15% by mass or less, and more preferably 0.5% by mass or more. On the other hand, if the negative electrode mixture is moldable without a binder, its content is preferably 0.5% by mass or less, more preferably 0.3% by mass or less, and even more preferably 0% by mass (i.e., no binder is included).
  • the negative electrode mixture can contain a solid electrolyte.
  • a solid electrolyte Specific examples include the same solid electrolytes as those exemplified above as those that can be contained in the positive electrode mixture.
  • it is preferable to use a sulfide-based solid electrolyte since it has high lithium ion conductivity and also has the function of increasing the moldability of the negative electrode mixture, and it is even more preferable to use a sulfide-based solid electrolyte with an argyrodite-type crystal structure.
  • the average particle size of the solid electrolyte in the negative electrode mixture is preferably 0.1 ⁇ m or more, more preferably 0.2 ⁇ m or more, and is preferably 10 ⁇ m or less, more preferably 5 ⁇ m or less.
  • the content of the solid electrolyte in the negative electrode mixture is preferably 30 parts by mass or more, and more preferably 35 parts by mass or more, when the content of the negative electrode active material is 100 parts by mass.
  • the content of solid electrolyte in the negative electrode mixture is preferably 130 parts by mass or less, and more preferably 110 parts by mass or less, when the content of the negative electrode active material is 100 parts by mass.
  • the current collector can be a sheet-like conductive porous substrate such as copper or nickel foil, punched metal, net, expanded metal, or foamed metal; or a carbon sheet; etc.
  • the sheet-like conductive porous substrate it is preferable to use a foamed metal porous body.
  • a specific example of a foamed metal porous body is "Celmet (registered trademark)" by Sumitomo Electric Industries, Ltd.
  • the negative electrode can be manufactured by applying a negative electrode mixture-containing composition (paste, slurry, etc.) made by dispersing the negative electrode active material, and optionally added conductive additives, solid electrolyte, binder, etc., in a solvent onto a current collector, drying the composition, and then, if necessary, subjecting the composition to pressure molding such as calendaring to form a compact of the negative electrode mixture (negative electrode mixture layer) on the surface of the current collector.
  • a negative electrode mixture-containing composition paste, slurry, etc.
  • conductive additives solid electrolyte, binder, etc.
  • Water or an organic solvent such as NMP can be used as the solvent for the negative electrode mixture-containing composition, but when the negative electrode mixture-containing composition also contains a solid electrolyte, it is desirable to select a solvent that is unlikely to deteriorate the solid electrolyte, and it is preferable to use the same solvents as those exemplified above for the solvent of the slurry for forming the solid electrolyte sheet.
  • the negative electrode mixture compact may be formed by compressing the negative electrode mixture prepared by mixing the negative electrode active material, and optionally the conductive additive, solid electrolyte, and binder, by pressure molding or the like.
  • the negative electrode mixture compact obtained by such a method can be used as it is as a negative electrode, or it can be bonded to a current collector by pressing, etc., and used as a negative electrode.
  • the thickness of the negative electrode mixture compact (negative electrode mixture layer) formed using the solvent-containing negative electrode mixture-containing composition is preferably 10 to 1000 ⁇ m.
  • the thickness of the negative electrode mixture compact obtained by pressure molding is preferably 0.15 to 4 mm.
  • the thickness of the negative electrode current collector is preferably 0.01 to 0.1 mm.
  • the negative electrode when a conductive porous substrate such as a punched metal is used for the negative electrode current collector, the negative electrode can be manufactured, for example, by filling the pores of the conductive porous substrate with the above-mentioned negative electrode mixture-containing composition, drying, and then, if necessary, performing pressure molding such as calendaring.
  • a negative electrode manufactured in this manner can ensure high strength, making it possible to hold a solid electrolyte sheet with a larger area.
  • a negative electrode mixture that does not contain a solvent and contains a negative electrode active material, a solid electrolyte, a binder, a conductive assistant, etc., may be dry-filled into the pores of a conductive porous substrate, and the negative electrode may be produced by a method of pressure molding such as calendaring as necessary.
  • the thickness is preferably 30 to 4000 ⁇ m.
  • negative electrodes having lithium or lithium alloy sheets those consisting of these sheets alone or those consisting of these sheets bonded to a current collector are used.
  • Alloying elements for lithium alloys include aluminum, lead, bismuth, indium, and gallium, with aluminum and indium being preferred.
  • the proportion of alloying elements in the lithium alloy is preferably 50 atomic % or less (in this case, the remainder is lithium and unavoidable impurities).
  • a laminate in which a layer containing an alloying element for forming a lithium alloy is laminated on the surface of a lithium layer (layer containing lithium) composed of metallic lithium foil or the like, for example by pressing the layer, and the laminate is brought into contact with a solid electrolyte in a battery to form a lithium alloy on the surface of the lithium layer, thereby forming a negative electrode.
  • a laminate having a layer containing an alloying element on only one side of the lithium layer may be used, or a laminate having layers containing an alloying element on both sides of the lithium layer may be used.
  • the laminate can be formed, for example, by pressing metallic lithium foil and a foil composed of an alloying element.
  • the current collector can also be used when forming a lithium alloy inside the battery to form the negative electrode.
  • a laminate having a lithium layer on one side of the negative electrode current collector and a layer containing an alloying element on the side of the lithium layer opposite the negative electrode current collector may be used, or a laminate having lithium layers on both sides of the negative electrode current collector and each lithium layer having a layer containing an alloying element on the side opposite the negative electrode current collector may be used.
  • the negative electrode current collector and the lithium layer may be laminated by crimping or the like.
  • the layer containing the alloying elements in the laminate to be used as the negative electrode can be, for example, a foil composed of these alloying elements.
  • the thickness of the layer containing the alloying elements is preferably 1 ⁇ m or more, more preferably 3 ⁇ m or more, and is preferably 20 ⁇ m or less, and more preferably 12 ⁇ m or less.
  • the lithium layer of the laminate to be used as the negative electrode can be, for example, metallic lithium foil.
  • the thickness of the lithium layer is preferably 0.1 to 1.5 mm.
  • the thickness of the sheet for the negative electrode having a lithium or lithium alloy sheet is also preferably 0.1 to 1.5 mm.
  • the current collector can be the same as the current collectors exemplified above as those usable for the negative electrode having a molded negative electrode mixture.
  • the positive electrode and the negative electrode can be used in a battery in the form of a laminated electrode body in which the positive electrode and the negative electrode are laminated with a solid electrolyte layer interposed therebetween, or in the form of a wound electrode body in which this laminated electrode body is wound.
  • a method can be adopted in which a positive electrode having a solid electrolyte coating layer formed on the surface of a positive electrode mixture compact (positive electrode mixture layer) and a negative electrode having a solid electrolyte coating layer formed on the surface of a negative electrode mixture compact (negative electrode mixture layer) are used, and these are stacked and pressure molded with a solid electrolyte sheet for forming the solid electrolyte layer (I) so that the solid electrolyte coating layers formed on the surfaces of the positive electrode mixture compact and the negative electrode mixture compact are on the solid electrolyte sheet side.
  • the coating layer may be formed to a thickness of, for example, 5 to 30 ⁇ m.
  • the form of the all-solid-state battery is not limited to one having an exterior body composed of an exterior can, a sealing can, and a gasket as shown in FIG. 1 , that is, one generally referred to as a coin-type battery or a button-type battery, and may be, for example, one having an exterior body composed of a resin film or a metal-resin laminate film, one having an exterior body having a metallic, bottomed, tubular (cylindrical or rectangular) exterior can and a sealing structure that seals the opening, or one having a box-shaped exterior body made of ceramics.
  • Example 1 Using xylene ("ultra-dehydrated” grade) with a moisture content of 0.001% by mass (10 ppm) or less, a sulfide-based solid electrolyte (Li6PS5Cl ) with an average particle size of 1.0 ⁇ m, an acrylic resin binder, and a dispersant were mixed in a mass ratio of 100:3:1 with a solid content of 40%, and the mixture was stirred for 10 minutes with a Thinky mixer to prepare a uniform slurry.
  • a PET nonwoven fabric having a thickness of 40 ⁇ m and a basis weight of 8 g/ m2 was used as the porous substrate.
  • the nonwoven fabric was passed through the slurry and pulled up, and then vacuum dried at 120° C. for 1 hour to prepare a solid electrolyte sheet having a thickness of 42 ⁇ m.
  • the solid electrolyte sheet was punched into a circular shape and used to assemble an all-solid-state battery.
  • a negative electrode mixture was prepared by mixing lithium titanate (Li 4 Ti 5 O 12 , negative electrode active material) having an average particle size of 2 ⁇ m, a sulfide-based solid electrolyte (Li 6 PS 5 Cl) having an average particle size of 0.7 ⁇ m, and graphene (conductive additive) in a mass ratio of 50:41:9.
  • the negative electrode mixture was placed in a powder molding die and pressure-molded using a press to produce a negative electrode molded body. Furthermore, a sulfide-based solid electrolyte (Li 6 PS 5 Cl) having an average particle size of 0.7 ⁇ m was placed on the upper surface of the negative electrode molded body, and pressure molding was performed using a press at a surface pressure of 70 MPa to form a provisionally molded layer (coating layer) of the solid electrolyte having a thickness of 10 ⁇ m.
  • a sulfide-based solid electrolyte Li 6 PS 5 Cl
  • LiCoO 2 positive electrode active material
  • LiNbO 3 coating layer formed on the surface LiNbO 3
  • a sulfide-based solid electrolyte Li 6 PS 5 Cl
  • graphene were mixed in a mass ratio of 65:30.7:4.3 to prepare a positive electrode mixture.
  • the positive electrode mixture was placed in a powder molding die and pressure-molded using a press to produce a positive electrode molded body. Furthermore, a sulfide-based solid electrolyte (Li 6 PS 5 Cl) having an average particle size of 0.7 ⁇ m was placed on the upper surface of the positive electrode molded body, and pressure molding was performed using a press at a surface pressure of 70 MPa to form a provisionally molded layer (coating layer) of the solid electrolyte having a thickness of 10 ⁇ m.
  • a sulfide-based solid electrolyte Li 6 PS 5 Cl
  • pressure molding was performed using a press at a surface pressure of 70 MPa to form a provisionally molded layer (coating layer) of the solid electrolyte having a thickness of 10 ⁇ m.
  • the solid electrolyte layer (II) joined to the positive electrode was the same size as the positive electrode in a plan view
  • the solid electrolyte layer (III) joined to the negative electrode was the same size as the negative electrode in a plan view
  • the solid electrolyte sheet [solid electrolyte layer (I)] was sized to extend 2 mm around the positive electrode and the negative electrode.
  • the total thickness of the solid electrolyte layer was 31 ⁇ m, and the thicknesses of the solid electrolyte layers (I), (II), and (III) were 25 ⁇ m, 3 ⁇ m, and 3 ⁇ m, respectively.
  • the electrode body was enclosed in a battery container consisting of an outer can and a sealing can to produce an all-solid-state battery.
  • Graphite sheets were placed between the electrode body and the outer can and between the electrode body and the sealing can.
  • Example 1 An electrode body was produced in the same manner as in Example 1, except that a provisionally molded layer (coating layer) of the solid electrolyte was not formed on the positive electrode and the negative electrode, and the negative electrode molded body and the positive electrode molded body were in direct contact with the solid electrolyte sheet.
  • the electrode body was used to fabricate an all-solid-state battery in the same manner as in Example 1.
  • Example 1 After charging and discharging the batteries of Example 1 and Comparative Example 1, the AC impedance was measured at 1 kHz with an applied voltage of 10 mV. The results are shown in Table 1.
  • Example 1 As shown in Table 1, in Example 1, the bonding between the positive and negative electrodes in the electrode body and the solid electrolyte layer was good, and the internal resistance of the battery was low, but in Comparative Example 1, the bonding between the positive and negative electrodes in the electrode body and the solid electrolyte layer was insufficient, and the internal resistance of the battery was high.
  • the all-solid-state battery of the present invention can be used in the same applications as conventionally known primary and secondary batteries, but because it has a solid electrolyte instead of an organic electrolyte, it has excellent heat resistance and can be preferably used in applications where it is exposed to high temperatures.

Landscapes

  • Secondary Cells (AREA)
PCT/JP2024/020301 2023-06-05 2024-06-04 全固体電池およびその製造方法 Ceased WO2024253075A1 (ja)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2025526110A JPWO2024253075A1 (https=) 2023-06-05 2024-06-04

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2023092577 2023-06-05
JP2023-092577 2023-06-05

Publications (1)

Publication Number Publication Date
WO2024253075A1 true WO2024253075A1 (ja) 2024-12-12

Family

ID=93796005

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2024/020301 Ceased WO2024253075A1 (ja) 2023-06-05 2024-06-04 全固体電池およびその製造方法

Country Status (2)

Country Link
JP (1) JPWO2024253075A1 (https=)
WO (1) WO2024253075A1 (https=)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000251938A (ja) * 1999-02-25 2000-09-14 Kyocera Corp 全固体リチウム電池の製造方法
JP2014086303A (ja) * 2012-10-24 2014-05-12 Kyocera Corp 二次電池およびその製造方法
JP2022144855A (ja) * 2021-03-19 2022-10-03 本田技研工業株式会社 全固体電池及び全固体電池の製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000251938A (ja) * 1999-02-25 2000-09-14 Kyocera Corp 全固体リチウム電池の製造方法
JP2014086303A (ja) * 2012-10-24 2014-05-12 Kyocera Corp 二次電池およびその製造方法
JP2022144855A (ja) * 2021-03-19 2022-10-03 本田技研工業株式会社 全固体電池及び全固体電池の製造方法

Also Published As

Publication number Publication date
JPWO2024253075A1 (https=) 2024-12-12

Similar Documents

Publication Publication Date Title
JP7538195B2 (ja) 固体電解質シートの製造方法、および全固体リチウム二次電池の製造方法
JP7579643B2 (ja) 全固体リチウム二次電池及びその製造方法
JP7345263B2 (ja) 全固体リチウム二次電池の製造方法
CN115699356B (zh) 全固体二次电池用负极、其制造方法和全固体二次电池
WO2024237330A1 (ja) 固体電解質シートおよび全固体電池
JPWO2024237330A5 (https=)
US20240387947A1 (en) All-solid-state battery
JP7657576B2 (ja) 全固体電池用正極および全固体電池
CN116490992B (zh) 全固体二次电池用负极及全固体二次电池
JP7712778B2 (ja) 全固体電池
WO2023189693A1 (ja) 電池およびその製造方法
JP7713760B2 (ja) 全固体電池
WO2024253075A1 (ja) 全固体電池およびその製造方法
JP7830494B2 (ja) 全固体電池
JP7776284B2 (ja) 全固体電池
JP7840764B2 (ja) 全固体電池
US20250118794A1 (en) Battery
JP7576400B2 (ja) 全固体二次電池用正極および全固体二次電池
JP2020149867A (ja) 全固体リチウム二次電池およびその製造方法
WO2024101355A1 (ja) 全固体電池
JP2024131954A (ja) 全固体電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24819305

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2025526110

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE