WO2024128209A1 - フォトレジスト除去用組成物およびフォトレジストの除去方法 - Google Patents

フォトレジスト除去用組成物およびフォトレジストの除去方法 Download PDF

Info

Publication number
WO2024128209A1
WO2024128209A1 PCT/JP2023/044366 JP2023044366W WO2024128209A1 WO 2024128209 A1 WO2024128209 A1 WO 2024128209A1 JP 2023044366 W JP2023044366 W JP 2023044366W WO 2024128209 A1 WO2024128209 A1 WO 2024128209A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
photoresist
copper
mass
pattern
Prior art date
Application number
PCT/JP2023/044366
Other languages
English (en)
French (fr)
Inventor
伸也 黒澤
和志 杉本
昌彌 曽根
聡 玉井
欣樹 宮下
Original Assignee
三菱瓦斯化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱瓦斯化学株式会社 filed Critical 三菱瓦斯化学株式会社
Publication of WO2024128209A1 publication Critical patent/WO2024128209A1/ja

Abstract

本発明によれば、銅を含むパターンを形成するためのフォトレジストを、前記パターンの形成後に除去するための組成物であって、　アルカノールアミン、第４級アンモニウムヒドロキシド、および無機アルカリからなる群から選択される少なくとも１種を含む、アルカリ剤、　ハンセン溶解度パラメータの座標が、δｄ＝１６．０、δｐ＝８．７、δｈ＝１５．５を中心とする半径３．６０ＭＰａ０．５以内の球の範囲内にある有機溶剤、及び、　アゾール化合物を含む、組成物を提供することができる。

Description

フォトレジスト除去用組成物およびフォトレジストの除去方法
　本発明は、フォトレジスト除去用組成物、それを用いるフォトレジストの除去方法などに関するものである。
　近年、電子デバイスの小型化、高機能化が進んでおり、当該電子デバイスに用いられるプリント配線板においても、小型化、高機能化が求められている。
　このような要望を満たすためのプリント配線板などを製造するために、以下のような方法が採用されている。例えば、銅配線を一部に有する絶縁層上にシード層と呼ばれる金属層を形成し、その表面にフォトレジスト層を形成し、露光現像してレジストパターンを形成したのち、パターン開口部に銅メッキを施し、次いで、フォトレジストおよびシード層を除去して銅配線の接続端子部となる回路パターンを形成する方法である。
　上述のように、プリント配線板などの製造方法においては、フォトレジストを除去する工程が含まれることが多く、フォトレジスト除去工程では、通常、様々な成分を有する水溶液が使用されている（特許文献１など）。
国際公開第２０２０／０２２４９１号
　従来のプリント配線板などの製造工程において、フォトレジストの除去が迅速かつ十分に行われない場合があった。フォトレジストを迅速かつ確実に除去させることが可能であれば、プリント配線板の生産性が向上しうる。
　また、フォトレジストを除去する工程において、従来の処理液が用いられると、銅メッキなどの最終的に必要とされる部材にダメージが与えられてしまう可能性もあった。
　以上のことから、例えばプリント配線板などの製造工程の一環としてフォトレジストを除去する性能に優れているとともに、銅メッキなどの銅を含む部材を確実に保護できる手段が求められている。
　本発明は、例えば、以下の態様を含む。
［１］銅を含むパターンを形成するためのフォトレジストを、前記パターンの形成後に除去するための組成物であって、
　アルカノールアミン、第４級アンモニウムヒドロキシド、および無機アルカリからなる群から選択される少なくとも１種を含む、アルカリ剤と、
　ハンセン溶解度パラメータの座標が、δｄ＝１６．０、δｐ＝８．７、δｈ＝１５．５を中心とする半径３．６０ＭＰａ０．５以内の球の範囲内にある有機溶剤と、
　アゾール化合物と、
を含む、組成物。
［２］前記有機溶剤のハンセン溶解度パラメータの座標が、δｄ＝１６．０、δｐ＝８．７、δｈ＝１５．５を中心とする半径３．００ＭＰａ０．５以内の球の範囲内にある、上記［１］に記載の組成物。
［３］前記有機溶剤が、エチレングリコールモノメチルエーテル、メチルヒドラジン、２，２，２－トリフルオロエタノール、ジアセチン、１－クロロ－２－プロパノール、ジメチルアミノエタノール、エチレンジアミン、１，９－ノナンジオール、２－ブロモアリルアルコール、２，３－ジクロロプロパノール、フルフリルアルコール、アジピン酸、エチレンクロロヒドリン、Ｎ－ホルミルエチルアミン、エチレングリコールモノプロピルエーテル、２－クロロ－２－プロペン－１－オール、１－（２－ヒドロキシエチル）－２－ピロリドン、ジエチレングリコールモノビニルエーテル、ジエチレントリアミン、１，３－ジクロロ－２－プロパノール、２－エトキシエタノール、３－クロロ－２－プロペン－１－オール、セロトニン、１，６－ヘキサンジオール、２－シクロペンテン－１－オール、メチルアミン、ギ酸、エチレングリコールモノイソプロピルエーテル、３－アジドプロペン、２，３－ブタジエン－１－オール、アリルアルコール、２－フルオロプロペン酸、酢酸、アジドエタン、イソシアン酸、ｎ－プロパノール、（Ｅ）－２－ブテン－１－オール、サリチル酸メチル、２－プロパノール、Ｌ－（－）－チロシン、ジプロピレングリコール、カルバミン酸エチル、および２，２－ジメチル－１－プロパノールからなる群から選択される少なくとも１種を含む、上記［１］に記載の組成物。
［４］銅のエッチングレートが、０．０５μｍ／ｍｉｎ未満である、上記［１］に記載の組成物。
［５］水溶性である、上記［１］に記載の組成物。
［６］前記組成物が、前記組成物の全量基準で、
　３．０～５０質量％の前記アルカリ剤、
　０．１～３０質量％の前記有機溶剤、及び、
　０．００１～１．０質量％の前記アゾール化合物を含む、
上記［１］に記載の組成物。
［７］前記パターンが、銅配線を少なくとも一部に有する絶縁層上に形成される前記銅配線の接続端子部となる回路パターンである、上記［１］に記載の組成物。
［８］銅を含むパターンを形成するためのフォトレジストに対して、上記［１］～［７］のいずれか１項に記載の組成物を接触させるフォトレジスト除去工程を含む、フォトレジストの除去方法。
［９］前記パターンが、銅配線を少なくとも一部に有する絶縁層上に形成される前記銅配線の接続端子部となる回路パターンである、上記［８］に記載のフォトレジストの除去方法。
［１０］銅を含むパターンを形成するためのフォトレジストに対して、上記［１］～［７］のいずれか１項に記載の組成物を接触させるフォトレジスト除去工程を含む、プリント配線板、半導体素子、又は半導体パッケージの製造方法。
［１１］前記パターンが、銅配線を少なくとも一部に有する絶縁層上に形成される前記銅配線の接続端子部となる回路パターンである、上記［１０］に記載のプリント配線板、半導体素子、又は半導体パッケージの製造方法。
　本発明によれば、フォトレジストを効率的に除去することができ、プリント配線板における銅メッキなどの銅を含む部材を確実に保護できるフォトレジスト除去用組成物等が提供される。
　本発明の組成物は、銅を含むパターンの形成後にフォトレジストを除去するために好適に用いられ、少なくとも、所定のアルカリ剤、有機溶剤及びアゾール化合物を含む。以下、組成物について詳細に説明する。
［Ｉ．組成物］
　組成物は、水溶性であることが好ましい。すなわち、組成物の少なくとも一部が水に溶解可能、あるいは懸濁可能であることが好ましく、任意の割合で水と均一に混合可能であることがより好ましい。
　また、組成物に含まれる水以外の成分の少なくとも一部が水に対して溶解可能であることが好ましく、組成物に含まれる水以外の成分と水とが均一に混合され得ることがより好ましい。
＜Ｉ－１．（Ａ）アルカリ剤＞
　組成物は、その合計質量を基準として、３．０～５０質量％の（Ａ）アルカリ剤（以下、成分（Ａ）ともいう）を含むことが好ましい。組成物におけるアルカリ剤の含有量は、組成物の全量基準で、４．０～４０質量％であることがより好ましく、５．０～３０質量％あるいは６．０～３５質量％であることがさらに好ましく、７．０～１５質量％、８．０～２０質量％あるいは９．０～１２質量％などであることが特に好ましい。
　成分（Ａ）を含む組成物において、フォトレジストの除去性を良好なものとし、また、銅配線の接続端子部となる銅、銅合金などを含む回路パターンのダメージを抑制する効果が認められる。
　（Ａ）アルカリ剤は、（Ａ－１）アルカノールアミン、（Ａ－２）第４級アンモニウムヒドロキシド及び（Ａ－３）無機アルカリの少なくともいずれかを含むことが好ましく、これらのうちの２種類を含むことがより好ましく、（Ａ－１）～（Ａ－３）をいずれも含むことが特に好ましい。
　（Ａ－１）アルカノールアミン
　組成物に成分（Ａ）として含まれ得る（Ａ－１）アルカノールアミンの種類は、特に限定されるものではないが、モノアルカノールアミン、ジアルカノールアミン、トリアルカノールアミン、およびこれらのアルキル化物（Ｎ－アルキル化物、Ｏ－アルキル化物）が挙げられる。
　アルカノールアミン（Ａ）としては、例えば、２－アミノエタノール（モノエタノールアミン）、Ｎ－メチルエタノールアミン、Ｎ－エチルエタノールアミン、Ｎ－プロピルエタノールアミン、Ｎ－ブチルエタノールアミン、ジエタノールアミン、１－アミノ－２－プロパノール（イソプロパノールアミン）、Ｎ－メチルイソプロパノールアミン、Ｎ－エチルイソプロパノールアミン、Ｎ－プロピルイソプロパノールアミン、２－アミノプロパン－１－オール、Ｎ－メチル－２－アミノ－プロパン－１－オール、Ｎ－エチル－２－アミノ－プロパン－１－オール、１－アミノプロパン－３－オール、Ｎ－メチル－１－アミノプロパン－３－オール、Ｎ－エチル－１－アミノプロパン－３－オール、１－アミノブタン－２－オール、Ｎ－メチル－１－アミノブタン－２－オール、Ｎ－エチル－１－アミノブタン－２－オール、２－アミノブタン－１－オール、Ｎ－メチル－２－アミノブタン－１－オール、Ｎ－エチル－２－アミノブタン－１－オール、３－アミノブタン－１－オール、Ｎ－メチル－３－アミノブタン－１－オール、Ｎ－エチル－３－アミノブタン－１－オール、１－アミノブタン－４－オール、Ｎ－メチル１－アミノブタン－４－オール、Ｎ－エチル－１－アミノブタン－４－オール、１－アミノ－２－メチルプロパン－２－オール、２－アミノ－２－メチルプロパン－１－オール、１－アミノペンタン－４－オール、２－アミノ－４－メチルペンタン－１－オール、２－アミノヘキサン－１－オール、３－アミノヘプタン－４－オール、１－アミノオクタン－２－オール、５－アミノオクタン－４－オール、１－アミノプロパン－２，３－ジオール、２－アミノプロパン－１，３－ジオール、トリス（オキシメチル）アミノメタン、１，２－ジアミノプロパン－３－オール、１，３－ジアミノプロパン－２－オール、２－（２－アミノエトキシ）エタノール等が好ましく挙げられる。これらは、１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　これらの中でも、アルカノールアミンとしては、２－アミノエタノール（モノエタノールアミン）および１－アミノ－２－プロパノールからなる群より選択される１種以上が好ましい。
　アルカノールアミンの含有量は、組成物の全量基準で、１．０～５０質量％であることが好ましく、１．５～４５質量％、１．５～４２質量％、２．０～３０質量％あるいは２．０～１５質量％であることがより好ましく、３．０～１２質量％であることがさらに好ましく、４．０～８．０質量％あるいは５．０～９．０質量％などであることが特に好ましい。
　（Ａ－２）第４級アンモニウムヒドロキシド
　組成物に成分（Ａ）として含まれ得る（Ａ－２）第４級アンモニウムヒドロキシドの種類は、特に限定されるものではなく、例えば、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、テトラプロピルアンモニウムヒドロキシド、トリエチルメチルアンモニウムヒドロキシド、エチルトリメチルアンモニウムヒドロキシド、トリメチル（２－ヒドロキシエチル）アンモニウムヒドロキシド、トリエチル（２－ヒドロキシエチル）アンモニウムヒドロキシドが挙げられる。これらは、１種単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　これらの中でも、第４級アンモニウムヒドロキシドとして、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、およびトリエチルメチルアンモニウムヒドロキシドからなる群から選ばれる１種以上が好ましい。
　第４級アンモニウムヒドロキシドの含有量は、組成物の全量基準で、０．３～１２質量％であることが好ましく、０．５～１０質量％であることがより好ましく、１．０～８．０質量％であることがさらに好ましく、１．５～５．０質量％あるいは２．０～６．０質量％などであることが特に好ましい。
　（Ａ－３）無機アルカリ
　　組成物に成分（Ａ）として含まれ得る（Ａ－３）無機アルカリの種類は、特に限定されるものではないが、水酸化リチウム、水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム、炭酸カリウム、ケイ酸ナトリウム、ケイ酸カリウム等のアルカリ金属化合物；水酸化マグネシウム、水酸化カルシウム、炭酸マグネシウム、炭酸カルシウム、ケイ酸カルシウム、ケイ酸マグネシウム等のアルカリ土類金属化合物；水酸化銅、水酸化鉄等の遷移金属化合物；アンモニア等が挙げられる。
　これらの中でも、無機アルカリとして、水酸化カリウム、水酸化ナトリウムなどが好ましい。
　無機アルカリの含有量は、組成物の全量基準で、０．００１～５．０質量％であることが好ましく、０．０１～３．０質量％であることがより好ましく、０．０５～２．０質量％であることがさらに好ましく、０．１～０．５質量％あるいは０．２～１．０質量％などであることが特に好ましい。
＜Ｉ－２．（Ｂ）有機溶剤＞
　組成物は、その合計質量を基準として、０．１～３０質量％の（Ｂ）有機溶剤（以下、成分（Ｂ）ともいう）を含むことが好ましい。組成物における有機溶剤の含有量は、組成物の全量基準で、０．５～２５質量％であることがより好ましく、１．０～２０質量％あるいは１．５～１５質量％であることがさらに好ましく、２．０～１０質量％、２．２～５．０質量％あるいは２．５～４．０質量％などであることが特に好ましい。
　組成物は、有機溶剤として少なくとも、ハンセン溶解度パラメータ（ＨＳＰ）の座標が、δｄ＝１６．０、δｐ＝８．７、δｈ＝１５．５である点（以下、中心点ともいう）を中心とする半径３．６０ＭＰａ０．５以内の球の範囲内にあるもの（以下、特定有機溶剤ともいう）、すなわち、ＨＳＰ座標における中心点からの距離が３．６０ＭＰａ０．５以下である有機溶剤を含む。このように、座標上の中心点からの距離が小さいＨＳＰ値を有する有機溶剤を含む組成物においては、フォトレジストの除去性、特に、水溶液に溶解させるよりもむしろフォトレジストを金属層から効率的に剥離させる性能が向上する効果が認められる。なお、中心点からの距離の算出式を以下に示す。
Figure JPOXMLDOC01-appb-M000001
　レジストの剥離除去の効果が認められる理由として、以下のことが挙げられる。ＨＳＰの座標における上述の中心点からの距離が近いＨＳＰ値を有する特定有機溶剤は、詳細を後述するドライフィルムなどのフォトレジストの成分に対する相溶性が低い傾向にあり、フォトレジストを溶解させる作用は小さいものと考えられる。しかしながら、特定有機溶剤は、ドライフィルムなどのフォトレジストに対するアルカリ剤と水との接触を促進させて、フォトレジストの末端カルボキシ基に対するアルカリ剤の反応を容易にさせ得る。このような特定有機溶剤の作用によって、フォトレジストの末端カルボキシ基とアルカリ剤との中和反応が生じ、フォトレジストと金属層との間に水溶液が浸漬し、フォトレジストが膨潤した状態を容易に生じさせ得る。その結果、膨潤したフォトレジストは表面を覆っていた金属層から容易に剥離される。
　このように、ＨＳＰ値に特徴を有する特定有機溶剤は、異なるＨＳＰ値を有する有機溶剤であって、フォトレジストを溶解させる作用を有する有機溶剤よりも効率的にフォトレジストを除去することが可能であると考えられる。フォトレジストを溶液中に溶解させるにはある程度、長い時間が必要とされるのに対し、フォトレジストが覆っている金属層とフォトレジストとの隙間に浸漬し易い組成物は、フォトレジストのより限定的な範囲に対して作用するだけで剥離による除去を可能とするためである。
　特定有機溶剤としては、ＨＳＰ座標における中心点からの距離が３．３０ＭＰａ０．５以下のものが好ましく、３．００ＭＰａ０．５以下のものがより好ましく、２．７０ＭＰａ０．５以下のものがさらに好ましい。特定有機溶剤として、ＨＳＰ座標における中心点からの距離が２．５０ＭＰａ０．５以下、２．３０ＭＰａ０．５以下、２．００ＭＰａ０．５以下、１．５０ＭＰａ０．５以下あるいは１．００ＭＰａ０．５以下のものを用いてもよい。また、特定有機溶剤として、ＨＳＰ座標における中心点からの距離が、例えば、０．７０ＭＰａ０．５～３．５０ＭＰａ０．５のもの、１．００ＭＰａ０．５～３．３０ＭＰａ０．５のもの、１．５０ＭＰａ０．５～３．００ＭＰａ０．５のもの、２．００ＭＰａ０．５～２．７０ＭＰａ０．５のもの、などを用いてもよい。
　特定有機溶剤の好ましい具体例として、以下のものが挙げられ、表１に、それらの化合物名、ＨＳＰ座標および中心点からの距離の値を示す。
　まず、ＨＳＰ座標における中心点からの距離が１．５０ＭＰａ０．５以下の特定有機溶剤として、エチレングリコールモノメチルエーテル、メチルヒドラジン、２，２，２－トリフルオロエタノールなどのトリフルオロエタノール、ジアセチン、１－クロロ－２－プロパノールなどのクロロプロパノールなどが挙げられる。
　ＨＳＰ座標における中心点からの距離が１．５０ＭＰａ０．５超かつ３．００ＭＰａ０．５以下の特定有機溶剤として、ジメチルアミノエタノール、エチレンジアミン、１，９－ノナンジオールなどのノナンジオール、２－ブロモアリルアルコールなどのブロモアリルアルコール、２，３－ジクロロプロパノールなどのジクロロプロパノール、フルフリルアルコール、アジピン酸、エチレンクロロヒドリン、Ｎ－ホルミルエチルアミン、エチレングリコールモノプロピルエーテル、２－クロロアリルアルコール（２－クロロ－２－プロペン－１－オール）などのクロロアリルアルコール、１－（２－ヒドロキシエチル）－２－ピロリドンなどの２－ヒドロキシエチル基を有する２－ピロリドン、ジエチレングリコールモノビニルエーテル、ジエチレントリアミン、１，３－ジクロロ－２－プロパノールなどのジクロロプロパノール、２－エトキシエタノールなどのエトキシエタノール、３－クロロ－２－プロペン－１－オールなどのクロロアリルアルコール、セロトニン、１，６－ヘキサンジオールなどのヘキサンジオール、２－シクロペンテン－１－オールなどのシクロペンテノール、メチルアミン、ギ酸、エチレングリコールモノイソプロピルエーテル、３－アジドプロペンなどのアジドプロペン、２，３－ブタジエン－１－オール、アリルアルコール、２－フルオロプロペン酸などのフルオロプロペン酸、酢酸、アジドエタン、イソシアン酸、ｎ－プロパノールなどのプロパノール、（Ｅ）－２－ブテン－１－オールなどのブテノール、サリチル酸メチル、２－プロパノールなどのプロパノール、Ｌ－（－）－チロシン、ジプロピレングリコール、カルバミン酸エチル、２，２－ジメチル－１－プロパノールなどが挙げられる。
　さらに、ＨＳＰ座標における中心点からの距離が３．００ＭＰａ０．５超かつ３．６０ＭＰａ０．５以下のものとして、４’－ヒドロキシアセトアニリド、１－ブタノール、１－メトキシメタノール、ジエチレングリコールモノメチルエーテル、３－ヒドロキシテトラヒドロフラン、イソブチルアルコール、２－ブタノール、乳酸エチル、トリエチレングリコールモノメチルエーテル、テトラヒドロフルフリルアルコール、２－ペンタノール、グリセロールホルマール、１－アミノシクロプロパンカルボン酸、１－ペンタノール、グリシドール、２－プロピン－１－オール、１，２－シクロヘキサンジオール、ジエチレングリコールモノエチルエーテル、イソオクチルアルコール、３－クロロ－１－プロパノール、２－メチル－２－ブタノール、サリチル酸、３－メトキシ－３－メチルブタノール、コニフェリルアルコール、シナピルアルコール、アセトンシアノヒドリン、クロトン酸などが挙げられる。
Figure JPOXMLDOC01-appb-T000002
　組成物に含まれる特定有機溶剤として、入手容易性などの観点から、上述の具体例のうちエチレングリコールモノプロピルエーテル（中心点からの距離が２．００ＭＰａ０．５）、ｎ－プロパノール（中心点からの距離が２．６９ＭＰａ０．５）などがより好ましい。
　特定有機溶剤として、１種類のものを用いても、また、２種類以上のものを用いてもよい。また、組成物における成分（Ｂ）有機溶剤として、特定有機溶剤以外のものをふくんでもよい。ただし、組成物における有機溶剤は、有機溶剤の全量基準で、３０質量％以上の特定有機溶剤を含むことが好ましく、５０質量％以上の特定有機溶剤を含むことがより好ましく、７０質量％以上の特定有機溶剤を含むことがさらに好ましく、９０質量％以上の特定有機溶剤を含むことが特に好ましく、有機溶剤として特定有機溶剤のみが組成物に含まれることが一段と好ましい。
＜Ｉ－３．（Ｃ）アゾ―ル化合物＞
　組成物は、その合計質量を基準として、０．００１～１．０質量％の（Ｃ）アゾ―ル化合物（以下、成分（Ｃ）ともいう）を含むことが好ましい。組成物におけるアゾ―ル化合物の含有量は、組成物の全量基準で、０．００５～０．８０質量％であることがより好ましく、０．０１～０．６０質量％あるいは０．０１５～０．７０質量％であることがさらに好ましく、０．０２～０．４０質量％、０．０２５～０．５０質量％あるいは０．０３～０．３０質量％などであることが特に好ましい。
　成分（Ｃ）を含む組成物においては、銅あるいは銅合金を含む金属層を保護し、銅のエッチングレートを低下させる効果が認められる。
　組成物におけるアゾ―ル化合物として、トリアゾール化合物、イミダゾール化合物、ベンゾイミダゾール化合物及びピラゾール化合物の少なくともいずれかを含むことが好ましい。
　トリアゾール化合物として、トリアゾール環を有する化合物であれば特に限定されないが、１，２，３－トリアゾール、１，２，４－トリアゾールのいずれでもよいトリアゾール、炭素数１０以下の置換基を有するトリアゾール、トリアゾール環に縮合した芳香環を有するトリルトリアゾールなどのトリアゾール、これらのトリアゾール塩などが挙げられる。
　イミダゾール化合物として、イミダゾール環を有する化合物であれば特に限定されないが、イミダゾール、炭素数１０以下の置換基を有するイミダゾール誘導体、例えば、１－メチルイミダゾールなどの１－アルキルイミダゾール、４－メチルイミダゾールなどの４－アルキルイミダゾール、２－メルカプト－イミダゾールなどのメルカプト－イミダゾール、これらのイミダゾリウム塩などが挙げられる。
　ベンゾイミダゾール化合物として、ベンゾイミダゾール骨格を有する化合物であれば特に限定されないが、ベンゾイミダゾール、炭素数１０以下の置換基を有するベンゾイミダゾール誘導体、例えば、１－アルキルベンゾイミダゾール、２－アルキルベンゾイミダゾール、７－アルキルベンゾイミダゾール、これらのベンゾイミダゾリウム塩などが挙げられる。
　また、ピラゾール化合物として、ピラゾール、炭素数１０以下の置換基を有するピラゾール、１－メチルピラゾールなどの１－アルキルピラゾール、３－メチルピラゾールなどの３－アルキルピラゾール、４－メチルピラゾールなどの４－アルキルピラゾール、５－メチルピラゾールなどの５－アルキルピラゾール、これらのピラゾール塩などが挙げられる。
＜Ｉ－４．水＞
　組成物は、水を含むことが好ましい。組成物に含まれる水の種類について、特に制限されないが、蒸留、イオン交換処理、フイルター処理、各種吸着処理などによって、金属イオンや有機不純物、パーテイクル粒子などが除去されたものが好ましく、純水がより好ましく、特に超純水が好ましい。
　組成物における水の含有量は、組成物の全量基準で、２０質量％以上が好ましく、より好ましくは２０質量％超であり、２０～９９質量％の範囲であることがより好ましく、さらに好ましくは４０～９７質量％、なお好ましくは６０～９５質量％、特に好ましくは７０～９５質量％である。水の含有量がこのように調整された組成物においては、フォトレジストに対する反応性、フォトレジストの除去性が向上する。
＜Ｉ－５．その他の成分＞
　組成物には、上述の効果を阻害しない範囲で、必要に応じてその他の二次的な成分を含有してもよい。その他の成分としては、ｐＨ調整剤、界面活性剤、消泡剤等が挙げられる。例えば、有機酸（有機酸イオン）、アンモニウムイオンなどを添加してもよい。有機酸、有機酸イオンを組成物に添加すると、ドライフィルムレジストに対する組成物の親和性の向上が図られる。また、アンモニウムイオンを組成物に添加すると、ドライフィルムレジストのカルボキシル基に対する組成物の反応性が向上する。
　また、組成物に、炭酸イオン、炭酸イオンを生じさせる炭酸塩、重炭酸塩などを添加してもよい。組成物に炭酸イオンなどを添加すると、銅防食性の向上が図られる。炭酸塩、重炭酸塩の具体例として、アンモニウムイオンの塩、アルカリ金属あるいはアルカリ土類金属の塩などが挙げられる。
　上述の成分を組み合わせて、安息香酸アンモニウムなどの有機酸アンモニウム塩、炭酸テトラメチルアンモニウムなどの炭酸アンモニウム塩などを組成物に添加してもよい。
　組成物における二次的な成分の含有量は、組成物の全量基準で、１０質量％以下が好ましく、より好ましくは５．０質量％以下であり、３．０質量％以下であることがより好ましく、さらに好ましくは２．０質量％以下、あるいは１．５質量％以下である。
　また、組成物における有機酸（有機酸イオン）、アンモニウムイオン、炭酸イオンを生じさせる塩の各成分の含有量は、それぞれ、好ましくは５．０質量％以下であり、３．０質量％以下であることがより好ましく、さらに好ましくは２．０質量％以下、あるいは１．５質量％以下である。
　なお、組成物は溶解液であることが好ましく、研磨粒子等の固形粒子は含有しない方が好ましい。
＜Ｉ－６．組成物の調製方法＞
　本発明の組成物は、（Ａ）成分、（Ｂ）成分、（Ｃ）成分、水、及び必要に応じて、その他の成分を加えて、好ましくは完全に均一になるまで攪拌することで調整される。組成物を製造するにあたり、各成分の添加、混合の順番については特に限定されない。例えば、（Ａ－１）～（Ａ－３）のいずれかの（Ａ）成分などに若干量の水を添加し、その他の水以外の成分を濃縮液として用意しておき、組成物を使用する現場にてそれらを混合させてもよい。このように濃縮した状態、すなわち水を含まない状態でいずれかの成分を運搬し、水を添加して組成物を調製してもよい。
＜Ｉ－７．組成物の性状＞
　本発明の組成物のｐＨの範囲は特に限定されないが、一態様における組成物のｐＨ値は８以上であり、好ましくは１０以上であり、より好ましくは１１以上である。ｐＨ値は、ｐＨメータを用いる汎用的な方法で測定できる。
　本発明の組成物によれば、銅および銅合金に対するダメージを抑えることが可能である。このため、詳細を実施例の欄にて後述する方法で評価する銅に対するエッチングレートを、０．０５０μｍ／分以下に抑えることが可能となり得る。より好ましくは、詳細を後述する方法で評価する銅のエッチングレートは０．０４０μｍ／分以下であり、さらに好ましくは０．０３０μｍ／分以下であり、特に好ましくは０．０２０μｍ／分あるいは０．０１５μｍ／分以下である。
　本発明の組成物によれば、フォトレジストを効果的に除去することができる。このため、詳細を実施例の欄にて後述する方法で評価する剥離速度に関するＬ．Ｐ．（リフティングポイント）の値を１００秒以下とすることが可能となり得る。より好ましくは、詳細を後述する方法で評価するＬ．Ｐ．の値は９０秒以下であり、さらに好ましくは８５秒以下であり、特に好ましくは８０秒以下あるいは７５秒以下である。
＜Ｉ－８．組成物の使用形態＞
　フォトレジストの除去のために組成物を使用する温度については、特に制限されないが、１０～７０℃の温度が好ましく、より好ましくは２０～６５℃であり、さらに好ましくは２５～６０℃である。このような温度範囲での組成物の使用により、フォトレジストの除去性が良好になるとともに、組成物の組成変化を抑制してフォトレジストの除去条件を容易に保つことができる。
　組成物によるフォトレジストの処理時間については、特に制限されないが、２０～６００秒が好ましく、３０～３００秒がより好ましく、３０～２４０秒であってもよい。処理時間は、組成物をフォトレジストに対して接触させる時間であり、除去対象物であるフォトレジストの表面の状態、組成物の濃度、温度および処理方法等の種々の条件により適宜選択すればよい。
　フォトレジストに本発明の組成物を接触させる方法については、特に制限されない。例えば本発明の組成物を、滴下（枚葉スピン処理）またはスプレー噴霧などの形式により除去対象物であるフォトレジストに接触させる方法、または除去対象物であるフォトレジストを本発明の組成物に浸漬させる方法などの方法を採用することができる。本発明においては、いずれの方法を採用してもよい。
＜ＩＩ．フォトレジストの除去方法＞
　本発明のフォトレジストの除去方法は、上述の本発明の組成物を、銅を含むパターンを形成するためのフォトレジストに対して接触させるフォトレジスト除去工程を含む。以下に、フォトレジストの除去方法について説明する。
　本発明の組成物は、例えば、銅配線を少なくとも一部に有する絶縁層上に、銅配線の接続端子部となる銅を含む回路パターンを形成するためのフォトレジストを、回路パターン形成後に除去する際に好適に用いることができる。
　ここで、「銅配線を少なくとも一部に有する絶縁層」とは、銅配線が表面または内部に埋め込まれた絶縁層であれば特に限定されなく、例えば、プリント配線板、半導体素子搭載用パッケージ基板、半導体ウェハのシリコン絶縁層などが挙げられる。
　また、「銅配線の接続端子部となる銅を含む回路パターン」とは、例えば、絶縁層が有する銅配線の接続端子部として、他の部材との電気的接続を行うためのものである。
　本発明の一実施態様において、接続端子部は、プリント配線板における銅配線の接続端子部である。また、本発明の一実施態様において、接続端子部は、半導体素子搭載用パッケージ基板における銅配線の接続端子部である。また、本発明の一実施態様において、接続端子部は、半導体素子における銅配線の接続端子部である。
＜ＩＩＩ．プリント配線等の製造方法＞
　本発明のプリント配線等の製造方法は、本発明の組成物を、銅を含むパターンを形成するためのフォトレジストに対して接触させるフォトレジスト除去工程を含む。プリント配線板の他に、半導体素子、半導体パッケージの製造方法におけるフォトレジスト除去工程でも、本発明の組成物が好適に用いられ得る。
　例えば、本発明の組成物は、プリント配線板（例えば半導体素子搭載用パッケージ基板）の製造工程において、銅配線を少なくとも一部に有する絶縁層上に、銅配線の接続端子部となる銅を含む回路パターンを形成するためのフォトレジストを、回路パターン形成後に除去する際に好適に用いることができる。
　また、本発明の組成物は、半導体素子の製造工程において、銅配線を少なくとも一部に有する絶縁層上に、銅配線の接続端子部となる銅、ならびに、錫および錫合金からなる群より選ばれる少なくとも１種を含む回路パターンを形成するためのフォトレジストを、回路パターン形成後に除去する際に好適に用いることができる。
　プリント配線板に用いられるフォトレジストとしては、たとえば、バインダーポリマー、光重合性モノマー、光重合開始剤およびその他添加剤を含む組成物が挙げられる。
　バインダーポリマーとしては、たとえばメタクリル酸およびアクリル酸の少なくとも１種を必須成分として、メタクリル酸エステル、アクリル酸エステル、スチレンなどの数種類のビニルモノマーを共重合して得られるものが挙げられる。
　光重合性モノマーとしては、メタクリル酸エステルおよびアクリル酸エステルの少なくとも１種が好ましく挙げられる。
　光重合開始剤としては、ベンゾフェノン、４，４’－ジアミノベンゾフェノン、４，４’－ビス（ジメチルアミノ）ベンゾフェノン、２－エチルアントラキノン、ベンゾイン、ベンゾインメチルエーテル、９－フェニルアクリジン、ベンジルジメチルケタール、ベンジルジエチルケタールからなる群の少なくとも１種が挙げられる。また、ヘキサアリールビイミダゾールと水素供与体（２－メルカプトベンゾキサザール、Ｎ－フェニルグリシン）からなる二分子系を用いてもよい。
　また、その他の添加剤としては、熱重合開始剤や染料などが挙げられる。
　半導体素子に用いられるフォトレジストとしては、フェノール－ホルムアルデヒド樹脂（「ノボラック樹脂」と総称される）と、感光成分であるナフトキノンジアジド化合物の組み合わせなどが好ましく挙げられる。
　また、金属配線間に配置されるレジストとしては、ドライフィルムレジスト、液体レジスト等が挙げられる。これらのうち、レジストは、ドライフィルムレジストであることが好ましい。ドライフィルムレジストとしては、特に制限されないが、感光性樹脂から形成されるものであることが好ましい。感光性樹脂としては、ネガ型感光性樹脂およびポジ型感光性樹脂が挙げられる。
　ネガ型感光性樹脂としては、特に制限されないが、アジド系感光性樹脂、ジアゾ系感光性樹脂、アセチレン性低分子系感光性樹脂、エチレン性低分子系感光性樹脂、不溶化高分子系感光性樹脂、クロム酸系感光性樹脂が挙げられる。これらのネガ型感光性樹脂は単独で用いても、２種以上を組み合わせて用いてもよい。
　ポジ型感光性樹脂としては、特に制限されないが、キノンジアジド系感光性樹脂、可溶化高分子系感光性樹脂等が挙げられる。これらのポジ型感光性樹脂は単独で用いても、２種以上を組み合わせて用いてもよい。
　これらのうち、ドライフィルムレジストは、ネガ型感光性樹脂から形成されることが好ましい。ネガ型感光性樹脂は、パターン形成時の露光処理によって硬化が進行して現像液に不溶となるため、露光処理部分（ネガ型感光性樹脂が硬化した部分）がドライフィルムレジストとして残存する。ここで、露光の際にはネガ型感光性樹脂は、特に露光に暴露される表面部分の硬化が進行しやすく、得られるドライフィルムレジストの表面部分は特に密な構造を有しうる。このため、組成物によってドライフィルムレジストを除去しようとしても、組成物がドライフィルムレジスト内部に浸透しづらいことがある。また、組成物によってはレジスト除去能が十分ではないため、ドライフィルムレジストの除去が進行しないことがある。その結果、ドライフィルムレジストの除去に時間を要することがある。
　これに対し、本発明の組成物はドライフィルムレジストに浸透しやすいため、ドライフィルムレジストの剥離除去を迅速に行うことができる。
（剥離性評価用サンプルの作成）
　剥離性評価用サンプルを以下のように作成した。まず、銅張積層板（三菱ガス化学株式会社製、ＣＣＬ－ＨＬ８３２ＮＳ（ＭＴ－ＦＬ）０．１ｍｍｔＣ／Ｃ）上に、化学銅メッキを施し、銅薄膜（厚み：１．０μｍ）を製膜した。この銅薄膜の表面にドライフィルムレジスト（昭和電工株式会社製、ＲＤ－３０２５、厚み：２５μｍ）を付着させ、その上に回路マスクパターンを施し、露光現像した。ドライフィルムレジストを露光現像して形成された回路パターン開口部に電気銅メッキ（厚み：１７μｍ）を施して、剥離性評価用サンプルを得た。剥離性評価用サンプルに施されたドライフィルムレジストのパターンは、１００～３００μｍφのドットである。
（銅防食性評価用サンプルの作成）
　銅防食性評価用サンプルを以下のように作成した。すなわち、銅張積層板（三菱ガス化学株式会社製、ＣＣＬ－ＨＬ８３２ＮＸ）の表面に電気銅メッキ（厚み：３５μｍ）を施して、銅防食性評価用サンプルを得た。
（剥離速度（Ｌ．Ｐ．（リフティングポイント）））
　上述の剥離性評価用サンプルに、実施例及び比較例に記載の水性組成物を、スプレー圧０．１５ＭＰａ、５０℃でスプレー噴霧して接触させた。
　そして、水性組成物のスプレー噴射したときから、ドライフィルムレジストが剥離性評価用サンプルの基板から完全にはがれるまでの時間を測定し、Ｌ．Ｐ（秒）とした。なお、Ｌ．Ｐ．の測定においては、剥離性評価用サンプルに施されたドットパターン部ではなく、その外周のベタ部を目視で観察し、ドライフィルムレジストが除去された時間とした。
（銅防食性（Ｃｕ Ｅ．Ｒ．（エッチングレート）））
　４ｃｍ×４ｃｍ角にカットした上述の銅防食性評価用サンプルに、実施例及び比較例に記載の水性組成物を、スプレー圧０．１５ＭＰａ、５０℃、５分間スプレー噴霧して接触させた。次いで、純水での水洗、５質量％硫酸での洗浄、純水での水洗を行った後、銅防食性評価用サンプルを十分に乾燥させた。
　Ｃｕ Ｅ．Ｒ．（μｍ／分）の値は、以下のように算出した。すなわち、上述の水性組成物の噴霧処理の前後の銅防食性評価用サンプル質量を測定し、その質量差と銅の密度（８．９３ｇ／ｃｍ３）、およびサンプルサイズ（処理面積［ｃｍ２］、なお、銅防食性評価用サンプルの裏面はマスキングテープで保護したため、処理面積はサンプル表面の面積である）から、エッチングされた厚みを算出して、１分間当たりのエッチング量を以下の式（Ｉ）により求めた。
Figure JPOXMLDOC01-appb-M000003
（剥離性）
　上述の剥離性評価用サンプルに、実施例及び比較例に記載の水性組成物を、スプレー圧０．１５ＭＰａ、５０℃、３分間スプレー噴霧して接触させた。次いで、純水での水洗、５質量％硫酸での洗浄、純水での水洗を行った後、十分に乾燥した。
　剥離性の評価は、以下のように行った。すなわち、光学顕微鏡（オリンパス株式会社製、ＭＸ－６１Ｌ対物レンズ５０倍）を使用し、上述の水性組成物の噴霧処理後の剥離性評価用サンプルのドライフィルムレジストの残渣を確認し、以下の基準に則って評価した。
　特に良好：１００～３００μｍφのドライフィルムレジストの残渣がいずれも５以下
　良好　　：１００～３００μｍφのドライフィルムレジストの残渣がいずれも１１０以下
　不良　　：１００～３００μｍφのドライフィルムレジストの残渣が１１０を超えるものがある
［実施例１］
　２４３ｇの純水に、モノエタノールアミン（ＭＥＡ）を最終的に６質量％となる量（７５％のＭＥＡ水溶液を３２ｇ）、テトラメチルアンモニウムヒドロキシド（ＴＭＡＨ）を最終的に４質量％となる量（２５％のＴＭＡＨ水溶液を６４ｇ）、水酸化カリウム（ＫＯＨ）を最終的に０．３質量％となる量（５０％ＫＯＨ水溶液を２．４ｇ）、エチレングリコールモノプロピルエーテルを最終的に２質量％となる量（８．０ｇ）、トリルトリアゾールを最終的に０．０９質量％となる量（０．３６ｇ）、安息香酸アンモニウムを最終的に１．５質量％となる量（６．０ｇ）、テトラメチルアンモニウム重炭酸塩（ＴＭＢＣ）を最終的に１１質量％となる量（４４ｇ）、それぞれ添加した水性組成物を準備した。得られた水性組成物のＬ．Ｐ．は６０ｓｅｃ、Ｃｕ Ｅ．Ｒ．は０．００７μｍ／ｍｉｎ、剥離性は特に良好であった。
　なお、テトラメチルアンモニウム重炭酸塩は、テトラメチルアンモニウムヒドロキシドの劣化物として生じ得るものであって、水性組成物によるドライフィルムレジストの剥離性能を低下させ得る。このため、長期間に渡り使用されてテトラメチルアンモニウム重炭酸塩が生じた場合の水性組成物による剥離処理を評価すべく、本実施例の水性組成物に当該重炭酸塩を添加した。
　水性組成物の性状と評価結果を下記表２に示す。
［実施例２～５及び比較例１～８］
　下記表２に示す通り、実施例１の組成物における各成分の種類及び量のいずれかを変更した他は、実施例１と同様に水性組成物を調製し、評価試験を行った。各実施例及び比較例の水性組成物の性状と評価結果を下記表２に示す。
　表２には、各実施例及び比較例の水性組成物に含まれた有機溶剤のハンセン溶解度パラメータの座標における中心点（δｄ＝１６、δｐ＝８．７、δｈ＝１５．５）からの距離が示されており、表３には、より詳細に、有機溶剤のハンセン溶解度パラメータの座標における位置が示されている。
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-T000005
　以上の結果から明らかであるように、ハンセン溶解度パラメータの座標における中心点（δｄ＝１６、δｐ＝８．７、δｈ＝１５．５）からの距離が近い有機溶剤を含む実施例の水性組成物によれば（表２の「中心点からの距離［ＭＰａ０．５］」欄及び表３参照）、比較例の水性組成物に比べ、Ｌ．Ｐ．（リフティングポイント）の値が示す時間が短く、フォトレジストを迅速に剥離できるとともに、レジストの残渣の発生を抑制できることが確認された。また、実施例においては、比較例に比べてＣｕ Ｅ．Ｒ．（エッチングレート）の値が低い傾向にあり、銅防食性に優れているという結果が得られた。 

Claims (11)

  1. 　銅を含むパターンを形成するためのフォトレジストを、前記パターンの形成後に除去するための組成物であって、
    　アルカノールアミン、第４級アンモニウムヒドロキシド、および無機アルカリからなる群から選択される少なくとも１種を含む、アルカリ剤と、
    　ハンセン溶解度パラメータの座標が、δｄ＝１６．０、δｐ＝８．７、δｈ＝１５．５を中心とする半径３．６０ＭＰａ０．５以内の球の範囲内にある有機溶剤と、
    　アゾール化合物と、
    を含む、組成物。
  2. 　前記有機溶剤のハンセン溶解度パラメータの座標が、δｄ＝１６．０、δｐ＝８．７、δｈ＝１５．５を中心とする半径３．００ＭＰａ０．５以内の球の範囲内にある、請求項１に記載の組成物。
  3. 　前記有機溶剤が、エチレングリコールモノメチルエーテル、メチルヒドラジン、２，２，２－トリフルオロエタノール、ジアセチン、１－クロロ－２－プロパノール、ジメチルアミノエタノール、エチレンジアミン、１，９－ノナンジオール、２－ブロモアリルアルコール、２，３－ジクロロプロパノール、フルフリルアルコール、アジピン酸、エチレンクロロヒドリン、Ｎ－ホルミルエチルアミン、エチレングリコールモノプロピルエーテル、２－クロロ－２－プロペン－１－オール、１－（２－ヒドロキシエチル）－２－ピロリドン、ジエチレングリコールモノビニルエーテル、ジエチレントリアミン、１，３－ジクロロ－２－プロパノール、２－エトキシエタノール、３－クロロ－２－プロペン－１－オール、セロトニン、１，６－ヘキサンジオール、２－シクロペンテン－１－オール、メチルアミン、ギ酸、エチレングリコールモノイソプロピルエーテル、３－アジドプロペン、２，３－ブタジエン－１－オール、アリルアルコール、２－フルオロプロペン酸、酢酸、アジドエタン、イソシアン酸、ｎ－プロパノール、（Ｅ）－２－ブテン－１－オール、サリチル酸メチル、２－プロパノール、Ｌ－（－）－チロシン、ジプロピレングリコール、カルバミン酸エチル、および２，２－ジメチル－１－プロパノールからなる群から選択される少なくとも１種を含む、請求項１に記載の組成物。
  4. 　銅のエッチングレートが、０．０５μｍ／ｍｉｎ未満である、請求項１に記載の組成物。
  5. 　水溶性である、請求項１に記載の組成物。
  6. 　前記組成物が、前記組成物の全量基準で、
    　３．０～５０質量％の前記アルカリ剤、
    　０．１～３０質量％の前記有機溶剤、及び、
    　０．００１～１．０質量％の前記アゾール化合物を含む、
    請求項１に記載の組成物。
  7. 　前記パターンが、銅配線を少なくとも一部に有する絶縁層上に形成される前記銅配線の接続端子部となる回路パターンである、請求項１に記載の組成物。
  8. 　銅を含むパターンを形成するためのフォトレジストに対して、請求項１～７のいずれか１項に記載の組成物を接触させるフォトレジスト除去工程を含む、フォトレジストの除去方法。
  9. 　前記パターンが、銅配線を少なくとも一部に有する絶縁層上に形成される前記銅配線の接続端子部となる回路パターンである、請求項８に記載のフォトレジストの除去方法。
  10. 　銅を含むパターンを形成するためのフォトレジストに対して、請求項１～７のいずれか１項に記載の組成物を接触させるフォトレジスト除去工程を含む、プリント配線板、半導体素子、又は半導体パッケージの製造方法。
  11. 　前記パターンが、銅配線を少なくとも一部に有する絶縁層上に形成される前記銅配線の接続端子部となる回路パターンである、請求項１０に記載のプリント配線板、半導体素子、又は半導体パッケージの製造方法。 
PCT/JP2023/044366 2022-12-12 2023-12-12 フォトレジスト除去用組成物およびフォトレジストの除去方法 WO2024128209A1 (ja)